• International Journal of Highway Engineering
• /
• v.15 no.2
• /
• pp.95-103
• /
• 2013

PURPOSES : To investigate the fundamental characteristics of blast-furnace slag mortar that was hardened with activating chemicals to capture and sequester carbon dioxide. METHODS : Various mix proportions were considered to find an appropriate stregnth development in regards with various dosages of activating chemicals, calcium hydroxides and sodium silicates, and curing conditions, air-dried, wet and underwater conditions. Flow characteristics was investigated and setting time of the mortar was measured. At different ages of 3, 7 and 28days, strength development was investigated for all the mix variables. At each age, samples were analyzed with XRD. RESULTS : The measured flow values showed the mortar lost its flowability as the activating chemicals amount increased in the scale of mole concentration. The setting time of the mortar was relatively shorter than OPC mortar but the initial curing condition was important, such as temperature. The amount of activating chemicals was found not to be critical in the sense of setting time. The strength increased with the increased amount of chemicals. The XRD analysis results showed that portlandite peaks reduced and clacite increased as the age increased. This may mean the $Ca(OH)_2$ keeps absorbing $CO_2$ in the air during curing period. CONCLUSIONS : The carbon capturing and sequestering activated blast-furnace slag mortar showed successful strength gain to be used for road system materials and its carbon absorbing property was verified though XRD analysis.

• Journal of the Korea Institute of Building Construction
• /
• v.11 no.4
• /
• pp.363-370
• /
• 2011

This study considerated reject ash, wastes of coal-fired power plants, to use mineral admixtures for cement. The pozzolan activity selected the fineness of the efficient reject ash through comparison and it compared to the fly ash that are widely used for concrete mixed material. Cement composites was prepared replacing of slag cement by fineness reject ash and fly ash, and properties of cement composites was tested by paste(setting time, fluidity, instrumental analysis) and mortar(compressive strength). Instrumental analysis results showed hydration reaction of fineness reject ash was not different from fly ash, but had more dense micro structures. Results of physical properties showed fineness reject ash shorten setting time, increased compressive strength compared by fly ash. Therefore using fineness reject ash with $6,000cm^2$/g to concrete mineral admixtures or cement composites was might be possible and could contribute to improve properties of concrete.

• Resources Recycling
• /
• v.22 no.3
• /
• pp.36-42
• /
• 2013

According to the recent community-based structures enlargement, specification, and diversification. It needs appropriate construction materials in terms of intensity and environmental aspects. Thus, in manufacturing the cement using micro limestone powder which is main material. It is also expected to save energies and reduces $CO_2$, by using the blast furnace slag and fly ash which are mitigated environmental load construction materials that emerged. In this research, The durability aspect tries to be grasped considering the chemical property according to the coherence of the hydration product. Consequently, The compressive strength was measured over 30 Mpa on 3rd. In addition, according to the content of the limestone powder, the setting time is promoted. It has the feature expanded in the length change. And it is determined because the possibility of replacing the existing for construction material such as it is measured compared with the time to use the portland cement usually that flexural strength is high with the age 7 days ago, so it is sufficient.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.255-261
• /
• 2019

The purpose of this study is to investigate effects of types of synthetic fibers on mechanical properties of alkali-activated slag composite. Materials and mixture proportion for matrix are determined, and the compressive strength, tensile performance, and cracking patterns of three composites reinforced by polypropylene, polyvinyl-alcohol, and polyethylene fibers. From the test results, it was observed that polyvinyl-alcohol fiber-reinforced composite and polyethylene fiber-reinforced composite had similar tensile performance. On the other hand, polypropylene fiber-reinforced composite showed low tensile performance. And it was exhibited that other factors except tensile strength and aspect ratio of fiber influence significantly tensile behavior of composite.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.200-207
• /
• 2021

The purpose of this study is to investigate experimentally the effects of type of superplasticizer on tensile behavior and cracking pattern of alkali-activated slag-based cementless composite. Three mixtures were prepared according to type of superplasticizer, and the compressive strength and tension tests were performed. Test results showed that differences of tensile strength, tensile strain capacity, and toughness of composites were up to 28.1%, 39.1%, and 66.2%, respectively, according to type of superplasticizer, although fiber balling or poor dispersion of fibers in fresh composites was not observed. It was also observed that the type of superplasticizer influenced number of cracks and maximum fiber bridging stress.

• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.511-519
• /
• 2015

Methods such table flow, slump and outflow time have used to be as a main evaluation criteria regards to fluidity of concrete. Since those methods mentioned above have some inaccuracies which are up to its condition of test. Studies that evaluate fluidity applying the rheology has increased its portion in this field. Meanwhile, demands for AAS binder have been increased in accordance with its demand for this market, studies for rheology of AAS binder are little though. Therefore, this paper mainly deals a rheological peculiarity of AAS binder according to its condition of W/B ratio and alkali activators. The fluidity of AAS paste was evaluated with the index of table flow and outflow time. And shear stress following its shear rate was analyzed through rheological test. Rheological parameters were deduced through this rheological test of Bingham model and analyzed its interrelation with fluidity test. As the final outcome, it proposed the interrelation among table flow, yield stress, viscosity and outflow time. In basis of this study, we would like to suggest a reference for mixing AAS mortars and concretes.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.2
• /
• pp.203-210
• /
• 2012

Recently, the interest and demand for large-scale buildings and skyscrapers have been on the rise, and the performance of concrete is an area of high priority. Securing 'mass concrete and high strength concrete' is very important as a key construction technology. For high strength concrete, the high heat of hydration takes place inside the concrete because of the vitality of hydration in cement due to the large amount of powder, and leads to problems such as an increase of thermal stress due to the temperature difference with the outside, which results in cracks and slump loss. For this reason, measures to solve these problems are needed. This study aims to reduce the hydration heat of high strength concrete to control the hydration heat of mass concrete and high strength concrete, by replacing the type of admixture, The purpose of this study is to control the hydration heat of high strength concrete and mass concrete. Our idea for this purpose is to apply not only the types and contents of admixture but also incorporation mixing water to ice-flake. As a result of the test, the use of blast furnace slag and fly ash as admixture, and the use of ice-flake as mixing water can improve the liquidity of concrete and reduce slump loss. Significantly dropping the maximum temperature will contribute greatly to reducing cracks due to hydration heat in mass concrete and high strength concrete, and improve quality.

• Journal of the Korean GEO-environmental Society
• /
• v.15 no.3
• /
• pp.33-40
• /
• 2014

In this paper, mechanical and germination characteristics of stabilized dredged soils were investigated to recycle dredged soil in eco-friendly manner such as waterfront construction. Non sintering binder (NSB), which was developed by using interchemical reactions between slag, high-calcium fly ash, alkali activator on the dredged marine clay, was added to dredged soil. Ordinary portland cement was also used for the comparison of two binders. Experimental tests such as flow test and unconfined compressive test were carried out to evaluate characteristics of stabilized dredged soil. Leaching test, pH measure, vegetation germination test were also conducted to consider environmental applicability. The unconfined compressive tests shows that unconfined compressive strength (UCS) also increases with the increase of curing time and mixed ratio. UCS of NSB mixtures were higher than those of OPC mixtures. Germination tests showed that germination and sprouting date are better in NSB mixture than OPC mixture. It can be explained that germination decreased as pH and 7-day strength increased.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.6
• /
• pp.720-727
• /
• 2017

This study determined the optimum mix proportions for volcanic-ash-based geopolymer by analyzing the flow, setting time, and compressive strength. $Na2SiO_3$ and NaOH were used as alkali activators, and NaOH concentrations of 2, 4, 6, and 8M were used for different experimental cases. The A/B ratios examined were 0.25, 0.3, 0.35, 0.4, and 0.45, and the ratios of volcanic ash to blast furnace slag binder were 7:3, 6:4, and 5:5. In the experiment, the flow and setting time tended to decrease and the compressive strength increased as the molarity of NaOH in the geopolymer increased. The optimum molarity of NaOH was determined to be 4M. As the A/B ratio increased, the setting time decreased and the compressive strength increased. The most advantageous A/B ratio for the setting time and strength was 0.35. Increasing the ratio of volcanic ash resulted in a longer setting time and lower compressive strength. The optimum binder ratio was chosen as 6:4 based on the setting time and compressive strength. Thus, 4M of NaOH, an A/B ratio of 0.35, and binder ratio of 6:4 are considered as the proper parameters for the volcanic-ash-based geopolymer.