• Tribology and Lubricants
• /
• v.4 no.1
• /
• pp.25-29
• /
• 1988

대부분의 기계장치는 철을 주재료로 하여 만들어진다. 철은 본래 순수 금속으로서는 존재하지 않고 주로 다른 원소와 결합하여 산화물로 존재한다. 철 산화물이나 철광석을 재련하면 순수금속(free metal)이 얻어지는데 성능을 개량하기 위해 소량의 다른 원소를 첨가하게 된다. 그러나 금속철을 철산화물로 되돌리려는 자연의 힘이 막강하여 유용한 금속이 못쓰게 된다. 이는 마치 인간이 철광석에서 유용한 금속을 만들어내는 것을 자연이 다시 환원시켜 인간의 성공에 반항하는 것 같다. 미국에서만 매년 철 종류의 부식에 대처하기 위해 사용되는 물질이 60억달러 이상 소요되는 것으로 추산되고 있으며 철 종류 50톤중 1톤이 매년 산화물인 녹으로 바뀌어 지고 있는 실정이다.

• Korean Chemical Engineering Research
• /
• v.46 no.6
• /
• pp.1029-1038
• /
• 2008

Transition-metal-oxide-incorporated hydrotalcites were prepared by hydrothermal reaction of their synthetic mixtures containing precursors of transition metal oxides and their properties of nitrogen dioxide adsorption was investigated. The dispersion of transition metal oxides on the hydrotalcites and the amount and the state of nitrogen dioxide adsorbed on them were examined by using XRD, SEM, XPS, nitrogen adsorption, a gravimetric adsorption system, FT-IR spectroscopy and temperature programmed desorption techniques. Transition metal oxides were mainly incorporated on their surface and the incorporation of iron and nickel oxides to the hydrotalcites increased their adsorption amounts of nitrogen dioxide. The dispersion of iron oxide on the hydrotalcites was effective in increasing the amount of nitrogen dioxide adsorption, while too much amount of iron oxide incorporation reduced the amount of nitrogen dioxide adsorption due to masking of surface basic sites by agglomerated iron oxide. Although the incorporation of iron oxide to the hydrotalcites lowered the adsorption strength of nitrogen dioxide, the incorporation of it with a proper amount enhanced the amount of nitrogen dioxide adsorption and the stability against the hydrothermal treatment.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.25.3-25.3
• /
• 2011

반도체형 가스센서의 가스 감응은 산화물 표면과 주변 가스와의 화학적 반응에 기인한 것이므로 나노 크기의 감응물질 입자를 합성하여 비표면적을 넓히려는 연구가 많이 진행되어 왔다. 일반적으로 감응 물질의 크기가 나노 스케일로 감소하면 가스 감응 특성이 증가하지만, 심한 응집으로 가스 확산이 어려워 가스 감응 특성이 저하되게 된다. 따라서 비표면적이 크면서도 응집이 덜한 나노 구조체가 산화물 가스 센서에 이용되어 왔다. 특히 중공구조는 응집이 적고 가스확산이 용이하며 큰 비표면적을 가지기 때문에 널리 연구되어진 나노구조체이다. 한편 산화철은 친환경적인 n-type 반도체로써 에너지 저장소, 촉매, 리튬-이온 배터리의 양극물질, 가스센서 등의 응용분야에 널리 이용되고 있다. 본 연구에서는 Solvothermal에 의한 자기조립 방법으로 산화철 중공구조를 합성하고 기능화를 위해 귀금속 촉매인 Pt를 첨가하였다. $400^{\circ}C$에서 에탄올 가스에 대한 가스 감응 측정을 통해 대조군인 산화철 응집체와 나노 스케일의 구에 비해 중공구조가 가스 감응에 유리함을 보고한다.

• Clean Technology
• /
• v.19 no.3
• /
• pp.233-242
• /
• 2013

The influences of Ca and Fe based oxides as dechlorination sorbents on the product distribution, boiling point distribution of liquid product, concentration of Cl of the products from the pyrolysis of PVC containing combustible wastes were investigated. With Fe based oxides as the sorbents, the yield of liquid product remarkably decreased whereas the decrease of the boiling point distribution of the liquid product was not noticeable. This phenomenon indicated that Fe based oxides worked as catalysts with weak catalytic activity. With Ca based oxides as the sorbents, the yield of liquid product did not decrease and the boiling point distribution of liquid product did not change significantly, but the dechlorination performance of these was much better than that with Fe based oxides.

• Proceedings of the KSEEG Conference
• /
• 2007.04a
• /
• pp.346-348
• /
• 2007

• Applied Chemistry for Engineering
• /
• v.18 no.5
• /
• pp.495-500
• /
• 2007

The inside wall of a coal gasifier is lined with refractory, and the corrosion of the refractory is an important factor affecting the refractory lifetime and the replacement period. This paper examines the changes in microstructure of a chromia refractory due to chemical reactions with slag having varying amounts of $Fe_2O_3$. Slag samples were prepared by adding $Fe_2O_3$ to KIDECO slag, and static corrosion experiments were carried out at $1550^{\circ}C$. The layer of $(Fe,Cr)_3O_4$ formation and the depth of Fe depletion in the infiltrating slag were determined. In addition, FactSage equilibrium calculations were carried out in order to determine the conditions of formation, and to compare with the experimental observations. In the sample exposed to KIDECO slag, which has about 10 wt% $Fe_2O_3$, the formation of $(Fe,Cr)_3O_4$ was not observed. As the $Fe_2O_3$ concentration in slag increased, $(Fe,Cr)_3O_4$ formation and Fe depletion depth increased. Increasing $Fe_2O_3$ concentration also made the slag/refractory interface indistinguishable. Equilibrium calculations predicted that higher $Fe_2O_3$ concentrations favor chromite formation at gasification temperatures. The chromite formation was most favorable when the amount of $Cr_2O_3$ was limited, as in the case of dissolved $Cr_2O_3$ in slag. When the concentration of $Fe_2O_3$ in slag was less than 20%, the formation of chromite was least favorable in the system with equal amounts of slag and refractory.

• Journal of the Korean Ceramic Society
• /
• v.11 no.4
• /
• pp.5-18
• /
• 1974

본 연구에 있어서는 연료유의 연소에 의한 내화물의 부식을 연구하기 위하여 시멘트소성용 회전가마, 보일러 및 판유리제조용 탱크가마에 쓰이는 여러 내화물을 짤라서 그 가운데에 구멍을 파고 중유재의 주성분인 V2O5, Na2CO3, Fe2O3, Fe 및 황산철을 미리 그 구멍속에 넣어 응용 확산시킨 다음 이들을 그들의 상용온도인 145$0^{\circ}C$로 황 함유량이 다른 연류유로 소성하여 얻은 결과는 다음과 같다. 일반적으로 5산화 바나듐-알루미나, 고알루미나질 및 염기성 내화물; 산화나트륨-고알루미나질, 실리마나이트질 및 염기성 내화물은 2%미만의 황 함유 연류유소성에 의하여 부식이 적고 3.5%이상의 황하유 연료유소성시는 황에 의하여 대개가 침식을 당하였다. 무수 아황산 분위기속에서 규산알루미늄 및 구석계의 내화점토질내화물은 산화철이 환원되어 색이 연해지고 고알루미나질 벽돌은 색이 짙어지는 경향이 있고 산화철은 황산철로 변하여 풍화의 원인이 되어 침식을 당하게 되었고, 소성시간이 길면 길수록 부식은 증가하고 황산소다보다 탄산소다에 의하여 훨씬 더 많이 부식을 당하였다.

• Applied Chemistry for Engineering
• /
• v.8 no.5
• /
• pp.830-836
• /
• 1997

The surface modification of iron oxide particle produced from steel-pickled acid by sodium-contained materials was studied. The molar ratio of $SiO_2$ to $Na_2O$ of sodium silicate was 1, 2, 3.5, respectively. The dispersion stability of iron oxide suspension as functions of amount of silica and pH was evaluated by surface charge and sedimentation velocity of iron oxide particle. Then the amount of sodium silicate was determined to provide a dispersion stability of iron oxide particle above pH 7. Finally, the surface modification of iron oxide particle with sodium silicate as silica-contained materials was done by wet ball milling. In the results of study, the dispersion stability of silica modified iron oxide particle was largely depended on amount of silica and pH together. The untreated iron oxide was unstable at pH 8, i.e. isoelectric point, but, the surface modified iron oxide particle with 0.8wt% silica was stable above pH 5. The dispersion stability was enhanced with 0.2wt% of anionic polyelectrolyte.

• Resources Recycling
• /
• v.5 no.2
• /
• pp.57-62
• /
• 1996

The regeneration of wastc piddlng acid from ironmaking industry produces Iron oxides as by products which are used for pigments and raw matcrial of ferrite. Thc impurilies level of iron axides for ferrile arc strictly regalated. Filtrat~on, adsorption medw technique, Fe leaching and ncutralizaiion wcre tried in order to remove silica impurities in the wasb pickling acid solution.

• Journal of the Mineralogical Society of Korea
• /
• v.25 no.4
• /
• pp.313-322
• /
• 2012

몽골 우기누르 지역 철-망간 광상과 타미르골 지역 철 광상의 광체는 먼곤체지 층 내에 렌즈상으로 협재되는 특성을 갖는다. 이러한 광상은 캠브리아 기에서 실루리아기에 이르는 화산 기원의 퇴적형 광상인 타미르골-요루골 광상구에 해당된다. 우기누르 지역의 철-망간 광체와 타미르골 지역의 철광체는 주로 규암과 편암을 모암으로 하여 먼곤체지 층 내에 렌즈상으로 협재되어 있다. 우기누르지역의 편암이 주로 세리사이트 편암인 데 비해 타미르골 지역은 주로 백운모 편암이 나타나는 차이를 갖는다. 또한 우기누르 지역의 광석은 망간이10에서 12% 함유되나 타미르골 지역의 광석은 망간이 1% 이하로 함량이 낮은 특성을 갖는다. 우기누르 철 망간 광상의 철 광물은 주로 자철석, 적철석이 우세하게 나타나고 기타 철 산화물과 황철석이 미량으로 수반되어 나타나며, 망간 광물은 주로스페사틴, 버네사이트가 우세하게 나타나고 기타망간 산화물이 수반되어 나타난다. 타미르골 지역의 철 광석은 자철석이 우세하게 나타나고 적철석이 수반되며 황철석, 철 산화물, 탄산질 철 등이 미량으로 수반되어 나타난다. 우기누르 철-망간 광상에 대한 육상 자력탐사 결과 높은 자기 이상값을보이는 영역이 지표에서 확인된 광체의 방향과 같은 약 $N30^{\circ}W$ 방향으로 나타나며 지표에서 확인된 광체 이외에 지표에 드러나지 않은 부분에서도 연장되는 것이 확인되었다.