• Resources Recycling
• /
• v.15 no.3 s.71
• /
• pp.74-80
• /
• 2006

In this article, we would like to investigate a durability characterization of cement mortar with inert filler, which is ground calcium carbonate(GCC). The kinds of techniques to evaluate cement mortar are chloride ion ingress, carbonation and sulfate attack. For the experimental result of the resistance of chloride ion ingress, carbonation and sulfate attack, as the addition of GCC makes decreasing the permeability by micro-filler effect, the specimens of $5{\sim}15%$ ratio of replacement are superior to the GCC0 mortar specimen with respect to durability of cement matrix in this scope.

• Journal of the Mineralogical Society of Korea
• /
• v.27 no.1
• /
• pp.17-30
• /
• 2014

Waste cement generated from recycling processes of waste concrete is a potential raw material for mineral carbonation. For the $CO_2$ sequestration utilizing waste cement, this study was conducted to obtain basic information on the aqueous carbonation methods and the characteristics of carbonate mineral formation. Cement paste was made with W:C= 6:4 and stored for 28 days in water bath. Leaching tests using two additives (NaCl and $MgCl_2$) and two aqueous carbonation experiments (direct and indirect aqueous carbonation) were conducted. The maximum leaching of $Ca^{2+}$ ion was occurred at 1.0 M NaCl and 0.5 M $MgCl_2$ solution rather than higher tested concentration. The concentration of extracted $Ca^{2+}$ ion in $MgCl_2$ solution was more than 10 times greater than in NaCl solution. Portlandite ($Ca(OH)_2$) was completely changed to carbonate minerals in the fine cement paste (< 0.15 mm) within one hour and the carbonation of CSH (calcium silicate hydrate) was also progressed by direct aqueous carbonation method. The both additives, however, were not highly effective in direct aqueous carbonation method. 100% pure calcite minerals were formed by indirect carbonation method with NaCl and $MgCl_2$ additives. pH control using alkaline solution was important for the carbonation in the leaching solution produced from $MgCl_2$ additive and carbonation rate was slow due to the effect of $Mg^{2+}$ ions in solution. The type and crystallinity of calcium carbonate mineral were affected by aqueous carbonation method and additive type.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.6
• /
• pp.123-129
• /
• 2018

Recently, there has been a growing interest in the study of treatment of $CO_2$ generated by industrial activities and resource recycling of industrial byproducts. The aim of this study is to investigate the applicability of industrial byproducts that can be used as concrete mixed materials by carbonation curing. For this purpose, the physical and chemical changes of the pastes with research cement(RC), blast furnace slag powder (GGBFS) and circulating fluidized bed combustion ashes (CFBC) were evaluated by carbonation curing. XRD and SEM analyzes were performed to investigate micro-structural changes. As a result, it was confirmed that calcium carbonate, which is a reaction product produced by carbonation curing, filled the space inside the paste and formed a dense micro-structure. Also, as the $CO_2$ curing time increased, it was confirmed that calcium carbonate crystals were grown together to form a dense micro-structure.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.317-318
• /
• 2023

This study is part of the carbonation degree DB accumulation through quantitative analysis of carbonation depth, Ca(OH)₂ and CO₂ according to the type of finish and years of use of old concrete structures in order to predict the amount of CO₂ that can be absorbed through carbonation of concrete. To this end, the depth of carbonation of the concrete core specimen is measured using an indicator, and the dry amount of water combined with CO₂ in the sample is measured using a differential thermal gravimetric analyzer for samples in the carbonation area and non-carbonated area classified by the indicator, and the absorption compared to the weight of the sample. The amount of absorbed CO₂ was calculated. In addition, the degree of carbonation was calculated through quantitative comparison of Ca(OH)₂ in the carbonation section and non-carbonation section. In the future, we will continue to add the survey and analysis data of dismantled structures and use them as basic data for estimating the amount of carbon dioxide that can be absorbed according to the exposure conditions and years of use by concrete mix.

• Journal of the Korea Concrete Institute
• /
• v.28 no.4
• /
• pp.445-454
• /
• 2016

With the increase of decrepit facilities, construction waste increased to a certain level and now the increase is more or less stabilized. Yet construction waste still constitutes the largest portion of the overall wastes. Also, it is inevitable to spend a huge amount of the national budget due to the aggravating shortage of aggregate caused by prohibition on collection of natural aggregates as well as due to the damage to the land and environment caused by development of the sources of aggregates. As a countermeasure to the situation, the Ministry of Land, Infrastructure and Transport promulgated the quality standard for recycled aggregate to manage the usage of recycled aggregate according to its quality. But use of recycled aggregate for the purpose of high added value still remains nominal. Therefore, this research aims to study the applicability of recycled aggregate concrete as structural concrete by evaluating the quality improvement effects and the performance of the recycled aggregate concrete including recycled fine aggregate and recycled coarse aggregate that have undergone carbonation for 4 days and 14 days respectively in the condition of 60% RH, 20% $CO_2$ and $20^{\circ}C$ temperature, suggested for carbonation modifying from the advance research. The result shows carbonation modify contributed to quality improvement with 0.91% decrease in absorption rate for recycled fine aggregate and 0.7% decrease in absorption rate for recycled coarse aggregate. The physical properties and durability of the recycled aggregate made of aggregate modified by carbonation showed results similar to general concrete, which confirmed the possibility of applying the recycled aggregate made of recycled aggregate modified by carbonation to structural concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.140-146
• /
• 2017

It is laser induced breakdown spectroscopy(LIBS) that enables qualitative and quantitative analysis of the elements contained in unknown specimen by comparing the wavelength characteristics of each element obtained from the spectral analysis of the standard specimen with the wavelength analysis results from unknown specimens. In this study, the applicability of LIBS to the analysis of major deterioration factors affecting concrete durability was experimentally analyzed. That is, the possibility of applying LIBS to the diagnosis of concrete deterioration by studying the quantitative detection of harmful deteriorating factors on chloride, sulfate and carbonated mortar specimens using LIBS was studied. As a result of LIBS test for each chloride and sulfate specimen, the LIBS spectral wavelength intensity of chlorine and sulfur ions increased linearly with increasing concentration. Carbon ion LIBS spectral wave intensities of carbonated specimens increased nonlinearly over the duration of carbonation exposure. From the above results, it can be partially confirmed that LIBS can be applied to the diagnosis of concrete deterioration. In case of concrete carbonation, it is presumed that carbon content is contained in the cement itself and is different from the detection of chloride and sulfate specimen. Therefore, it is considered that more various parameter studies should be performed to apply LIBS to concrete carbonation.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.373-380
• /
• 2023

This study investigated the carbonation of concrete brick cured in a CO₂ environment for the utilization of CO₂ captured in power plants. Concrete brick specimens were produced with electric arc furnace reducing slag (ERS) and electric arc furnace oxidizing slag (EOS), and cured for 3 days in a CO₂ chamber with a concentration of 20 % or in a constant temperature and humidity chamber. The weight change, compressive strength, flexural strength and carbonation depth of concrete bricks were measured. From the results, it was found that when subjected to CO₂ curing, CO₂ was absorbed at the level of 2.4 % of the weight of the specimen. The specimen incorporating ERS showed the highest carbonation depth, and satisfied KS F4004 standards for the concrete brick. Therefore, it is expected that the captured CO₂ can be utilized in the CO₂ curing process of concrete brick.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.1
• /
• pp.53-60
• /
• 2024

Compressive strength in concrete has many affecting parameters and varies with exposure conditions. Although the concrete has same mix proportions, its properties are different with exposure conditions, and sea-environment can be classified into three groups such as tidal, atmospheric, and sea submerged region particularly. In this study, compressive strength was evaluated on 7-year-cured concrete and the results from previous equations (KDS, ACI, CEB, and JSCE) were compared with them. Furthermore the strength and carbonation progress were evaluated on concrete cured for 7 years exposed to three different sea environment. Three levels of w/c (water to cement) ratio (0.37, 0.42, and 0.47) and three different exposure conditions (tidal, atmospheric, and submerged) were considered. The results from wet-cured condition are all higher than those from the previously proposed equations, and the results from different sea exposure conditions (tidal, atmospheric, and submerged region) were lower than those from wet-cured condition. A reduction of strength was evaluated with increasing w/c ratio and the minimum strength was evaluated in the sea-submerged conditions. Several experimental constants applicable to the previous equations were obtained from regression analysis since the strength change with w/c ratios were not considered in those equations. Regarding carbonation depth with different exposure conditions, higher carbonation depth clearly was observed with increasing w/c ratios, and evaluated in the order of atmospheric, submerged, and tidal region. Considerable carbonation depth was observed in submerged and tidal region due to sulfate ion and dissloved carbon dioxide as well.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.2
• /
• pp.49-58
• /
• 2008

Generally, steel corrosion occurs in concrete structures due to carbonation in down-town area and underground site and it propagates to degradation of structural performance. In general diagnosis and inspection, only carbonation depth in sound concrete is evaluated but unsound concrete such as joint and cracked area may occur easily in a concrete member due to construction process. In this study, field survey of carbonation for RC columns in down-town area is performed and carbonation depth in joint and cracked concrete including sound area is measured. Probability of durable failure with time is calculated through probability variables such as concrete cover depth and carbonation depth which are obtained from field survey. In addition, service life of the structures is predicted based on the intended probability of durable failure in domestic concrete specification. It is evaluated that in a RC column, various service life is predicted due to local condition and it is rapidly decreased with insufficient cover depth and growth of crack width. It is also evaluated that obtaining cover depth and quality of concrete is very important because the probability of durable failure is closely related with C.O.V. of cover depth.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.5
• /
• pp.222-228
• /
• 2019

In this study, we carried out the experiment to prepare lithium carbonate powder through gas-liquid reactions with a lithium-containing solution and $CO_2$ gas using lithium hydroxide, lithium chloride, and lithium sulfate. Thermodynamically, the carbonation reaction of a lithium-containing solution showed that aqueous reaction of lithium hydroxide occurs spontaneously, but aqueous reactions of lithium chloride and lithium sulfate does not occur spontaneously. In the case of lithium hydroxide solution, the recovery rate of lithium carbonate was 69.8 % at room temperature ($25^{\circ}C$), and increased to 89.4 % at $60^{\circ}C$. In the case of lithium chloride and lithium sulfate solution, lithium carbonate could be prepared using sodium hydroxide as an additive, but the recovery rates were 19.2 % and 16.7 %, respectively.