• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.5
• /
• pp.77-86
• /
• 2013

This study investigates the fundamental properties of the water-binder (W/B) ratio and fine aggregate-binder (F/B) ratio in the alkali-activated slag cement (AASC) mortar. The W/B ratios are 0.35, 0.40, 0.45, and 0.50, respectively. And then the F/B ratios varied between 1.00 and 3.00 at a constant increment of 0.25. The alkali activator was an 2M and 4M NaOH. The measured mechanical properties were compared, flow, compressive strength, absorption, ultra sonic velocity, and dry shrinkage. The flow, compressive strength, absorption, ultra sonic velocity and dry shrinkage decreased with increases W/B ratio. The compressive strength decreases with increase F/B ratio at same W/B ratio. Also, at certain value of F/B ratio significant increase in strength is observed. And S2 (river sand 2) had lower physical properties than S1 (river sand 1) due to the fineness modulus. The results of experiments indicated that the mechanical properties of AASC depended on the W/B ratio and F/B ratio. The optimum range for W/B ratios and F/B ratios of AASC is suggested that the F/B ratios by 1.75~2.50 at each W/B ratios. Moreover, the W/(B+F) ratios between 0.13 and 0.14 had a beneficial effect on the design of AASC mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.152-160
• /
• 2021

Converter steel slag(BOF slag) is a vast amount of solid waste generated in the steelmaking process which has very low utilization rate in Korea. Due to the presence of free CaO which can derive bad volume stability in BOF slag, it usually land filled. For recycling BOF and identify its applicability as fine aggregate, this study investigates the fundamental characteristics of mortar with cement replaced ferronickel slag(FNS), which has the potential to be used as a binder. The results suggest that the mineral phases of BOF slag mainly include larnite(CaSiO₄), mayenite(Ca₁₂Al₁₄O₃₃) and wuestite(FeO) while olivine crystallines are shown in FNS. The results of flow and setting time reveals that the flowability and process of hardening increased when the amount of FNS and BOF slag incorporated was increased. The length change shows that the amount of change in the length of the mortar was almost constant regardless of mix proportion while compressive strength was reduced. Micro structure test results revealed that FNS or/and BOF slag mix took a long time to react in the cement matrix to form a complete hydration products. To achieve the efficient utilization of B OF slag as construction materials, proper replacement rate is necessary.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.623-629
• /
• 2002

Porous concrete enables water and air to pass through a firmly hardened material and allows required nutrients to reach roots of plants. The purpose of this study is to analyze void ratio, strength property and planting ability when using silica fume and fly ash, the change of aggregate gradation and ratio of paste to aggregate. The results of an experiment from the planting ability of the porous concrete to its influence on the compressive strength are reported in this paper. As a result of the experiment, the compressive strength is higher when the gradation of aggregate is smaller, and it also goes higher when the ratio of paste to aggregate gets larger. The planting ability of porous concrete is decided by the germination and the grass length of perennial ryegrass. The grass length of perennial ryegrass is longer when the gradation of aggregate is greater and the ratio of paste to aggregate gets smaller. Therefore the efficiency of planting goes through the perennial ryegrass is in compliance with the void ratio, aggregate gradation.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.477-480
• /
• 2008

With an increase of power consumption due to industrial development, the generation of coal ash has been growing tremendously and, accordingly, environmental concern over its disposal and insufficiency in disposal sites have been raised as other issues to be considered. In order to examine the usability of coal ash as an aggregate for concrete, such fundamental information as slump, air contents, mechanical properties and durability of concrete has been secured by way of setting 10, 20 or 30 wt. % of fine aggregate alternative rate of ash and identifying its basic properties at each pond-ash contents. The results of the study indicate that slump and air content heavily depend on the site of generation, and this might greatly influence on the content of fine particles of the ash. It is also shown that its freezing and thawing resistance tends to be relatively lower than that of Plain, which requires comprehensive examination over next few years on the absorptiveness and properties of mixed water of the ash collected from each disposal site.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.613-620
• /
• 2005

There are some problems in utilizing recycled concrete aggregate go structural use because of the difficulties concerning about quality control and durability. It seems to be possible to utilize recycled concrete aggregate for making concrete products because quality control of concrete products is easier than ready-mixed concrete, but there are little studies about the properties of the steam-cured recycled aggregate concrete. In this study, various tests were performed such as compressive strength, flexural strength, splitting tensile strength, bonding strength and chloride ion penetration test to evaluate the effect of substitution of recycled concrete aggregate. The results of strength test showed that the concrete strength decreased with the increase of the substitution ratio of recycled concrete aggregate, but it was in the reasonable range and almost equal to that of normal concrete below the substitution ratio of $50\%$. On the other hand, strength test of furnace slag cement concrete shows that the strength of recycled concrete with furnace slag cement under curing condition lower than that of recycled concrete with ordinary portland cement under same condition. From the result of this study, it can be concluded that recycled concrete aggregate is able to be utilized for structural use but substitution ratio should be decided with care in each case. The result of this study could be used as the basic data for the structural use of recycled concrete aggregate.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.2
• /
• pp.97-103
• /
• 2004

In this study, the experiment was carried out to investigate and analyze the influence of coarse aggregate's mix ratio and maximum size on the properties of concrete. The main experimental variables were water/cement ratio 45% and 65%, coarse aggregate/fine aggregate ratio 90%, 130% and 170%, maximum size of coarse aggregate 15mm, 25mm and 40mm. According to the test results, the principal conclusions are summarized as follows. 1) The slump and flow of fresh concrete were found to be higher in the order of G/S ratio 170%, 130%, 90%, also in the order of maximum size 40mm, 25mm, 15mm. 2) The compressive strength of hardened concrete were found to be higher in the order of G/S ratio 170%, 130%, 90%, also in the order of maximum size 15mm, 25mm, 40mm.

• International Journal of Highway Engineering
• /
• v.14 no.1
• /
• pp.45-53
• /
• 2012

This study was performed to analyze test results on drying shrinkage for concrete specimens mixed with various constituents in concrete mixes. Test variables are coarse aggregate types(Limestone, Sandstone, Granite, Andesite, Gneiss), fine aggregate types(natural sand, crushed sand) and cement amounts(normal strength, high strength). Epoxy coating of(U&V-H(A,B)) was applied onto the specimen surface to simulate diverse volume surface ratios(22.2, 40, 85.7, 150, 200, 300) with different specimen sizes. The experiments had been executed during 1,014 days at a condition of $20^{\circ}C$ and relative humidity of 60% in environmental chambers. Test results showed that shrinkage strain from the specimen equivalent to real pavement decreased to 39% compared to the standard specimen recommended by KS. Test results also showed that shrinkage strain of the specimen mixed with Limestone was 56~76% of that with Sandstone, thus Limestone mix seems to be suitable to the concrete pavement.

• Journal of the Korean Geotechnical Society
• /
• v.26 no.1
• /
• pp.75-83
• /
• 2010

Controlled low strength material (CLSM) is a flowable mixture and does not need to be compacted. It is produced by mixing portland cement, fly ash, fine aggregates, water and chemical admixtures. Sand is the most commonly used fine aggregates in the conventional CLSM, but it is getting more and more difficult to obtain sand in Korea. In this study, the characteristics of unconfined compressive strength, flow and applicability of a new CLSM that is produced by mixing of pond ash, fly ash, water, cement are examined. An unconfined compressive strength satisfies the standard unconfined compressive strength (0.5~1.0 MPa) were obtained when the mixture ratio of pond ash and fly ash is 30:70~70:30, cement ratio is 3.0~5.0%, and water content is 31~34%. The results of flow test indicate that the mixture ratio of pond ash and fly ash which satisfy the standard How value (0.2 m) is 30:70~70:30.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.77-84
• /
• 2012

It is known that some components of wood obstruct the hydration of cement when wood is mixed with cement. In order to examine the effect of pretreatment of wood chips in hot water, this study conducted the experiments for the setting and compressive strength of mortar by sieving pine wood chips with a 2.4mm sieve, dipping them in waters of different temperatures, and then using them as a part of the fine aggregate. For the experiments, water-cement ratio of the mortar was 0.50 and the amount of the fine aggregate substituted by wood chips was set at 0%, 2%, 4%, 6%, 8%, and 10% of the mass of the fine aggregate. As a result of the test, it was found out that when wood chips were used to substitute fine aggregate for the production of mortar, more usage of wood chips postponed setting more, and the treatment of wood chips with water improved the problem of the delay in setting time. Especially, the final setting time of the mortar which used 2~6% of wood chips treated in $100^{\circ}C$ water for 30 minutes was almost the same as the final setting time of the mortar which used no wood chips. Also, the compressive strength of the mortar which used the wood chips treated with water was compared to that of the mortar which used the wood chips not treated with water. The result showed that the strength improved for age of 7 days and 28 days, while there was little change in strength for age of 3 days.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.129-136
• /
• 2010

This study is to investigate experimentally the engineering characteristics of cement mortar according to the replacement method and contents of recycled aggregate powder (RP) by collecting the recycled aggregate powder with the maximum size of below 0.08 mm and 0.15 mm. then, the results of the study can be summarized as follows. The flow of flesh mortar represented a trend in decreasing while the recycled aggregate powder was substituted as it is compared with that of plain. In addition, in case of correlation between tests, it appeared that the correlation between flow and ring flow is big. In the case of the characteristics of hardened mortar, the strength showed more improvements as the RP was substituted to aggregate than the case, which is substituted to aggregate. In addition, it was verified that the results in which the RP was substituted to aggregate by 5% represented similar values to that of the plain according to the passage of age.