• Polymer(Korea)
• /
• v.28 no.3
• /
• pp.253-262
• /
• 2004

Poly(vinyl alcohol)(PVA)/chitosan blend films with non-toxicity, biodegradability, and biocom-patibility were prepared by solution casting. Variation of the physicochemical properties of the blend films was investigated through to several analysis methods. Examination of antibacterial properties revealed that bacterio-static ratios of all blend samples containing chitosan more than 10 wt％ were greater than 99.9％. Moisture regain was increased with increasing chitosan content but the degree of swelling was decreased. Up to chitosan content 15 wt％t, the melting and crystallization temperature of blend films was increased with chitosan content. The blends containing chitosan content 10 and 15 wt％ gave melting temperature 229 and 228$^{\circ}C$, respectively. However, the melting temperature was decreased if chitosan content exceeded 20 wt％. The mechanical properties of the blend films were increased with increasing chitosan content in both dry and wet states. The blend film including 15 wt％ chitosan exhibited unusually high tensile strength.

• Elastomers and Composites
• /
• v.33 no.4
• /
• pp.281-289
• /
• 1998

Tensile properties including Young's modulus and tear strength were measured for four different rubber compounds; natural rubber(NR), styrene-butadiene copolymer(SBR), ethylene-propylene diene monomer (EPDM), and brominated isobutylene-p-methyl-styrene copolymer(BIMS) as a function of temperature and degree of cure. To see the effect of over cure, a measurement was made of the tensile strength and swelling behavior of the over-cured rubber compounds. Young's modulus, E, was found to have linear dependency on the degree of cure for all rubber compounds. EPDM and BIMS showed the highest and lowest slopes, respectively. The slope of NR and SBR lay between EPDM and BIMS. Tear strength, Gc, decreased in the order of NR>BIMS>SBR>EPDM. As the cure time was extended the degree of cure of NR and SBR decreased, while that of BIMS increased. EPDM showed little change in the degree of cure.

• Journal of Digital Convergence
• /
• v.19 no.3
• /
• pp.287-293
• /
• 2021

Tablets were conventionally used to treat choline urticaria. Disadvantages of tablets included sleep inducing problems, accessibility and reduced dosage. To address this, hydrogel containing Cetirizine HCl was manufactured. The experimental method was to measure viscosity, gel fraction, degree of swelling, content evaluation, and permeability. Studies have shown that hydrogels containing Cetirizine HCl can be directly applied to occurrence area to improve Cholinergic urticaric with minimal side effects associated with the marketable tablets. This hydrogel includes other important substances including steroids which gives it an advantage when applied on the skin, improving its accessibility. In addition, it is expected that the drug manufacturing process will be able to proceed as this hydrogel is effective even when used alone.

• Nuclear Engineering and Technology
• /
• v.8 no.2
• /
• pp.89-99
• /
• 1976

The grafting of acrylic acid in aqueous solution to polyvinyl chloride fibers tab been studied in the presence of ferrous, ferric, and cupric salts, The mutual irradiation technique was adopted using a Co-60 source or a Van do Graaff accelerator. The grafting and homopolymerization were suppressed by the cations. Particularly the grafting was suppressed by the cations in the following order of effectiveness : $Cu^{2+}$>$Fe^{2+}$>$Cu^{3+}$. The rate of grafting (in %/hr) was proportional to the 0.76th power of the dose rate over the range from 8.5f $10^3$ rad/hr to $1.4\times10^5$ rad/dr. The apparent activation energy for the grafting was determined to be 6.1 Kcal/mole between $25^{\circ}$ and $75^{\circ}C$ for the mixture of AA-HaO-$(CH_2Cl)_2$, containing Mohr's salt, $4\times10^{-3}$ mole/l. The increase of the grafting was observed when total dose and dose intensity were raised, or when ethylene dichloride as a swelling agent was saturated in the monomer mixture. The grafted polyvinyl chloride fibers showed considerable improvement in moisture regain, heat shrinkage, and melting properties, but tensile properties were not significantly affected by grafting.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.5 no.1
• /
• pp.6-12
• /
• 1999

This study was conducted to investigate the application of edible films to Raymyun soup packaging. The sorption isotherm curve and BET monolayer moisture content of Raymyun soup were estimated as a basic experiment. Also, the mechanical properties, water vapor permeability, and solubility of the films were investigated. Methylcellulose, sodium caseinate, and K-carrageenan films were used as edible films and glycerol and polyethylene glycol(MW 400) were used as plasticizers. In case tensile strength, methylcellulose films was 68.56 MPa and sodium caseinate film was 7.11 MPa. The elongations of sodium caseinate, methylcellulose, and K-carrageenan film were 115.41%, 23.79% and 0.60%, respectively. The water vapor permeabilties values of methylcellulose, sodium caseinate, and K-carrageenan film between 50% and 70% RH were $0.25-0.38ng{\cdot}m/m^2{\cdot}sec{\cdot}Pa,\;0.62-0.84ng{\cdot}m/m^2{\cdot}sec{\cdot}Pa\;and\;0.31-0.55ng{\cdot}m/m^2{\cdot}sec{\cdot}Pa$, respectively. For the solubility of films, sodium caseinate film showed the highest solubility and methylcellulose film showed the lowest solubility.

• Clean Technology
• /
• v.18 no.1
• /
• pp.57-62
• /
• 2012

Aqueous poly (vinyl alcohol) (PVA) solution was modified by using hydrophobic vinyltriethoxysilane (VTEOS) and then adding different amounts of poly (acrylic acid) (PAA) to the resulting solution. Thermal and mechanical properties, contact angle, water vapor transmission rate (MVTR) and oxygen gas transmission rate ($O_2TR$) of the film samples fabricated by these solutions were investigated. The glass transition temperature (Tg) of the VTEOS-modified films was sightly increased and the value remained unchanged according to the amount of PAA. The tensile strength of the VTEOS-modified films was found to be 9.48~10.72 $kg/mm^2$ which showed no significant difference compared with that of PVA. The film prepared with VTEOS-modified PVA/PAA (= 90/10), of which the swelling and solubility were measured to be 198% and 0%, respectively, showed improved water-resistance. The MVTR and $O_2TR$ for the PET film (thickness 50 ${\mu}m$) coated with VTEOS-modified PVA/PAA (= 90/10) film (thickness 2.5 ${\mu}m$) were measured to be 11.04 $g/m^2/day$ and 3.1 $cc/m^2/day$, respectively.

• Korean Chemical Engineering Research
• /
• v.55 no.1
• /
• pp.34-39
• /
• 2017

In this study, intermolecular crosslinked carboxymethyl cellulose sodium salt (CMC) and porcine Cartilage Acellular Matrix (PCAM) blended hydrogel films for anti-adhesive barriers were prepared by gamma-ray radiation. The effects of the CMC/PCAM concentration and blending ratio on the morphology, gel fraction, gel strength, and degree of swelling were determined. The results indicated that crosslinked CMC/PCAM films show significantly lower the gel-fraction than CMC films. The degree of attachment and proliferation of human vascular endothelial cells on CMC/PCAM films was lower than the CMC films. We show the capacity of the CMC and PCAM to be hydrogel films, and the ability to reduce cell adhesion and proliferation on these films by modification with cell anti-adhesion molecules of PCAM. In conclusion, this study suggests that radiation cross-linked CMC/PCAM hydrogel films endowed with anti-adhesion ligands may allow for improved regulation of cell anti-adhesion behavior for prevent peritoneal adhesions.

• Nuclear Engineering and Technology
• /
• v.8 no.4
• /
• pp.231-242
• /
• 1976

The effects of temperature and pressure of leaching water on the leaching of radionuclides from bitumen-waste products were studied. The principal results are as follows: The fraction of $^{90}$ Sr and $^{137}$ Cs leached for periods of up to 120 days at 8atm was 2.1$\times$10$^{-6}$ ($\textrm{cm}^2$/g)$^{-1}$ , day$^{-1}$ and 6.02$\times$10$^{-5}$ ($\textrm{cm}^2$/g)$^{-1}$ day$^{-1}$ respectively and at 5$^{\circ}C$, 1.7$\times$10$^{-5}$ ($\textrm{cm}^2$/g)$^{-1}$ day$^{-1}$ and 4.01$\times$10$^{-5}$ ($\textrm{cm}^2$/g)$^{-1}$ day$^{-1}$ respectively. These values were lower than those in atmospheric pressure and room temperature. No diffence in the leaching rate with sea and distilled water was observed for the bitumen-waste products containing 40wt% salts. It appears that these results could be saved by improving safety in the dumping of sea. The effect of the softening point of pure asphalt or bitumen-waste product by $^{60}$ Co irradiation was increased with increasing total dose. Irradiation of asphalts at a total dose of 5.8$\times$10$^{8}$ rad showed no evidence of volume and caused no swelling. The functional groups of blown asphalt by infrared spectra are also identified.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.1
• /
• pp.62-71
• /
• 2017

This study was investigated on the properties of board made from carbonized rice husk differed in density of board, resin addition ratio and sawdust addition ratio. Water absorption is showed the lowest value to 80.09% when the resin addition ratio of 25%, as the density increased and sawdust addition ratio decreased, the water absorption was decreased. The measured thickness swelling satisfied with the quality standards of KS F 3104, so the feasibility of building interior has been confirmed in the dimensional stability. In case of resin addition ratio of 25%, the internal bond strength was satisfied quality standards of KS F 3104 to $0.244N/mm^2$. With increasing the density, resin and sawdust addition ratio, brinell hardness increased.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.103-103
• /
• 2011

비스코스레이온(Viscose Rayon)소재는 목재 펄프를 원료로 한 재생섬유(습식방사)로서 Drape성과 반발성은 탁월하나, 습식방사에 따른 분자구조적 불안정성으로 건 습열처리시 형태불안정(치수변화율이 큼)으로 제직(준비) 및 후공정상 여러 가지 Trouble 유발과 완제품 세탁시 수축발생으로 종종 Dry Creanning 해야 하는 문제점들이 내재되어 있다. 또한 수분흡수시 강도저하, 수축과 구김, 염색 불균염 등의 문제점과 섬유공정상 생활취급상에 많은 애로를 가지고 있으며, 구성고분자가 수소결합에 의해 강고하여 "신축문제", 수분흡수시 팽윤(Swelling)에 의한 형태불안, 즉 "수축문제"가 개선해야 할 고질적 문제로 남아있다. 따라서 본 연구에서는 레이온 소재의 형태안정화 제품을 개발하기 위하여 복합사고공 및 염색가공 기술을 개발하고자한다. 신축 및 복합기술에 의한 Rayon DTY, N/R 신축 및 복합기술에 의한 Rayon DTY, N/R 복합가공사를 개발, 제편직 요소기술과 염가공기술을 연구하므로서 형태안정성 레이온 복합소재 제품을 개발하고자 한다. Rayon 소재의 후공정 용이성과 형태안정성을 부여하기 위하여, 레이온 DTY가공사, Rayon-합섬 장(長)-장(長) 복합사를 개발하여 CoolBiz용 냉감소재 및 스포츠 웨어 소재 등으로 활용하고자 한다. 사가공기술에 의한 신도 16%, 수축률 1.6%인 형태안정 Rayon DTY 소재를 개발하였으며, 선연후가공기술에 의하여 N/R 복합가공사를 개발, 신도 18%, 수축률 1.2%인 차별화 레이온 소재를 개발하였다. 이에 기존 Rayon 후가공 및 염색공정과 상이한 개발된 선연후 가연 Rayon DTY가공사 및 T/R혼방사를 활용한 직물에 대하여 최적 전처리, 염색 후가공 공정의 최적 조건을 알아보았다.