In this paper, a studied the SAW system being developed shipbuilding and plant industry with changing welding method to progress productivity. It studies a SAW system using one sensor instead previous one which is using two sensors. It suggests SAW system which has AC output with high current makes high speed welding and DC output with accurate arcing makes detailed control.

• 한국건설순환자원학회논문집
• /
• 제4권3호
• /
• pp.243-249
• /
• 2016

본 연구에서는 시멘트계 보수재 코팅이 철판의 부식 저항성에 미치는 영향을 평가하가 위해 보통 철판(Normal), 용접철판(Welding), 용접 후 보수재 철판(Welding & coating)의 세 가지 경우에 대하여 7일간 ICM(Impressed Current Method)를 통하여 부식을 촉진시켰다. 이후 Faraday 법칙을 통해 얻은 이론 부식률, 실험 부식률 그리고 부식 실험 후 측정한 휨 강도를 비교 평가하였다. Normal case와 Welding case에서는 약 70% 수준의 부식률이 측정되었으며, Welding & coating case에서는 약 17%정도의 부식률이 측정되었다. 이는 시멘트계 보수재료의 코팅이 염화물 이온의 침투를 효과적으로 차단하였으며 이로 인해 부식전류의 발생이 억제되었기 때문이다. 휨 강도 역시 부식률 평가와 같은 경향을 나타내었으며 Welding & coating case에서 Welding case 대비 약 3.4배 큰 강도가 평가되었다. 시멘트계 보수재 코팅이 용접부에 시행되면 용접부 철판의 부식 차단에 효과적일 것으로 판단된다.

• 한국해양공학회지
• /
• 제26권4호
• /
• pp.64-69
• /
• 2012

Laser welding was carried out on austenitic 304 (STS 304) and 22 APU stainless steels. In this case, the differences between the corrosion characteristics of the welding zones of the two stainless steels were investigated using electrochemical methods. The Vickers hardness values of the weld metal (WM) zones in both cases, the STS 304 and 22 APU stainless steels, showed relatively higher values than those of other welding zones. The corrosion current densities of the heat affected zone (HAZ) of the 22 APU and the base metal (BM) zone of the STS 304 exhibited the highest values compared to the other welding zones. It is generally accepted that when STS 304 stainless steel is welded using a general welding method, intergranular corrosion is often observed at the grain boundary because of its chromium depletion area. However, when laser welding was performed on both the STS 304 and 22 APU stainless steels, no intergranular corrosion was observed at any of the welding zones. Consequently, it is considered that the intergranular corrosion of stainless steel can be controlled with the application of laser welding.

• 전력전자학회논문지
• /
• 제5권5호
• /
• pp.419-426
• /
• 2000

일반적으로 아크용접기의 정류기로 다이오드정류기가 사용되고 있다. 이것의 문제점은 높은 고조파전류가 발생된다는 것이고 아울러 전원측의 오염문제를 야기한다. 본 논문에서는 PWM 컨버터를 사용함으로써 아크용접기의 입력특성이 개선됨을 보인다. 회로구조상 다이오드 정류기와 PWM컨버터로 대체되고 부하단에 안정적인 전력을 공급하기 위하여 직류단전압이 PI제어기에 의해 제어된다. PI 제어기가 직류단 전압제어를 위해 사용되는 경우 예측불가능한 용접부하의 특성상 높은 전압맥동성분이 발생된다. 따라서 본 논문에서는 전압제어기의 속응성을 개선하기 위하여 전향보상기가 도입되었고 이의 분석을 통하여 전압제어기의 외란으로 간주되는 부하전류의 변동이 전압의 맥동성분에 영향을 줄이는 이론적 예측을 시뮬레이션과 실험을 통해 검증한다.

• 동력기계공학회지
• /
• 제14권2호
• /
• pp.71-77
• /
• 2010

This paper was studied on microstructure, mechanical properties and corrosion characteristics of 316L stainless steel pipe welds was fabricated by orbital welding process. S-Ar specimen was fabricated by using Ar purge gas and S-$N_2$ specimen was fabricated by using $N_2$ purge gas. Ferrite was not detected in weld metal of S-$N_2$ specimen but the order of 0.13 Ferrite number(FN) was detected in weld metal of S-Ar specimen. Oxygen and Nitrogen concentration of S-$N_2$ specimen was higher than S-Ar specimen on HAZ and inner bead. The welds microstructural characteristics of S-Ar and S-$N_2$ specimens are similar. The microvickers hardness values of S-Ar and S-$N_2$ specimens welds were similar and average values of each regions were in the range of 174~194. The microstructures of S-Ar and S-$N_2$ weld metal were full austenite by primary austenite solidification. The Solidification structures of S-Ar and S-$N_2$ weld metal were formed directional dendrite toward bead center. The potentiodynamic polarization curve of STS 316L pipe welds exhibited typical active, passive, transpassive behaviour. Corrosion current density$(I_{corr.})$ and corrosion rate values of S-Ar specimen in 0.1M HCl solution were $0.95{\mu}A/cm^2$ and $0.31{\mu}A$/year respectively. The values of S-$N_2$ specimen were $1.4{\mu}A/cm^2$ and $0.45{\mu}m$/year.

• 한국기계가공학회지
• /
• 제10권6호
• /
• pp.128-133
• /
• 2011

In this study, the steel material for shipbuilding(LR-A class) was used, and FCAW was taken advantage of 3G attitude and they are welded by different welding ways. As a result of analyzing wave with welding monitoring system, the stable values are obtained which are the first floor(electronic current 164~182 A, voltage 24 V), the second floor(electronic current 174~190 A, voltage 22~25 V), the third floor(electronic current 158~188 A, voltage 22~25 V), and fourth floor(electronic current 172~184 A, voltage 22~25 V), at this time, the stable wave standard deviation and changing coefficient could be obtained. When the welding testing through nondestructive inspection was analyzed know defect of welding, there was no defect of welding in A, D, E, but some porosities in B, and slag conclusion near the surface in C, because the length of arc was not accurate, and the electronic current and voltage was not stable. After observing the change of heat affect zone through micro testing, each organization of floor formed as Grain Refinement, so welding part was fine, the distance of heat affect zone is getting wider up to change the values of the electronic current and voltage. As a result of degree of hardness testing, the hardness orders were the heat affect zone(HAZ), Welding Zone(WZ), and Base Metal(BM). When the distribution of degree of hardness is observed. B is the highest degree of hardness The reason why heat effect zone is higher than welding zone and base metal, welding zone is boiled over melting point($1539^{\circ}C$) and it starts to melt after the result of analysis through metal microscope, so we can know that delicate tissue is created at the welding zone. Therefore, in order to get the optimal conditions of the welding, the proper current of the welding and voltage is needed. Furthermore the precise work of welding is required.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2010년도 춘계학술발표대회 초록집
• /
• pp.75-75
• /
• 2010

3D 패키징 기술은 전기소자의 소형화, 고용량화, 저전력화, 높은 신뢰성등의 요구와 함께 그 중요성이 대두대고 있다. 이러한 3D 패키징의 연결방법은 와이어 본딩 또는 플립칩등의 기존의 방법에서 TSV(Through Silicon Via)를 이용하여 적층하는 방법이 주목받고 있다. TSV는 기존의 와이어 본딩과 비교하여 고집적도, 빠른 신호전달, 낮은 전력소비 등의 장점을 가지고 있어 많은 연구가 진행되고 있다. TSV의 세부 공정 중 비아필링(Via filling)기술은 I/O수 증가와 미세피치화에 따른 비아(Via) 직경의 감소 및 종횡비(Via Aspect Ratio)증가로 인해 기존 필링 공정으로는 한계가 있다. 기존의 비아 홀(Via hole)에 금속을 필링하기 위한 방법으로 전기도금법이 많이 사용되고 있으나, 전기도금법은 전기도금액 조성, 첨가제의 종류, 전류밀도, 전류모드 등에 따라 결과물에 큰 차이가 발생되어, 최적공정조건의 도출이 어렵다. 또한 20um이하의 비아직경과 높은 종횡비로 인하여 충진시 void형성등의 문제점이 발생하기도 한다. 본 연구에서는 용융솔더와 진공을 이용하여 비아를 필링시켰다. 이 방법은 관통된 비아가 형성된 웨이퍼 양단에 압력차를 주어, 작은 직경을 갖는 비아 홀의 표면장력을 극복하고, 용융상태의 솔더가 관통된 비아 홀 내부로 필링되는 방법이다. 관통 비아홀이 형성 된 웨이퍼 위에 솔더페이스트를 $250^{\circ}C$이상 온도를 가해 용융상태로 만든 후 웨이퍼 하부에 진공을 형성하여 필링하는 방법과 용융솔더를 노즐을 통하여 위쪽으로 유동시켜 그 위에 비아홀이 형성된 웨이퍼를 접촉하고 웨이퍼 상부에 진공을 형성하여 필링하는 방법으로 실험을 각각 실시하였다. 이 때, 웨이퍼 두께는 100um이하이며 홀 직경은 20, 30um, 웨이퍼 상부와 하부의 진공차는 약 0.02~0.08Mpa, 진공 유지시간은 1~3s로 실시하여 최적 조건을 고찰하였다. 각 조건에 따른 필링 후 단면을 전자현미경(FE-SEM)을 통해 관찰하였다. 실험 결과 0.04Mpa 이상에서 1s내의 시간에 모든 비아홀이 기공(Void)없이 완벽하게 필링되는 것을 관찰하였으며 이 결과는 기존의 방법에 비하여 공정시간을 감소시켜 생산성이 대폭 향상 될 수 있는 방법임을 확인하였다.

• 동력기계공학회지
• /
• 제13권3호
• /
• pp.33-39
• /
• 2009

The aim of this study is to analyze the welds characteristics of the 205 stainless steel pipe for application of street pole material. The welds corrosion behavior of STS 205 pipe in 0.1 N sulphuric acid solution and 5% NaCl solution at room temperature was studied using both salt spray test and potentiodynamic polarization experiment. The morphology and components of corrosion products on surface of STS 205 pipe welds were investigated using SEM/EDX. The tensile strength and yield strength values of STS 205 plate were 715 MPa and 369 MPa respectively. The microvickers hardness values of STS 205 pipe welds were slightly increased than that of STS 304 pipe welds. Corrosion current density($I_{corr.}$) and critical current density($I_{crit.}$) values of STS 205 pipe welds in 3.5% NaCl solution were $1.89{\times}10^{-6}$ $A/cm^2$ and $15.8{\times}10 ^{-6}$ $A/cm^2$. The corrosion resistance of SIS 205 pipe welds was similar to its STS 304 pipe welds. The STS 205 and 304 pipe welds passive films were chromium oxide. Especially, the STS 205 pipe welds showed good corrosion resistance in 0.1 N sulphuric acid. This is attributed to the forming of protective chromium oxide on the surface of STS 205 pipe welds.

• 융합신호처리학회논문지
• /
• 제22권4호
• /
• pp.185-192
• /
• 2021

용접 비드의 불량유무를 판단하기 위하여 다양한 방법들이 제안되어왔으며, 최근에는 센서 자료 검사와 영상 자료 검사가 꾸준히 발표되고 있다. 센서 자료 검사는 정확도가 높고, 2차원 기반의 영상 자료 검사는 용접된 비드의 위치를 파악할 수 있다는 장점이 있다. 하지만 센서 자료만으로 분석 할 경우 정확한 위치에 용접이 되었는지 파악하기가 어렵다. 반면 영상 자료 방법은 잡음과 측정오차가 발생하여 정확도가 높지 않다. 본 논문에서는 평균 전압, 평균 전류, 혼합가스인 센서 자료 검사와 영상 검사 방법을 융합함으로써 각 검사 방법들의 단점을 보완하고 장점을 높여서 정확도를 향상시키고 검사 속도를 높일 수 있는 방법과 이를 소프트웨어로 구현하였다. 그리고 그래픽 사용자 인터페이스(graphical user interface; GUI)를 이용하여 분석을 수행하고 검사에 사용된 자료와 검사 결과를 확인할 수 있도록 하여 사용자가 편리하고 직관적으로 분석을 수행하고 결과를 파악할 수 있도록 하고자 한다. 이 때 각 센서 자료의 특성을 이용하여 센서 검사가 수행되고, 모폴로지 축지적 활성화 윤곽선을 적용하여 영상 자료가 검사된다. 실험 결과를 통하여 98%의 정확도를 보였으며, 네 개의 용접 영상과 센서 자료 검사를 모두 수행할 경우 검사 시간은 약 1.9초로서 용접공정에서 실시간 검사기로 사용 가능한 소프트웨어의 성능을 보였다.

• 수산해양기술연구
• /
• 제37권2호
• /
• pp.147-152
• /
• 2001

본 연구에서는 수도수 중에서 Mg합금유전양극에 의한 연강재 온수보일러의 음극방식특성을 연구한 결과 다음과 같은 결론을 얻었다. 1) 온수보일러 관체의 개로전위에서나 전위가 높은 구간에서 모재의 부식전류밀도가 용접부위의 부식전류밀도보다 더 적게 배류된다. 2) 주조된 표면 그대로의 Mg합금 유전양극의 전류밀도는 주조된 표면을 연마한 상태의 Mg합금 유전양극의 전류밀도보다 더 많이 배류된다. 3) Mg합금 유전양극으로부터 거리가 멀어질수록 연강재 온수보일러의 음극방식전위는 높게 나타나고, 음극방식시간이 경과하면서 방식전위는 높게 나타나다가 6-10일 이후부터 방식전위는 안정되고 있다.