• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.661-664
• /
• 2000

It is known that high flowing concrete performs much higher fluidity, segregation resistibility and better placeability than normal concrete. However, it is hard to apply high fluidity concrete in field because of high manufacturing cost. Therefore, we intend to investigate the validity of segregation reducing type superplasticizer which is made by combining 0.61 of viscosity agent and 0.022 of AE agent for 1 of superplasticizer. Test are conducted on high flowing concrete using fly ash by applying segregation reducing type superplasticizer. According to experimental results, As contents of fly ash increase, fluidity, segregation resistibility and placeability shows favorable results. And also compressive strength at early age shows to be retarded, while it gains high strength at later age.

• 한국농공학회지
• /
• 제37권3_4호
• /
• pp.90-98
• /
• 1995

The recycled concrete, average compressive strength of which was 2l0kg/cm$^2$ or higher with slump range of 14~18cm, was prepared by replacing 25% and 50% by weight of coarse aggregate with recycled aggregate from waste concrete. Mix design method for crushed aggregates was used and all specimens were cured by normal moisture curing method. A plasticiser and a fly ash were added to the mix to improve performance of recycled concrete. Flexural strength, stress- strain relationship and fracture toughness were evaluated by comparing with those of normal concretes. Recycled concrete showed, in general, lower flexural strength and fracture toughness, and higher strain under the same stress level. Fly ash in the concrete had an effect of reducing the strength and fracture toughness on both normal and recycled concretes. Since fly ash is known to improve many properties of concrete, while reducing strength properties, decision for using fly ash should be made carefully depending on the intended usage of the recycled concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.501-504
• /
• 2005

This paper discusses the development of drying shrinkage reducing type superplasticizer(DSRS) by varying dosage of polycarboxylic based superplasticizer, liquid type expansive admixture and antifoaming agent. Adequate mixture proportion of each admixture is fixed at 0.3$\%$ of superplasticizer, 0.15$\%$ of liquidtype expansive admixture and 0.0005$\%$ of antifoaming agent to insure the improvement in drying shrinkage as well as comparable to the slump and air content of conventional concrete. With this mixture proportion, compressive strength of concrete using DSRS is comparable to that of conventional concrete. The use of DSRS studied by the authors has a favorable effect on reducing drying shrinkage due to the effect of water content and expansion by expansive admixture.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 봄 학술논문 발표대회
• /
• pp.95-96
• /
• 2022

Carbon nanotubes has a positive effect on the mechanical properties, functionality, and durability of cement-based materials. In this study, carbon nanotube solutions mixed with two different types of superplasticizers were dispersed by high-pressure homogenizer, and used for preparation of cement paste. The 7and 28day compressive strength were evaluated.

• 대한화장품학회지
• /
• 제35권2호
• /
• pp.103-110
• /
• 2009

Oil in water (O/W)에멀젼에서 에멀젼 안정화제로 사용되는 고급알코올과 고급지방산이 O/W에멀젼의 유동특성에 미치는 영향을 점도와 rheograms으로 분석하였다. 고급알코올과 고급지방산의 탄소 체인 길이가 증가할수록 O/W에멀젼의 점도가 상승하는 경향을 나타내었으며 고급알코올의 점도 상승 효과가 고급지방산보다 우수하였다. 또한 에멀젼 제조에 사용된 계면활성제의 친유부의 탄소 체인 길이에 유사한 스테아릴알코올과 세테아릴알코올의 점도 상승 효과가 가장 우수하였다. 고급알코올과 고급지방산이 첨가된 O/W에멀젼은 화장품 에멀젼이 보여주는 유동특성인 shear thinning을 나타내는 pseudo-plastic유체였다. 세틸알코올, 세테아릴알코올과 스테아릴알코올이 첨가된 O/W에멀젼은 thixotropy이었으며 농도가 증가할수록 thixotropic 현상이 증가하는 경향을 나타내었다. 또한 고급지방산보다는 고급알코올이 첨가된 O/W에멀젼이 더 thixotropic한 유동특성을 나타내었다. O/W에멀젼의 안정성과 관련된 점도상승과 사용감과 관련된 spreadability 향상을 위해 에멀젼 안정화제로 고급지방산보다는 고급알코올의 사용이 적합하리라 생각된다.

• 한국건축시공학회지
• /
• 제4권2호
• /
• pp.129-136
• /
• 2004

High fluidity concrete(HFC) requires high dosage of superplasticizer to acquire sufficient fluidity, and high contents of fine powder and viscosity enhancing admixtures to resist segregation. The use of high amount of admixtures to make HFC at batcher plant in ready mixed concrete company is one of the reasons to raise the manufacturing cost of HFC. For this reason, new type of manufacturing method of HFC are described using both flowing concrete method and segregation reducing superplasticizer(SRS) in order to gain economical profit and offer the convenience for quality control.. As dosage of melamine based superplasticizer increases, it shows that fluidity and bleeding increase, while air contents and ratio of segregation resistance decrease. It also shows that addition of viscosity agent into superplasticizer reduce bleeding and improve segregation resistance of concrete. Dosage of AE agent into superplasticizer containing viscosity agent recovers loss of air contents during flowing procedure. Combination of proper contents of superplasticizer, viscosity agent and AE agent make possible to develope segregation reducing type superplasticizer. Compressive strength of high fluidity concrete applying flowing method with it is higher than that of base concrete. No differences of compressive strength between compacting methods are found. For the estimation of construction cost of high fluidity concreting using segregation reducing type superplasicizer, under same strength levels, although material cost of high fluidity concrete is somewhat higher than that of plain concrete due to segregation reducing type superplasticizer cost, labor cost and equipment cost of high fluidity concrete is cheaper than that of plain concrete. However, based on the strength differences, high fluidity concrete shows lower material cost, labor cost and equipment cost than that of plain concrete due to decreasing in size of member and re-bar caused by high strength development of concrete.

• 한국건축시공학회지
• /
• 제10권5호
• /
• pp.137-143
• /
• 2010

본 연구는 거푸집에 부착하는 코팅재료에 따른 콘크리트 표면광택도 비교 분석으로서 시멘트모르터로 제작한 시험체의 광택도를 분석하고 유동화제를 혼합한 콘크리트와 혼합하지 않은 콘크리트의 노출콘크리트 표면 광택의 특성을 분석한 것이다. 시멘트모르터를 이용한 코팅재료별 광택도 분석에서 광택도가 가장 높게 나타난 코팅재료는 7번 재료로 액체포장재의 일부이며 2번째는 3번 재료로 투명필름을 이용한 재료이다. 코팅필름의 소재에 따라 광택도가 다르게 나타난 것으로 미루어 소재의 표면입자 상태와 화학적 구성요소의 따라 다른 것으로 판단된다. 콘크리트의 표면상태를 매끄럽게 하기 위해서는 불투수성이며 매우 밀실한 표면을 가진 코팅재료를 사용하는 것이 효과적이다.

• 한국지반환경공학회 논문집
• /
• 제11권12호
• /
• pp.37-45
• /
• 2010

초미립자시멘트는 입자 크기가 마이크로화되어 실트성 지반까지 주입가능하지만 점성이 높아 침투성이 저하되는 단점이 있다. 본 연구에서는 유동화제를 사용하여 점성을 낮춘 초미립자주입재의 그라우팅 효과를 평가하고자 암반에서 초미립자주입재와 보통시멘트주입재의 주입효과를 비교하였다. 시추조사, 현장수압시험, 공내재하시험, 공내전단시험, 단위주입량분석, p~q~t chart 유형 분석을 실시하였다. 시험 결과 초미립자주입재를 사용하는 경우가 보통시멘트 주입재를 사용하는 경우보다 투수성, 탄성계수 및 변형계수, 단위주입량 및 주입재 회수율 등 측면에서는 유리하지만 전단응력 측면에서는 차이가 거의 없는 것으로 나타났다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.77-77
• /
• 2018

Panel level packaging (PLP) 공정은 차세대 반도체 패키징 기술로써 wafer level packaging 대비 net die 면적이 넓어 생산 단가 절감에 유리하다. PLP 공정에 적용되는 구리 재배선 층 (RDL, redistribution layer)은 두께 불균일도에 의해 전기 저항의 유동이 민감하게 변화하기 때문에 RDL의 두께를 균일하게 형성하는 것은 신뢰성 측면에서 매우 중요하다. 구리 RDL은 주로 도금 공정을 통해 형성되며, 균일한 도금막 형성을 위해 도금조에 평탄제를 첨가하여 도금 속도를 균일하게 한다. 도금막에 대한 흡착은 주로 평탄제의 imine 작용기에 포함된 질소 원자가 관여하며, imine 작용기의 4차화에 의한 평탄제의 흡착 정도를 제어하여 평탄제 성능을 개선할 수 있다. 본 연구에서는 도금 평탄제에 포함된 imine 작용기의 질소 원자를 4차화하여 구리 RDL의 도금 두께 불균일도를 제어하고자 하였다. 유기첨가제와 4차화 반응을 위해 알킬화제로써 dimethyl sulfate의 비율을 조절하여 각각 0, 50, 100 %로 4차화 반응을 진행하였다. 평탄제의 4차화 여부를 확인하기 위해 gel permeation chromatography (GPC) 분석을 실시하였다. 도금은 20 ~ 200 um의 다양한 배선 폭을 갖는 구리 RDL 미세패턴에서 진행하였으며, 4차화 평탄제를 첨가하여 광학 현미경과 공초점 레이저 현미경을 통해 도금막 표면과 두께에 대한 분석을 실시하였다. GPC 분석을 통해 4차화 반응 후 알킬화제에 의해 나타나는 GPC peak이 감소한 것을 확인하였다. 광학 현미경 및 공초점 레이저 현미경 분석 결과, 4차화된 질소 원자가 존재하지 않는 평탄제의 경우, 도금 시 도금막의 두께가 불균일하였으며 단면 분석 시 dome 형태가 관찰되었다. 또한 100 % 4차화를 실시한 평탄제를 첨가하여 도금 한 경우 마찬가지로 두께가 불균일한 dish 형태의 도금막이 형성되었다. 반면, 50 % 4차화를 적용한 평탄제를 첨가한 경우, 도금막 단면의 형태는 평평한 모습을 보였으며 매우 양호한 균일도를 가지는 것으로 확인되었다. 이로 인해 imine 작용기를 포함한 평탄제의 4차화 반응을 통해 구리 RDL의 단면 형상 및 불균일도가 제어되는 것을 확인하였으며, 4차화된 imine 작용기의 비율을 조절하여 높은 균일도를 갖는 구리 RDL 도금이 가능한 것으로 판단되었다.

• 한국건설순환자원학회논문집
• /
• 제7권2호
• /
• pp.63-69
• /
• 2012

최근 시멘트 제조시 발생되는 다량의 이산화탄소로 인한 온난화 현상이 심각한 실정이며, 이러한 환경문제와 자원 고갈 문제를 동시에 해결하기 위해 고로슬래그와 같은 산업부산물을 콘크리트 배합에 사용하는 사례가 증가하고 있다. 일반적으로 고로슬래그는 대체율 20~50%의 범위에서 가장 많이 사용되고 있으나, 최근에는 고로슬래그를 100% 사용한 알칼리 활성 슬래그 콘크리트의 개발 및 실용화 연구가 활발히 진행되고 있다. 본 연구에서는 고강도 알칼리 활성 콘크리트의 구조 부재 적용을 위한 기초 자료를 확보하기 위해 알칼리 활성화 슬래그 모르타르의 초기 재령특성을 조사하였다. 물-결합재비(W/B)는 0.3, 0.4, 0.5의 3수준으로 하고 알칼리 활성화제인 NaOH를 슬래그 질량대비 4%, 8%, 12% 첨가한 AAS 모르타르의 압축강도, 플로우, 초결과 종결, 초음파속도를 측정하였다. 그 결과, 물-결합재비가 낮을수록 높은 압축강도가 발현되었으나 시간 경과에 따라 플로우가 저하하고 응결시간이 빨라지는 것으로 나타나 고강도 알칼리 활성 콘크리트를 제조하기 위해서는 적절한 유동화제의 사용이 필수적이라고 판단된다.