• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.49-54
• /
• 2000

The new green $Al_3GdB_4O_{12}:Tb^{3+} and red Al_3GdB_4O_{12}:Eu_{3+}$ phosphors were synthesized and then characterized their optical properties for PDP application. And also the photoluminescence properties of these phosphors were compared with the commercial green $Zn_2SiO_4:Mn^{2+} and (Y,Gd)BO_3: Eu^{3+}$ red PDP phosphors. The phosphors were synthesized by solid state reaction at 115$0^{\circ}C$ for 4hr. It was found that the emitting brightness of $Al_3GdB_4O_{12}:Tb^{3+}$(15mol%) green phosphor under 147nm excitation was higher than that of commercial $Zn_2SiO_4: Mn^{2+}$ green PDP phosphor. However, the color coordinate of this new green phosphor was inferior to the commercial one. On the other hand, the emitting intensity of $Al_3GdB_4O_{12}:Eu^{3+}$(15mol%) red phosphor was smaller than the $commercial(Y,Gd)BO_3: Eu^{3+}$ red one, but the CIE coordinate was slightly improved. The excitation spectrum showed that $Al_3GdB_4O_{12}$ phosphors had a strong excitation band at $\lambda=160nm$ associated with the host absorption. And the photoluminance excitation (PLE) intensity in VUV range for $Al_3GdB_4O_{12}:Tb^{3+}$ green phosphor was higher than that of $Zn_2SiO_4: Mn^{2+}$, but the PLE intensity of $Al_3GdB_4O_{12}:Eu^{3+}$ red phosphor was smaller than $(Y,Gd)BO_3: Eu^{3+}$.

• Journal of the Korean Society of Radiology
• /
• v.7 no.6
• /
• pp.403-408
• /
• 2013

This study made a tentative estimation of the shielding rate of barium compound by thickness through monte carlo simulation to apply medical radiation shielding products that can replace existing lead. Barium sulfate($BaSO_4$) was used for the shielding material, and thickness of the shielding material specimen was simulated from 0.1 mm to 5 mm by applying $15{\times}15cm^2$ of specimen area, $4.5g/cm^3$ of density of barium sulfate, and $11.34g/cm^3$ density of lead. Entered source was simulated with 10kVp Step in consecutive X-ray energy spectrum(40 kVp ~ 120 kVp). Absorption probability in 40 kVp ~ 60 kVp showed same shielding rate with lead in 3 mm ~ 5 mm of thickness, but it was identified that under 2 mm, the shielding rate was a bit lower than the existing lead shielding material. Also, the shielding rate in 70 kVp ~ 120 kVp energy band showed similar performance as the existing lead shielding material, but it was tentatively estimated as fairly low shielding rate below 0.5 mm. This study estimated the shielding rate of barium compound as the thickness function of x-ray energy band for medical radiation through monte carlo simulation, and made comparative analysis with existing lead. Also, this study intended to verify application validity of the x-ray shielding material for medical radiation of pure barium sulfate. As a result, it was estimated that the shielding effect was 95% higher than the existing lead 1.5 mm in at least 2 mm thickness of barium compound in medical radiation energy band 70 kVp ~ 120 kVp, and this result is considered valid to be provided as a base data in weight lightening production of radiation shielding product for medical radiation.

• Progress in Medical Physics
• /
• v.12 no.1
• /
• pp.51-58
• /
• 2001

Synchrotron radiation (SR) has several advantages over convetional x-rays, including its phase, collimation, and high flux. A synchrotron radiation beamline 5C1 at Pohang Light Source (PLS) was recently built for imaging applications. We have shown that a SR imaging system is useful in imaging microscopic structures. SR with broad-band energy spectrum were adjusted to an object by Si wafers and their energy were approximately ranging from 6 keV to 30 keV. SR were passed through an object and finally transformed into visible lights by CdWO$_4$ scintillator screen. The visible lights which were reflected at an angle of 90 degrees by gold plated mirror were detected by a CCD camera and the image data were acquired using image acquisition system. A high-resolution phantom, capacitor, adult tooth, child tooth, cancerous breast tissue, and mouse lumbar vertebra were imaged with SR imaging system. The Objects were rotated within the field of view of the CCD detector, and their projection image data were obtained at 250 steps over 180 degrees rotation. Image reconstructions were carried out in a PC by using IDLTM(Research systems, Inc., US) program. The spatial resolution of the images acquired by the SR imaging system was measured with a high-resolution chart manufactured for several micrometer resolution. The specimens were also imaged with conventional x-ray radiography system to compare the image quality of radiography obtained with the SR imaging system. The results showed more structural details and high contrast images with SR imaging system than conventional x-ray radiography system. The SR imaging system may have a potential for imaging in biological researches, material applications, and clinical radiography.

• Progress in Medical Physics
• /
• v.21 no.2
• /
• pp.232-237
• /
• 2010

The shielding materials designed for replacement of lead equivalent materials for lighter apron than that of lead in diagnostic photon beams. The absorption characteristics of elements were applied to investigate the lead free material for design the shielding materials through the 50 kVp to 110 kVp x-ray energy in interval of 20 kVp respectively. The idea focused to the effect of K-edge absorption of variable elements excluding the lead material for weight reduction. The designed shielding materials composited of Tin 34.1%, Antimon 33.8% and Iodine 26.8% and Polyisoprene 5.3% gram weight account for 84 percent of weight of lead equivalent of 0.5 mm thickness. The size of lead-free shielder was $200{\times}200{\times}1.5\;mm^3$ and $3.2\;g/cm^3$ of density which is equivalent to 0.42 mm of Pb. The lead equivalent of 0.5 mm thickness generally used for shielding apron of diagnostic X rays which is transmitted 0.1% for 50 kVp, 0.9% for 70 kVp and 3.2% for 90 kVp and 4.8% for 110 kVp in experimental measurements. The experiment of transmittance for lead-free shielder has showed 0.3% for 50 kVp, 0.6% for 70 kVp, 2.0% for 90 kVp and 4.2% for 110 kVp within ${\pm}0.1%$. respectively. Using the attenuation coefficient of experiments for 0.5 mm Pb equivalent of lead-free materials showed 0.1%. 0.3%, 1.0% and 2.4%, respectively. Furthermore, the transmittance of lead-free shielder for scatter rays has showed the 2.4% in operation energy of 50 kVp and 5.9% in energy of 110 kVp against 2.4% and 5.1% for standard lead thickness within ${\pm}0.2%$ discrepancy, respectively. In this experiment shows the designed lead-free shielder is very effective for reduction the apron weight in diagnostic radiation fields.

• Korean Journal of Agricultural Science
• /
• v.12 no.1
• /
• pp.47-54
• /
• 1985

An investigation was made to find regional differences and seed characteristics of buckwheats collected from 36 areas in Chungnam province in 1984, and the results obtained are summarized as follows; 1. Grain types of the collected buckwheats were classified as winged, semi-winged and common types. All collections were on the average composed of 50.1 % of common grain types, 26.8 % of semi-winged type and 23.1 % of winged types, respectively. However, there was a great regional difference in components of each grain type among collections. 2. The mean 1000 grain weight was 24.9 gr. The regional differences in 1000 grain weight showed that a collection (collection no. 30) from Susan was 17.4 gr and a collection (collection. no. 16) from Suchon was 31.9 gr. There wasn't any significant relationship between grain types component and 1000 grain weight. 3. Germination of seeds was accelerated as temperature goes up from $5^{\circ}C$ to $30^{\circ}C$. However, interesting germination pattern was observed. That is, seeds from Suchon (collection no. 16), Hongsung (collection no. 23), Cheonweon(collection no. 35), and Yesan (collection no. 27) showed abrupt decrease of germination rate at the temperature of $15^{\circ}C$. The seeds collected from Suchon (collection no. 29), Dangjin (collection no. 32) and from Chungyang (collection no. 21) showed decrease of germination rate at $25^{\circ}C$. These seeds showed, however, the increase of germination percentage at temperature higher than $15^{\circ}C$ and $25^{\circ}C$, respectively. The germination rate for the most collections at $5^{\circ}C$ was less than 10%. However, seeds from Asan (collection no. 33) and Daeduk (collection no. 3) showed 20% and 30% of germination rate at $5^{\circ}C$, respectively. 4. Color of seed coat could be classified into two maj or colors, dark and dark brown. Based on the seed coat color and grain types, all the collections could be classified into the following six categories: winged-black, semi-winged-black, common-black, winged-dark brown, semi-winged dark brown and common-dark brown. The different light absorption rate was found within the UV light zone (190-390 nm) depending upon the two different major seed coat color.

• Korean Journal of Food Science and Technology
• /
• v.28 no.2
• /
• pp.345-351
• /
• 1996

Studies on extraction and color characteristics of purple sweet potato (PSP) pigment were performed to provide the basic information for the utilization of PSP as a new source of natural food colorant. PSP pigment was extracted well with the polar solvents such as distilled water, ethanol, and methanol. but hardly extracted with the non-polar solvents. Among the tested solvents, 20% ethanol solution containing 0.1% citric acid was found to be the most efficient for extraction of the pigment from PSP. PSP contained high amount of pigment not only in the epidermis but also in the flesh of the potato. The PSP pigment was heat stable even under pretreatments such as autoclaving and blanching of the potato before extraction. The optimum temperature of the extraction for the PSP Pigment was decided to be $30^{\circ}C$ by considering the stability and the rate of extraction. The pigment was markedly influenced by the change of pH. The color of the pigment solution was red at the pH range of $1.0{\sim}3.0$, became blue at $7.0{\sim}8.0$, then turned green at $9.0{\sim}10.0$. A characteristic batho-chromic shift of the pigment solution was observed as the pH of the solution increased.

• Journal of Korean Society of Forest Science
• /
• v.27 no.1
• /
• pp.15-21
• /
• 1975

According to Yoshihisa Kuroki's report that the total amount of carotenoid was more in the susceptible to pine bark beetle, than in the resistant ones, carotenoids were extracted from needle leaves of one year old seedlings of Pinus thunbergii, Pinus desiflora, Pinus rigida, Pinus koraiensis, Pinus rigitaeda and Pinus taeda which are all important pines in Korea, to find their resistant ratio to the insect. The carotenoids were analyzed and compared using the spectra of them by spectrophotometer. The results were as follows: 1. The visible absorption spectra of carotenoids in those pine trees were proved to be very similar. 2. The total amount of carotenoids in needles differed with the tree species and the contents were arranged in decreasing order P. koraiensis>P. rigida>P. thunbergii>P. rigitaeda>P. taeda, it seemed that there was corelation between the cartenoid content and the extent of harm caused by the pine bark beetles except P. koraiensis. 3. But carotenoids were contained in Robinia pseudoacacia, Castanea crenata, Chamaecyparis obtusa and Cedrus deodra leaves too. 4. The total amounts of carotenoids in these pines of 9 species were arranged in decreasing order Robinia pseudoacacia>Pinus koraiensis>Pinus rigida>Pinus thunbergii>Castanea crenata>Pinus rigitaeda>Pinus taeda>Chamaecyparis obtusa>Cedrus deodara. Therefore, it was proved that there was no correlation between carotenoid cotent and extent of resistance to the insect. 5. In the thin-layer chromatography of these carotenoids, 13 kinds of components in P. densiftora, P. koraiensis and P. rigida and 12 kinds of spots in other pines, were detected respectively, under ultra-violet fluorescent lamp $3,600{\AA}$ and $2,537{\AA}$. 6. The eighth spots from the bottom in P. densiflora, P. koraiensis and P. rigida were not found in other pines and other 4 species (Robinia pseudoacacia, Castanea crenata, Chamacyparis obtusa, Cedrus deodra). Especially the spot in P. densiflora fluoresced strong cobalt blue-fluorescence under ultra-violet fluorescent lamp $2,537{\AA}$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.425-433
• /
• 2000

The stochiometric mix of evaporating materials for the $CuGaTe_2$single crystal thin films was prepared from horizontal furnance. Using extrapolation method of X-ray diffraction patterns for the $CuGaTe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0 and c_0$ were 6.025 $\AA$ and 11.931 $\AA$, respectively. To obtain the single crystal thin films, $CuGaTe_2$mixed crystal was deposited on throughly etched semi-insulator GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $670^{\circ}C$ and $410^{\circ}C$ respectively, and the thickness of the single crystal thin films is 2.1$\mu\textrm{m}$. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility dependence on temperature. The carrier density and mobility of $CuGaTe_2$single crystal thin films deduced from Hall data are $8.72{\times}10{23}$개 $\textrm m^3$, $3.42{\times}10^{-2}$ $\textrm m^2$/V.s at 293K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuGaTe_2$single crystal thin film, we have found that the values of spin orbit coupling $\Delta$s.o and the crystal field splitting $\Delta$cr were 0.0791 eV and 0.2463 eV at 10 K, respectively. From the PL spectra at 10 K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be 0.0470 eV and the dissipation energy of the donor-bound exciton and acceptor-bound exciton to be 0.0490 eV, 0.0558 eV, respectively.

• Korean Journal of Weed Science
• /
• v.12 no.2
• /
• pp.144-157
• /
• 1992

The study was conducted to compare the interprete methods and examine the feasibility of mixture use of oxyfluorfen and bensulfuron in controlling principal Paddy weeds, annuals and perennials. Application ratio of both chemicals were obtained from the combinations of 5 levels(0, 5, 10, 15, 20 g ai/ha) of each chemicals, respectively. All the treatments were applied at 5 days after transplanting and water was maintained at 3.0cm in depth. Shoot fresh-weight of weeds was assessed at 35 days after treatments. Data obtained was analysed by Colby, Isobole, Calculus, Regression and EQM method, respectively. The results from the analysis of variance on the principal weeds treated with oxyfluorfen and bensulfuron showed significant interactions at 1% level on both Echinochloa crus-galli and Eleocharis Kuroguwai, and total species at 0.5% level on both Potamogeton distinctus and Cyperus serotinus, but non significant on Scirpus juncoides and Sagittaria pygmaea. Thereafter, the results of the models applied to Echinochloa crus-galli, Eleocharis kuroguwai and total species were as follows ; 1. The Colby method gave values nearly identical to regression estimate method (both multiplicative models) as provided by Akobundu et al. The Colby method and Regression method indicated synergistic toward Echinochloa curs-galli, and total species, but antagonistic toward Eleocharis kuroguwai. 2. The Isobole method shows synergism on Echinochloa crus-galli at $ID_{50}$, and total species at $ID_{60}$ on Eleochari kuroguwai. 3. The Calculus method gave positive signs for the first differentiation and negative signs for the second differentiation except for some rates on Echinochloa crus-galli and total species, but reverse on Eleocharis kuroguwai. These result does not agree with the observed values. 4. ${\theta}$ value from the EQM method was greater than one at all combinations. This result was quite different from those of other methods. 5. The various models did not show the same results, but mixture of oxyfluorfen and bensulfuron tend to have synergistic effect. Weeding effect also was high. Treatment in terms of two chemical combination was expected to reduce rates, and to enhence weeding efficacy compared with single treatment.

• KIPS Transactions on Software and Data Engineering
• /
• v.11 no.1
• /
• pp.41-50
• /
• 2022

In this paper, a method to directly calculate the major elements of skin color such as melanin and hemoglobin from the RGB signal of the camera is proposed. The main elements of skin color typically measure spectral reflectance using specific equipment, and reconfigure the values at some wavelengths of the measured light. The values calculated by this method include such things as melanin index and erythema index, and require special equipment such as a spectral reflectance measuring device or a multi-spectral camera. It is difficult to find a direct calculation method for such component elements from a general digital camera, and a method of indirectly calculating the concentration of melanin and hemoglobin using independent component analysis has been proposed. This method targets a region of a certain RGB image, extracts characteristic vectors of melanin and hemoglobin, and calculates the concentration in a manner similar to that of Principal Component Analysis. The disadvantage of this method is that it is difficult to directly calculate the pixel unit because a group of pixels in a certain area is used as an input, and since the extracted feature vector is implemented by an optimization method, it tends to be calculated with a different value each time it is executed. The final calculation is determined in the form of an image representing the components of melanin and hemoglobin by converting it back to the RGB coordinate system without using the feature vector itself. In order to improve the disadvantages of this method, the proposed method is to calculate the component values of melanin and hemoglobin in a feature space rather than an RGB coordinate system using a feature vector, and calculate the spectral reflectance corresponding to the skin color using a general digital camera. Methods and methods of calculating detailed components constituting skin pigments such as melanin, oxidized hemoglobin, deoxidized hemoglobin, and carotenoid using spectral reflectance. The proposed method does not require special equipment such as a spectral reflectance measuring device or a multi-spectral camera, and unlike the existing method, direct calculation of the pixel unit is possible, and the same characteristics can be obtained even in repeated execution. The standard diviation of density for melanin and hemoglobin of proposed method was 15% compared to conventional and therefore gives 6 times stable.