• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.213-214
• /
• 2010

An objective of this experimental research is to investigate the diffusion characteristics for chloride ion of concrete subjected to sulfate attack. For this purpose, concretes with three types of cement such as ordinary portland cement(OPC), binary blended cement(BBC), and ternary blended cement(TBC) containing mineral admixtures were made for water-binder ratios of 32% and 43%. The concrete specimens were immersed in sulfate solution for 365 days, and then the resistance against chloride ion penetration of them were estimated by using NT BUILD 492. It was observed from the test results that the resistance to chloride ion penetration of concrete subjected to sulfate attack was greatly decreased than that of standard curing concrete under the same age.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.553-556
• /
• 2008

We have studied about chloride penetration test by electrical conductance to 10 specimens made from same test batch. The coefficient of variation of total passed charge(Colombs) was about 24% in same specimens, and we draw a conclusion this method has a low reliability. Owing to complicated reaction ; heterogeneous material, mixing error and error of testing method, then we must consider the scope of the error which is introduced. Specially when you trying to get one test result against one spcimen, you can commit a big error, therefore we recommend that you use mean value against 3 specimens at least.

• Journal of the Korea Concrete Institute
• /
• v.15 no.4
• /
• pp.606-614
• /
• 2003

The major cause of deterioration for the concrete bridge decks exposed to de-icing chemicals would be chloride-induced reinforcement corrosion. Thus, in this paper, in order to predict time to corrosion for concrete bridge decks in the urban area, chloride concentration was measured with depth from the surface. A frequency analysis on surface chloride concentration and chloride diffusion coefficient of concrete bridge deck equals 0.192, 29.828 in the scale parameter and 7.899, 1.983 in the shape parameter of gamma distribution. The average value of surface chloride concentration equals 1.5 kg/㎥ and condenses from 1 to 2 kg/㎥ in the level of probability 70%. From the probabilistic results, it is confirmed that 26mm of minimum cover depth in order to target 20 years over is calculated. The countermeasure strategy to extend the service life of concrete bridge deck exposed to de-icing chemicals would be an effective method to increase cover depth and to place high performance concrete, which could lead to reduce the chloride diffusion coefficient and distribution range.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1077-1080
• /
• 2008

Material parameters such as surface chloride content, water permeability coefficient, chloride diffusivity and critical chloride content are a substantial key parameter for understanding the durability performance of concrete and its micro-structural densification. Over the past few decades, a considerable number of studies on the durability design for marine concrete structures have been carried out. However, the results are different to each other. In order to establish a consistent durability design system of concrete, it is a precondition to define material parameters, which affect deterioration of concrete due to chloride penetration. Such parameters are surface chloride content, chloride diffusivity, and critical chloride content. Usually these parameters are assumed as temporary constant values or obtained from the experimental results for short term. However, it is necessary to define these parameters reasonably, because these significantly influence the calculation of service life of concrete. In this paper, it is introduced to define material parameters of concrete for chloride diffusion, such as surface chloride content $[Cl]_s$, water permeability coefficient K, chloride diffusivity $D_{Cl}$, critical chloride content $[Cl]_{cr}$. These are expressed as time function considering hydration evolution of hardened cement paste. The definition of the material parameters is a prerequisite to simulate chloride penetration into concrete as time elapsed.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.2
• /
• pp.152-159
• /
• 2017

In marine environment, the durability of concrete and reinforcing steel is known to be deteriorate by the permeation of chloride ion into concrete. In this study the conductive photocatalyst was used to improve the seawater corrosion resistance of the concrete and steel. Mortar and concrete samples were prepared by mixing with various amounts of conductive active carbon and photocatalytic powder($TiO_2$). The compressive strength of concrete was decreased with the increase of the amount of conductive carbon powders. The samples containing conductive carbon and photocatalytic powders showed the superior seawater corrosion resistance compared with the ordinary sample, which was verified by XRF analysis showing the concentration of chloride ion($Cl^-$) of mortars and concretes. The inhibitive effect of photocatalyst against chloride attack was discussed with the diffusion coefficient of chloride ion into mortar and concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.1
• /
• pp.34-39
• /
• 2014

The purpose of this experimental research is to evaluate the resistance of reinforcement corrosion and chloride ion penetration of high volume fly ash (HVFA) concrete. For this purpose, concrete test specimens were made for various strength level and replacement ratio of fly ash, and then compressive strength and diffusion coefficient for chloride ion of them were measured for 28, 91 and 182 days, respectively. Also, corrosion monitoring by half cell potential method was carried out for the made lollypop concrete test specimens to detect the time of corrosion initiation for reinforcement in concrete. As a result, it was observed from the test results that compressive strength of HVFA concrete was decreased with increasing replacement ratio of fly ash but long-term resistance against reinforcement corrosion and chloride ion penetration of that was increased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.4
• /
• pp.1-9
• /
• 2020

This study conducted to understand effects of CA (CaAl₂O₄) and CA₂ (CaAl₄O₇) ratio on chloride binding ability and compressive strength and pore structure of cement mortar incorporating mixture of CA and CA₂. The Portland cement based specimens were mixed with the clinkers CA and CA₂, and these calcium aluminate clinker mixture were replaced 0, 5, 10% by weight of cement. After all the test specimens were cured for 28 days under water curing, they were immersed in the distilled water and NaCl solution. As a result, 28 days compressive strength of all specimens was similar, and As the replacement ratio of calcium aluminate clinker in the specimen increased, Friedel's salt production tended to increase. However, it was dependent on the amount of Al₂O₃ in the level of 5% replacement and CA ratio in the level of 10% replacement. Through equilibrium isotherm result, it was also indicated that as replacement ratio of calcium aluminate clinker in cement matrix increased, chloride binding capacity was improved, and chloride penetration was suppressed. In this study, the specimen replaced with 10% of the calcium aluminate clinker mixture (CA 39%, CA₂ 60%) was remarkable to control chloride attack. We figured out necessity to understand optimal CA/CA₂ ratio to effectively apply CA₂ as a sustainable building material by improving the chloride binding ability in Portland cement based system.

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2000.05a
• /
• pp.55-57
• /
• 2000

제주도 동부지역 지하수 염수화 원인을 규명하고자 주요이온성분분석과 환경동위원소 ${^3}H$함량분석을 하였다. 제주도 동부지역 지하수에 대한 각 주요이온과 염소이온과의 상관관계를 보면 지하수의 조성성분비율이 이 지역 연안해수의 것과 유사한 경향을 나타내고 있어 이들 지하수가 해수에 의해 염수화되고 있는 것으로 사료된다. 또한 ${^3}H$함량이 연안과의 거리가 먼 관정일수록 높게 나타났고, 가까운 관정은 해수침입의 영향을 받아 다른 관정보다 ${^3}H$함량이 낮고, 염소이온농도는 높게 나타난 것으로 보아 이 지역 지하수 염수화는 자연 염지하수나 암염등의 용해의 영향인 것으로 사료된다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.3
• /
• pp.142-154
• /
• 2011

This study predicted the probability of corrosion initiation of reinforced concrete tunnel boxes structures using the Monte Carlo Simulation. For the inner wall and outer wall in the tunnel boxes, exposed to airborne chloride ion and seawater directly respectively, statistical values of parameters like diffusion coefficient D, surface chloride content $C_s$, cover depth c, and the chloride threshold level $C_{lim}$ were examined from experiment or literature review. Their average values accounted for $3.77{\times}10^{-12}m^2/s$, 3.0% by weight of cement, 94.7mm and 45.5mm for outer wall and inner wall, respectively, and 0.69% by weight of cement for D, $C_s$, c, and $C_{lim}$, respectively. With these parametric values, the distribution of chloride contents at rebar with time and the probability of corrosion initiation of the tunnel boxes, inner wall and outer wall, was examined by considering time dependency of chloride transport. From the examination, the histogram of chloride contents at rebar is closer to a gamma distribution, and the mean value increases with time, while the coefficient of variance decreases with time. It was found that the probability of corrosion initiation and the time to corrosion were dependent on the time dependency of chloride transport. Time independent model predicted time to corrosion initiation of inner wall and outer wall as 8 and 12 years, respectively, while 178 and 283 years of time to corrosion was calculated by time dependent model for inner wall and outer wall, respectively. For time independent model, the probability of corrosion at 100 years of exposure for inner wall and outer wall was ranged 59.5 and 95.5%, respectively, while time dependent model indicated 2.9 and 0.2% of the probability corrosion, respectively. Finally, impact of $C_{lim}$, including values specified in current codes, on the probability of corrosion initiation and corrosion free life is discussed.

• Journal of the Korea Concrete Institute
• /
• v.29 no.4
• /
• pp.389-397
• /
• 2017

Friedel's salt is an important product of chemical adsorption between cement hydrate and chloride ions because it contains chlorine in its structure. When cement reacts with water in the presence of chloride ions, the $C_3A$ phase, and $C_4AF$ phase react with chloride to produce Friedel's salt. If chloride ions penetrate into concrete from external environments, many calcium aluminate hydrates, including AFm, can bind chloride ions. It is very important, therefore, to investigate the chloride binding isotherm of $C_3A$ phase, $C_4AF$ phase, and AFm phase to gain a better understanding of chloride binding in cementitious materials. Meanwhile, the adsorption isotherm can provide us with the fundamental information for the understanding of adsorption process. The experimental results of the isotherm can supply not only the quantitative knowledge of the cement-Friedel's salt system, but also the mechanism of adsorption and the properties of their interactions. The purpose of this study is to explore the time dependant behaviors of chloride ions adsorption with $C_3A$, $C_4AF$ and AFm phases. The chloride adsorption isotherm was depicted with Langmuir isotherm and the adsorption capacity was low in terms of the stoichiometric point of view. However, the chloride adsorption of AFm phase was depicted with Freundlich isotherm and the value was very low. Since the amount of the adsorption was governed by temperature, the affecting parameters of isotherm were expressed as a function of temperature.