• Journal of Welding and Joining
• /
• v.27 no.3
• /
• pp.73-79
• /
• 2009

This present paper investigated the mechanical properties and the microstructures of each penetration shapes classifying the conduction shape area and the keyhole shape area about electron beam welded 120(T)mm thick plated aluminum 5052 112H. As a result the penetration depth is increased linearly according to the output power, but the aspect ratio is decreased after the regular output power. In the conduction shape area, the Heat affected zone is observed relatively wider than the keyhole shape area. In the material front surface of the welded specimen, the width is decreased but the width in the material rear surface is increased. After the measuring the Micro Vikers Hardness, it showed almost similar hardness range in all parts, and after testing the tensile strength, the ultimate tensile strength is similar to the ultimate tensile strength of the base material in all the specimens, also the fracture point was generated in the base materials of all the samples. In the result of the impact test, impact absorbed energy of the Keyhole shape area is turned up very high, and also shown up the effect about four times of fracture toughness comparing the base material. In the last result of observing the fractographs, typical ductile fraction is shown in each weld metal, and in the basic material, the dimple fraction is shown. The weld metals are shown that there are no other developments of any new chemical compound during the fastness melting and solidification.

• Journal of Welding and Joining
• /
• v.23 no.3
• /
• pp.68-75
• /
• 2005

The fatigue life of welded joints is associated with crack initiation and propagation life. Theses cannot be easily separated, since the definition of crack initiation is vague due to the initiation of multiple cracks that are distributed randomly along the weld toes. In this paper a method involving a notch strain and fracture mechanical approach, which considers the characteristics of welded joints, e.g. welding residual stress and statistical characteristics of multiple cracks, is proposed, in an attempt to reasonably estimate these fatigue lives. The fatigue crack initiation life was evaluated statistically, e.g. the probability of failure occurrence in 2.3, 50 and $97.7\%$, in which the cyclic response of the local stress/strain hi the vicinity of the weld toes and notch factors derived by the irregular shape of the weld bead are taken into account. The fatigue crack propagation life was simulated by using Monte-Carlo method in consideration of the Ad-factor and the mechanical behavior of mutual interaction/coalescence between two adjacent cracks. The estimated total fatigue life, $(N_T)_{P50\%}$, as a sum of crack initiation and propagation life under the probability of failure occurrence in $50\%$ showed a good agreement with the experimental results. The developed technique for fatigue lift estimation enables to provide a quantitative proportion of crack initiation and propagation life in the total fatigue life due to the nominal stress range, ${\Delta}S$.

• Composites Research
• /
• v.13 no.6
• /
• pp.23-29
• /
• 2000

The internal residual stresses within the multilayered structure with sharp interface induced by the difference in thermal expansion coefficient between the materials of adjacent layers often provide the source of failure such as delamination of interfaces etc. Recent development of the multilayered structure with functionally graded interface would be the solution to prevent this kind of failure. However a systematic thermo-mechanical analysis is needed for the customized structural design of multilayered structure. In this study, theoretical model for the thermo-mechanical analysis is developed for multilayered structures of the $Al-SiC_p$ functionally graded composite for electronic packaging. The evolution of curvature and internal stresses in response to temperature variations is presented for the different combinations of geometry. The resultant analytical solutions are used for the optimal design of the multilayered structures with functionally graded interface as well as with sharp interface.

• Journal of Welding and Joining
• /
• v.6 no.2
• /
• pp.30-39
• /
• 1988

Generally, as the welded region of weld structures has the incomplete bead and welded deposit which are able to behave like the surface cracks occasinally, there is a high possibility that the fatigue fracture of the weld structures is due to the surface cracks on the wlded region. This study was done to investigate the effects of post weld heat treatment (PWHT) on the fatigue behaviors of the surface crack of the heat affected zone (HAZ) for the multi-pass welds under the repetitive pure bending moment. The obtained results are summarized as follows : 1. The crack grows to the depth direction initially as the number of cylces increase, the amount of crack length is increased for the surface dir3ction and cive versa for the depth direction. 2. The fatigue life is increased in a order of as weld, PWHT specimens and parent. 3. As the number of cycles increase, the crack length is increased to th surface direction. The increase of the depth length is blunted at the center of specimen thickness. 4. The fatigue crack growth of PWHT specimens to the surface direction is dependent upon the holding time and applied stress during PWHT. In order words, the crack growth rate decreases with the holding time and increases with the applied stress during PWHT. 5. As the crack grows, the aspect formed in the course of crack propagation approaches to semicircle for parent and ellipse with the largest semidiameter for PWHT ($1/4hr, 15kgf/mm^2$) 6. At depth direction, it is difficult to apply to the paris' equation because of the scattered data between the crack growth rate and the stress intensity factor range.

• Journal of Welding and Joining
• /
• v.26 no.2
• /
• pp.62-68
• /
• 2008

Effects of gravitational orientation on gas tungsten arc welding (GTAW) for 304 stainless steel were studied to determine the critical factors for weld pool formation, such as weld surface deformation and weld pool shape. This study was accomplished through an analytical study of weld pool stability as a function of primary welding parameters (arc current and arc holding time), material properties (surface tension and density), and melting efficiency (cross-sectional area). The stability of weld pool shape and weld surface deformation was confirmed experimentally by changing the welding position. The arc current and translational velocity were the major factors in determining the weld pool stability as a function of the gravitational orientation. A 200A spot GTAW showed a significant variation of the weld pool formation as the arc held longer than 3 seconds, however the weld pool shape and surface morphology for a 165A spot GTAW were 'stable', i.e., constant regardless of the gravitational orientation. The cross-sectional area of the weld (CSA) was one of the critical factors in determining the weld pool stability. The measured CSA ($13.5mm^2$) for the 200A spot GTAW showed a good agreement with the calculated CSA ($14.9mm^2$).

• Journal of Welding and Joining
• /
• v.35 no.2
• /
• pp.43-51
• /
• 2017

The automatic welding systems, have received much attention in recent years, because they are highly suitable not only to increase the quality and productivity, but also to decrease manufacturing time and cost for a given product. Automatic welding work in semiconductor or space industry to be carried out in pipe line and butt joint mostly and plasma arc welding(PAW) is actively applied. To get the desired quality welds in automated welding system is challenging, a mathematical model is needed that has complete control over the relevant process parameters in order to obtain the required mechanical properties. However, In various industries the welding process mathematical model is not fully formulated for the process parameter and on the welding conditions, therefore only partial variables can be predicted. Therefore, this paper investigates the interaction between the welding parameters and mechanical properties for predicting the weld bead geometry by analyzing the S/N ratio.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.8
• /
• pp.649-656
• /
• 2019

Flux cored arc welding (FCAW), which is used widely in many fields, such as shipyards, bridge structures, construction machinery, and plant industry, is an alternative to shielded metal arc welding (SMAW). FCAW is used largely in the welding of carbon and alloy steel because it can be welded in all poses and obtain excellent quality in the field under a range of working conditions. In this study, the mechanical properties of welded parts were analyzed after different welding of SS400 and SM490A using FCAW. The following conclusions were drawn. The tensile test results satisfied the KS standard tensile strength in the range of 400~510 N/mm2 in all welding positions. The bending test confirmed that most of the specimens did not show surface breakage or other defects during bending and exhibited sufficient toughness, even after plastic deformation. The hardness test results were lower than the standard value of 350 Hv of KS B 0893. Similar to the hardness test, were greater than the KS reference value. The macro test revealed no internal flaws, non-metallic inclusions, bubbles or impurities on the entire cross section of the weld, and there were no concerns regarding lamination.

• Conservation Science in Museum
• /
• v.29
• /
• pp.153-162
• /
• 2023

Clay figure of Baekje, produced by forming and molding various shapes using clay, are mainly excavated from temple sites and provide essential information for studying the Buddhist art of Baekje. Research on clay figures of Baekje primarily focuses on the characteristics of Baekje-era temples in which such figures are excavated, as well as the role and production techniques of clay figures, by comparing regional and morphological characteristics. In particular, research on the manufacturing method of clay figures is mainly carried out by visual observation, whereas precise scientific analysis is required to understand production techniques and characteristics of raw materials in greater detail. In this study, to confirm such production techniques and material characteristics, computed tomography (CT) scans were conducted on the Clay Bodhisattva excavated from the Neungsan-ri Temple site in Buyeo. As a result, it was found that the Clay Bodhisattva was made using a cylindrical core of fine clay, tied together with several thin branches or reeds with straws. The clay used in the figure bore traces indicating the presence of herbaceous plants, which increase adhesion between clay and prevent cracks in the contraction process. On the other hand, the density of the fine clay differs on the inside and outside of the clay figure. Based on this, it is presumed that the clay was applied around the cylindrical core to shape the Clay Bodhisattva. The clay was reapplied on top of the figure to express the detailed shape and pattern.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.73-73
• /
• 2010

합금원소가 다량 첨가된 고합금강, 스테인리스강, Ni기 초내열합금 등은 용접시 혹은 후열처리 동안 열영향부 (HAZ: heat-affected-zone)에서 결정립계를 따라서 액화균열이 종종 발생한다. 이러한 액화균열은 급속한 가열시 HAZ의 결정립계가 국부적으로 용융되어 액상필름을 형성하고, 냉각시 수축으로 인한 인장구속응력에 의해 필름을 따라서 균열이 발생하여 생성된다. HAZ 결정립계 액화는 탄화물, 황화물, 인화물, 보론계 화합물 등이 급가열시 기지와의 반응에 의해 표피 액상을 형성하는 조성적 액화 (constitutional liquation)에 의한 액상의 결정립계 침투로 설명되거나, 결정립계 자체의 용융점을 상당량 낮추는 보론(B), 인(P), 황(S)등의 편석에 의한 국부적 입계 용융으로 주로 연관 지어 해석한다. HAZ 액화균열은 고온 입계균열 현상이므로, 결정립계의 특성에 따라 크게 영향을 받으며 결정립계 character 설계에 의해 액화균열 저항성을 개선시킬 수 있음을 유추할 수 있다. 한편, 본 연구자들은 최근 Ni기 초내열합금에 있어 입계 serration 현상을 새롭게 발견하였으며, 이론적 접근법을 통해 serration을 위한 특별한 열처리 방법을 개발하였다. 형성된 파형입계는 결정학적인 관점에서 조밀 {111} 입계면을 갖도록 분해 (dissociation)되어 낮은 계면에너지를 갖게 됨을 확인하였으며, 입계형상 변화뿐만 아니라 탄화물 특성변화까지 유도하여 크리프 수명을 기존대비 약 40% 정도 향상시킴을 확인하였다. 본 연구에서는 이러한 직선형 입계 대비 'special boundary'로 간주되는 파형입계가 도입될 경우, 보론 편석 및 HAZ 액화거동에 미치는 영향을 고찰하고자 하였다. SIMS (secondary ion mass spectrometry)를 이용하여 열처리 직후 결정립계 보론편석 정도를 비교하였다. 파형입계 시편의 경우, 일반직선형 시편에 비해 결정립계에 보론편석 저항성이 우수함을 확인할 수 있었다. 재현 HAZ 열사이클 시험을 통해 미세조직을 정량적으로 분석하였다. 파형입계 시편 및 일반직선형 시편 모두 최고온도 $1060^{\circ}C$이상부터 입계 탄화물이 기지내로 완전 용해되고 입계가 액화되기 시작하였다. 최고온도별로 입계액화비율을 정량적으로 비교한 결과, 파형입계가 직선입계 대비 훨씬 낮음을 확인할 수 있었으며, 때때로 액화된 필름이 입계를 따라 전파되지 않고 부분적으로 단락되어 있음이 관찰되었다. 액화시험 후 투과전자현미경을 이용한 EDS (energy dispersive spectrometry) 분석을 통해 결정립계 액화의 주요원인은 입계 $M_{23}C_6$의 조성적 액화반응 보다는 보론 편석 (원자 및 $M_{23}(CB)_6$)으로 인한 결정립계 국부용융이 더 유력함을 유추할 수 있었다. 따라서 상기 결과로부터 입계구조가 안정되어 계면에너지가 낮은 파형입계가 보론편석에 대한 저항성이 우수하였으며, 이러한 결과는 액화 저항성에 대응되어 영향을 미침을 알 수 있었다. 게다가 파형입계에 액상 필름이 생성되더라도 낮은 계면에너지에 의해 비롯된 상대적으로 낮은 적심성 (wettability)에 의해 필름이 쉽게 전파되지 않음을 'Smith 입계 wetting 이론'을 이용하여 해석할 수 있었다.

• Journal of Korea Water Resources Association
• /
• v.49 no.12
• /
• pp.1015-1025
• /
• 2016

In general, manholes installed as urban drainage facilities are a variety forms such as straight path manholes, 90 degree bend manhole, three-way combining manhole, and four-way combining manhole. In particular, the surcharged flow at a four-way manholes installed in the downstream of urban sewer system is the main cause of the urban inundation caused by the energy loss. Therefore, it is necessary to analyze the flow characteristics and estimate the head loss coefficients at surcharged four-way combining manholes. The hydraulic experimental apparatus which can change the manhole shapes (square, circle) and flow ratios were installed to estimate the head loss coefficients. In the experiments, two inflows ($Q_m$, $Q_{lat}$) were varied from 0 to $4.8{\ell}/sec$ and 24 combinations were tested in total. The flow ratios $Q_{lat}/Q_{out}$ were varied from 0 to 1 for a total flow $Q_{out}$ ($Q_{out}=Q_m+2Q_{lat}$) of 2, 3, 4, and $4.8{\ell}/sec$, respectively. The variation of head losses were strongly influenced by the lateral inflow because the head loss coefficient increases as the flow ratios $Q_{lat}/Q_{out}$ increases. It was estimated head loss coefficients of the circular manhole is slightly lower than those of the square manhole. However, there was no significant difference of head loss as discharges change. The range of head loss coefficients at four-way combining manhole according to the change of the lateral inflow ratio was estimated to be 0.4 to 0.8. Also, the relation equations between the head loss coefficients (K) and the lateral inflow ratios ($Q_{lat}/Q_{out}$) were suggested in this paper.