A Study on Concentration and Application Time of Lithium Sulfate-Contained Polyacrylic Acid for Adequate Crystal Growth

법랑질 표면에 크리스탈을 형성시키기 위해 사용한 황산리튬이 함유된 폴리아크릴산의 농도와 적용시간에 관한 연구

The purpose of this study was to compare shear bonding strengths and debonding patterns of the ceramic brackets attached on the crystal which were grown on the enamel surface of a tooth with different concentrations of lithium sulphate-contained polyacrylic acid in different application times. Four kinds of concentrations of mixed solutions were made and applied to the enamel surface on extracted human premolars. The solutions were made by adding 0.3M or 0.6M of lithium sulfate to $50\%\;or\;65\%$ of polyacrylic acid with 0.3M sulfuric acid. The solutions were applied for 30 or 60 seconds. After bonding, a universal testing machine was used to measure the shear bond strength, and then observations were made of debonding patterns through the stereoscope. And the enamel surface was observed through the scanning electron microscope to examine the pattern of crystal growth and debonding. The results were as follows: 1. Shear bond strength in the enamel surface treated with $50\%$ polyacrylic acid was higher than that with $65\%$ polyacrylic acid. 2. There were no statistical differences in shear bond strength according to concentration of lithium sulfate and application time of solutions . 3. Enamel surface was almost free of resin debris after debonding. 4. Enamel surface treated with $50\%$ polyacrylic acid showed higher density of crystal growth than that with $65\%$ polyacrylic acid under scanning electron microscope.

본 연구는 각각 다른 농도의 황산리튬을 함유한 폴리아크릴산을 적용시간을 변화시켜 치아의 법랑질 표면에 도포하여 크리스탈을 형성하고 그 위에 도제브라켓을 부착한후 전단결합강도와 파절양상을 비교하기 위하여 시행하였다. 농도가 서로다른 흔합용액 4종류를 교정치료를 위해 발거된 건전한 소구치 48개의 법랑질 표면에 적용시켰다. 실험용액들은 $50\%$의 폴리아크릴산과 $65\%$의 폴리아크릴산을 기본 용액으로 하여 0.3M의 황산을 공통으로 첨가하고 각각 0.3M 이나 0.6M의 황산리튬을 첨가하여 만들었다. 30초나 60초 동안 준비된 용액을 법랑질 표면에 적용한 후 브라켓을 부착시켜 전단결합강도를 측정하였다. 또한 브라켓 부착 전과 부착 후의 크리스탈 형성 양상을 주사전자현미경을 통하여 관찰하였다. 치아 표면의 잔여 레진 양을 입체현미경을 통하여 관찰하고 분류하여 다음과 같은 결과를 얻었다. 1. $50\%$ 폴리아크릴산으로 처리하였을 때의 전단결합강도가 $65\%$ 폴리아크릴산에 비해 높았다. 2. 황산리튬의 농도나 적용시간에 따른 전단결합강도의 차이는 인정되지 않았다. 3. 브라켓 제거 후 법랑질 표면에서 레진이 거의 관찰되지 않았다. 4. $50\%$ 폴리아크릴산으로 처리하였을 때의 크리스탈 형성 밀도가 $65\%$ 폴리아크릴산의 경우 보다 높았다.