• Solar Energy
• /
• v.10 no.1
• /
• pp.57-62
• /
• 1990

The influence of substrate materials on the thermal stability of black chrome coating was investigated by Rutherford backscattering spectrometry(RBS). In order to study thermal degradation the sample were annealed in air for 24 hour at temperature of 450. Cu, Ni, and S.S(Stainless steel 304) were used as substrate for selective coating. The experimental results of substrate diffusion was discussed. It was found that little diffusion of substrate material occurred for the sample pre. pared on stainless steel.

• Solar Energy
• /
• v.10 no.1
• /
• pp.92-97
• /
• 1990

The electrochemical approach to the characteristics of black chrome solar selective coatings has been reviewed. Based on the formula of the ChromOnyx bath solution manufactured by Harshaw Company, the chromic acid-propionic acid bath solutions have been prepared by KIER. Comprehensive review of the black chrome electrodeposition mechanism also has been performed on the role played by constituents in the bath solution during electrodeposition. The optical properties such as absorption and emittance of electrodeposited black chrome coatings obtained from the new formula and their surface analysis will be reported in detail.

• Journal of the Korean Solar Energy Society
• /
• v.26 no.1
• /
• pp.57-64
• /
• 2006

Cr-CrO cermet solar selective coatings with a double cermets layer film structure were prepared using a special direct current (dc) magnetron sputtering technology. The typical films structures from surface to bottom substrate were measured to be an $Al_2O_3$ anti-reflection layer on a double Cr-CrO cermet layer on an Al metal infrared reflection layer. Optical properties of optimized Cr-CrO cermet solar selective coating were absorptance (${\alpha}$) = 0.95 and emittance (${\varepsilon}$) = 0.10 ($100^{\circ}C$). Atomic force microscopy (AFM) image showed that Cr-CrO cermet film was very smooth and their grain size was also very small The results of thermal stability test showed that the Cr-CrO cermet solar selective coatings were stable for use at temperature of $400^{\circ}C$.

• Journal of the Korean Solar Energy Society
• /
• v.31 no.4
• /
• pp.48-56
• /
• 2011

Black cobalt solar selective coatings were prepared by thermal oxidation of electroplated cobalt metal on copper and nickel substrates. The optical properties and structure of the black cobalt selective coating for solar energy utilizations were characterized by glow discharge spectrometry (GDS), ultraviolet-visible-near infrared (UV-VIS-NIR) spectrometer, atom force microscopy(AFM) and X-ray photoelectron spectroscopy(XPS). The optical properties of optimum black cobalt selective coating prepared on copper substrate were a solar absorptance of 0.82 and a thermal emittance of 0.01. From the GDS depth profile analysis of these coatings, the concentration of cobalt particles near the interface was higher than at the surface, but oxygen concentration at the surface was higher than at the interface. These results suggest that the selective absorption was dominated by this chemical composition variation in the coating. The surface of this film exhibited morphology with root-mean-square(rms) roughness of about 144.3nm. XPS measurements data showed that several phases of Co coexist($Co_3O_4$,CoO) in the film.

• Journal of the Korean Solar Energy Society
• /
• v.28 no.1
• /
• pp.33-42
• /
• 2008

Zr-O ($Zr-ZrO_2$) cermets solar selective coatings with a double cermets layer film structure were prepared using a DC (direct current) magnetron sputtering method. The typical film structure from surface to bottom substrate were an $Al_2O_3$ anti-reflection layer on a double Zr-O cermets layer on an Al metal infrared reflection layer. Optical properties of optimized Zr-O cermets solar selective coating had an absorptance of ${\alpha}\;=\;0.95$ and thermal omittance of ${\epsilon}\;=\;0.10\;(100^{\circ}C)$. The absorbing layer of Zr-O cermets coatings on glass and silicon substrate was identified as being amorphous by using XRD. AFM showed that ZF-O cermets layers were very smooth and their surface roughness were approximately $0.1{\sim}0.2 nm$. The chemical analysis of the cermets coatings were determined by using XPS. Chemical shift of photoelectron binding energy was occurred due to the change of Zr-O cermets coating structure deposited with increase in oxygen flow rate. The result of thermal stability test showed that the Zr-O cermets solar selective coating was stable for use at temperature below $350^{\circ}C$.

• Journal of the Korean Solar Energy Society
• /
• v.35 no.4
• /
• pp.9-15
• /
• 2015

Black cobalt solar selective coatings were prepared by using an electroplating method. The changes in the optical properties of the black cobalt selective coating due to thermal degradation were analyzed by using the Auger electron spectroscopy (AES) and spectrophotometer. The black cobalt selective coating was prepared on a copper substrate by using a synthesized electrolyte with $CoCl_2$ and KSCN at a current density of ${\sim}0.5A/dm^2$ for 45s ~ 60s. Its optical properties were a solar absorptance (${\alpha}$) of the order of 0.80 ~ 0.84 and a thermal emittance (${\epsilon}$) of 0.01. From the AES depth profile analysis of heated sample, thermal degradation of the black cobalt selective coating heated for 33 hours at temperature of $350^{\circ}C$ occurred primarily due to interdiffusion at interface of cobalt and copper substrate. This results were predictable that the ${\alpha}$ decreases due to the thermal oxidation and diffusion.

• Journal of the Korean Solar Energy Society
• /
• v.32 no.4
• /
• pp.43-50
• /
• 2012

Metal-metal oxide (M-M oxide) cermet solar selective coatings with a double cermet layer film structure were deposited on the Al-deposited glass substrate by using a directed current (DC) magnetron sputtering technology. M oxide (CrO and ZrO) was used as the ceramic component in the cermets, and Cr and Zr used as the metallic components. In addition, black Cr (Cr-$Cr_2O_3$ cermet) solar selective coatings were deposited on the Ni-plated Cu substrate by using a electroplating method for comparison. The thermal stability tests were carried out for performance evaluation of solar coatings. Reflectance measurements were used to evaluate both solar absorptance(${\alpha}$) and thermal emittance (${\epsilon}$) of the solar coatings before and after thermal testing by using a spectrometer. Optical properties of optimized cermet solar coatings were ${\alpha}{\simeq}0.94-0.96$ and ${\epsilon}{\simeq}0.1$ ($100^{\circ}C$). The results of thermal stability test of M-M oxide solar coatings showed that the Cr-CrO cermet solar selective coatings were more stable than the Zr-ZrO cermet selective coatings at temperature of both $400^{\circ}C$ in air and $450^{\circ}C$ in vacuum. The black Cr solar selective coatings were degraded in air at temperature of $400^{\circ}C$. The main optical degradation modes of these coatings were diffusion of metal atoms, and oxidation.

• Journal of the Korean Solar Energy Society
• /
• v.33 no.3
• /
• pp.27-35
• /
• 2013

One of the most important factors that have a large influence on performance of the solar water heater system is performance of the solar collector, more detailedly, coating technology on the surface of the solar collector, which can provide high solar absorptance and low emittance. The core of the coating technology is to coat solar selective surfaces. In this study, various performance experiments are carried out using $Cr_2(SO_4)_3{\cdot}15H_2O$ coating technology. Here, IGBT(Insulated Gate Bipolar Transistor) of 5000A-15V was used as the surface processing rectifier which can stably output power and also can control voltage and current. The plating solution mainly contains black chrome$^{+3}$ concentration, H-y Conductivity, N-u Complex, NF Additive and NC-2 Wetter. Before applying the black chrome coating on the copper plate, optimal conditions are provided by using various preprocessing methods such as removal of fat, activation, electrolytic polishing, nickel strike, copper sulfate plating and bright neckel plating, and then the automatic continuous coating experiment are performed according to plating time and cathode current density. In the experiment, after the removal of fat, chemical polishing, nickel strike and activation processes as the preprocessing methods, the black chrome coating was performed in a plate solution temperature of $28^{\circ}C$ and a cathode current density of $18A/cm^2$ for 90 seconds. The thickness of chrome and nickel on the coated plate is $0.389{\mu}m$, $159{\mu}m$ respectively. As a result of the coating experiment, it showed the most excellent performance having a high solar absorptance of 98% and a low emittance of $5{\pm}1%$ when the black chrome surface had a thickness of $0.398{\mu}m$.

• Solar Energy
• /
• v.9 no.2
• /
• pp.69-77
• /
• 1989

The thermal degradation of electroplated black chrome coating on Ni substrates has been investigated by using Auger electron spectroscopy technique. The sample was prepared by electroplating at $20^{\circ}C$ for 20 seconds with the current density at $0.4A/cm^2$. Its surface oxidation process was investigated with 1 hour annealed sample for a temperature range of $300-550^{\circ}C$. While its optical solar absorption was dominated by fine metallic Cr particles, thermal degradation was occurred primarily by oxidation of metallic Cr particles as increasing the annealing temperature.

• Journal of the Korean Solar Energy Society
• /
• v.34 no.4
• /
• pp.39-44
• /
• 2014

The elemental composition of electro-deposited black Cr solar selective coatings before and after heating in air by using secondary ion mass spectrometry (SIMS) was investigated for optical property analysis. In addition, black Cr selective coating exposed by solar radiation for 5 months was compared with heated sample. SIMS investigation shows that $OH^+$ bearing ions were related to a near surface region of CrOH and CrO compound. The optical degradation of this coating after heating at $500^{\circ}C$ reveals that diffusion of the Cu and Ni elements in substrate material, the chemical interactions adjacent to the interface, and the interface width broadening.