Room Temperature Plasma Nitridation of silicon was investigated as a new LOCOS (local oxidation of silicon) process in order to reduce the bird's beak length. In $N_2$ plasma formed by 100kHz, 400W AC power, a thin silicon nitride film (<100${\AA}$) was uniformly grown on a silicon substrate. SEM studies showed that the nitride layer formed by this method can effectively protect the silicon from oxidation and reduce the bird's beak length to $0.2{mu}m$ when 4000${\AA}$ field oxide is grown. This is a considerable improvement comparing with 0.7${mu}m,$ the bird's beak, for the conventional LOCOS process using a thick LPCVD nitride. No appreciable crystalline defect could be found around the bird's beak with SEM cross-section afrer Secco etch. Leakage current tests were carried out on the $N^+/P^-$ well and $P^+/N^-$ well diodes formed by this new LOCOS process. The electrical tests indicate that this new process has electrical properties similar or superior to those of the conventional LOCOS process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.446-446
• /
• 2009

표면 패시베이션 기술로 이용되는 수소화된 실리콘 질화막은 제조원가의 절감을 위한 실리콘 기판재료의 두께 감소에 따른 특성상의 문제점을 해결하기 위해 중요한 영향을 미치는 요소이다. 실리콘 질화막은 강한 기계적 강도, 우수한 유전적 특성, 수문에 의한 부식과 유동적 이온에 대한 우수한 저항력 때문에, 반도체 소자 산업에서 널리 사용되고 있다. 수소화된 실리콘 질화막은 반사방지 특성과 함께 표면 패시베이션의 질을 향상시킬 수 있다. 굴절률 1.9 ~ 2.3 범위에서 쉽게 변화 가능한 수소화된 실리콘 질화막은 굴절률 1.4 ~ 1.5 사이의 열적 산화막 보다 효과적인 반사방지막이다. 수소화된 실리콘 질화막을 사용한 태양전지에서는 효율을 높이기 위해서 기판 표면에서의 케리어 재결합이 억제되어져야한다. 또한, 수소화된 실리콘 질화막은 최적화된 두께와 굴절률을 가져야한다. 본 연구에서는 고효율 태양전지에 적용하기 위해 반송자 수명이 향상된 수소화된 실리콘 질화막을 플라즈마 화학 기상 증착법을 이용하여 증착하였다. 박막은 $250^{\circ}C\;{\sim}\;450^{\circ}C$에서 증착되었으며 증착된 박막은 1.94 to 2.05 굴절률 값을 가지고 있다. 반송자 수명을 증가시키기 위해 $650^{\circ}C\;{\sim}\;950^{\circ}C$에서 어닐링 하였고 반송자 수명을 측정하여 패시베이션 특성을 분석하였다. 수소화된 실리콘 질화막은 $850^{\circ}C$의 어닐링 온도와 굴절률 2.0 조건에서 가장 좋은 반송자 수명을 나타냈다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.129-129
• /
• 2003

최근에 능동 영역 액정 표시 소자(Active Matrix Liquid Crystal Display, AMLCD)에서 고해상도와 빠른 응답속도를 요구하게 되면서부터 다결정 실리콘(poly-Si) 박막 트랜지스터(Thin Film Transistor, TFT)가 쓰이게 되었다. 그리고 일반적으로 디스플레이의 기판을 상대적으로 저가의 유리를 사용하기 때문에 저온 공정이 필수적이다. 따라서 새로운 저온 결정화 방법과 부가적으로 최근 디스플레이 개발 동향 중 하나인 대화면에 적용 가능한 공정인 금속유도 결정화 (Silicide Mediated Crystallization, SMC)가 연구되고 있다. 이 소자는 top-gated coplanar구조로 설계되었다. (그림 1)(100) 실리콘 웨이퍼위에 3000$\AA$의 열산화막을 올리고, LPCVD로 55$0^{\circ}C$에서 비정질 실리콘(a-Si:H) 박막을 550$\AA$ 증착 시켰다. 그리고 시편은 SMC 방법으로 결정화 시켜 TEM(Transmission Electron Microscopy)으로 SMC 다결정 실리콘을 분석하였다. 그 위에 TFT의 게이트 산화막을 열산화막 만큼 우수한 TEOS(Tetraethoxysilane)소스로 사용하여 실리콘 산화막을 1000$\AA$ 형성하였고 게이트는 3000$\AA$ 두께로 몰리브덴을 스퍼터링을 통하여 형성하였다. 이 다결정 실리콘은 3$\times$10^15 cm^-2의 보론(B)을 도핑시켰다. 채널, 소스, 드래인을 정의하기 위해 플라즈마 식각이 이루어 졌으며, 실리콘 산화막과 실리콘 질화막으로 passivation하고, 알루미늄으로 전극을 형성하였다 그리고 마지막에 TFT의 출력특성과 전이특성을 측정함으로써 threshold voltage, the subthreshold slope 와 the field effect mobility를 계산하였다.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.5
• /
• pp.483-491
• /
• 1992

Plasma silicon oxynitride film has been applied as a final passivation layer for semiconductor devices, because it has high resistance to humidity and prevents from alkali ion's penetration, and has low film stress. Structure properties of plasma silicon oxynitride film have been studied experimentally by the use of FT-IR, AES, stress gauge and ellipsometry. In this experiment,Si-N bonds increase as NS12TO/(NS12TO+NHS13T) gas ratio increases. Peaks of Si-N bond, Si-H bond and N-H bond were shifted to high wavenumber according to NS12TO/(NS12TO+NHS13T) gas ratio increase. Absorption peaks of Si-H bond were decreased by furnace anneal at 90$0^{\circ}C$. The atomic composition of film represents that oxygen atoms increase as NS12TO/(NS12TO+NHS13T) gas ratio increases, to the contrary, nitrogen atoms decrease.

• Korean Journal of Materials Research
• /
• v.10 no.3
• /
• pp.212-217
• /
• 2000

Dielectric thin films for TFT(thin film transistor)s, such as silicon nitride$(Si_3N_4)$ and silicon oxide$(SiO_2)$, are usually deposited at $200~300^{\circ}C$. In this study, authors have tried to form dielectric films not by deposition but by oxidation with ECR(Electron Cyclotron Resonance) oxygen plasma, to improve the interface properties was not intensionally heated during oxidation. THe oxidation was performed consecutively without breaking vacuum after the deposition of a-Si: H films on the substrate to prevent the introduction of impurities. In this study, especially pulse mode of microwave power has been firstly tried during FCR oxygen plasma formation. Compared with the case of the continuous wave mode, the oxidation with the pulsed ECR results in higher quality silicon oxide$SiO_X$ films in terms of stoichiometry of bonding, dielectric constants and surface roughness. Especially the surface roughness of the pulsed ECR oxide films dramatically decreased to one-third of that of the continuous wave mode cases.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.247-251
• /
• 2004

반도체 소자의 제조에 있어 실리콘 표면에 성장한 자연산화막을 제거하기 위해 일반적으로 습식 세정 기술이 이용되어 왔다. 하지만 소자의 최소 선폭(design rule)이 nano급으로 고집적화 됨에 따라 contact hole 바닥의 자연산화막을 깨끗이 제거하는데 있어서 그 한계를 나타나고 있다. 이에 대한 효과적인 대안 공정으로 가스 건식 세정 기술이 연구되고 있다. 본 논문에서는 한 번에 50매 이상의 웨이퍼를 처리함으로써 생산성 측면에서 월등한 배치식 설비에서 원거리 플라즈마(remote plasma) 장치에서 2.450Hz의 마이크로웨이브(${\mu}$-wave)에 의해 형성시킨 수소라디칼과 $NF_3$ 가스를 이용하여 실리콘에 결함을 주지 않고 자연산화막을 선택적으로 제거하는 공정에 대해 고찰하였다. AFM을 이용한 표면분석, TEM을 이용한 물성분석, 그리고 ToF-SIMS 및 XPS를 이용한 화학 분석을 습식 및 건식 세정을 비교 평가한 결과, 건식 세정 공정이 실리콘 표면에 결함을 주지 않고 자연산화막을 제거 할 수 있음을 확인하였다. 산화막$(SiO_2)$, 질화막$(Si_3N_4)$, 그리고 다결정 실리콘(Poly-Si) 등의 각 막질별 식각 특성을 고찰하였으며, $NH_3$의 캐리어 가스인 $N_2$의 주입량을 조절함으로써 수소라디칼 형성 효율의 개선이 가능하였으며, 이로부터 게이트와 소스/드레인 사이를 절연하기 위해 이용되는 질화막의 식각 선택비를 2배 정도 개선할 수 있었다. nano급 소자에 실장하여 평가한 결과에서 불산(HF)에 의한 습식 세정 방식에 비하여 약 $20{\sim}50%$ 정도의 contact 저항 감소 효과가 있음이 확인되었다.두 소자 모두 $40mA/cm^2$ 에서 이상적인 화이트 발란스와 같은(0.33,0.33)의 색좌표를 보였다.epsilon}_0=1345$의 빼어난 압전 및 유전특성과 $330^{\circ}C$의 높은 $T_c$를 보였고 그 조성의 vibration velocity는 약4.5 m/s로 나타났다.한 관심이 높아지고 있다. 그러나 고 자장 영상에서의 rf field 에 의한 SAR 증가는 중요한 제한 요소로 부각되고 있다. 나선주사영상은 SAR 문제가 근원적으로 발생하지 않고, EPI에 비하여 하드웨어 요구 조건이 낮아 고 자장에서의 고속영상방법으로 적합하다. 본 논문에서는 고차 shimming 을 통하여 불균일도를 개선하고, single shot 과 interleaving 을 적용한 multi-shot 나선주사영상 기법으로 $100{\times}100$에서 $256{\times}256$의 고해상도 영상을 얻어 고 자장에서 초고속영상기법으로 다양한 적용 가능성을 보였다. 연구에서 연구된 $[^{18}F]F_2$가스는 친핵성 치환반응으로 방사성동위원소를 도입하기 어려운 다양한 방사성의 약품개발에 유용하게 이용될 수 있을 것이다.었으나 움직임 보정 후 영상을 이용하여 비교한 경우, 결합능 변화가 선조체 영역에서 국한되어 나타나며 그 유의성이 움직임 보정 전에 비하여 낮음을 알 수 있었다. 결론: 뇌활성화 과제 수행시에 동반되는 피험자의 머리 움직임에 의하여 도파민 유리가 과대평가되었으며 이는 이 연구에서 제안한 영상정합을 이용한 움직임 보정기법에 의해서 개선되었다. 답이 없는 문제, 문제 만들기, 일반화가 가능한 문제 등으로 보고, 수학적 창의성 중 특히 확산적 사고에 초점을 맞추어 개방형 문제가 확