• Journal of the Korea Concrete Institute
• /
• v.19 no.1
• /
• pp.39-46
• /
• 2007

In this study, for the establishment of the performance evaluation methods and the quality control standards of durability recovery method, the quantitative exposure data by long term exposure test under the coast and normal atmosphere is accumulated and analyzed. Investigating and evaluating the result of exposure test during 30 months of exposure age under the coastal and normal atmosphere environment, carbonation depth and chloride-ion penetration depth very little penetrated than cover depth. It seems reasonable to conclude that main cause of Corrosion of reinforcing bar are chloride-ion and macro cell from the result of corrosion area and corrosion velocity. Therefore, it is considered to be applied as the fundamental data on the performance evaluation and quality control standards of repair material and method through continuous exposure test in the future.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.3D
• /
• pp.325-330
• /
• 2008

This study carried out the repeated freezing-thawing test in order to understand the long-term degradation mechanism of GFRP dowel bars. The mechanical property measured by shear test. In addition, analyzes repeated freezing-thawing degradation mechanism of GFRP dowel bars by observe the microstructure through Scanning Electron Microscope (SEM) and Gas Physisorption techniques. As the result of test, it was found that the mechanical property didn't decreased as the exposure time to water and repeated freezing-thawing environment. It shows clearly observed microstructure investigations.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.181-187
• /
• 2009

This paper is to investigate about a new technique (Bow system) which is to develop the disadvantages of the external post-tensioned method. The purpose of this paper is to analyze about the prestress loss when the loads apply along the long term and to improve the capacity of the members strengthened by Bow system. The variables in the test program are the span/depth ratio, the amount of tendon area. And the test was carried out to confirm the long term behaviour. It is shown that can apply the current code in the design, and have no the structural problems about the prestress loss.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.39 no.1
• /
• pp.50-55
• /
• 2011

In this study, simultaneous aero-structural design was performed for HALE aircraft wing. The span and the shape of main spar were considered as design variables. To maximize aerodynamic performance and to minimize weight, multi-objective optimization was used. Nonlinear static aeroelastic analysis was performed to compute large deflection of wing. Design of experiment and response surface method were used to reduce computation cost in the design process. Also, aerodynamic performances of deformed wing and rigid wing were compared.

• Journal of the Korea Concrete Institute
• /
• v.23 no.6
• /
• pp.817-826
• /
• 2011

Concrete using eco-cement has a problem with long-term strength development. However, currently, a long-term strength development mechanism is not confirmed, resulting in a lack of application of eco-cement in construction fields. In this study, the curing humidity influence on development in long-term strength of concrete using eco-cement and the relationship between strength and pore structure were examined. The results showed that wet cured eco-cement with a high water/cement ratio showed serious long-term strength reduction due to non-reduction of pore volume (pore size over 10 nm) in mortar caste with eco-cement. Also, the study results on improvement of long-term strength of eco-cement by partial replacement with ordinary portland cement and finely-ground fly ash showed that both of these alternatives improved long-term strength of concrete caste with eco-cement due to gradual refinement of their micro-structure.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.28 no.5
• /
• pp.563-570
• /
• 2015

The existing research on the damage detection method for building structures has considered the damages from the excessive loadings such as the earthquake. However, the structural performance of building structures could be reduced due to the deterioration based on the chloride, carbonation during the long-term time. Thus, to effectively manage the healthiness of structures, the deterioration influences on the structures should be checked. In this study, the corrosion of rebars by the chloride is considered as the deterioration factor. To consider the structural performance reduction of the corroded rebars, the yield strength, cross-sectional area, rupture strain of rebars and the compressive strength of cover concrete based on the corrosion level are estimated. These properties of rebars and cover concrete are used for the procedure to evaluate the structural performance reduction of structural member level and the building level. The moment-curvature analysis is performed to evaluate the structural performance reduction of structural member level. Also, the eigenvalue analysis and the pushover analysis are performed to investigate the natural period and mode shape and the strength and deformation performance of buildings, respectively.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2013.11a
• /
• pp.141-142
• /
• 2013

철골건축물은 화재에 취약한 구조로써 내화성능 확보를 위하여 내화피복이 필수적이다. 국내에서 가장 많이 사용되고 있는 철골내화피복재는 내화뿜칠재로 폭 넓게 사용되고 있으나, 기존 제도에서 인정 당시의 내화성능은 확인이 가능하나 시간경과에 따른 내구성저하와 이에 따른 내화성능 저하가 예상된다. 이에 본 연구에서는 실내조건에서 장시간 자연폭로실험을 실시함으로써 내화뿜칠피복재의 시간경과에 따른 내화성능 저하현상을 확인하였다.

• Magazine of the Korea Concrete Institute
• /
• v.11 no.3
• /
• pp.70-84
• /
• 1999

HPC를 사용한 장기수명 바닥판 콘크리트의 시공에 관한 4가지 접근방법을 제시하였다. Nebraska, New Hampshire, Texas 그리고 Virginia 등 4개주의 프로젝트에서 보면 아래와 같이 여러 가지 유사성을 알 수 있었다. $\cdot$ HPC의 사용은 장기 수명의 교량 바닥판을 건설하기 때문에 life cycle cost와 유지관리비의 감소가 예상된다. $\cdot$ 교량 바닥판에 대한 HPC의 중요성은 더 큰 강도보다는 내구성과 시공성을 일관성있게 양호하게 개선한다는 것이다. $\cdot$ 그 지역의 재료와 기존의 방법을 가능한 최대한 범위로 사용한다. $\cdot$ 많은 실험실 및 현장 시험 배합표가 개발되었고 배합되었다. 성능 특성은 혼합 재료의 형태, 상품 및 배합에 따라 다르게 나타났다. $\cdot$ 향상된 성질을 갖는 균일하고 일관성 있는 제품의 사용에 덧붙여 적절한 시공 기술은 장기 수명의 콘크리트 구조물을 위해서는 필수적이다. $\cdot$ 알카리-골재 반응을 갖고 있는 지역이나 높은 황산염을 갖고 있는 지역과 같이 특별한 문제점이 예상되는 지역에서는 화학적 내구성을 검토하기 위해 별도의 실험이 필요하다. $\cdot$ 현장에서 소요의 성능특성을 얻기 위해서는 시작부터 모든 분야 사이의 원활한 의견 교환과 협력이 요구된다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.1
• /
• pp.125-132
• /
• 2010

In the recent construction industry, an external strengthening method using fiber reinforced polymers has been widely used. Since reinforced concrete structures strengthened with fiber reinforced polymers are always under sustained loads, influence of creep and shrinkage on the structures is inevitable. Due to the creep and shrinkage, behaviors of the structures, such as deflection, deformation, recovery capability, strength and so on are also under the influence of creep and shrinkage. Thus, in order to estimate efficacy, creep recovery and residual strength of FRP strengthened RC beams, long-term flexural experiments and static flexural experiments were carried out. As the result of the experiments, FRP strengthened RC beams were very effective in terms of deflection control. Furthermore, the strengthened beams had higher immediate deformation recovery than immediate deformation. Through the static flexural experiments, it was shown that the CFRP strengthened beam had high residual strength. It seems that the sustained loads did not affect bond and residual strength of the beams.

• Journal of the Korea Institute of Building Construction
• /
• v.11 no.2
• /
• pp.189-199
• /
• 2011

Installation of a proper root barrier in a green roof system is very important in order to protect the concrete slab of roof and the root penetration in the waterproofing layer. To select the proper root barrier materials and methods, it is necessary to understand the environmental conditions affecting the waterproofing-root barrier system in green roof construction site. Therefore, we suggested as the environmental performance indexes four kinds of performance requirements; root penetration, chemical attack by chemical agent or fertilizer, load impact by soil depth and size of plant, and water pressure. The related four test methods were suggested for the inspection of these performance indexes. In this research, we could suggest for kinds of test methods as standard test methods to evaluate the environmental performance of waterproofing-root barrier for greening roof system.