• Resources Recycling
• /
• v.25 no.6
• /
• pp.73-81
• /
• 2016

Geopolymers produced from aluminosilicate materials such as metakaolin and coal ash react with alkali activators and show higher fire resistance than portland cement, due to amorphous inorganic polymer. The percentage of thermal shrinkage of geopolymers ranges from less than 0.5 % to about 3 % until $600^{\circ}C$, and reaches about 5 ~ 7 % before melting. In this study, geopolymers paste having Si/Al = 1.5 and being mixed with carbon nanofibers, silicon carbide, pyrex glass, and vermiculite, and ISO sand were studied in order to understand the compressive strength and the effects of thermal shrinkage of geopolymers. The compressive strength of geopolymers mixed by carbon nanofibers, silicon carbide, pyrex glass, or vermiculite was similar in the range from 35 to 40 MPa. The average compressive strength of a geopolymers mixed with 30 wt.% of ISO sand was lowest of 28 MPa. Thermal shrinkage of geopolymers mixed with ISO sand decreased to about 25 % of paste. This is because the aggregate particles expanded on firing and to compensate the shrinkage of paste. The densification of the geopolymer matrix and the increase of porosity by sintering at $900^{\circ}C$ were observed regardless of fillers.

• Resources Recycling
• /
• v.21 no.3
• /
• pp.28-38
• /
• 2012

The purpose of this paper is to develop the alkali-activated concrete which uses 100% fly ash as a binder without any cement. The compressive strength of the mortar was examined depending on the chemical change in alkali-activator through SEM and SEM/EDS observations and the XRD analysis. It was found from the test that the higher molar concentration induced the greater effect on the initial strength, and that $Si^{4+}$ and $Al^{3+}$ were eluted relative to the compressive strength of mortar. In addition, it was confirmed that Al and Si were determined to be most influential ingredients on the microstructural development of the mortar, and that the different ingredient of the activator was almost no change in solidity from the XRD analysis.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.255-257
• /
• 2012

Epoxy resin without any hardener can harden in the presence of hydroxide ions in cement mortars and concretes at ambient temperature. The purpose of present study is to examine the hardening properties of hardener-free epoxy-modified mortars by curing conditions. The hardener-free epoxy-modified mortars using diglycidyl ether of A epoxy resin are prepared with various polymer-cement ratios, and subjected to initial moist/dry curing, initial steam(90℃) curing, initial steam/heat(80℃, 100℃) curing.As a result, degree of hardening of epoxy resin in initial moist/dry cured, initial steam cured and initial steam/heat(80℃) cured hardener-free epoxy-modified mortars is decreased with increasing polymer-cement ratio. However, it is markedly improved with additional dry-curing periods. On the other hand, regardless of the polymer-cement ratio and dry curing periods, degree of hardening of hardener-free epoxy-modified mortars with initial steam/heat(100℃) cure is over 95%.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.482-488
• /
• 2022

In this study, the durability of ultra rapid hardening mortar for sewage pipe was evaluated by type of mortar binder. As a result of analyzing the internal structure for each type of mortar, it was confirmed that Al₂(OH)₃ was generated in the internal structure of the CAC-based mortar, and its corrosion resistance was superior to that of other types of mortar. As a result of the compressive strength test, OPC had the tsmallest strength, followed by CAC100 > CAC100P > CAC80. This trend was similar to the previous study results. Chloride ion penetration resistance and freeze-thaw test showed similar trends. That is, CAC and C12A7 were better than OPC, and CSA was worse than OPC. This is mostly beacuse of cracks caused by expansion of CSA-based mortar. CAC100P mix showed the best chemical resistance. It is thought that this is because the alumina gel formed inside the mortar and the polymer combine to make the internal structure more dense.

• Polymer(Korea)
• /
• v.35 no.4
• /
• pp.363-369
• /
• 2011

To study the effect of incorporation of a surface crosslinking layer on a crosslinked poly (sodium acrylate) (cPSA) absorbent with ethylene glycol dimethacrylate CEGDMA), we synthesized several surface crosslinked cPSAs with EGDMA by an inverse emulsion polymerization method to delay the absorption of excess water in concrete, Liquid paraffin was used as a continuous phase. cPSA was synthesized with acrylic acid (AA) neutralized with aqueous 8 M sodium hydroxide solution as a monomer, N,N-methylene bisacrylamide (MBA) as crosslinking agent and ammonium persulfate (APS) and sodium metabisulfite (SMBS) as a redox initiator system by inverse emulsion polymerization. FTIR spectroscopy was used to characterize $Ca^{2+}$ ion interaction with cPSA and cPSA-EGDMAs. The swelling ratios of synthesized absorbents were evaluated from the absorption in deionized water, cement saturated aqueous solution and aqueous solution of calcium hydroxide (pH 12). Equilibrium swelling times for cPSA and surface crosslinked cPSA with EGDMA were 2 and 3 hrs, respectively. We also observed an increase in setting time of the cement and an increase in the compressive strength of mortar by addition of the synthesized cPSA-EGDMA.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.6
• /
• pp.53-60
• /
• 2019

The purpose of this study is to evaluate the degree of improvement in strengths by mixing blast-furnace slag and fly ash in polymer cement mortar(PCM). The test specimens are prepared with EVA polymer dispersion, two types of Admixtures (blast-furnace slag and fly ash), five kinds of polymer-cement ratios (0, 5, 10, 15 and 20%), and six kinds of admixtures (0, 3, 5, 10, 15 and 20%). Plain cement mortar is also made for comparison. From the test results, the flowing of PCM is greatly improved with the mixing of the admixtures, and strengths of PCM compared to ordinary cement mortar are also improved due to a decrease in water cement ratio. In addition, the strength characteristics of PCM by admixtures are greatly improved in flexural strength with fly ash compared to other strengths. It is apparent that the optimum mix proportions with polymer-cement ratio of 10% or more, admixture contents 5 to 10% of flay ash for flexural strength improvement of EVA-cement mortar are recommended in this study.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.1
• /
• pp.25-34
• /
• 2016

From 1990's, a study on the development of exothermic concrete, a concrete which electro-conductive material is mixed, has been proceeded. However, due to the difficulty of exothermic reproducibility of concrete specimen, the study has been unable to continuously carried out. Accordingly, this study was focused on developing an exothermic concrete for the purpose of snow-melting material. Cement paste and mortar specimens mixed with graphite, conductive metal powder and chemical admixture were made. The evaluation of exothermic performance and reproducibility was conducted under $-2^{\circ}C$ of low temperature. In addition, micro-chemical analysis was carried out to investigate a cause of exothermic reproducibility. As a test result, the specimen mixed with graphite and superplasticizer with air entrained showed the best exothermic performance and reproducibility. Through micro-chemical analysis, it is judged that polymer or methacrylic acid (MAA), the contents inside the superplasticizer with air entrained, gave exothermic reproducibility by generating the electrochemical reaction with graphite.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.48 no.1
• /
• pp.51-60
• /
• 2006

This study was conducted to investigate experimentally the drying shrinkage and the strength properties of redispersible SBR and PAE powder-modified mortars. Polymer-cement ratio, content of shrinkage-reducing agent and antifoamer content were manipulated as the experimental variables. The peculiarity of this study is to obtain a high early-age strength by using the portland cement and alumina cement with the ratio of 8 : 2. Until 7 days of age, the drying shrinkage remarkably increased up to $1\~2\times10^{-4}$, while it tended to decrease as the ratio of polymer to cement ratio and the content of shrinkage-reducing agent increased. Polymer-cement ratio was effective in improving the flexural, tensile and adhesive strengths: As the ratio increased, the strengths correspondingly increased. The flexural strength was in the range of $7\~11$ MPa, the tensile strength was $3.5\~5$ MPa and the adhesive strength was $1.2\~3.9$ MPa. On the other hand, the compressive strength tended to decrease as the polymer-cement ratio increased, and it was in the range of $23\~39$ MPa. All strengths, flexural, tensile, adhesive and compressive strengths, decreased as the content of powder shrinkage-reducing agent increased. It turned out that the polymer-cement ratio influenced more on the behavior of drying shrinkage and the properties of strength than the powder shrinkage-reducing agent did.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.289-298
• /
• 2023

In this study, the development of a self-healing concrete waterproofing agent was examined, focusing on its manufacturing and waterproofing properties. The optimal ratio using microcapsules for the concrete waterproofing agent was determined through assessments of flow, compressive strength, and permeability conducted during the mortar stage. These findings aimed to provide fundamental data for evaluating the self-healing properties of the concrete waterproofing agent designed for use in concrete structures. The self-healing concrete waterproofing agent was comprised of three types of inorganic materials commonly used for repair purposes. From experimental results, a composition ratio with a high potassium silicate content, referred to as SIM-2, was found suitable. A surfactant mixing ratio of 0.03 % was identified to enhance the dispersibility of the concrete waterproofing agent, while a mixing ratio of 0.2 % distilled water was deemed suitable for viscosity adjustment. For the magnetic self-healing concrete waterproofing agent's healing agent, using microcapsules in the range of 0.5 % to 0.7 % met the KS F 4949 and KS F 4926 standards.