• Magazine of the Korea Concrete Institute
• /
• v.11 no.2
• /
• pp.147-156
• /
• 1999

An investigation was conducted into the flexural behavior of earthquake damaged reinforced concrete columns repaired with carbon fiber sheets. Six column specimens were tested to failure under reversed cyclic loading. Two columns were specimens for control with no sheets and tested. These columns were repaired with carbon fiber sheets and retested to evaluate the effect of the confinement of the carbon fiber on the damaged column. Another two columns were repaired and tested with no pre-cyclic loading. The test specimens were designed to model single bent under a constant axial force with reversed cyclic lateral loading. Carbon fiber sheets were used to repair damaged concrete columns in the critically stressed areas near the column footing joint and the physical, mechanical properties of carbon fiber sheets are described. The performance of repaired columns in terms of their hysteretic response is evaluated and compared to those of the original columns. The results indicate that the repaire technique with carbon fiber sheets is highly effective. Both flexural strength and displacement ductility of repaired columns were higher than those of the original columns.

• Applied Chemistry for Engineering
• /
• v.24 no.4
• /
• pp.363-369
• /
• 2013

In this work, the effects of ozone treatments on mechanical interfacial properties of carbon fibers-reinforced nylon-6 matrix composites were investigated. The surface properties of ozone treated carbon fibers were studied by Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS). Mechanical interfacial properties of the composites were investigated using critical stress intensity factor ($K_{IC}$). The cross-section morphologies of ozone-treated carbon fiber/nylon-6 composites were observed by scanning electron microscope (SEM). As a result, $K_{IC}$ of the ozone-treated carbon fibers-reinforced composites showed higher values than those of as-received carbon fibers-reinforced composites due the enhanced $O_{1s}/C_{1s}$ ratio of the carbon fiber by the ozone treatments. This result concludes that the mechanical interfacial properties of nylon-6 matrix composites can be controlled by suitable ozone treatments on the carbon fibers.

• Applied Chemistry for Engineering
• /
• v.27 no.5
• /
• pp.472-477
• /
• 2016

We studied the effects of anodic oxidation treatments of carbon fibers on interfacial adhesion of the carbon fibers-reinforced epoxy matrix composites with various current densities. The surface of treated carbon fibers was characterized by atomic force microscope (AFM), field emission-scanning electron microscope (FE-SEM), Fourier transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS). The interlaminar shear strength (ILSS) of the composites was determined by a short beam shear test. This result showed that both the roughness and oxygen group of the carbon fibers surface increased in proportion to the current density. After anodic-oxidation-treated, the ILSS also increased as a function of the current density. In addition, the proportional relationship between ILSS and phenolic hydroxyl group was confirmed. The ILSS of the CF-2.0 sample increased by 4% compared to that of the CF-AS sample, because the anodic oxidation treatment increased the oxygen group and roughness on the carbon fibers surface, which leading to the improvement of the interfacial adhesion of the carbon fibers-reinforced epoxy matrix composites. Among these, the phenolic hydroxyl group which has the proportional relationship with ILSS is found to be the most important factor for improving the interfacial adhesion of the carbon fibers-reinforced epoxy matrix composites.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.1
• /
• pp.131-136
• /
• 2013

The purpose of this study is to establish the flexural strengthening method of the concrete members. To accomplish this objective, a total of seven concrete beams were tested. From this study, it is found that the initial flexural stiffness and strength of the beams reinforced with NSM CFRP strips were significantly improved compared to the beam without CFRP strip. Failure of the beam reinforced with NSM strips is initiated by failure of NSM strips, eventually sudden explosive compressive failure in the loaded region. This strengthening method combined with NSM CFRP strips and high performance mortar for concrete cover recovery is evaluated by a good strengthening method for the strength, durability and good appearance of concrete structures.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.8 no.4
• /
• pp.1-10
• /
• 2004

The purpose of this study is to investigate the flexural behavior of square concrete filled carbon tube (CFCT) columns subjected to constant axial load with the cyclic lateral load. Two parameters, wnding angle and thickness of tube, were chosen to evaluate the flexural capacity and behavior of rectangular CFCT columns. Selected two parameters were considered simultaneously in order to evaluate the flexural behavior of a rectangular CFCT columns more precisely. Flexural strength, deformation capacity, ductility and energy dissipation capacity of rectangular CFCT columns were evaluated by calculating the area of load-displacement envelope curves and load-dispalcement hysteresis curves obtained from experiment. Also, the ductile capacity obtained from experiment was compared to that of reinforced masonry wall for the comparison of existing structural element.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.27 no.2
• /
• pp.115-123
• /
• 2007

For investigating self-diagnosis applicability, a method based on monitoring the changes in the electrical resistance of carbon fiber reinforced concrete has been tested. Then after examining change in the value of electrical resistance at each flexural weight-stage of carbon fiber in CFGFRP (carbon fiber and glass fiber reinforcing plastic) with new type rib and carbon sheet for concrete reinforcing, the correlations of electrical resistance and load as a function of strain, deflection were analyzed. As the results, it is clarified that when carbon fiber rod, rib and sheet fracture, the electrical resistance of it increase largely, and specially in case of CFGFRP, afterwards glass fiber tows can be resist the load due to the presence of the hybrid (carbon and glass) reinforced fiber. Therefore, it can be recognized that reinforcing bar and new type rib of CFGFRP and sheet of CF could be applied for self-diagnosis of fracture in reinforced FRP concrete.

• Journal of the Korean Society for Railway
• /
• v.12 no.6
• /
• pp.1059-1066
• /
• 2009

Recently, the amount of thermosetting plastic wastes has increased with the production of reinforced plastic composites and causes serious environmental problems. The epoxy resins, one of the versatile thermosetting plastics with excellent properties, cannot be melted down and remolded as what is done in the thermoplastic industry. In this research, a series of experiments that decompose epoxy resin and recover carbon fibers from carbon fiber reinforced epoxy composites applied to railway vehicles was performed. We experimentally examined various decomposition processes and compared their decomposition efficiencies and mechanical property of recovered carbon fibers. For the prevention of tangle of recovered carbon fibers, each composites specimen was fixed with a Teflon supporter and no mechanical mixing was applied. Decomposition products were analyzed by scanning electron microscope (SEM), gas chromatography mass spectrometer (GC-MS), and universal testing machine (UTM). Carbon fibers could be completely recovered from decomposition process using nitric acid aqueous solution, liquid-phase thermal cracking and pyrolysis. The tensile strength losses of the recovered carbon fibers were less than 4%.

• Composites Research
• /
• v.25 no.6
• /
• pp.205-210
• /
• 2012

The single carbon fiber tensile test was performed with electrical resistance measurement. Tensile property of single carbon fiber which accompanied by the relationship between the electric resistance and the strain was investigated. Since the collected data showed a linear relationship between them, the coefficient of fiber slip ratio (FSR) was obtained by computation. The fragmentation specimen (FS) was tested under tensile loading, and the single carbon fiber broke first due to the stress transferring form matrix to reinforcing fiber. The stress distribution of carbon fiber could be observed via the electrical resistance change. Slipping between carbon fiber and matrix was predicted based on the fragmentation test results, and the FSR was used to evaluate interfacial adhesion comparatively. The large FSR indicated poor interfacial bonding. Work of adhesion between carbon fiber and matrix was measured to verify the FSR method, and two results exhibited a consistent conclusion.

• Applied Chemistry for Engineering
• /
• v.24 no.5
• /
• pp.476-482
• /
• 2013

In this work, the effects of electrochemical oxidation of carbon fiber surfaces on mechanical interfacial properties of carbon fibers-reinforced polarized-polypropylene matrix composites were studied with various current densities during the treatments. Surface properties of the fibers before and after treatments were observed by SEM, AFM, XPS, and contact angle measurements. Mechanical interfacial properties of the composites were measured in terms of critical stress intensity factor ($K_{IC}$). From the results it was found that $O_{1s}$ peaks of the fiber surfaces were strengthened after electrochemical oxidation which led to the enhancement of surface free energy of the fiber, resulting in good mechanical performance of the composites. It can be concluded that electrochemical oxidation of the carbon fiber surfaces can control the interfacial adhesion between the carbon fibers and polarized-polypropylene in this composites system.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.6
• /
• pp.791-796
• /
• 2013

In this study, the mechanical properties of a carbon fiber/polypropylene composite were evaluated according to the carbon fiber surface treatment. Carbon fiber surface treatments such as silane coupling agents and plasma treatment were performed to enhance the interfacial strength between carbon fibers and polypropylene. The treated carbon fiber surface was characterized by XPS, SEM, and single-filament tensile test. The interlaminar shear strength (ILSS) of the composite with respect to the surface treatment was determined by a short beam shear test. The test results showed that the ILSS of the plasma-treated specimen increased with the treatment time. The ILSS of the specimen treated with a silane coupling agent after plasma treatment increased by 48.7% compared to that of the untreated specimen.