• Journal of Welding and Joining
• /
• v.23 no.6
• /
• pp.99-105
• /
• 2005

The mixing ratio effect of the GTD-111(base metal) powder and the GNI-3 (Ni-l4Cr-9.5Co-3.5Al-2.5B) powder on TLP(Transient Liquid Phase) bonding phenomena and mechanism was investigated. At the mixing ratio of the base metal powder under $50wt\%$, the base metal powders fully melted at the initial time and a large amount of the base metal near the bonded interlayer was dissolved by liquid inter metal. Liquid insert metal was eliminated by isothermal solidification which was controlled by the diffusion of B into the base metal. The solid phases in the bonded interlayer grew epitaxially from the base metal near the bonded interlayer inward the insert metal during the isothermal solidification. The number of grain boundaries farmed at the bonded interlayer corresponded with those of base metal. At the mixing ratio above $60wt\%$, the base metal powder melted only at the surface of the powder and the amount of the base metal dissolution was also less at the initial time. Nuclear of solids firmed not only from the base metal near the bonded interlayer but also from the remained base metal powder in the bonded interlayer. Finally, the polycrystal in the bonded interlayer was formed when the isothermal solidification finished. When the isothermal solidification was finished, the contents of the elements in the boned interlayer were approximately equal to those of the base metal. Cr-W borides and Cr-W-Ta-Ti borides formed in the base metal near the bonded interlayer. And these borides decreased with the increasing of holding time.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.25-25
• /
• 2009

종래의 위보기 자세에서 용접은 중력이 모재의 표면으로 향하고 있어 용융금속이 중력에 의해 표면방향으로 흘러내리게 되어 용접 실시가 불가능하였다. 이에 Shield Gas Force, Trailing Gas Force 그리고 Ahead Gas Force를 적절히 적용하여 Position Welding에서 중력으로 인해 Molten Metal이 처지는 문제를 극복하여 생산성 향상으로 연결할 수 있음을 선행 실험을 통해 확인하였으나 기존의 C(Convergent)형, CP(Convergent Divergent)형 및 P(Parrallel)형 가스 노즐은 용접조건에 따라 실드 가스의 소모량이 많고, 토출되는 실드가스력이 부족하여 용접시 볼록한 이면 비드 형성을 위한 용융 풀을 효과적으로 제어 할 수 없다. 따라서 본 연구에서는 동일량의 실드 가스 공급시 가스 노즐을 통해 토출되는 실드가스의 소모를 줄이고 실드가스력을 극대화하여 저가의 고생산성을 가진 친 환경 용접기술(Green welding)에 부합하는 CDP(Convergent Divergent Parrallel)형 가스 노즐을 제작하여 기존의 CP형 가스 노즐과 비교 분석하였다. 또한 Overhead Position에서의 비드형상제어와 Flat Position에서 방풍효과를 비교해 보았다. 그 결과 CDP Nozzle은 CP Nozzle보다 동일한 유량에서 풍속은 3.5배, 냉각능력은 1.5배, 가스압력은 6.25배로 우수한 성능을 확인할 수 있었고, Overhead Position에서 가스 유량을 동일하게 하여 용접하였을 때 CP Nozzle의 경우 오목한 이면비드가 나타났지만 CDP Nozzle의 경우 볼록하게 양호한 이면비드 형상이 나타났고, Flat Position에서의 방풍효과 비교실험에서 CDP Nozzle에서는 깊고 균일한 용입을 CP Nozzle에서는 불안정한 용입이 나타났는데 이는 CDP Nozzle의 경우 풍속에 의한 Arc Blow가 적게 발생하여 상대적으로 더 나은 용입을 확인하였다.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.45-45
• /
• 2009

원가 측면에서 유리한 저항점용접(Resistance Spot Welding)이 차체 용접에 80%이상으로 가장 많이 적용되고 있다. 첨단고강도강(Advanced High Strength Steel)의 저항점용접성 및 용접부 특성에 미치는 공정 변수의 영향에 대한 연구결과는 많으나, 합금원소의 영향에 대해서는 전무하다. 특히, Si는 DP(Dual Phase)강에 첨가 시 균일한 마르텐사이트의 분포를 촉진하는 원소로 저항 점용접성 및 용접부 특성에 영향을 미칠 것으로 예상되며, 이에 대한 연구는 보고된바 없다. 본 연구에서는 냉연 DP강의 저항 점용접시 중요한 인자 중 하나인 너깃경과 전단인장강도에 미치는 Si함유량의 영향을 검토하였다. 사용된 강재 및 용접기는 1.2mm 두께의 Si함유량(0, 0.5, 1.0, 1.5wt%)이 다른 인장강도 780~1000MPa급 냉연 DP강과 단상 AC용접기를 사용하였다. 용접조건은 ISO 18278-2규격에 따라 가압력 4kA, 초기가압시간 40cycle, 유지시간 17cycle로 고정하고, 용접전류만 변화하여 용접을 실시하였다. 너깃경은 용접부 단면을 컷팅 후 폴리싱 하여, 광학현미경과 Image Pro plus를 이용하여 측정했으며, 인장시편규격은 JIS Z 3137를 이용하였다. Si함유량이 증가에 따라 스패터 발생 전류는 감소했고, 너깃경은 직선적으로 증가했다. Si함유량 증가에 따른 너깃경 증가 이유는 저항(R) 측정결과, Si함유량 증가에 따라 모재의 저항이 높아져, 따라서 입열량($Q=I^2Rt$)이 많아지기 때문으로 판단되었다. 인정전단강도는 Si함유량 증가에 따라 직선적으로 증가했다. 이러한 이유는 Si함유량 증가에 따라 너깃경이 증가되기 때문으로 판단되었고, 너깃경과 인장전단강도 사이에 직선적 관계(PL(kN)=$3.2N_{dia.}$-0.81, $R^2$=0.93)를 가지고 있었다. 파단양상은 Si함유량에 상관없이 5.4kA이하에서는 계면파단이 일어났고, 6.0kA이상에서는 풀 아웃 파단이 일어났다. 계면파단주원인은 용접부 가장자리에 지름이 약 $5{\mu}m$이하의 예리한 노치가 존재하여 노치응력집중과 HAZ계면 근처에 미접합부가 존재하기 때문으로 판단되었다. 6.0kA이상에서는 예리한 노치가 없었고, HAZ부가 완전히 접합되어 있기 때문에 풀 아웃 파단이 일어난 것으로 판단되었다. 따라서, Si함유량 증가에 따라 적정용접전류 구간은 감소했고, 너깃경은 직선적으로 증가했다. 또한, Si함유량 증가에 따라 인장전간강도는 증가 했으며, 너깃경과 인장전단강도 사이에 직선적 관계를 가지고 있었다. 파단 양상은 Si함유량에 상관없이 5.2kA이하에서는 계면파단이, 6.0kA이상에서는 풀 아웃 파단이 일어났다.

• Journal of Welding and Joining
• /
• v.15 no.6
• /
• pp.24-31
• /
• 1997

2매의 금속을 맞대어 그 한 쪽에 접촉면과 평행하게 고주파진동을 가하면 단 시간에 접합된다. 이공정을 초음파 용접이라고 하며 그 물리적인 본질은 아직 불분명 하지만, 첫째로는 강한 마찰에 의해 금속 자유면의 산화물층이 제거되기 때문이라는 점과 둘째로는 마찰에 의해 금속 표면이 강하게 가열되어 이에 따른 연화에 의해 접합 이 된다고 하는 점이다. 그러나 이와 같이 가열된다고 하더라도 가열은 표면부에만 국한되고 다른 부분은 가열되지 않는다. 따라서 초음파용접은 냉간접합이라고도 한다. 또 가압력과 진동에 의한 힘이 동시에 작용하기 때문에 용접할 면을 미리 청정하게 할 필요는 없고 용접전의 단계에서 자연적으로 청정화가 이루어진다고 하는 사실이 간접 적으로 증명되고 있다. 초음파 용접(Ultrasonic welding)의 특징을 요약하면 고상용접 의 일종으로서 용접중에 국부적으로 고주파 진동에너지와 압력을 가하여 용접하는 방법이다. 이 때 모재를 용융시키지 않고 건전한 야금학적 결합부가 얻어진다는 데에 큰 특징이 있다. 또한 초음파용접은 다른 용접법에 비해 경제성이 매우 높고, 초음파 용접에 필요한 출력이 전기아크 용접에 필요한 출력의 5 - 10%로 충분한 경우가 많다. 초음파 용접은 통상의 방법으로는 용접하기 어려운 동종 금속이나 이종 금속의 용접에 널리 사용된다. 이 용접법은 반도체, 미세회로, 전기 접점의 형성에 대한 생산기술 로서 사용되고 있는데 소형 모터, 알루미늄 박의 가공, 알루미늄 합금의 조립 등에 이용되고 있다. 한편 최근에는 자동차, 우주항공산업 분야의 구조제 용접용으로도 채용되고 있다.출함이 바람직하다.분비되는 배설-분비 항원의 자극과 깊은 관계가 있음을 알 수 있었다.넌트 명세서를 대한 XML DTD(Document Type Definition)를 정의하고, HTML 기반 검색 방법과 XML 기반 검색 방법에 대한 컴포넌트 검색 성능을 비교한다.따라 NO 생산 및 세포독성이 증가하였고. NO 생산을 저하시키는 약제들은 활성화된 복강 대식세포 및 RAW264.7 세포에 의한 질편모충에 대한 세포독성을 현저히 감소시키는 것으로 보아 NO는 질편모충에 대한 대식세포의 숙주 방어기전에서 중요한 역할을 감당할 것으로 생각된다.nction index) 와 최대개구시 동통의 정도는 시술전과 시술 4주후간에 유의한 차이가 관찰되었다.피부온도는 검사자간에는 특정부위에 따라 다소 차이가 있을 수 있으나 일반적으로 높은 재현성을 보여줌으로서 향후 교근 및 측두근의 임상연구 평가에 피부온도조사는 도움이 되리라 사료된다. lactobacilli의 양은 peroxidase system을 함유하거나(p < 0.01) 함유하지 않은(p < 0.05) 치약을 사용한 군 모두에서 양치전에 비해 유의성있게 감소하였다. 6. 양치후 30분에 채취한 구강건조증 환자의 자극성 전타액내 S. mutans 양은 peroxida system을 함유한 세치제를 사용한 군에서 대조군에 비해 유의성있게 낮았다(p < 0.05). 7. 양치후 30분에 채취한 구강건조증 환자의 자극성 전타액내 lactobacilli양은 peroxidase system을 함유한 세치제를 사용한 군에서 대조군에 비해 상대적으로 낮게 나타났으나(p = 0.067)

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.505-512
• /
• 1998

In this study, two-layer thermal barrier coatings composed of plasma sprayed 0.3mm $ZrO_2(8wt% Y_2o_3)$ ceramic coating layer and O.lmm $NiCrAlCoY_20_3$ bond coating layer on AISI 316 were investigated microstructure of the coating, oxidation of the metallic bond coating and adhesive strength to evaluate the durability of coating layer after cyclic and isothermal test at 90$0^{\circ}C$. And quantitative phase analysis of $ZrO_2(8wt% Y_2o_3)$ ceramic coating was performed as a function of thermal exposure time using XRD technique. The results showed that the amount of m - 2rO, phase in the coating was slightly increased with increasing thermal exposure time at 90$0^{\circ}C$. The c/a ratio of t' - $ZrO_2$ in the as-sprayed coating was 1.0099 and slightly increased to 1.0115 after 100 hours heat treatment. It was believed that $Y_2O_3$ in high yttria tetragonaJ(t') was transformed to low yttria tetragonaJ(t) by $Y_2O_3$ diffusion with increasing thermal exposure time. The adhesive strength was gradually decreased as thermal exposure time increased. After the isothermal test, the failure predominantly occured in ceramic coating layer. On the other hand. the specimens after cyclic thermal test were mostly failed at bond coating/ceramic coating interface. The failure was oeeured by decreasing the bond strength between bond coating and oxide scale which were formed by oxidation of the metallic elements within bond coating and by thermal stress due to thermal expansion mismatches between the oxide scale and ceramic coating.

• Journal of Welding and Joining
• /
• v.14 no.5
• /
• pp.134-144
• /
• 1996

A study was performed to investigate the properties of base metal and weldment for two HSLA steels and one HY-100 steel. Tensile, yield strength and elongation of HSLA-A steel were superior to those of HY-100 steel and yield ratios in HSLA-A and HSLA-B steels were higher than HY-100 steel owing to the precipitation of $\varepsilon$-Cu phase. The impact energy of HSLA-A steel was greater at all aging temperatures than that of HY-100 steel. HSLA-A and HY-100 steels had low impact transition temperature of about -l$25^{\circ}C$ and high upper shelf energy, The peak hardness of weldment in HSLA-A, HSLA-B and HY-100 steels were Hv 299, Hv 275 and Hv 441, respectively. The hardenability of HY-100 steel was largest due to the higher amount of carbon. The y-groove test showed that HSLA steels had superior resistance to cold cracking. Toughness of weld joint at the F. L. and F. L. ＋1mm in HSLA-A was almost the same as HY-100, but those at F. L.＋3mm and F. L.＋5mm was greater in HSLA-A steel.

• Journal of Welding and Joining
• /
• v.8 no.1
• /
• pp.23-30
• /
• 1990

The robotic welding has been adapted positively in many welding shops forthe purpose of improving the welding efficiency and liberating operators from the severe working atmosphere. But for a large-size structure with thick plates like ship-building and every kind of plants manufacturing, the application of the arc welding robots is not established yet. The reason is assumed that the conventional arc welding robots are not adaptive for multi-pass welding of thick plates whose grooves are not so accurate. As one solution to this problem, a guidance system which uses the welding arc itself as a sensor is largely used. In this study the velocity controller which changes the tip to workpiece distance for regulating the weld proposed. The proportional and integral gain of velocity controller were determined by using the computer simulation of the control system, and the simulation results compared with the experimental ones. It was revealed that the developed control system using the arc sensor principle has a good capability of tracking the weld joint, although some more studies will be needed to refine the model of arc current.

• Journal of Welding and Joining
• /
• v.14 no.6
• /
• pp.131-139
• /
• 1996

The response of the arc sensor using the welding current and/or welding voltage as its outputs has been obtained by the analysis and/or experiments of the static characteristics of arc sensor. But in order to improve the reliability of arc sensor, it is necessary to know its dynamic characteristics. So in this paper, it is presented the dynamic model of arc sensor including the power source, arc voltage, electrode burnoff rate, and wire feed rate. A numerical simulation of the dynamic model of arc sensor was implemented, computing the welding current with input of CTWD. The results of computer simulations and experiments of $CO_2$arc welding showed that a linear relationship between weaving center - weld line distance and current area difference was established. Additionally, a real-time weld seam tracking system interfaced with industrial welding robot was constructed, the result of the weld seam tracking experiment for weld line with an initial offset error of 5$^{\circ}$was good.

• Journal of Welding and Joining
• /
• v.25 no.1
• /
• pp.30-36
• /
• 2007

A joining of dissimilar metal combination faces significant problems such as poor strength and cracking associated with brittle intermetallic compounds(IMC) formed. An application of laser allows low heat input; leading to less dilution and smaller heat affected zone. The $CO_2$ laser overlay was conducted on an AC2B alloy with feeding Fe-based powders. The overlay area was significantly influenced from the travel velocity rather than the powder feeding rate. The interface between the overlay and substrate consisted of the hard and brittle IMC($FeAl_3,\;Fe_3Al,\;Fe_2Al_5$), which initiating and propagating the crack. The reciprocating test for the slide wear was conducted on a multi-pass overlay experiment. Comparing with the multi-pass overlay with no overlap, the overlay with 50% overlap showed better wear resistance.

• Journal of Welding and Joining
• /
• v.10 no.1
• /
• pp.12-19
• /
• 1992

용접능률의 향상을 위한 대입열용접법의 적용은 과도한 입열량으로 인하여 용접부의 인성이 저 하한다는 점에서 그 적용에 주의를 요한다. 본 보에서는 대입열용접시 열영향부의 인성 저하의 원인과 그 대책을 강재의 측면에서 검토하였다. 고장력강을 용접하면 입열량이 증가함에 따라 오스테나이트 결정립이 조대화되고 상부 베이나이트와 도상 마르텐사이트가 생성되어 인성이 저하한다. 그 대책으로서는 용접 열싸이클과정중 안정한 질화물, 산화물등을 모재에 미세분산시켜 오스테나이트 결정립 성장을 억제하고, 페라이트, 펄라이트 변태를 촉진시킨다. 이러한 석출물의 형성을 위해서는 주로 Ti, Ca, REM, B등의 합금원소가 이용된다. 소입성이 높은 주질고장력 강에서는 석출물의 분산에 의한 페라이트의 변태 촉진 보다는 Mn, Ni, Cr, Mo, V등의 합금원 소를 첨가하여 소입성을 높여 인성이 우수한 하부 베이나이트 조직을 형성하든가, 탄소량을 저 감시켜 도상 마르텐사이트의 생성을 억제하므로서 인성을 확보한다. 현재 국내에서 제조되고 있는 대입열용접용강중 인장강도 50kgf/mm$^{2}$급강은 기본적으로 용접부 인성이 우수한 TMCP법으로 제조되며, Ti등을 첨가하여 석출물의 효과를 이용하고 N을 억제하여 기지의 인 성을 향상시키는 등의 방법을 병용하고 있다. 인장강도 60kgf/mm$^{2}$ 급강은 조질처리에 의하여 제조되며, 50kgf/mm$^{2}$급강과 같이 Ti, B등의 첨가에 의한 석출물의 효과를 이용 하고 있다.