The antiferromagnet IrMn based four different GMR-SV multilayers on Corning glass were prepared by using ion beam deposition and DC magnetron sputtering system. The magnetoresistance (MR) properties for single-type and dual-type GMR-SV multilayer films were investigated through the measured major and minor MR curves. The exchange bias coupling field ($H_{ex}$) and coercivity ($H_c$) of pinned layer, the $H_c$ and interlayer exchange coupling field ($H_{int}$) of free layer for the dual-type structure GMR-SV multilayer films consisted of top IrMn layer were 410 Oe, 60 Oe, 1.6 Oe, and 7.0 Oe, respectively. The minor MR curve of two free layers was performed the squarelike feature having a MR ratio of 8.7 % as the sum of 3.7 % and 5.0 %. The value of average magnetic field sensitivity (MS) was maintained at 2.0 %/Oe. Also, the magnetoresistance properties of the single-type and dual-type structure GMR-SV multilayer films consisted of bottom IrMn layer were decreased more than those of top IrMn layer. Two antiparallel states of magnetization spin arrays of the pinned and free layers in the dual-type GMR-SV multilayer films occurred the maximum MR value by the effect of spin dependence scattering.

• Journal of the Korean Magnetics Society
• /
• v.18 no.5
• /
• pp.180-184
• /
• 2008

The relation of ferromagnet anisotropic magnetization and the antiferromagnet atomic spin configuration has been investigated for variously angles of unidirectional deposition magnetic field of FeMn layer in Corning glas/Ta(5 nm)/NiFe(7 nm)/FeMn(25 nm)/ Ta(5 nm) multilayer prepared by ion beam deposition. Three unidirectional deposition angles of FeMn layer are $0^{\circ},\;45^{\circ}$, and $90^{\circ}$, respectively. The exchange bias field ($H_{ex}$) obtained from the measuring easy axis MR loop was decreased to 40 Oe in deposition angle of $45^{\circ}$, and to 0 Oe in the angle of $90^{\circ}$. One other side hand, $H_{ex}$ obtained from the measuring hard axis MR loop was increased to 35 Oe in deposition angle of $45^{\circ}$, and to 79 Oe in the angle of $90^{\circ}$. Although the difference of uniderectional axis between ferromagnet NiFe and antiferromagnet FeMn was 90o, the strong antiferromagnetic dipole moment of FeMn caused to rotate the weak ferromagnetic dipole moment of NiFe in the interface. This result implies that one of origins for exchange coupling mechanism depends on the effect of magnetic field angle during deposition of antiferromgnet FeMn layer.

• Journal of the Korean Magnetics Society
• /
• v.27 no.4
• /
• pp.123-128
• /
• 2017

The magnetic isotropy property from the magnetoresistance (MR) curve and magnetization (MH) loop for the PtMn based spin valve (SV) multilayer films fabricated with different the bottom structure after post-annealing treatment was investigated. The exchange biased coupling field ($H_{ex}$), coercivity ($H_c$), and MR ratio of Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/Ta(4 nm) SV multilayer film without antiferromagnetic PtMn layer are 0 Oe, 25 Oe, and 3.3 %, respectively. MR curve for the Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/PtMn(6 nm)/Ta(4 nm) SV multilayer film showed $H_{ex}=2Oe$, $H_c=316Oe$, and MR (%) = 4.4 % with one butterfly MR curve having by the effect of antiferromagnetic PtMn layer. MR curve for the dualtype Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/PtMn(6 nm)/CoFe(3 nm)/Cu(2.5 nm)/CoFe(6 nm)/Ta(4 nm) SV multilayer film showed $H_c=37.5Oe$ and 386 Oe, MR = 3.5 % and 6.5 % with two butterfly MR curves and square-like hysteresis MH loops. The anisotropy property in CoFe spin valve-PtMn multilayer is neglected by the effects of a very small value of $H_{ex}$ and a very slightly shape magnetic anisotropy. This result is possible to explain the effect of magnetization configuration spin array of the bottom SV film and the top SV film of PtMn layer.