• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.5
• /
• pp.33-39
• /
• 1998

The BST (Ba$_{1-x}$ Sr$_{x}$TiO$_{3}$)(50/50) thin film has been grown by RF magnetron reactive sputtering and its characteristics such as crystallization, surface roughness, and electrical properties have been investigated with varying the film thickness. The crystallization and surface roughness of BST thin film are investigated by using XRD and AFM, respectively The BST thin film anealed at 800.deg. C for 2 min has pure perovskite structure and good surface roughness of 16.1.angs.. We estimate that the thickness and dielectric constant of interface layer between BST film and electrode are 3nm and 18.9, respectively, by measuring the capacitance with various film thickness. As the film thickness increases form 80nm to 240nm, the dielectric constant at 10kHz increases from 199 to 265 and the leakage current density at 200kV/cm decreases from 0.682.mu.A/cm$^{2}$ to 0.181 .mu.A/cm$^{2}$. In the case of 240nm-thick BST thin film, the charge storage density and leakage current density at 5V are 50.5fC/.mu.m$^{2}$ and 0.182.mu.A/cm$^{2}$, respectively. The values indicate that the BST thin film is a very useful dielectric material for the DRAM capacitor.or.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.4
• /
• pp.63-69
• /
• 1999

The electrical properties of rf-magnetron sputtered $Ba_{0.5}Sr_{0.3}TiO_3$ (BST) capacitors were investigated by varying annealing temperature and atmosphere of the rapid thermal annealing (RTA). The electrical properties of Pt/BST/Pt capacitors were found to strongly depend on the RTA condition. It seems that the dependence of the electrical properties of the Pt/BST/Pt capacitors on the RTA condition is related to the oxygen vacancies in BST thin films. In order to clarify the relation between the oxygen vacancies and the electrical properties of Pt/BST/Pt capacitors, we have examined the two different annealing methods. One annealing method was performed in $O_2$ gas and the other was done in $O_2$-plasma at the same condition of 450$^{\circ}C$, 20 mtorr. It was found that the leakage current densities of $O_2$-plasma annealed capacitor were much lower than those of $O_2$ annealed capacitor. The dielectric constants of $O_2$ annealed capacitor decreased about 14% comparing with those of as-deposited. In contrast, there was no decrease in the dielectric constant of $O_2$-plasma annealed. These results indicate that $O_2$-plasma annealing is very effective in compensation the oxygen vacancies in BST thin films. It can be also concluded that the oxygen vacancies greatly affect the electrical properties of Pt/BST/Pt capacitors.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.6
• /
• pp.120-126
• /
• 1996

In the present study, we have studied on the characteristics of BST thin films with various Ba/Sr ratios by using sol-gel method. Barium-acetate, strontium-acetate and titanium isopropoxide are used as starting materials to fabricate BST thin films by sol-gel method. The fabrication conditions are estabilished through the TG-dT analyses and XRD measurements. BST thin films with the Ba/Sr ratios of 90/10, 70/30, 50/50 and 30/70 were deposited on the Pt/Ta/SiO$_{2}$Si substrate with the estabilished sol-gel process, and their characteristics were examined. The relative permittivity and the leakage current density at 5V vary from 287 to 395 and from 2.3 to 220${\mu}$A/cm$^{2}$, respectively, with various Ba/Sr ratio. Among the films investigatd in this research, BST (70/30) thin film shows the best relative permittivity and dielectric loss of BST (70/30) thin film are 395 and 0.045, respectively and the leakage current density at 5V is 2.3${\mu}$A/cm$^{2}$.

• Journal of Food Hygiene and Safety
• /
• v.5 no.4
• /
• pp.179-186
• /
• 1990

This study was performed for assessing carcinogenicity of several synthetic hormones; Diethylstilbesterol (DES), 17-ethinylestradiol ($EE_2$) and Bovine somatotrophin (BST). Six weeks old F344 rats were divided into five groups and given an intraperitoneally injection of 200 mg of diethylnitrosamine (DENA). At two week after beginnig of experiment, DES, $EE_2$, BST. Phenobarbital were administered to group 1, 2, 3 and 4 respectively, group 4 is positive control and group 5 is negative control. At the same time, all groups received a single i.p. injection of D-galactosamine at a dose of 300 mg/kg and underwent 2/3 partial hepatectomy at week 5. All rats were sacrificed at the end of week 8 for assessment of liver lesion development. The liver was processed for immunohistochmical staining for GST-P and quantitatively analyzed by image analyzer. It was concluded that two synthetic estrogen hormones (DES, $EE_2$) was different significantly (p < 0.01) but BST was not different as compared with control group. Therefore, we thought that DES, $EE_2$ was promoting effects and BST was not in rat hepatocarcinogenesis.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05b
• /
• pp.103-106
• /
• 2002

The applicability of models based on fractal morphology to characterize $(Ba\;Sr)TiO_{3}$ thin film surfaces was investigated. The fractal morphology of coated barium strontium titan oxide thin film surfaces was described using fractal dimension from scanning electro microscopy image. The $(Ba\;Sr)TiO_{3}$ coating were deposited on silicon wafers using $(Ba\;Sr)TiO_{3}$ solution and spin coater. BST solution was composited by mol ratio, and then spin-coated from 3 times to 5 times coating on $Pt/SiO_{2}/Si$ substrate. Qualitative thin film analysis was performed with scanning electro microscopy (SEM), and surfaces parameters such as average grain diameter, roughness exponent and fractal dimension were determined.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.329-332
• /
• 1999

In this paper, BST((Bao.&o,dTi0:3) thin films were deposited by the rf magnetron sputtering method on Pt/$SiO_2$/Si substrate. Pt, $RuO_2$, Ag, Cu films for the formation of top electrode were deposited on BST thm films. And then Top Electrodes/BST/Pt capacitors were annealed with rapid thermal annealing(RTA) at various temperature. We have investigated effect of post-annealing on the electrical properties such as dielectric constant and leakage current of the capacitors. It was found that electrical properties of the capacitors were greatly depended on the annealing temperatures as well as the materials of top electrodes. In BST thin films with Pt top electrode was annealed at $700^{\circ}C$. the dielectric constant was measured to the value of 346 at l[kHzl and the leakage current was obtained to the value of $8.76\times10^8$[A/$\textrm{cm}^2$] at the forward bias of 2[V].

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.6
• /
• pp.44-51
• /
• 1999

The electrical conduction mechanism of high dielectric $(Ba,Sr)TiO_3$ (BST) thin film capacitor, which is the promising cell capacitor for high density DRAM, was investigated in low field region (<0.2MV/cm). It is known that the current in the low field region consists of dielectric relaxation current and leakage current. The current-time (I-t) measurement technique under the constant voltage was used for extracting successfully each current component. The conduction mechanism of the BST capacitor was deduced from the dependency of the current on the measurement temperature, strength of electric field, the polarity of applied electric field and post annealing process. From these results, it was suggested that the dielectric relaxation current and the leakage current are originated from the redistribution of internally trapped electron by hopping process and Pool-Frenkel conduction mechanism, respectively. It was also concluded that traps causing these two current components are due to oxygen vacancies within the BST film.

• Journal of Powder Materials
• /
• v.30 no.4
• /
• pp.318-323
• /
• 2023

The thermoelectric effect, which converts waste heat into electricity, holds promise as a renewable energy technology. Recently, bismuth telluride (Bi2Te3)-based alloys are being recognized as important materials for practical applications in the temperature range from room temperature to 500 K. However, conventional sintering processes impose limitations on shape-changeable and tailorable Bi₂Te₃ materials. To overcome these issues, three-dimensional (3D) printing (additive manufacturing) is being adopted. Although some research results have been reported, relatively few studies on 3D printed thermoelectric materials are being carried out. In this study, we utilize extrusion 3D printing to manufacture n-type Bi_1.7Sb_0.3Te₃ (N-BST). The ink is produced without using organic binders, which could negatively influence its thermoelectric properties. Furthermore, we introduce graphene oxide (GO) at the crystal interface to enhance the electrical properties. The formed N-BST composites exhibit significantly improved electrical conductivity and a higher Seebeck coefficient as the GO content increases. Therefore, we propose that the combination of the extrusion 3D printing process (Direct Ink Writing, DIW) and the incorporation of GO into N-BST offers a convenient and effective approach for achieving higher thermoelectric efficiency.

• Biomolecules & Therapeutics
• /
• v.19 no.2
• /
• pp.211-217
• /
• 2011

Panax ginseng CA Meyer, a herb from the Araliaceae, has traditionally been used as a medicinal plant in Asian countries. Ginseng extract fermented by ginsenoside-${\beta}$-glucosidase treatment is enriched in ginsenosides such as Rh2 and Rg3. Here we show that a fermented ginseng extract, BST204, has anti-proliferative and anti-invasive effects on HT-29 human colon cancer cells. Treatment of HT-29 cells with BST204 induced cell cycle arrest at $G_1$ phase without progression to apoptosis. This cell cycle arrest was accompanied by up-regulation of tumor suppressor proteins, p53 and p21$^{WAF1/Cip1}$, down-regulation of the cyclin-dependent kinase/cyclins, Cdk2, cyclin E, and cyclin D1 involved in $G_1$ or $G_1/S$ transition, and decrease in the phosphorylated form of retinoblastoma protein. In addition, BST204 suppressed the migration of HT-29 cells induced by 12-O-tetradecanoylphorbol-13-acetate, which correlated with the inhibition of metalloproteinase-9 activity and extracellular signal-regulated kinase activity. The effects of BST204 on the proliferation and the invasiveness of HT-29 cells were similar to those of Rh2. Taken together, the results suggest that fermentation of ginseng extract with ginsenoside-${\beta}$-glucosidase enhanced the anti-proliferative and the anti-invasive activity against human colon cancer cells and these anti-tumor effects of BST204 might be mediated in part by enriched Rh2.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.263-266
• /
• 2001

In this paper, we investigated dielectric properies for BST thin films that was deposited on MgO/Si substrates using RF magnetron sputtering. In here, MgO film was used to perform that a diffusion b arrier between the BST film and Si substrate and a buffer layer to assist the BST film growth. A d eposition condition for MgO films was RF Power of 50W, substrate temperature of room temperature and the working gas ratio of Ar:O$_2$ were varied from 90:10 to 60:47. Finally we manufactured the cap acitor of Al/BST/MgO/Si/Al structure to know electrical properties of this capacitor through I-V, C-V measurement. In the results, C-V aha racteristic curves was shown a ferroelectric property so we measured P-E. A remanent poliazation and coerceive electric field was present 2$\mu$C/cm$^2$ and -27kV/cm respectively at Ar:O$_2$=90:10. And a va clue of dielectric constant was 86 at Ar:02=90:10.