• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.109.1-109
• /
• 2000

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.05a
• /
• pp.67-67
• /
• 1996

• 한국전기화학회:학술대회논문집
• /
• 1999.04a
• /
• pp.61-61
• /
• 1999

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.62-69
• /
• 2023

For the nuclear power concrete plant structures in the UAE, it is necessary to consider the deterioration from high sulfate ions in the atmosphere and high chloride ions from the coast. In this study, two strength grade concrete mixture (40 MPa and 27 MPa) and two curing/diffusion temperatures (20 ℃ and 50 ℃) were considered for evaluating the temperature effects on diffusion and strength due to high average temperature above 38 ℃ a year in UAE. When the initial curing temperature was high, the compressive strength increased in high-temperature curing to 7 days, but the strength slightly increased in the 20 ℃ curing condition at 28 days. Regarding diffusion test, unlike the compressive test results, reduced chloride diffusion coefficients were evaluated both in 40 MPa and 27 MPa grade at 28 days. In the case of 91 days of curing, an increase in diffusivity due to high temperature and a decrease in diffusivity due to age effect occur simultaneously. Compared to the results of the curing and diffusion tests at 20 ℃ and 28 days, when the curing and diffusion tests were conducted at 50 ℃ in 91 days, the diffusion coefficients decreased to 76.2 % in 40 MPa grade and 85.4 % in 37 MPa grade with increasing curing period, respectively.

• Analytical Science and Technology
• /
• v.9 no.3
• /
• pp.292-301
• /
• 1996

The synthesis of poly(ether)tailed bipyridine complex as redox reaction probes has advanced attempts to interpret very slow diffusion and heterogeneous electron transfer. Diffusion coefficients as low as $1.5{\times}10^{-15}cm^2/s$ have been observed for the oxidation of neat $Co(bpy(ppgm)_2)_{3^-}(ClO_4)_2$ with $LiClO_4$ electrolyte. Heterogeneous electron transfer rate constants of materials were found to vary with diffusion coefficient. The decrease in k as the diffusion coefficient decreases was actually caused by the decreasing D. Diffusion coefficient for compound of strong ion pairing anion($ClO{_4}^-$) was much smaller than the diffusion coefficient for compound of weak ion pairing anion($CF_3COO^-$).

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.23-30
• /
• 1997

Semiconductive SrTiO3 ceramic bodies were prepared by conventional ceramic powder processes in-cluding sintering in a reducing atmosphere. Sodium or potassium ions were diffused from the surface of the sintered bodies into the inner region using thermal diffusion process at 800-120$0^{\circ}C$. The effects of such ther-mal treatments on the electrical and chemical characteristics of the grain boundaries were investigated. The presence of sodium or potassium ions at grain boundaries produces non-linear current-voltage behaviors, electrical boundary potential barriers of 0.1-0.2eV, and threshold voltages of 10-70V. The diffused ions form diffusion layers with thicknesses of 20-50nm near the grain boundaries, reducing the concentration of strontium and oxygen.

• Journal of the Korea Concrete Institute
• /
• v.29 no.3
• /
• pp.307-314
• /
• 2017

Concrete is a durable and cost-benefit construction material, however performance degradation occurs due to steel corrosion exposed to chloride attack. Penetration of chloride ion usually decreases due to hydrates formation and reduction of pores, and the reduced chloride behavior is considered through decreasing diffusion coefficient with time. In the work, HPC (High Performance Concrete) samples are prepared with 3 levels of W/B (water to binder) ratios of 0.37, 0.42, and 0.27 and 3 levels of replacement ratios of 0%, 30% and 50%. Several tests containing chloride diffusion coefficient, passed charge, and compressive strength are performed considering age effect of 28 days and 180 days. Chloride diffusion is more reduced in OPC concrete with lower W/B ratio and GGBFS concrete with 50% replacement ratio shows significant reduction of chloride diffusion in higher W/B ratio. At the age of 28 days, GGBFS concrete with 50% replacement ratio shows more rapid reduction of chloride diffusion than strength development, which reveals that abundant GGBFS replacement has effective resistance to chloride penetration even in the early-aged condition.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.297-309
• /
• 1995

본 연구에서는 이온선보조증착법에 의해 Si(100)기판위에 정합성장된 $Si_{0.5}$Ge_{0.5}$층의 핵성성과 성장을 고찰하였다. 성장층에 대한 AFM(Atomic Force Microscopy), RHEED(Reflection High Energy Electron diffraction) 등의 분석결과 Si(100)기판위에 이온선보조증착에 의하여 성장된 $Si_{0.5}$Ge_{0.5}$층은 Stranski-Kranstanov(SK)기구로 성장되며, 300eV, 10 $\mu$A/$cm^{2}$의 Ar이온선을 조사시키는 경우 결정성이 향상되었고, SK 성장 방식의 임계두께가 증가하였다. Ar 이온선 조사에 의해 MBE에 의한 정합성장온도(55$0^{\circ}C$-$600^{\circ}C$)보다 훨씬 낮은 20$0^{\circ}C$에서 정합성장이 가능하였으며, $x_{mn}$값은 10.5%로 MBE에 의한 정합성장시 보고된 $x_{mn}$ 값보다 낮았다. 이온충돌에 의해 발생한 3차원 island의 분해와 표면확산의 증가가 $Si_{0.5}$Ge_{0.5}$층의 성장에 현저한 영향을 미쳤으며, 이온충돌의 영향은 3차원 island의 생성보다 3차원 island의 분해가 더 안정한 낮은 증착온도에서만 관찰되었다.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 2002.05a
• /
• pp.115-119
• /
• 2002

고분자 전해질 연료전지는 전해질로 고체고분자막을 사용하는 연료전지로 고분자막은 수소 이온의 활발한 전달을 위해 일정량의 수분이 존재해야 한다. 따라서 연료전지의 운전 중에 고분자막은 항상 수화되어 있어야 하며 수분이 부족하게 되면 수소이온 전도도가 떨어지고, 막의 수축으로 인해 전극과 막 계면의 저항이 증가한다. 반대로 수분이 많이 존재하면 촉매 표면에 반응기체의 확산이 어려워져 전지 성능이 감소하게 된다.(중략)

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.221-226
• /
• 2001

Chloride diffusion effect of cement paste, freezing and thawing test, carbonation of concrete specimen were carried out using inorganic coating material. According to the chloride ions diffusion test, it is elucidated that permeability and diffusion coefficient of Cl￣ ions and apparent coefficient of coated cement paste is smaller than plain cement paste. A durability of coated concrete specimen was enhanced by the experiment result of concrete carbonation and freezing thawing test.