• Fire Science and Engineering
• /
• v.25 no.1
• /
• pp.42-49
• /
• 2011

In the high temperature situation like in a fire, the high strength of concrete (HSC) has extreme danger named explosive spalling. It is assumed that the major cause of explosive spalling is water vapour pressure inside concrete. This paper examines the effect of the compressive strength and the moisture content on the initial occurrence of explosive spalling. For the effective experiment of the initial explosive spalling, the curve of ISO834 temperature profile is applied on the basis of 15 minute and 30 minute. As a result, the more increase the compressive strength and the moisture content, the more increase the occurrence and phenomenon of explosive spalling. This paper analyzes the territory of explosive spalling depending the compressive strength and the moisture content. The explosive spalling is not examined in the case of the compressive strength 50~100 MPa and the moisture content below 3% and the compressive strength over 100 MPa and the moisture content below 1%. Also, due to the HSC, which makes it more difficult to transport vapour and moisture, very high vapour-pressure may occur close to the surface, there is a greater risk that HSC spalls compared with normal strength concrete (NSC).

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.4
• /
• pp.115-122
• /
• 2008

This paper is to investigate the affecting factors on spalling of the high strength concrete including W/B, air content and moisture condition as well as PP fiber contents subjected to fire. An increase with 0.05% of PP fiber resulted in a reduction of slump flow by as much as 11%. Ten percent of air contents due to excessive amounts of AE agent does not lead to variance of slump flow, regardless of PP fiber content. For the effect of the compressive strength, high strength concrete with 15, 25 and 35% of W/B gained 60 MPa~100 MPa of the compressive strength. High strength concrete with H-air had half of compressive strength of that with L-air due to large amount of air. Fire test was conducted in accordance with KS F 2257-1 for 1 hour. Spalling did not occur with all specimens containing more than 0.10% of PP fiber except those with 15% of W/B. Moreover, it is interesting to note that the specimens with more than 10% of air content and with oven dried condition, respectively, had no spalling even if the content of PP fiber is 0.05 vol.%.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1105-1108
• /
• 2008

This paper investigated measures of spalling prevention and mechanism to secure stability of subjected to a fire circumstance. The results were summarized as following. 1) There were 4 kinds of methods for spalling prevention, such as declining percentage of water content and cement water ratio, isolating from high temperature with fire proof covering, giving lateral resistance stress, and discharging vapor pressure using fibers. 2) It was confirmed that methods using fibers to a new construction and fire proof covering to a existing construction on the basis of investigation for the spalling mechanism through the existing theory of spalling and a new theory of WPB.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.475-476
• /
• 2009

This study investigates fundamental and spalling resistance properties of high strength concrete, W/B 28%, designed with the various diameters and contents of PET fiber. The flowability and compressive strength showed similar tendency in the range of below 0.05vol.% of fiber content. For the spalling resistance properties after fire test, the specimens with 40${\mu}m$ diameters of fiber did not spall at 0.05vol.% of fiber content. And the specimens with 20${\mu}m$ diameters of fiber did not spall even at 0.03vol.% of fiber content.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2007.11a
• /
• pp.3-8
• /
• 2007

초고층건축물이 증가함에 따라 고강도콘크리트의 사용량이 증가하는 추세이다. 고강도콘크리트는 내구성 및 사용성이 우수한 장점을 가지고 있는 반면 화재시 심각한 폭렬현상을 발생시켜 콘크리트 내역 감소 및 철근의 노출로 인해 건물이 붕괴까지 이르게 되는 원인이 된다. 따라서 고강도콘크리트의 내화특성을 고려한 해석(열응력, 질량 이동, 폭렬) 과정을 거쳐 폭렬 저감방안을 모색하여야 한다. 이러한 폭렬 저감방안을 표층부의 온도상승 온도구배 저감 방안, 수중기압 저감/수분 이동을 용이하게 하는 방안, 폭렬억제형 피복콘크리트 이용방안, 폭렬에 의한 콘크리트의 비산을 방지하는 방안 등이 있으며 각 방안들은 장단점을 내포하고 있어 상황에 따라 탄력적으로 적용하여야 하며, 향후 고강도 콘크리트의 역학적 성상을 고려하여 단점을 보완하고 추가적인 대책용 수립할 수 있도록 많은 연구가 필요 할 것으로 판단된다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.481-482
• /
• 2009

This study analyzed fire resistance characteristics of high strength concrete according to changes in curing method and PP fiber content, and the results are as follows. First in case of standard curing, spalling was prevented at PP fiber content of 0.05 % or higher. Autoclave and steam curing showed prevention of spalling at content of 0.1 % or higher. For residual compressive strength, measurement of strength for plain was impossible due to spalling phenomenon. A satisfactory trend was shown with increase in PP fiber content with the strength of about 30 MPa.

• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.173-183
• /
• 2012

Recently, experimental studies to prevent explosive spalling based on spalling mechanism and addition of Polypropylene fiber in high strength concrete (HSC) are performed actively. However, with respect to ultra high strength concrete (UHSC), its compact internal structure is more difficult release vapor pressure at rapid rising temperature compared to HSC. Therefore, in this study, an experiment was conducted to evaluate spalling properties of UHSC using ${\Box}$ $100mm{\times}100{\times}H200mm$ rectangular specimen according to ISO-834 standard fire curve. With respect melting point of fiber, three fiber types of Polyethylene, Polypropylene, and Nylon fibers with melting temperature of $110^{\circ}C$, $165^{\circ}C$, and $225^{\circ}C$, respectively, were considered. Mixed fiber of 0.15% and 0.25% of concrete volume was used to consider spalling properties based on water vapor pressure release. Then, TGDTA test on fiber and FEM analysis were performed. The results showed that it is difficult to prevent initial spalling without loss of fiber mass even if fiber melting temperature is low. Also, in preventing thermal spalling, fiber that melts to rapidly create porosity within 10 minutes of fire is more effective than that of low melting temperature property of fiber.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2011.11a
• /
• pp.99-102
• /
• 2011

본 연구는 일본 교토대학의 유전사회(有田史繪)의(2000년(年)) "화재시 고강도 콘크리트의 폭렬에 관한 이론적 연구(火災時における高强度コンクリ-トの爆裂に關する理論的硏究)"를 고찰 한 결과 콘크리트 압축강도 Fc[kgf/$cm^2$]와 밀도[kg/$cm^3$]가 분리되면, 열과 수분의 이동에 관련된 물성치가 예측되며, 해석 모델을 통해 해석된다. 이에 대하여 내부응력과 더불어 열특성, 콘크리트의 역학특성, 강재의 역학특성을 파악하여 내화설계를 구축을 위한 기초자료로 제시하였다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.381-384
• /
• 2008

This study investigated spalling prevention and fire resistance properties of the high strength concrete using pre-mixed cement containing fiber to prepare the method for the effective throwing of hybrid fiber. For result of a fire test, almost specimens were protected from fire except 15% of W/C. Totally, the pre-mixed cement containing fiber was favorable compared with passive mixing method for the spalling prevention. It is more effective to prevent spalling caused by fine diversion of fiber even in high strength concrete because it contained many corporate materials. Moreover, the temperature history of the side steel bar on the column test with pre-mixed cement containing fiber did not over 538$^{\circ}C$ which is the average for the standard of fire resistance performance.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.3
• /
• pp.223-229
• /
• 2014

In this study, the fire resistance of high strength concrete with organic fibers and polymer powder (PW) was investigated. Two types of the specimens of ${\phi}100{\times}200mm$ and $300{\times}300{\times}600mm$ sizes were prepared. As a result of the test, it was found that the fiber-to-PW mixing ratio of 1:1 achieved the highest fluidity. Further, it was found that the mixing ratios of PP 0.05% + PW 0.05%, PNY 0.05% + PW 0.05% was sufficient to protect the high strength concrete from spalling. For the mock-up specimens of $300{\times}300{\times}600mm$ size, if the required amounts of fibers were added in the concrete. the concrete spalling was resisted. Likewise, in the case of the polymix (PM) together with PW, all the tested specimens were satisfactory for fire resistance performance.