• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.44-48
• /
• 2001

The pipelines for natural gas transmission were buried in the ground of 1.5m depth. The pipelines were continuously subjected to vehicle load and internal pressure change by the quantity consumed of natural gas. In this paper, high cycle fatigue properties of natural gas transmission pipelines were studied. Fatigue specimens were obtained from the base and weld metal of circular pipe. Fatigue strength increased with increasing yield strength. Especially, the fatigue strength of base metal was higher than the yield strength of base metal and the fatigue strength of weld metal by manufactured process of TMCP.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.46-46
• /
• 2009

과거 고강도강 용접부에서 발생하는 저온균열은 주로 용접열영향부에서 발생하였는데, 이러한 문제점을 해결하기 위하여 강재 메이커들은 고강도강의 용접성을 향상시키고자 노력하였다. 이러한 노력의 결과로 TMCP, HSLA 강 등이 개발되었고 이들 강재는 예열온도를 저하시킬 수 있다는 장점 때문에 보편화되어 사용되었다. 이러한 강재는 모재 예열온도를 기준으로 적용하게 되면 용착금속에서 저온균열이 발생하는 경우가 있다. 따라서 이제는 용접재료의 용접성, 즉 용접재료의 저온균열 저항성을 평가 할 수 있는 기법이 요구된다. 본 연구의 목적은 용착금속의 저온균열 저항성을 평가하는 것인데, 저온균열 저항성은 용착금속의 미세조직에 따라 다르게 나타날 수 있다. 용착금속의 합금조성은 기본적으로 용착금속에 요구되는 최저 강도와 충격인성을 만족할 수 있도록 설계한다. 하지만 유사한 강도의 유사한 합금조성이더라도 일부 합금 성분에 의해 용착금속의 미세조직들은 상이하게 나타날 수 있는데, 미세조직 특성에 의하여 용착금속의 강도와 저온인성이 결정된다. 용착금속의 저온균열 저항성을 평가하기위하여 Gapped Bead-on-Groove(G-BOG) 시험에 사용된 모재는 50mm 두께의 mild steel을 사용하였으며, 모재의 희석을 방지하기위해 15mm 깊이로 V-groove 가공 후 buttering 용접 하였다. 용접된 시편은 다시 5mm 깊이로 V-groove로 2차 가공 후 Ar + 20% $Co_2$ gas를 사용하여 용접하였다. 용접재료는 ER-100S-G grade로 비슷한 합금조성을 갖는 2 종류를 사용하였다. A용접재료는 Ti 이 0.1% 함유 되었으며, B용접재료는 Ti 함유되지 않은 것을 사용하였다. 또한 예열 온도에 따라 저온균열 감수성을 평가하기위하여 모재의 예열온도를 각각 상온, $50^{\circ}C,\;75^{\circ}C,\;100^{\circ}C$로 하여 실험을 진행하였다. 용착금속의 미세조직을 확인해본 결과 Ti 함유된 A 용착금속 미세조직은 대부분 침상형페라이트로 나타났으며, Ti 함유되지 않은 B 용착금속 미세조직은 대부분 베이나이트로 나타났다. G-BOG 시험 결과 Ti 함유된 A 시편이 Ti 함유되지 않은 B 시편보다 저온균열 발생량이 적었다. 이는 용착금속의 미세조직분포 및 특성에 따라 저온균열감수성이 다르다는 것을 나타낸다.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.18-18
• /
• 2010

최근에 건조되는 선박이나 구조물들은 점차 대형화 되어가고, 이에 사용되는 판재들은 점차 고강도 극후판재화 되어가고 있다. 극후판재의 용접성을 향상시키기 위해서는 대입열 용접이 주로 적용되고 있는 실정인데, 30 mmt 이상의 후판을 1 pass로 용접하기 위해서는 EGW(Electro-gas welding) 기법을 사용한다. 대입열 용접은 용접입열(heat input)이 매우 높아 용착금속과 열영향부의 냉각속도가 매우 느려 용접열영향부에서 특히 fusion line 근처의 열영향부는 결정립 조대화 및 취약한 미세조직을 형성함으로서 저온인성을 크게 저하시키고, 연화 현상(softening effect)을 발생시켜 강도가 저하되는 문제점이 주로 발생하였다. 하지만 이런 문제점을 해결하기 위해 대입열용접에 사용된는 강재의 미세조직을 제어하여 AlN, TiN, $TiO_2$ 등의 석출물을 이용한 용접열영향부의 저온인성을 향상시켰다. 이러한 문제점이 발생하는 대입열용접에서 저온인성 시험은 주로 fuison line + 1, 2mm에서 수행한다. 하지만 대입열 용접시 용착금속의 냉각속도도 매우 느리기 때문에 용착금속의 위치에 따라 저온 인성 특성이 다르게 나타날 수 있다. 본 연구에서는 EGW 용착금속의 위치에 따른 저온인성 특성을 평가하기 위해 EH-36N, 40mmt 판재를 사용하여 1pole EG 용접 하였다. 용착금속의 저온인성 특성을 평가하기위해 충격 시편의 노치 위치가 fusion line - 2mm와 용접부 중앙을 기준으로 4곳을 선정하여 충격시험을 수행하였다. 또한 용착금속의 경도 분포를 알아보기 위해 micro vickers hardness tester(mitutoyo UR-501)을 사용해 hardness mapping 시험을 하였다. 용착금속의 저온인성은 미세조직과, 산소량에 따라 변화 할 수 있기 때문에 용착금속 위치를 달리하여 미세조직과 산소량도 각각 분석하였다. 용착금속의 저온인성을 향상시킬 수 있는 침상형페라이트와 비금속개재물의 상관관계에 관해 검토 하였다.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.30-30
• /
• 2010

고강도강의 용접성은 저온균열 저항성으로 대변되는데, TMCP강과 HSLA강 등이 개발되면서 고강도강의 저온균열저항성이 크게 향상되어 무예열 용접성이 확보되었다. 그러나 용접재료 측면에서는 그에 상응하는 재료의 개발이 지연되어 강재 개발로 인한 우수한 성능을 충분히 발휘하지 못하고 있으며 용접부의 건전성 문제가 심각하게 인식되고 있다. 이로 인해 고강도강에 적용시킬 수 있는 무예열 용접재료의 필요성이 대두되어 개발이 진행되고 있으며 상용화를 앞두고 있다. 이러한 용접재료의 개발단계에서 합금설계는 가장 중요한 항목으로 합금 조성에 따라 용착금속의 강도 및 인성에 상당한 변화를 가져오기 때문이다. 합금원소 중 Al은 강재의 탈산을 돕기 때문에 가능한 많은 양의 첨가를 요구하지만 적정량 이상을 초과하게 되면 오히려 용착금속의 저온인성 특성에 부정적인 영향을 미치게 된다. 본 연구에서는 고강도 GMA 용착금속의 Al함량을 단계적으로 변화시켜 용착금속 내 최적의 Al의 함량을 찾고자 하였다. 또한 높은 비용 및 많은 시간을 필요로 하는 와이어로드를 제작하지 않고도 Al함량을 조절 할 수 있는 방법을 고안하고자 하였다. 실험의 모재는 HSLA-100강을 사용하였으며 용접재료는 ER120S-G급의 GMA용접 재료를 사용하였다. 모재 성분과의 희석을 방지하기 위해 V-Groove 가공 후 6패스 Buttering 용접을 실시하였고, 다시 Buttering용접부에 V-Groove 가공을 하여 최종 용접을 실시하였다. 이 때 Al함량을 조절하기 위해 최종 용접 개선부 밑면에 홈을 판 후 Al fiber(직경 0.3mm)를 깔고 용접(입열량 20kJ/cm)하여 Al함유량을 총 3가지(0.003~0.04% Al)로 제어하였다. 용접 후 각각의 시편에 대해 미세조직, 충격시험, O/N분석, 성분분석 등의 시험을 수행하여 저온인성과의 상관관계를 알아보았다.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.6
• /
• pp.100-107
• /
• 2021

As a significant technology in the smartization era promoted by the Fourth Industrial Revolution, the secondary battery industry has recently attracted significant attention. The demand for lithium-ion batteries (LIBs), which exhibit excellent performance, is considerably increasing in different industrial fields. During the manufacturing process of LIBs, it is necessary to join the cathode and anode sheets with thicknesses of several tens of micrometers to lead taps of the cathode and anode with thicknesses of several hundreds of micrometers. Ultrasonic welding exhibits excellent bonding when bonded with very thin plates, such as negative and positive electrodes of LIBs, and dissimilar and highly conductive materials. In addition, ultrasonic welding has a small heat-affected zone. In LIBs, Cu is mainly used as the negative electrode sheet, whereas Cu or Ni is used as the negative electrode tab. In this study, one or two electrode sheets (t0.025 mm Cu) were welded to one lead tab (t0.1 mm Cu). The welding energy and pressure were used as welding parameters to determine the welding strength of the interface between two or three welded materials. Finally, the effects of these welding parameters on the welding strength were investigated.

• Tribology and Lubricants
• /
• v.9 no.2
• /
• pp.1-8
• /
• 1993

기어가 비교적 큰 하중과 고속의 운전상태에서 사용되는 경우 되풀이 응력에 의한 피로를 대상으로 하는 면압이나 굽힘강도 이외에 치면에서 발생되는 긁힘이나 융착(瀜着) 또는 용착(溶着)을 대상으로 한 스코어링(scoring) 강도를 고려하여야 한다. 스코어링은 주로 치의 이끝 부분에서 접촉방향으로 긁힘이 나타나는 손상으로 특징지워진다. 미국기어제조협회(AGMA)에서는 윤활막 파손에 의한 금속과 금속과의 접촉에 기인하여 발생되는 여러형태의 손상, 예를 들면 scuffing, seizing, galling 등을 광범위하게 스코어링으로 통칭하고 있다. 미국계통의 기술분야에서는 스코어링을 고온 스코어링(hot scoring)과 저온 스코어링(cold scoring)으로 구분하고 있다. 고온 스코어링은 고속 운전시 표면의 섬광온도(flash temperature)에 기인한 용착과 접촉방향으로 재료를 이탈시키는 형태를 나타내고, 저온 스코어링은 저속의 기어에서 윤활막 파단으로 표면에 줄질(filing)한 듯한 손상이 발생되는 것을 나타낸다. 유럽에서는 고온 스코어링 손상은 스커핑이라 하고 저온 스코어링손상만을 스코어링이라 부르고 있다.

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.101-103
• /
• 2001

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.3
• /
• pp.1070-1077
• /
• 2011

This paper is studied on the influence of machining conditions on weldability obtained by ultrasonic machining. The weldability estimation of dissimilar Ni-Cu sheets with the optimization of one-wavelength horn is confirmed by the use of ultrasonic machining. The optimal welding condition with tensile test by setting the ultrasonic machining parameters is suggested and the weldability is estimated by SEM observation and EDX-ray analysis. Experimental studies are worked with the measure of tensile strength and the analysis of SEM photograph after the ultrasonic machining of workpiece. Machining parameters of machining time, pressure, and amplitude are also applied to this paper.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.39-39
• /
• 2009

고강도강의 용접성은 저온균열 저항성으로 대변되는데, TMCP강과 HSLA강 등이 개발되면서 고강도강의 저온균열저항성이 크게 향상되어 무예열 용접성이 확보되었다. 그러나 용접재료 측면에서는 그에 상응하는 재료의 개발이 지연되어 용착금속부에서의 저온균열이 심각한 문제로 대두되고 있는 실정이다. 이러한 문제는 800 MPa급인 HY-100강재를 HSLA-100강으로 대체하는 과정에서 현실적인 문제로 제기 되었다. 즉 HSLA강은 용접 예열이 필요치 않았으나 기존의 용접재료, 즉 HY-100 강재에 사용하던 용접재료를 사용하게 되면 용착금속부에서 저온균열이 발생하여 용접예열을 생략할 수 없다는 판단에 이르게 되었던 것이다. 이에 본 연구의 목적은 HSLA-100강을 무예열 용접할 수 있는 GMA 용접와이어 개발하는 것이며, 구체적인 개발 목표는 무예열 용접조건에서 800 MPa 이상의 인장강도를 가지며 $-50^{\circ}C$에서의 충격인성이 50 J 이상인 GMA 용접와이어 개발하는 것이다. 이러한 용접재료를 합금설계함에 있어 무예열 용접성을 확보하기 위하여 용접재료의 탄소함량을 0.01% 수준으로 하고, 용착금속의 인장강도와 저온 충격치에 미치는 Mn과 Mo 함량의 영향을 검토하고 각각의 조성을 실험계획법으로 확정하였다. 그리고 확산성수소량에 따른 저온균열 발생 여부를 확인하여 무예열용접성을 확보하기 위해서는 확산성수소량이 3ml/100g 이하가 되어야 한다는 사실을 실험적으로 확인하였다. 그리고 이를 달성하기 위해서는 원자재인 와이어로드의 표면 품질이 중요하다는 사실도 확인할 수 있었다. 다음으로는 실험계획법에 의거하여 선정된 합금조성의 신뢰성을 검증하기 위하여 800kg 중량의 시제품을 생산하였으며, 생산된 시제품에 대해서는 실험계획법에서 사용한 Ar+5%CO2외에도 Ar+20%CO2를 적용하여 보호가스의 영향을 검토하였다. 검토 과정에서 Ar+20%CO2용으로 사용하기 위해서는 용접재료의 Si 및 Mn 함량이 상향조정되어야 함을 확인할 수 있었다. 그리고 탄소함량을 0.05% 수준으로 증가시키면 Mo 함량을 크게 저하시킬 수 있음도 확인할 수 있었다. 이러한 과정을 거쳐 개발된 GMA 용접재료는 무예열 용접조건에서 저온균열이 발생하지 않았으며, 인장강도는 830 MPa이었으며 $-50^{\circ}C$에서의 충격치는 90 J 이상이었다.

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.181-184
• /
• 1999