• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.4
• /
• pp.57-64
• /
• 2022

Chloride, which is one of the main deterioration factors in reinforced concrete structures, can degrade the performance of the structure due to chloride-induced corrosion of steel. Chloride content at steel depth or the rate of chloride penetration is necessary to determine deterioration of reinforced concrete or to calculate initiation time of steel corrosion caused by chloride attack. Chlorides in concrete are generally identified with typical two methods including chloride profiling using potentiometric titration method and discoloration method using AgNO₃ solution. The former is advantageous to estimate chloride penetration rate (diffusion coefficient in general) with measured chloride contents directly, but it is laborious. In the case of latter, while the result is obtained easily with the range of discoloration, the error may occur depending on workmanship when the depth of chloride ingress is measured. This study shows that chloride penetrated depth is evaluated with the results obtained from discoloration method through image analysis, thereby the error is minimized by workmanship. In addition, the effect of micro-crack in concrete is studied on chloride penetration. In conclusion, the depth of chloride penetration was quantified with image analysis and as it was confirmed that chlorides can rapidly penetrate through micro-cracks, caution is especially required for cracks in concrete structure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.401-404
• /
• 2008

Crack is a penetration path of harmful material such as chloride ion, and causes a serious deterioration in durability. So, the characteristics of chloride penetration are investigated for the cracked flexural concrete members using high-durable materials. For these, the flexural crack of beam specimen is introduced by transverse loading. And, Rapid Chloride Penetration Test (RCPT) and Long-term chloride penetration test are carried out to compare the chloride penetration depth. From test results when crack is happened, the chloride penetration resistance of the durable member was superior than that of the normal member. Blast furnace slag concrete member has a excellent chloride penetration resistance in long-term chloride penetration test.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.2
• /
• pp.79-87
• /
• 2011

In this study, the chloride penetration tests were performed for the initially cracked reinforced concrete members. The chloride diffusion characteristics and the critical crack width are compared, and the properties of self-healing are investigated. According to the test results, the chloride penetration resistance was greatly reduced as the surface crack width increased. When the mineral admixtures are added, the chloride penetration resistance of uncracked specimens were effectively increased, however, in case of the blast furnace slag and fly ash, the cracked specimens showed the more reduced resistance than OPC case, inversely. Also, the critical width was $29{\mu}m$, on average, for immersion test. The crack width with $4{\sim}15{\mu}m$ was restored by self-healing, The parts restored by self-healing were seemed to be visually restored, however, the chloride penetration resistance was not restored, perfectly.

• Journal of the Korea Institute of Building Construction
• /
• v.21 no.6
• /
• pp.583-591
• /
• 2021

In this study, the applicability and reproducibility of LIBS in the analysis of chloride penetration in the mortar section were investigated. Standard analysis (IC, potentiometric titration) and LIBS analysis were simultaneously performed on the accelerated and immersed mortar by chloride concentration. Through LIBS analysis after making an eluate at the same depth for each concentration, the signal intensity of chloride ions was confirmed according to the depth and concentration at the wavelength of 837.59 nm, and a correlation between the LIBS signal intensity and the chloride concentration was confirmed. Although it is an aqueous solution-based LIBS analysis, the applicability and reproducibility of LIBS were confirmed not only for the incorporation of chloride but also for the amount of permeated chloride.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.10 no.1
• /
• pp.15-22
• /
• 2010

Chloride-induced corrosion of steel bars in concrete exposed to marine environments has become one of the major causes of deterioration in many important facilities made of reinforced concrete. A study on chloride penetration in concrete has developed through long period exposure test along seawater, assesment of chloride ion diffusion by electrochemical techniques and so on. However, reasonable and exclusive chloride penetration model considering concrete material properties with mixture, degree of hydration, binding capacity has not been established. Therefore, in this paper, chloride penetration analysis of non-steady state is accomplished with material properties of concrete. Comparing with the results of analysis and chloride ponding test, we could accept the effect of binding capacity on chloride penetration in concrete and these results could be applied to a service life prediction of R.C. structures submerged in seawater. Therefore, there are 20~40% differences of service life to SHRP prediction.

• Journal of the Korea Concrete Institute
• /
• v.18 no.1 s.91
• /
• pp.65-71
• /
• 2006

Concrete has a void, which exists as one of defect in concrete. If the porosity of concrete increases, durability of concrete decreases. In this paper, to improve surface void of concrete, surface penetration sealers are applied to specimen. And, it were investigated that the resistances of chloride penetration and freezing and thawing for concrete with surface penetration sealer of two types. According to the results, surface penetration sealer has not show a harmful influence on strength and resistance of freezing and thawing. Surface penetration sealers were effective in the resistance of chloride penetration.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.6
• /
• pp.10-16
• /
• 2020

Deterioration of reinforced concrete structure caused by chloride ingress is the main issue and regrading this, many studies have been investigated with both experiments and computational modelling. In addition to chloride diffusion, chloride sorption should be considered as a chloride transport mechanism in concrete structure and cracks formed in concrete structures are the main variable to evaluate the performance of the structures. In this study, after making two types of cracks width (0.1 and 0.3 mm) in reinforced concretes, chloride absorption tests were performed. Weight change and colour change using 0.1 AgNO3 solution from the samples were performed to measure chloride ingress. Image processing was also carried out to quantify range of colour change in carck face. From the result, it were confirmed that the amount of chloride absorption increases with exposure time and increasing crack width, and chlorides reached at steel depth within 1 hour. It would be possible that chloride can move through interface bewteen steel and concrete, thereby further study regarding this is required.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.617-620
• /
• 2008

When the RC structure repaired by patching repair method, which method refilles with patching repair material after removes degraded area, It is necessary to determine chloride ion's permeation from outside of the RC structure repaired by patching repair material. Therefore, in this study, damage from sea environment of structure was predicted, moreover, diffusion coefficient of concrete also determined to figure out rebar's corrosion and concentration of chloride ion. RCPT(Rapid Chloride Permeability Test) was used for ditermination of patching repair material's diffusion coefficient, also connection between material thickness and effect of chloride ion's permeation was examined in analytically. Results which derived by experimental test was used in FEM(Finite Element Method) and equation suggested by JSCE to predict concentration of chloride ion in different distance from surface.

• Journal of the Korea Concrete Institute
• /
• v.29 no.3
• /
• pp.299-306
• /
• 2017

In this research, it was examined chloride ion penetration resistance of slag-replaced concrete and cementless slag concrete considering marine environmental exposure conditions of splash zone, tidal zone and immersion zone. In the design strength of grade 24 MPa, the specimens were tested to determine their compressive strength, scanning electron microscopy images and chloride migration coefficient. Further, chloride ion penetration depth and carbonation depth of specimens exposed to marine environment were measured. Experimental results confirm that chloride migration coefficient of specimens tended to decrease with increasing the replacement ratio of ground granulated blast-furnace slag in accelerated laboratory test. In addition, the specimens exposed to the tidal zone were found to be the greatest chloride ion penetration depth compared to splash zone and immersion zone. On the other hand, the chloride ion penetration depth of the specimens exposed to splash zone tended to increase with increasing the replacement ratio of ground granulated blast-furnace slag in contrast with the results for the tidal zone and immersion zone.

• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.100-109
• /
• 2002

Significant damage to concrete results from the intrusion of corrosive solutions, for example, dissolved chlorides corrode reinforcing steel and cause spatting. Effectively blocks the penetration of these solutions will eliminate or greatly reduce this damage and lead to increased durability. This study is to investigate the effects of pozzolanic admixtures, fly ash and silica fume, and a blast furnace slag on the chloride ion penetration of concretes. The main experimental variables wore the water-cementitious material ratios, the types and amount of admixtures, and the curing time. And it is tested for the porosity and pore size distributions of cement paste, chloride ion permeability based on electrical conductance, and 180-day ponding test for chloride intrusion. The results show that the resistance of concrete to the penetration of chloride ions increases as the w/c was decreased, and the increasing of curing time. Also, concrete with pozzolans exhibited higher resistance to chloride ion penetration than the plain concrete. The significant reduction in chloride ion permeability(charge passed) of concrete with pozzolans due to formation of a discontinuous macro-pore system which inhibits flow. It is shown that there is a relationship between chloride ion permeability and depth of chloride ion penetration of concrete, based on the pore structure (porosity and pore size distributions) of cement paste.