• Journal of the Society of Naval Architects of Korea
• /
• v.33 no.3
• /
• pp.1-7
• /
• 1996

The stress concentration factor gives the significant effect the fatigue strength of welded joints. The model used herein is the type of the load carrying fillet welded cruciform joint with full or partial penetration. In order to obtain the stress concentration factor at the weld toe of fillet joint, the reasonable element size of the toe part is investigated and the stress analysis for the series models by FEM under tensile load is performed. On the basis of the calculation results, the estimated formulae for the stress concentration factor(Kt) at weld toe part of the fillet welded joint, which the effect of toe radius, flank angle and other parameters are taken into account, is derived.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.3
• /
• pp.220-226
• /
• 2003

This paper presents the result of an investigation on the application of the acoustic emission method to the monitoring of fatigue crack initiation, growth and track location in welded joints. Fatigue test was carried out for a typical fillet welded joint of ship structure. AE parameter such as ring down count was analyzed in time domain and crack locations were examined by source location and cluster option which is one of the functions of AE signal processor The usability of AE mettled was confirmed for the detection of the initiation and location of through crack.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.113-114
• /
• 2007

• Journal of Korean Society of Steel Construction
• /
• v.11 no.3 s.40
• /
• pp.319-327
• /
• 1999

This study makes mechanism of the fatigue strength improvement by the processing of weld toe clear for the vertical cross rib specimens which was made fillet weld joint, also it proposes to the appropriate later processing. As a result of tension fatigue test, the fatigue strength improvement could have been seen in later processed specimens than as-weld specimens. Especially fatigue crack initial life $N_c$ increased in specimens which processed grinder after hammer-peening. Also, fatigue crack propagation life $N_p$ improved more in hammer-peening specimens than as-weld or TIG specimens. It thinks that $N_c$ is because of the geometrical shape of weld toe, i.e. the relaxation of the stress concentration and also that $N_p$ is because the big compression residual stress which was introduced in the surface by hammer-peening is restraining the propagation of fatigue crack.

• Journal of Welding and Joining
• /
• v.12 no.3
• /
• pp.90-100
• /
• 1994

In this study the fatigue crack growth behavior was investigated for the surface cracks in aluminum alloy A5083-O plate and its weldment. Several kinds of specimens were tested at room temperature. The Eccentric specimens(E1.0, E2.5) subjected to combined stresses(tension+bending) were tested and the welded specimens with weld toes(TOE1, TOE2) were tested in order to verify the method to consider the stress concentration such as weld toe. It was ascertained that the surface crack growth property in the weld toe could be predicted by the corrected Pang's equation proposed in this study.

• Journal of the Society of Naval Architects of Korea
• /
• v.33 no.4
• /
• pp.133-141
• /
• 1996

The mode of fatigue failure is depended on the characteristics of the fatigue crack initiated and propagated from the weld toe and the weld root in the load-carrying fillet welded joints. The characteristics of fatigue crack are deeply affected by the geometry of fillet and the stress range. The purpose of this study is to investigate critical weld size and stress range in order to occur toe failure under pulsating tension loading in the load-carrying fillet welded cruciform joints.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.4
• /
• pp.323-330
• /
• 2008

High cycle bending fatigue of socket welded small bore pipe was characterized, and also the fatigue crack initiation of small bore pipe was monitored in situ by the acoustic emission (AE) technique. The STS 316L stainless steel specimens were prepared by gas tungsten arc welding (GTAW) process having the artificial defect (i.e., lack of penetration) and defect free at the root. The fatigue failure was occurred at the loc for high stress and root for relatively low stress. The crack initiation cycles ($N_i$) was defined to the abrupt increase in AE counts during the fatigue test, and then the cracks were observed by the radiographic test and electron microscope before and after the fatigue crack initiation cycles. The socket welded pipe damaged by bending fatigue was studied regarding the welding defect, failure mode, and crack initiation cycles for the diagnosis and monitoring.

• Composites Research
• /
• v.36 no.6
• /
• pp.388-394
• /
• 2023

In composites manufacturing, increasing resin impregnation is a key way to speed up the manufacturing process and improve product quality. While resin improvement is important, simple fiber surface treatments can also improve resin flowability. In this study, different plasma treatment times were applied to carbon fiber fabrics to improve the impregnation between resin and fiber. Electrical resistivity measurements were used to evaluate the dispersion of resin in the fibers, which changed with plasma treatment. The effect of fiber surface treatment on resin spreadability could be observed in real time. When inserting a carbon fiber tow into the resin, the amount of resin that soaked into the tow was measured to objectively compare resin impregnation. Five minutes of plasma treatment improved the tensile and compressive strength of the composite by more than 50%, while reducing the void content and increasing the fire point impregnation flow rate. Finally, a dynamic flexural fatigue test was conducted using a portion of the composite used as an architectural composite part, and the composite part did not fail after one million cycles of a 3 kN load.

• Journal of Welding and Joining
• /
• v.18 no.5
• /
• pp.33-40
• /
• 2000

Fatigue crack propagation life of weld toe crack through residual stress field was estimated with Elber's crack concept. Propagation of weld toe crack is heavily influenced by residual stress caused by welding process, so it is essential to take into account the effect of residual stress on the propagation life of weld toe crack. Fatigue crack at transverse and longitudinal weld toe was studied respectively, which represent typical weld joint in ship structure. Numerical and experimental studies are performed for both cases. Residual stress near weldment was estimated through nonlinear thermo-elasto-plastic finite element method, and residual stress intensity factor with Glinka's weight function method. Effective stress intensity factor was calculated with Newman-Forman-de Koning-Henriksen equation which is based on Dugdale strip yield model in estimating crack closure level U at different stress ratio. Calculated crack propagation life coincided well with experimental results.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.4
• /
• pp.7-13
• /
• 2001

This Study is to investigate the influence of weld residual stresses on the fatigue crack growth behaviors in pressure ves-sel reinforcement. In order to perform this study, the automatically welded specimens are prepared. The material is ASTM A516 grade 60 steel used in pressure vessel mainly. For pad-on-plate of skip welding continuous welding and PWHT specimen, fatigue crack initiation is generally initiat-ed at weld starting and end toe zone, and ruptured at weld starting toe zone, Fatigue life if pad-on-plate continuous speci-men is increased more than that of pad-on-plate skip fillet welding specimene about 85% under low load, about 20% under high load, and decreased than that of two-pad continuous welding specimen about 85%. In da/dN-$\Delta$ Κ curve under low load, pad-on-plate skip fillet welding specimen showed retardation on the initial crack, and the fatigue crack growth rate at the low region of $\Delta$Κ greater specimene E(3.8{\times}10^{-6}$mm/cycle). And the fatigue life of welding specimen was smaller than that of PWHT specimen.