• Restorative Dentistry and Endodontics
• /
• v.35 no.2
• /
• pp.106-115
• /
• 2010

The purpose of this study was to evaluate the microtensile bond strength (${\mu}TBS$), failure modes and bonding interfaces of self-etching and three self-adhesive resin cements to dentin and indirect composite resin. Cylindrical composite blocks (Tescera, Bisco Inc.) were luted with resin cements (PA: Panavia F 2.0, Kuraray Medical Inc., RE: RelyX Unicem Clicker, 3M ESPE., MA: Maxem, Kerr Co., BI: BisCem, Bisco Inc.) on the prepared occlusal dentin surfaces of 20 extracted molars. After storage in distilled water for 24 h, $1.0\;mm\;{\times}\;1.0\;mm$ composite-dentin beams were prepared. ${\mu}TBS$ was tested at a cross-head speed of 0.5 mm/min. Data were analyzed with one-way ANOVA and Tukey's HSD test. Dentin sides of all fractured specimens and interfaces of resin cements-dentin or resin cements-composite were examined at FESEM (Field Emission-Scanning Electron Microscope). In conclusion, PA and RE showed higher bond strength and closer adaptation than MA and BI when indirect composite blocks were luted to dentin using a self-etching and three self-adhesive resin cements.

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.397-405
• /
• 2009

This study compared the effect of an activator, intermediate bonding resin and low-viscosity flowable resin on the microtensile bond strength of a self-curing composite resin used with two-step total etching adhesives. Twenty extracted permanent molars were used. The teeth were assigned randomly to nine groups (n=10) according to the adhesive system and application of additional methods (activator, intermediate adhesive, flowable resin). The bonding agents and additional applications of each group were applied to the dentin surfaces. Self-curing composite resin buildups were made for each tooth to form a core, 5mm in height. The restored teeth were then stored in distilled water at room temperature for 24h before sectioning. The microtensile bond strength of all specimens was examined. The data was analyzed statistically by one-way ANOVA and a Scheffe's test. The application of an intermediate bonding resin (Optibond FL adhesive) and low-viscosity flowable resin (Tetric N-flow) produced higher bond strength than that with the activator in all groups. Regardless of the method selected, Optibond solo plus produced the lowest ${\mu}TBS$ to dentin. The failure modes of the tested dentin bonding agents were mostly adhesive failure but there were some cases showed cohesive failure in the resin.

• Restorative Dentistry and Endodontics
• /
• v.35 no.6
• /
• pp.486-491
• /
• 2010

Objectives: This study examined the effect of 2% chlorhexidine on the ${\mu}TBS$ of a direct composite restoration using one-step self-etch adhesives on human dentin. Materials and Methods: Twenty-four extracted permanent molars were used. The teeth were assigned randomly to six groups (n = 10), according to the adhesive system and application of chlorhexidine. With or without the application of chlorhexidine, each adhesive system was applied to the dentin surface. After the bonding procedure, light-cure composite resin buildups were produced. The restored teeth were stored in distilled water at room temperature for 24 hours, and then cut and glued to the jig of the microtensile testing machine. A tensile load was applied until the specimen failed. The failure mode was examined using an operating microscope. The data was analyzed statistically using one-way ANOVA, Student's t-test (p < 0.05) and Scheffet's test. Results: Regardless of the application of chlorhexidine, the Clearfil $S^3$ Bond showed the highest ${\mu}TBS$, followed by G-Bond and Xeno V. Adhesive failure was the main failure mode of the dentin bonding agents tested with some samples showing cohesive failure. Conclusions: The application of 2% chlorhexidine did not affect the ${\mu}TBS$ of the resin composite to the dentin using a one-step self-etch adhesive.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.4
• /
• pp.661-672
• /
• 2006

This study was performed to compare the shear bond strength of AQ Bond $Plus^{TM}$ with AQ $Bond^{TM}$ and Single $Bond^{TM}$. Also by observing the fractured interface under scanning electro-microscope, the fracture pattern and the quality of hybrid layer were analyzed. The possibility of clinical application of all-in-one system which has an advantage to reduce chair time for children with difficult behavior pattern was evaluated, The results obtained are as follows ; 1. There was no significant difference between AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$ in shear bond strength and Single Bond showed the highest bond strength with statistical significant difference (p<0.05). 2. Adhesive fracture pattern was mainly observed in both enamel/dentin in AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$ group while Single Bond group showed equal numbers for cohesive and adhesive pattern. 3. Under scanning electro-microscope, resin tags observed in AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$ were very weak and tangled while strong and thick tags were shown with many lateral branches in Single Bond. Careful case selection and accurate clinical application is recommended when using AQ $Bond^{TM}$ and AQ Bond $Plus^{TM}$considering the result showing its weaker strength than Single $Bond^{TM}$.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.39 no.4
• /
• pp.187-194
• /
• 2023

Purpose: A mismatched size in the post and post space is a common problem during post-fixation. Since this discordance affects the bonding strength of the fiber-reinforced composite resin post (FRC Post), a corresponding luting agent is required. The aim of this study was to evaluate the bonding strength of the FRC post according to the fitness of the fiber post and the type of luting agent. Materials and Methods: Thirty mandibular premolar were endodontic-treated and assigned to two groups according to their prepared post space: Fitting (F) and Mismatching (M). These groups were further classified into three subgroups according to their luting agent: RelyX Unicem (ReX), Luxacore dual (Lux), and Duolink (Duo). A push-out test was performed to measure the push-out bond strengths. The fractured surfaces of each cross-section were then examined, and the fracture modes were classified. Results: In the ReX and Duo subgroups, the F group had a higher mean bond strength; however, the Lux subgroup had no significant difference between the F and M groups. In the analysis of the failure modes, the ReX subgroup had only adhesive failures between the cement and dentin. Conclusion: The result of this study showed that the bond strength of an FRC post was influenced by the type of luting agent and the mismatch between the diameter of the prepared post space and that of the post.

• The korean journal of orthodontics
• /
• v.28 no.6 s.71
• /
• pp.947-954
• /
• 1998

The purpose of this study was to compare shear bonding strengths and debonding patterns of the ceramic brackets attached on the crystal which were grown on the enamel surface of a tooth with different concentrations of lithium sulphate-contained polyacrylic acid in different application times. Four kinds of concentrations of mixed solutions were made and applied to the enamel surface on extracted human premolars. The solutions were made by adding 0.3M or 0.6M of lithium sulfate to $50\%\;or\;65\%$ of polyacrylic acid with 0.3M sulfuric acid. The solutions were applied for 30 or 60 seconds. After bonding, a universal testing machine was used to measure the shear bond strength, and then observations were made of debonding patterns through the stereoscope. And the enamel surface was observed through the scanning electron microscope to examine the pattern of crystal growth and debonding. The results were as follows: 1. Shear bond strength in the enamel surface treated with $50\%$ polyacrylic acid was higher than that with $65\%$ polyacrylic acid. 2. There were no statistical differences in shear bond strength according to concentration of lithium sulfate and application time of solutions . 3. Enamel surface was almost free of resin debris after debonding. 4. Enamel surface treated with $50\%$ polyacrylic acid showed higher density of crystal growth than that with $65\%$ polyacrylic acid under scanning electron microscope.

• Restorative Dentistry and Endodontics
• /
• v.34 no.2
• /
• pp.113-119
• /
• 2009

The purpose of this study was to compare the tensile bond strength of several self-adhesive resin cements bonded to dentin surfaces with different wet conditions. Three self-adhesive resin cements: Rely-X Unicem (3M ESPE, St. Paul, MN. USA). Embrace Wetbond (Pulpdent. Oakland. MA. USA). Maxcem (Kerr. Orange. CA. USA) were used. Extracted sixty human molars were used. Each self-adhesive resin cement was adhered to the dentin specimens (two rectangular sticks from each molar) in different wet conditions. Tensile bond strength were measured using universal testing machine (EZ Test. Shimadzu corporation. Kyoto. Japan) at a crosshead speed of 1.0mm/min. After the testing. bonding failures of specimens were observed by Operative microscope (OPMI pro, Carl Zeiss. Oberkochen, Germany). T-test was used to evaluate the effect of dentin surface wetness. One-way ANOVA test was used to evaluate the tensile bond strength of self-adhesive resin cements in the same condition. Scheffe's test was used for statistical analyzing at the 95% level of confidence. The result showed that wetness of dentin surface didn't affect tensile bond strength of self-adhesive resin cements and Maxcem showed the lowest tensile bond strength.

• The Journal of Korean Academy of Prosthodontics
• /
• v.60 no.1
• /
• pp.9-18
• /
• 2022

In vitro studies are essential to predict the clinical performance of ceramic widely used as restorative materials. Traditional experiments such as fracture toughness and flexural strength have been used to evaluate the properties of brittle ceramics. However, these experiments have a limitation that the load conditions, failure patterns, and load values at which failure occurs are not similar to human occlusal force ranges or clinical failures. On the other hand, the edge chipping test (ECT), which was recently introduced to study chipping fracture of ceramics, has similar failure patterns to clinical trials. In addition, the failure loads from ECT were similar to human occlusal force. ECT can be usefully used in the study of ceramic properties. In this literature review, a more clinically meaningful experimental study of ceramics by examining the meaning and limitations of traditional ceramic failure tests and comparing them with ECT.

• The korean journal of orthodontics
• /
• v.25 no.1 s.48
• /
• pp.55-72
• /
• 1995

The purpose of this study is to evaluate the effects of mechanical and thermal fatigue on the shear bond strength(SBS) in orthodontic brackets bonded to human premolars with chemically cured adhesive(Mono-$Lok^2$, Rocky Mountain Orthodontics). Two types of metal brackets (Ormesh, Microloc) and three types of ceramic brackets (Fascination, Starfire, Transcend 2000) were used in this study. The $10^6$ loadcycles of $|7.4{\times}10{^2}sin2{\pi}ft|g{\cdot}cm$ and the 1,000 thermocycles of 15 second dwell time each in $5^{\circ}C\;and\;55^{\circ}C$ baths were acturated as mechanical and thermal fatigue stress, and SBS were measured after each fatigue test. The fracture sites were examined by stereoscope and scanning electron microscope. The results obtained were summarized as follows, 1. In static shear bond test, Fascination brackets showed the maximum SBS($20.78\pm3.45$ MPa) and Microloc brackets showed the minimum SBS($14.88\pm3.10$ MPa). Fascination and Starfire brackets showed significantly greater SBS than Microloc brackets(P<0.05). 2. In mechanical fatigue test, Fascination brackets showed the maximum SBS ($20.19\pm3.45$ MPa) and Starfire brackets showed the minimum SBS($9.10\pm8.33$ MPa). The SBS or Transcend 2000 brackets(P<0.01) and Starfire brackets(P<0.05) significantly decreased after $10^6$ loadcycles. 3. In thermocycling test, Ormesh brackets showed the maximum SBS ($19.36\pm2.76$ MPa) and Starfire brackets showed the minimum SBS($11.94\pm6.86$ MPa). The SBS of Transcend 2000(P<0.01), Microloc and Starfire brackets(P<0.05) significantly decreased after $10^3$ thermocycles. 4. Failure sites of thermocycling groups were similar to those of static groups but after mechanical fatigue test, Ormesh and Transcend 2000 brackets failed at the bracket/resin interface and Microloc brackets failed within adhesive. Facination brackets failed at the enamel/resin interface irrespective of experimental condition.

• The korean journal of orthodontics
• /
• v.34 no.4 s.105
• /
• pp.325-332
• /
• 2004

A self-etching primer that combines the etchant and primer in one chemical compound saves time and should be mote cost-effective to the clinician and patient. The purpose of this study was to evaluate the clinical effectiveness of a self-etching primer by measuring shear bond strengths according to various conditions and observing adhesive failure patterns. For this Investigation, 120 upper and lower premolars extracted for orthodontic purposes were used and randomly divided into six groups of twenty teeth each. Human premolars were embedded in a metal cylinder with orthodontic resin. Metal brackets and ceramic brackets were bonded with XT primer and self-etching primer by means of XT adhesive. Upon curing, plasma arc light and visible light were used. After bonding, the shear bond strength was tested by Instron universal testing machine, and the amount of residual adhesive that remained on the tooth after debonding was measured by stereoscope and assessed with an adhesive remnant index. The results were as fellows: 1. When brackets were bonded, if other conditions remained the same, there was no significant difference in shear bond strength due to the type of primer - either self-etching primer or XT primer. 2. When metal brackets were bonded, there was no significant difference in shear bond strength according to the source of light - plasma arc light or visible light - and type of primer. 3. There was a very significant difference in shear bond strength according to the type of brackets - metal or ceramic brackets. The shear bond strength of ceramic brackets was stronger than metal brackets. 4. When the adhesive failure patterns of metal brackets bonded with self-etching primer were observed by using the adhesive remnant index, the bond failure of the metal bracket occurred more frequently at the bracket-adhesive. The failure of the ceramic bracket, however, occurred more frequently at the enamel-adhesive interface. The adhesive failure patterns of metal brackets bonded with XT primer observed the same patterns. The above results suggest that self-etching primer can be clinically useful for bonding the brackets without fear of a decrease in shear bond strength.