• Transactions of the Korean hydrogen and new energy society
• /
• v.5 no.2
• /
• pp.99-109
• /
• 1994

To develop high capacity hydrogen storage alloys for secondary Ni/MH batteries, electrochemical charge/discharge characteristics of $Zr_{1-x}Ti_xMn_{1-y}V_yNi_{1-z}M_z$ (M=Al,Co,Fe) alloys were investigated, in which $0.2{\leq}x{\leq}0.6$, $0.2{\leq}y{\leq}0.8$, $0.2{\leq}z{\leq}0.4$. With increasing Ti content(x) and/or decreasing V content(y), lattice constants and maximum theoretical capacities of the alloys were decreased and equilibrium pressure of hydrogen absorption were increased. Electrochemical discharge capacities were increased with increasing Ti content(x). Especially, the alloys of x= 0.4~0.6 showed better charge/discharge efficiencies than those of x<0.4. Discharge capacities of $Zr_{0.4}Ti_{0.6}Mn_{0.4}V_{0.6}Ni_{0.8}Fe_{0.2}$, $Zr_{0.4}Ti_{0.6}Mn_{0.4}V_{0.6}Ni_{0.8}Al_{0.2}$ and $Zr_{0.5}Ti_{0.5}Mn_{0.4}V_{0.6}Ni_{0.6}Co_{0.4}$ were 385, 328 and 333mAh/g, respectively. These alloys were fully activated within five charge/discharge cycles and had a good charge and discharge rate capabilities and temperature characteristics.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.2
• /
• pp.79-85
• /
• 2014

Silicon (Si) has been investigated as promising negative-electrode (anode) materials because its theoretical specific capacity of 4200 mAh/g for $Li_{4.4}Si$ is far higher than that of carbonaceous anodes in current commercial products. However, in practice, the application of Si to Li-ion batteries is still quite challenging because Si suffers from severe volume expansion and contraction and lead to a continuous solid electrolyte interphase (SEI)-filming process by cracking of Si. This process consumes the limited $Li^+$ source, builds up thick and unstable SEI layer on the Si active materials, and will eventually disable the cell. Since unstable SEI reduces electrochemical performance and thermal stability of the Si anode, the surface chemistry of the anode should be modified by using a functional additive. It is found that lithium bis(oxalato)borate (LiBOB) as an additive effectively protected the Si anode surface, improved capacity retention when stored at $60^{\circ}C$, and alleviated exothermic thermal reactions of fully lithiated Si anode.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.179-179
• /
• 2012

국내에는 나노 분말 제조를 위한 RF 열플라즈마 시스템 제조 기술이 확보되어 있지 않고, 또한 나노 파우더 제조를 위한 공정 기술 역시 외국 업체에 전적으로 의존하고 있다. 본 연구에서는 나노 분말 제조를 위한 RF 열 플라즈마 토치 시스템 개발과 고품질의 나노 파우더 합성 공정 기술을 확립하여 필요 기관에 제공하는데 있다. 80 kW RF Plasma torch system의 설계 및 제작을 위해 플라즈마 Simulator인 CFD-ACE+를 이용하여 플라즈마 토치 및 반응로 내의 온도 분포, 유체 유동, 열전달 등의 해석을 통해 플라즈마 토치 및 반응로의 반경 및 길이, 구조의 설계 값을 도출하여 반응로를 설계하여 RF 파워, RF 플라즈마 토치(Torch), 반응기(Reactor), 사이클론(Cyclone), 포집부(Collector), 열교환기 및 진공배기 시스템으로 구성하였다. Si 나노 소재의 경우, 이차전지 음극재에 적용이 가능한 대표적인 소재로서 높음 비용량과 충/방전시 부피팽창을 감소시킬 수 있어 이차전지의 고용량 구현을 위해서는 가장 중요한 소재중 하나로 많은 관심 재료로 평가 받고 있다. 따라서 본 연구에서는 상용화된 Si 원료 powder를 사용하여 고상 분체 공급 장치를 통하여 고온의 플라즈마를 통과시켜 기상화 및 결정화과정을 통해 Si 나노분말을 제조하였다. 공정 변수로서 공정압력 및 플라즈마 power, Gas의 변화량에 따른 나노 분말의 제조 특성에 대한 실험을 진행한 후 제조된 나노 분말을 비표면적측정(BET) 및 SEM 측정 결과 분석을 통하여 시스템 특성을 파악하였으며 제조된 Si 나노 파우더는 이차전지 음극재로서 770 mAh/g의 용량과 93%@50 cycle 수준의 유지율을 나타내었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.3
• /
• pp.63-69
• /
• 2017

This paper presents a highly efficient power management system for UAV-drones. For free from the battery cell-balancing issue, the proposed system allows the drone to utilize a single-cell Li-Po battery. To realize low-voltage input of 3.7V, the switch-mode step-up DC-DC converter is optimally designed with high power efficiency. The prototype DC-DC converter was implemented with an output voltage of 5V, which will be provided to digital parts of the drone. The power efficiency was measured to be max. 91.3% with low surface temperature. The measured line and load regulations were 0.02V/V and 0.15V/A, respectively. Thanks to the proposed power management system, the available time-to-fly of the drone is expected to be significantly extended in virtue of the enhanced power efficiency.

• Korean Chemical Engineering Research
• /
• v.56 no.4
• /
• pp.561-567
• /
• 2018

In this study, the electrochemical characteristics of Silicon/Carbon anode materials were analyzed to improve the cycle stability of silicon as an anode materials of lithium ion battery. Porous silicon was prepared from TEOS by the $st{\ddot{o}}ber$ method and the magnesiothermic reduction method. Silicon/Carbon anode materials were synthesized by varying the mass ratio between porous silicon and pitch. Physical properties of the prepared Silicon/Carbon anode materials were analyzed by XRD and TGA. Also the electrochemical performances of Silicon/Carbon anode materials were investigated by constant current charge/discharge, rate performance, cyclic voltammetry and electrochemical impedance tests in the electrolyte of $LiPF_6$ dissolved in organic solvents (EC : DEC = 1 : 1 vol%). The Silicon/Carbon anode composite (silicon : carbon = 5 : 95 in weight) has better capacity (453 mAh/g) than those of other composition cells. The cycle performance has an excellent capacity retention from 2nd cycle to 30th cycle.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.415-420
• /
• 2016

To enhance electrochemical performances of anode materials, the surface of coal tar pitch (CTP) was modified by incorporating heteroatoms through chemical treatment with phosphoric acid ($H_3PO_4$). The prepared anode materials with modified CTP was analyzed by XRD, FE-SEM and XPS. The electrochemical performances of modified CTP were investigated by constant current charge/discharge test, rate performance, cyclic voltammetry and impedance tests using the electrolyte of $LiPF_6$ dissolved in the mixed organic solvents (ethylene carbonate : dimethyl carbonate = 1 : 1 vol% + vinylene carbonate 3 wt%). The coin cell using modified CTP ($H_3PO_4/CTP$ = 3 : 100 in weight) has better initial capacity and initial efficiency (489 mAh/g, 82%) than those of other composition coin cells. Also, it was found that the capacity retention was 86% after 30 cycles and the rate capability was 87% at 2 C/0.1 C.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.462-462
• /
• 2009

$CeO_2$는 고체 산화물 연료전지 (SOFC, soild oxide fuel cell)의 전해질 재료와 CMP(Chemical Mechanical Polishing) 슬러리 재료, 자동차의 3원 촉매, gas sensor, UV absorbent등 여러 분야에서 사용되고 있다. 본 연구에서는 위의 활용범위 외에 $CeO_2$의 구조적 안정성과 빠른 $Ce^{3+}/Ce^{4+}$의 전환 특성을 이용하여 lithium ion battery의 anode 재료로서 전기화학적 특성을 알아보고자 실험을 실시하였다. $CeO_2$ 합성에 사용되는 전구체인 cerium carbonate의 형상 및 크기, 비표면적과 같은 물리화학적 특성이 $CeO_2$ 분말의 특성에 직접적인 영향을 주기 때문에 전구체의 합성 단계에서 입자의 특성을 조절하였다. 전구체 합성의 출발원료로 cerium nitrate hexahydrate 와 ammonium carbonate를 사용하였고 반응온도 및 농도 등을 변화시켜 입자의 형상 및 결정상을 fiber형태의 orthorombic $Ce_2O(CO_3)_2{\cdot}H_2O$와 구형의 hexagonal $CeCO_3OH$의 세리아 전구체를 합성하였다. 이를 $300^{\circ}C$에서 30분 동안 하소하여 전구체의 입자형상을 유지하는 cubic $CeO_2$를 합성하고 X-ray diffraction, FE-SEM, micropore physisorption analyzer 분석을 통하여 입자의 결정상과 형상, 비표면적 등을 비교 분석하고 $Li/CeO_2$ couple의 충,방전 용량과 수명특성을 비교 분석하여 $CeO_2$의 전기화학적 특성을 알아보았다.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.2
• /
• pp.98-103
• /
• 2011

[ $Li[Ni_{0.8}Co_{0.15}Al_{0.05}]O_2$ ]cathode material for lithium secondary battery is obtained using co-precipitation method. To determine the optimal metal solution concentration value, the CSTR coprecipitation was carried out at various concentration values(1-2 mol/L). The surface morphology of coated samples was characterization by SEM(scanning electron microscope) and XRD (X-Ray Diffraction)analyses. Impedance analysis and cyclic voltammogram presented that internal resistance of the cell was dependent upon the concentration of metal solution. such data is very helpful in determining the optimal content of metal solution concentration to enhancing electrochemical property by adjusting powder size distribution and crystal structure.

• Membrane Journal
• /
• v.24 no.5
• /
• pp.386-392
• /
• 2014

Two commercial membranes (porous membrane and cation exchange membrane) were evaluated as a separator in the Zn-Br redox-flow battery (ZBRFB). The performance properties of ZBRFB were test in the current density of $20mA/cm^2$. The electromotive forces (OCV at SOC 100%) of ZBRFB using SF-600 (porous membrane) and Nafion 117 (cation exchange membrane) were 1.87 V and 1.93 V, respectively. The cycle performance of ZBRFB using each membrane was evaluated during 7 cycles. The performance of ZBRFB using SF-600 membrane was 89.76%, 83.46% and 74.88% for average current efficiency, average voltage efficiency and average energy efficiency, respectively. The performance of ZBRFB using Nafion117 membrane was 97.7%, 76.33% and 74.56% for average current efficiency, average voltage efficiency and average energy efficiency, respectively.

• Polymer(Korea)
• /
• v.31 no.1
• /
• pp.74-79
• /
• 2007

Polypyrrole (PPy) was made by an emulsion polymerization using iron (III) chloride ($FeCl_3$) as an initiator and dodecyl benzene sulfuric acid (DBSA) as an emulsifier and dopant. Poly (2,6-dimethyl-1,4-phenylene oxide) (PPO) was sulfonated by chlorosulfonic acid (CSA). The cathode was composed of $PPy^+DBS^-$ complex, conductor powder, and PPO or sulfonated poly (2,6-dimethyl-1,4-phenylene oxide) (SPPO) as a binder or dopant. The charge-discharge performance of $PPy^+DBS^-/SPPO$ cathode was increased as the extent of about 50%, than $PPy^+DBS^-/PPO$. This is because SPPO played a role as a binder as well as a dopant. In addition, sulfonation brings out the increase of miscibility between PPy and SPPO, and the increase of contact area between cathode and electrolyte.