• Journal of the Korea Institute of Building Construction
• /
• v.15 no.1
• /
• pp.25-33
• /
• 2015

In this study, initial crack index was evaluated by FEM analysis to find the crack propagation from hydration heat in precast concrete. As results, as the usage of hardening accelerator increased, initial compressive strength increased and setting time was shortened. Additionally, as amounts of hardening accelerators increased, the central temperature of concrete increased and the time to reach the highest temperature was shortened. It was demonstrated that the hardening accelerators accelerated the hydration reaction of cement, and caused the increase of hydration heat within the short period of time. Furthermore, the crack index for evaluating the heat level was performed by FEM. As results, there was no problem about the cracks, despite of the growth of initial high hydration heat. This is because of the increased tensile strength that is large enough to sustain the thermally induced-stress.

• International Journal of Highway Engineering
• /
• v.13 no.1
• /
• pp.139-148
• /
• 2011

Asphalt concrete overlay method is used by general maintenance and rehabilitation of construction for aged concrete pavement in Korea. However, in case of the AC overlay method to extend service life of the existing concrete pavements, various distresses of reflection crack, pothole and rutting are the typical problems of the asphalt overlay on existing concrete pavement since it has different physical characteristics between asphalt overlay and existing concrete pavement. To achieve this, application of concrete overlay method is required instead of AC overlay method. Concrete overlay method has advantages that can reduce maintenance cycle and costs since it has excellent bearing value for heavy vehicles and no rutting. However, technical problems of detour road construction, traffic control and other disadvantages happened by long curing time. Thus, in this study and experimental research were launched to evaluate the workability, durability and resistance against environmental loading of Very Rapid Hardening Acrylic Polymer Modified Concrete(VRH-APMC) for application of bonded concrete overlay method. Test results showed that the compressive and bond strength were exceed 21MPa and 1.4MPa of target strength after four hours for rapid traffic opening properties. And tests of resistance against environmental loading results showed that VRH-APMC secured excellent durability. Thus, it was known that VRH-APMC was suitable material for large scale bonded concrete overlay method, and it was possible to use maintenance and rehabilitation method which needs enough workability and rapid traffic opening.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.156-162
• /
• 2017

Recently, researches on High-Volume Fly ash Cement(HVFC), which is replacing high portion of cement to fly ash, have been actively conducted to reduce $CO_2$ formation. Though HVFC has various advantages, low strength development in early ages is pointed out as the biggest problem in the application of fly ash. In order to overcome such limitations, this study investigated the hydration and compressive strength characteristics of HVFC paste depending on the fly ash content with the mixing ratio varying from 0 to 80 %. Experimental results show that the HVFC paste with low water-binder ratio can overcome the limitation of low compressive strength at early ages. Also, from the result of heat flow delay, 50 % of fly ash weight ratio was the critical point of the filler effect.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.4
• /
• pp.529-535
• /
• 2013

A new thin sandwich panel composed of an aluminum expanded metal core adhesively jointed with stainless steel face sheets is introduced, and its mechanical behavior under three-point bending is investigated. The strength and stiffness are analyzed theoretically, and the press-formability and strength enhancement are evaluated experimentally. The specimens with the specific configurations exhibit face yielding well before face-core separation, which means that the sandwich panel can be formed by a press without failure. The measured load levels corresponding to the face yielding and the face-core separation agree fairly well with the theoretical estimations. For a given weight, the sandwich panel is superior to a solid panel in terms of strength, stiffness, and press-formability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.309-312
• /
• 2008

This paper describes ultimate load tests which were performed to show the effects of prestress loss and tendon corrosion on the flexural strength of post-tensioned concrete beams and the occurrence of wire fracture. Five test specimens were fabricated in laboratory with the variations of the prestress of tendons and the loss of tendon area. For two specimens, small area of tendon at the center of the beam was exposed by using diameter 25mm drill and the exposed tendon was corroded using accelerated corrosion equipment. During the tests, deflections, crack width, and strain changes were measured and acoustic events were monitored with two acoustic sensors. Tests results show that the ultimate flexural strength of test specimens with corroded tendons is smaller than the predicted flexural strength which is calculated considering the loss of tendon area. It is considered that estimation of flexural strength of PSC beams with corroded tendons is very complicated just based on the loss of tendon area obtained by one-side visual inspection.

• The Journal of Engineering Geology
• /
• v.1 no.1
• /
• pp.11-18
• /
• 1991

A series of laboratory tests were conducted to verify the unhardening phenomena of Soil-Cement Wall (SCW) and the results are presented in this paper. Specimens are prepared by mixing the site soil with cement and additives at a various ratio. The hydration of the cement mixed with the in-situ soil was retarded due to the higher organic content of the soil. In order to remove the influence of the organic matters in hydration reaction, calcium chloride (CaCI$_2$) was added as an acceleration additive at a different ratio. The optimum ratio of the calcium chloride for the higher SCW strength was determined as 2% of cement weight. The strength, however, was decreased by adding 4 and 6% of the additives. The effect of other additives, NaOH and NaSiO$_2$, were also investigated and the results are included. The strength of SCW by adding sodium hydroxide was lowered. And the short term strength by adding sodium silicate was increased but the long term strength was decreased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.6
• /
• pp.112-119
• /
• 2022

Recently, as carbon neutrality has been important factor in the construction industry, many studies have been conducted on the high-volume fly ash concrete. High volume fly ash concrete(HVFC) is usually made by replacing more than 50% of cement with fly ash. However, HVFC has a disadvantage of low compressive strength in early age. To overcome this shortcoming of HVFC, improve this, interest in techonolgy using nanomaterials is increasing. Nano silica is expected to improve the early age strength of HVFC as a pozzolanic material. This study investigated the effect of nano silica on the early hydration reaction and microstructure of HVFC. The early hydration reaction of HFVC was analyzed through setting time, isothermal calorimeter, compressive strength and thermal weight analysis. In addition, the microstructure of HVFC was measured by mercury intrusion porosimetry. From the test results, it was confirmed that nano silica increased the early age strength and improve the microstructure of HVFC.

• Journal of the Korea Institute of Building Construction
• /
• v.24 no.1
• /
• pp.11-21
• /
• 2024

This research elucidates the fundamental properties of carbon dioxide (CO₂)-cured mortar as influenced by varying substitution rates of blast furnace slag fine powder. The findings indicate that CO₂ curing enhances the formation of calcium carbonate (CaCO₃), contributing to pore reduction and the early development of strength. While calcium hydroxide (Ca(OH)₂) plays a more pivotal role in the primary development of strength compared to CaCO₃, an increase in the substitution rate of blast furnace slag fine powder results in reduced production of Ca(OH)₂. Nonetheless, the maintenance of strength through CaCO₃ formation is observed even after the depletion of Ca(OH)₂, suggesting that the required performance can be sustained post-exposure to the atmosphere following CO₂ curing. It is noted that substitution rates exceeding 50% lead to performance deterioration due to CO₂, highlighting the necessity for careful adjustment of the substitution ratio.

• Journal of the Korea Concrete Institute
• /
• v.14 no.6
• /
• pp.942-948
• /
• 2002

When fresh concrete is exposed to low temperature, the concrete may suffer frost damage due to freezing at early ages and the strength development may be delayed. One of the solution methods to resolve these problems is to reduce freezing temperature of concrete by the use of chemical admixture called Accelerator for freeze protection. In this study we Investigate the effect on the strength development of cement mortar using accelerator for freeze protection with the variable curing condition. As the result of this study, the mortar using accelerator for freeze protection show continuously the strength development in curing condition of -5$^{\circ}C$. And the compressive strength under variable temperature condition was higher than constant temperature condition in same maturity.

• Journal of the Korea Institute of Building Construction
• /
• v.10 no.5
• /
• pp.95-102
• /
• 2010

In recent years, the demand for the development of high quality and cost effective materials, as well as the competition to ensure a diverse and sufficient amount of ready-mixed concrete, has been increasing rapidly. In this experiment, concretes made with different admixtures are blended with each other in different combinations and ratios, in order to identify potential problems. The first test was a slump level test, in which all of the concretes met the required numbers, as they also did in the test for air content. Plain organic acid concrete scored the highest in bleeding amount, but organic acid mix in general showed a similar outcome. In the early measurement of compressive strength, plain naphthalene concrete was the strongest. Of the blends, the 5:5 mix of organic acid and naphthalene was the strongest. In the standard measurement, the 5:5 mix of naphthalene and lignin was the strongest. Tensile strength tests revealed similar results. Length change rate proved to be greater in blended concrete than in plain concrete, and dry shrinkage rate was highest in the 7:3 ratio blends. Through SEM photo analysis, it was confirmed that the 7:3 ratio blends contained more micro-voids. In conclusion, with the exception of a specific few combinations, it was found that the blending of different types of concrete is undesirable due to the delayed coagulation time as well as the early decrease in strength.