• 열처리공학회지
• /
• 제29권1호
• /
• pp.8-14
• /
• 2016

This article presents a study on the tensile properties of hypoeutectoid steels with different ferrite-pearlite microstructures. Nine kinds of hypoeutectoid steel specimens were fabricated by varying carbon content and isothermal transformation temperature. The microstructural factors such as ferrite & pearlite fraction, interlamellar spacing, and cementite thickness were quantitatively measured and then tensile tests were carried out on the specimens in order to investigate the correlation of the microstructural factors with strength and ductility. The pearlite volume fraction usually increased with decreasing transformation temperature, while the pearlite interlamellar spacing and cementite thickness decreased mostly with decreasing transformation temperature, irrespective of carbon content. The tensile test results showed that the yield and tensile strengths of all the steel specimens increased and their ductility was also improved as the transformation temperature decreased. For the steel specimens investigated, the difference in the transformation temperature dependence of strength and ductility could be explained by the fact that the variation in pearlite fraction with transformation temperature noticeably affected various microstructural factors such as pearlite interlamellar spacing and cementite thickness associated with pearlite fracture mechanism such as void initiation, cementite necking, and cracking.

• 한국재료학회지
• /
• 제28권10호
• /
• pp.570-577
• /
• 2018

This study examines the effect of microstructural factors on the strength and deformability of ferrite-pearlite steels. Six kinds of ferrite-pearlite steel specimens are fabricated with the addition of different amounst of Mn and V and with varying the isothermal transformation temperature. The Mn steel specimen with a highest Mn content has the highest pearlite volume fraction because Mn addition inhibits the formation of ferrite. The V steel specimen with a highest V content has the finest ferrite grain size and lowest pearlite volume fraction because a large amount of ferrite forms in fine austenite grain boundaries that are generated by the pinning effect of many VC precipitates. On the other hand, the room-temperature tensile test results show that the V steel specimen has a longer yield point elongation than other specimens due to the highest ferrite volume fraction. The V specimen has the highest yield strength because of a larger amount of VC precipitates and grain refinement strengthening, while the Mn specimen has the highest tensile strength because the highest pearlite volume fraction largely enhances work hardening. Furthermore, the tensile strength increases with a higher transformation temperature because increasing the precipitate fraction with a higher transformation temperature improves work hardening. The results reveal that an increasing transformation temperature decreases the yield ratio. Meanwhile, the yield ratio decreases with an increasing ferrite grain size because ferrite grain size refinement largely increases the yield strength. However, the uniform elongation shows no significant changes of the microstructural factors.

• 한국재료학회지
• /
• 제25권11호
• /
• pp.583-589
• /
• 2015

This paper presents a study on the room- and low-temperature impact toughness of hypoeutectoid steels with ferrite-pearlite structures. Six kinds of hypoeutectoid steel specimens were fabricated by varying the carbon content and austenitizing temperature to investigate the effect of microstructural factors such as pearlite volume fraction, interlamellar spacing, and cementite thickness on the impact toughness. The pearlite volume fraction usually increased with increasing carbon content and austenitizing temperature, while the pearlite interlamellar spacing and cementite thickness mostly decreased with increasing carbon content and austenitizing temperature. The 30C steel with medium pearlite volume fraction and higher manganese content, on the other hand, even though it had a higher volume fraction of pearlite than did the 20C steel, showed a better low-temperature toughness due to its having the lowest ductile-brittle transition temperature. This is because various microstructural factors in addition to the pearlite volume fraction largely affect the ductile-brittle transition temperature and low-temperature toughness of hypoeutectoid steels with ferrite-pearlite structure. In order to improve the room- and low-temperature impact toughness of hypoeutectoid steels with different ferrite-pearlite structures, therefore, more systematic studies are required to understand the effects of various microstructural factors on impact toughness, with a viewpoint of ductile-brittle transition temperature.

• 한국재료학회지
• /
• 제27권4호
• /
• pp.184-191
• /
• 2017

This present study deals with the effect of micro-alloying elements and transformation temperature on the correlation of microstructure and tensile properties of low-carbon steels with ferrite-pearlite microstructure. Six kinds of low-carbon steel specimens were fabricated by adding micro-alloying elements of Nb, Ti and V, and by varying isothermal transformation temperature. Ferrite grain size of the specimens containing mirco-alloying elements was smaller than that of the Base specimens because of pinning effect by the precipitates of carbonitrides at austenite grain boundaries. The pearlite interlamellar spacing and cementite thickness decreased with decreasing transformation temperature, while the pearlite volume fraction was hardly affected by micro-alloying elements and transformation temperature. The room-temperature tensile test results showed that the yield strength increased mostly with decreasing ferrite grain size and elongation was slightly improved as the ferrite grain size and pearlite interlamellar spacing decreased. All the specimens exhibited a discontinuous yielding behavior and the yield point elongation of the Nb4 and TiNbV specimens containing micro-alloying elements was larger than that of the Base specimens, presumably due to repetitive pinning and release of dislocation by the fine precipitates of carbonitrides.

• Journal of Plant Biotechnology
• /
• 제42권1호
• /
• pp.49-54
• /
• 2015

본 연구의 결과를 바탕으로 중요한 양앵두 왜성대목의 하나인 'Gisela 5'의 미세번식을 위한 일련의 체계적 과정을 제안한다. 봄철 새롭게 생장한 신초로부터 절취한 정단조직을 IBA 0.5 mg/L와 BA 0.5 또는 1.0 mg/L가 첨가된 1/2MS배지에 치상하였을 때 hyperhydricity가 없고 왕성한 생장을 하는 정상 신초의 획득율이 90%에 달하였다. 다음단계로, 기내에서 유지된 모식물체로부터 채취한 신초를 IBA 0.5 mg/L와 BA 0.5 mg/L가 첨가된 전MS배지에 이식하면 약 9배에 이르는 수준으로 신초가 증식되었다. 증식된 신초는 IBA 2.0 mg/L가 첨가된 1/2MS배지로 이식하면 지상부의 정상생장과 함께 왕성하게 발근하였다. 발근한 유식물체는 비교적 손쉽게 최종적으로 기외 순화시킬 수 있었는데, 기외 이식 상토로는 버미큘라이트, 펄라이트 및 피트모스의 혼합비율을 1:1:1로 하는 것이 가장 적합하였다. 본 연구의 결과가 양앵두 재배와 양앵두 대목의 생산에 유용하게 활용되기를 기대한다.

• 대한기계학회논문집A
• /
• 제41권8호
• /
• pp.721-728
• /
• 2017

보통회주철(GC300)에 Cr, Mo, Cu 첨가제를 넣어 고급 회주철(HCI350)을 제작하고, 미세 조직과 기계적 물성치, 피로강도의 변화를 연구하였다. 주철을 환봉형과 평판형 주물로 제작하였으며, 이들을 절단 및 연마하여 나이탈 수용액으로 에칭한 후 미세조직의 면적비율을 측정하였다. 첨가물에 의해 편상 흑연결정(flake graphite)의 크기가 감소하고 고밀 펄라이트 함량이 증가하여 인장강도, 피로강도의 향상이 확인되었다. 피로시험 결과 획득한 피로수명 데이터를 바탕으로 최우추정법이 적용된 2모수 와이블 분포를 이용하여 확률-응력-수명 곡선을 산출하였다. 확률-응력-수명곡선 산출 결과 HCI350은 GC300에 비해 피로강도는 크게 개선되었고 수명데이터의 분산성은 낮아졌으나, 피로응력완화에 따른 피로수명의 증가가 크게 나타났다. 산출된 확률-응력-수명 곡선을 이용하여 요구수명 사이클 수에 대한 허용응력 값을 정량적으로 제시함으로써 신뢰성 수명설계에 위한 기초자료를 제시하였다.

• 한국주조공학회지
• /
• 제43권6호
• /
• pp.279-285
• /
• 2023

본 연구에서는 임계간 온도 범위에서 열처리한 구상흑연주철의 열처리 온도에 따른 물성 예측을 위해, 인장강도 450 MPa 급 구상흑연주철을 다양한 온도에서 열처리한 후 공냉하여 물성 예측에 필요한 미세조직을 분석하고 브리넬 경도를 측정하였다. 임계간 온도 구간에서 열처리 온도가 증가할수록 구상흑연주철 내 페라이트 분율은 감소함과 동시에 펄라이트 분율은 증가하였으나, 흑연 구상화율 및 구상흑연입수는 주방상태에서 측정된 값과 유사하였다. 열처리한 구상흑연주철의 브리넬 경도는 열처리 온도가 증가할수록 점점 증가하였다. 측정된 합금 조성 및 각 안정상의 분율, 그리고 문헌에 알려진 구상흑연주철의 브리넬 경도 예측 모델을 활용하여 열처리 온도 별 구상흑연주철의 경도 값을 계산해 본 결과, 측정값과 매우 유사한 값을 얻을 수 있었다. 또한 열역학 계산을 통해 예측된 상분율을 활용하여 정확한 경도 예측이 가능할지 확인해보기 위해, 열처리 온도 별로 구상흑연주철 내 흑연, 페라이트 및 오스테나이트의 부피를 계산한 후, 이를 면적으로 변환하여 동일한 구상흑연주철의 경도 예측 모델에 적용하였다. 이렇게 열역학 계산과 경도 예측 모델을 동시에 활용하여 계산된 구상흑연주철의 경도 값은 실제 측정한 브리넬 경도 대비 최대 27의 오차 범위 내에서 유사한 값을 나타내었다.

• 한국자원식물학회:학술대회논문집
• /
• 한국자원식물학회 2019년도 춘계학술대회
• /
• pp.57-57
• /
• 2019

본 연구는 관상 및 조경용으로 개발이 가능한 남방계 양치식물인 점고사리[Hypolepis punctata (Thunb.) Mett.]의 전엽체 증식 및 포자체 형성에 적합한 배양조건을 구명하고자 수행되었다. 무가온 온실에서 성숙한 포자엽을 채집한 후 포자를 기내에서 발아시켜 전엽체를 획득하였으며, 8주 간격으로 계대배양 하여 실험의 재료로 사용하였다. 배지종류에 따른 전엽체의 증식 및 형태형성을 확인하고자, 배양된 전엽체 0.3g을 메스로 잘게 다진 후, 농도를 1/4, 1/2, 1, 2배로 조절한 MS배지에 8주간 배양하였다. 이후 선발된 배지를 기준으로 sucrose, 활성탄, 질소급원의 농도를 조절하여 전엽체의 증식과 형태형성을 확인하였다. 그 결과, 1MS배지에서 전엽체의 생체중이 초기 접종량인 0.3g에 비해 10.7배 증가한 3.2g으로 가장 높은 증가율을 보였다. 형태관찰에서도 장정기의 형성이 관찰되었으며, 전엽체의 쿠션조직이 비교적 잘 발달하였다. 전엽체 증식에 가장 좋은 효과를 보인 1MS배지를 기준으로 sucrose의 농도를 0-4%로 달리하여 실험한 결과, 1%의 처리구에서 6.7g으로 가장 높은 생체중을 보였다. 활성탄의 농도를 0-0.8%로 첨가한 네 처리구 중에서는 0.8%의 처리구에서 14.2g으로 무처리구에 비해 생체중이 2배 이상 증가하였다. 전엽체의 형태 또한 정상적인 발달을 보였다. 질소급원의 비율을 30-120mM로 조절한 배지에서는 60mM의 처리구에서 4.9g으로 가장 높은 생체중을보였다. 이후 포자체 형성을 위한 최적의 토양조건을 구명하고자, 원예상토, 피트모스, 펄라이트 및 마사토의 비율을 달리하여 5종류의 배양토를 조성하였다. 혼합된 토양은 사각분($7.5{\times}7.5{\times}7.5cm$)에 충진 하였으며, 배양된 전엽체 1g을 증류수와 함께 10초간 분쇄한 다음 준비된 토양표면에 분주하여 재배하였다. 12주간의 재배 결과, 원예상토를 단용한 토양에서 포자체의 수가 포트당 250.0개로 가장 많이 형성되었으며, 포자체의 생육 또한 다른 처리구에 비해 우수한 결과를 보였다. 한편 피트모스가 혼합된 토양에서는 포자체가 형성되지 않았다. 따라서 점고사리의 전엽체 대량증식에 적합한 배지는 sucrose 1%와 질소급원의 농도를 60mM, 활성탄을 0.8% 첨가한 1MS배지로 판단되며, 포자체 대량생산을 위해서는 원예상토를 단용한 토양이 적합하다고 판단된다.

• 한국지능시스템학회:학술대회논문집
• /
• 한국퍼지및지능시스템학회 2003년도 추계 학술대회 학술발표 논문집
• /
• pp.105-119
• /
• 2003

일반적인 로봇시스템은 자신이 이동해야 할 목표 지점을 자율적으로 생성할 수 없으므로 어떤 다른 시스템의 정보를 이용하여 주변을 탐색하거나 장애물을 인식하고 식별하여 자신의 제어전략을 수립한다. 그러므로 본 논문에서 제시한 시스템은 초소형 비행체를 이용하여 주위 환경과 자율 이동로봇의 위치 정보를 탐색할 수 있도록 시스템을 구성하였다 이러한 시스템의 성능은 로봇이 위치하고 있는 주위의 불완전한 정보로부터 적절한 결론을 유도해 낼 수 있어야 한다. 그러한 비선형적인 문제는 현재까지도 문제 해결을 위해 많은 연구가 진행되고 있다. 본 연구에서는 자율이동로봇의 행동 환경을 공간상의 제약을 받지 않는 비선형 시스템인 초소형 비행체에 극초단파(UHF16채널) 영상장치를 이용하여 호스트 PC로 전송하고 호스트 PC는 로봇의 현재 위치, 이동해야 할 목표위치, 장애물의 위치와 형태 등을 분석한다. 분석된 결과 파라메타는 RF-Module을 이용해서 로봇에 전송하고, 로봇은 그 데이터를 분석하여 동작하게 된다. 로봇이 오동작 또는 장애물로 인해 정확한 목적지까지 도달하지 못할 때 호스트 PC는 새로운 최단경로를 생성하거나 장애물을 회피 할 새로운 전략을 로봇에게 보내준다. 본 연구에 적용한 알고리즘은 초소형 비행체에서 탐지한 불완전한 영상정보에서도 비교적 신뢰도 놀은 결과를 보이는 A* 알고리즘을 사용하였다 적용한 알고리즘은 실험을 통하여 실시간으로 정보를 처리할 수 있었으며, 자율 이동로봇의 충돌회피나 최단 경로 생성과 같은 문제를 실험을 통하여 그 성능과 타당성을 검토하였다.delta}textitH]$를 도출하였다.rc}C$에서 30 ㎫의 압력으로 1시간동안 행하였다 소결한 시편들은 직사각형 형태로 가공하였으며 표면은 0.5$\mu\textrm{m}$의 다이아몬드 입자로 연마하였다. XRD, SEM 및 TEM을 이용하여 상분석 및 미세조직관찰을 행하였다. 파괴강도는 3중점 굽힘 법으로 (3-point bending test) 측정하였다. 이때 시편 하부의 지지 점간의 거리는 30mm, cross-head 속도는 0.5 mm/min으로 하였고 5개의 시편을 측정하여 평균값을 구하였다.ell/\textrm{cm}^3$, 혼합재료 3은 0.123$\ell/\textrm{cm}^3$, 0.017$\ell/\textrm{cm}^3$, 혼합재료 4는 0.055$\ell/\textrm{cm}^3$, 0.016$\ell/\textrm{cm}^3$, 혼합재료 5는 0.031$\ell/\textrm{cm}^3$, 0.015$\ell/\textrm{cm}^3$, 혼합재료 6은 0.111$\ell/\textrm{cm}^3$, 0.020$\ell/\textrm{cm}^3$로 나타났다. 3. 단일재료의 악취흡착성능 실험결과 암모니아는 코코넛, 소나무수피, 왕겨에서 흡착능력이 우수하게 나타났으며, 황화수소는 펄라이트, 왕겨, 소나무수피에서 다른 재료에 비하여 상대적으로

• 화훼연구
• /
• 제18권1호
• /
• pp.50-56
• /
• 2010

본 실험은 분식물의 삽목번식시 배지에 첨가한 규산질 비료가 분식물의 발근과 생육에 미치는 영향을 조사하였다. 칼란코에 'Kaluna'와 'Taos' 품종은 50구 트레이에 번식하였고 카네이션 'Kazan'과 'Tula' 품종은 128구 트레이에 삽목하였다. 규산질 비료를 상업배지(토실이 상토, 신안그로)와 펄라이트를 5 : 1(v/v)로 섞어 배지 1L당 규산질 비료[MgCa(SiO3)2]를 0, 40, 80, 120, 또는 160g을 첨가하여 발근한 후 정식하였다. 두 작물 모두 배지 1L당 규산질 비료를 40g 첨가한 처리구에서 초장, 엽두께, 뿌리의 생체중과 건물중이 가장 높았다. 하지만 두 작물 모두 규산질 비료의 농도가 높아질수록 초장이 억제되었다. 주사전자현미경(SEM) 촬영을 통한 식물조직 관찰 결과 규산질 비료를 첨가해주었을 경우 뿌리와 잎의 조직이 더 조밀해졌다.