• Journal of the Korean Society for Precision Engineering
• /
• v.23 no.4 s.181
• /
• pp.109-115
• /
• 2006

This paper is designed to estimate friction and powdering characteristic of coating layer on galvannealed sheet steel with different annealing temperature, which is 465, 505, 515 and $540^{\circ}C$, Estimations of powdering and friction were done using a $60^{\circ}$ bending test and one side friction test, respectively. In order to obviously understand the effect of coatings on friction cross-section of coatings before and after friction test was also observed by SEM. The results show that powdering of coatings is increased with increasing of annealing temperature and that friction characteristic greatly depends on powdering which leads to increase of real contact area between tools and coatings.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.138-138
• /
• 2016

의료용 공구로 사용되는 합금은 마르텐사이트계 스테인리스강의 대표 강종인 420스테인리스강이 사용되며, 이 합금은 고온의 오스테나이트 상태에서 ?칭하면 마르텐사이트 조직으로 변태하여 현저하게 경화하는 특징을 가지고 있으며, 오스테나이트화 후 템퍼링시 우수한 기계적 성질이 얻어진다. 그러나 템퍼링 온도의 영향으로 석출탄화물이 형성되어 기계적 성질이나 내식성이 저하되는 단점이 있다. 본 연구에서는 STS 420스테인리스강의 템퍼링 온도에 의한 내식성 문제점을 개선시키기 위해 STS630 합금을 사용하여 다양한 석출 열처리 조건 및 플라즈마 질화공정을 연구하였다. 구입한 소재의 균일한 성분 조정을 통한 미세 편석 및 물성부여를 위한 균질화 조건 도출 열처리를 실시하였으며, STS630의 고용화열처리는 오스테나이트 균일조직이 되는 온도영역으로 가열하여 급냉하는 것으로 마르텐사이트 변태시키는 열처리를 진행하였으며, 열처리온도는 $1020{\sim}1060^{\circ}C$로 설정하였다. 석출경화 열처리는 $460{\sim}480^{\circ}C$와 $500{\sim}520^{\circ}C$의 온도에서 실시, 제품에 따른 인성을 부여하였으며, 질화공정은 플라즈마 장비를 이용하여 플라즈마 가열 ${\rightarrow}$플라즈마 이온질화를 통하여 가장 최적의 공정을 도출하였다.- 질화가 마무리 된 시료는 내식성 및 물성 평가를 통해 제품으로서의 특성을 평가하였다. 석출경화 열처리에 의해 STS420합금에 버금가는 인장강도 및 경도값이 나타났으며, 플라즈마 질화에 따라 물성 값의 향상이 나타났다. 용출실험결과 STS420합금의 경우 Fe, Cr원소의 용출이 나타나며 변색이 형성되었으나 STS630합금의 경우 그 현상이 미미하였다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.1012-1015
• /
• 2005

This paper is designed to estimate friction and powdering characteristic of coating layer on galvannealed sheet steel with different annealing temperature, which is 465, 505, 515 and $540^{\circ}C$. Estimations of powdering and friction were done using a $60^{\circ}$ bending test and one side friction test, respectively. In order to obviously understand the effect of coatings on friction cross-section of coatings before and after friction test was also observed by SEM. The results show that powdering of coatings is increased with increasing of annealing temperature and that friction characteristic greatly depends on powdering which leads to increase of real contact area between tools and coatings.

• Journal of Hydrogen and New Energy
• /
• v.20 no.6
• /
• pp.512-518
• /
• 2009

Mg 및 Mg합금은 수소 저장량이 7.6wt.%로 비교적 높고 자원도 풍부하여 값이 싼 장점을 가지고 있으나 산화반응성이 높고 활성화 에너지가 크기 때문에 반응온도가 높고 반응시간이 긴 단점을 가지고 있다. 이러한 단점을 극복하기 위해 일반적으로 Mg 및 Mg합금의 표면 개질화, 금속간 화합물 형성, 전이금속 첨가에 대한 연구가 활발히 진행되고 있다. 본 연구에서는 전이금속인 Nb를 촉매제로 사용하여 수소화 특성을 개선하고자 기계적 합금화법(MA;Mechanical Alloying)을 실시하여 복합재료를 합성한 후 수소화 반응을 평가하였다. XRD, SEM, TEM, PSA, TG/DSC 분석을 수행하였으며 Sievert's 형 PCT를 이용하여 온도 및 압력 변화에 따른 특성평가를 하였다. 전이금속인 Nb의 첨가로 수소화 반응개시온도가 낮아지고 수소 저장량이 향상되는 거동을 보였다. 특히, 5mass%Nb가 10mass%Nb 보다 수소 저장량 및 반응속도가 좋은 결과를 보였다.

• Journal of Korea Foundry Society
• /
• v.23 no.5
• /
• pp.286-290
• /
• 2003

본 연구에서는 Ni-Zr-Ti의 3원계 합금을 기본으로 하여, Si 및 Sn 등의 원소를 첨가하여 Ni-rich 영역에서 벌크 비정질 합금을 제조하였다. $Ni_{59}Zr_{20}Ti_{16}Si_2Sn_3$ 조성의 합금에서 injection casting에 의하여 약 58 K의 과냉각액상영역을 가지고 있는 직경 3 mm의 벌크 비정질 시편을 제조하였다. 이러한 우수한 비정질 형성능은 액상온도의 저하로 인해 낮은 온도까지 액상이 쉽게 과냉되기 때문인 것으로 사료된다. $Ni_{59}Zr_{20}Ti_{16}Si_5$ 합금은 두 단계에 걸쳐 결정화가 일어나는 반면, $Ni_{59}Zr_{20}Ti_{16}Si_2Sn_3$ 합금은 단일 단계에 의해 orthorhombic $Ni_{10}{(Zr,Ti)}_7$ 결정상과 cubic NiTi 결정상으로 결정화가 일어난다. 벌크 비정질 $Ni_{59}Zr_{20}Ti_{16}Si_2Sn_3$ 합금의 경우 압충강도는 2.7 GPa, 연신율은 약 2% 정도의 값을 가진다.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.4
• /
• pp.1-5
• /
• 2000

Properties of AC applied hot pressed ($Pb_{1-x}Sn_{x}$) Te thermoelectrics were investigated. Mechanical alloying process used to produce alloyed powder to reduce the inhomogeneity and to avoid vaporization of constituents. It showed an increase in the mechanical alloying time with increasing of Sn contents in ($Pb_{1-x}Sn_{x}$)Te. ($Pb_{1-x}Sn_{x}$)Te were sintered at 873 to 923K for 1-4 minutes, under 150 kgf/$\textrm{cm}^2$ by AC applied hot pressng method. The short sintering time of AC applied hot pressing process could reduce the vaporization of Te. The density of ($Pb_{1-x}Sn_{x}$) Te was more dependent on the sintering temperature than the sintering time. The p-n transition was observed at x=0.1 but only p type conduction behavior was observed at more than 20 mol% of Sn compositions. The maximum value of Seebeck coefficient is 250 $\mu$V/K for x=0.2 at 500K. As the amount of Sn increases, the peak value of Seebeck coefficient drops and shifts to higher temperature and the peak value of electrical conductivity decreased with increasing temperature.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.59.1-59.1
• /
• 2011

Ni기 초내열합금을 사용하는 터빈엔진의 효율향상 및 다양한 초고온함금에 대한 관심이 높아지면서, 이를 대체할 수 있는 초고온합금으로 Mo기지 복합재료에 대한 연구가 활발히 진행되고 있는 가운데 실질적으로 Mo 합금은 취약한 산화성으로 인하여 내산화성이 문제가 되고 있다. Mo-Si-B합금이 초고온에 노출될 경우 산화물의 점도가 매우 낮아 산화층을 형성하기 곤란하고, 저온에서는 산화층이 합금을 보호하지 못한다고 알려져 있다. 따라서, 본 연구에서는 Mo-Si-B 합금기지에 Si 확산코팅을 수행하여 내산화성을 높이고자 하였다. $1,100^{\circ}C$와 $800^{\circ}C$의 온도에서 시간에 따른 코팅 층의 두께 및 성장거동을 속도론적으로 고찰하였고, 내산화성을 평가하였다. 코팅된 시험편의 XRD 및 SEM 분석 및 무게측정 결과 내산화성이 크게 개선된 것으로 나타났으며, 내산화성에 대한 기구를 고찰하였다.

• Resources Recycling
• /
• v.26 no.5
• /
• pp.22-28
• /
• 2017

In-Bi-Sn alloy sheet has been used as a thermal fusible parts of secondary battery safety system. This study offers a simple process to make In-Bi-Sn alloy fusible parts. The process consists of two procedures, melting and sheeting by tape casting. 62.5 wt%-In 20.0 wt%-Bi 17.5 wt%-Sn (M.P. $92.4^{\circ}C$) alloy sheet obtained by tape casting was used as the thermal fusible sheet of thermal fuse system for mobile telephone. The performance test of the system was carried out in oil bath, and the fusible alloy sheet was melted and cut off at $95^{\circ}C$. This results confirmed the possibility that the alloy sheet obtained by tape casting can be usable as a thermal fusible parts of battery safety system. And this process can be applied as a simple process to recycle the In-Bi-Sn alloy scrap separated from the used thermal fuse system.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.130-135
• /
• 1998

Zr합금의 재결정에 미치는 Sn, V, Sb의 영향을 조사하기 위해 2원계와 3원계로 구성된 12종의 Zr합금에 대하여 미세 조직 관찰 및 경도 측정을 실시하였다. 고진공 분위기의 여러 온도 조건에서 열처리된 시편의 미세조직을 편광광학현미경으로 관찰하였고 미소경도계로 경도값을 측정하였다. 미세조직 사진을 관찰한 결과 열처리 온도가 올라감에 따라 약 50$0^{\circ}C$ 까지는 가공조직을 그대로 유지하다가 첨가원소에 따라 다소 차이는 있었지만 55$0^{\circ}C$ ~ $700^{\circ}C$ 사이에서 재결정이 완료되었다. 재결정이 일어난 후에는 첨가원소의 첨가량이 적은 합금의 경우 결정립이 급격히 성장하는 모습을 보였다. 온도에 따른 경도값의 측정으로 재결정 거동을 확실히 핑가할 수 있었으며 경도값의 변화와 미세조직 변화는 일치하는 경향을 보였다. 이와 같이 첨가원소가 증가함에 따라 재결정이 늦어지고 결정립이 미세화 되는 것은 첨가원소의 대부분이 석출물로 형성되어 각 합금의 재결정과 결정립 성장을 억제하기 때문이라고 사료된다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.227-227
• /
• 2009

Zn-Mg 합금박막 강판의 열처리 온도에 따른 내식특성 변화를 연구하기 위하여 XRD 분석 및 전기화학적 실험을 실시하였다. 실험 결과에 의하면, 부식전위(Ecorr)상승을 통해 합금화 정도를 간접적으로 측정할 수 있었음은 물론 부식전류밀도(Ecorr) 측정을 통해 내식성을 비교 평가 할 수 있었다.