• Resources Recycling
• /
• v.25 no.6
• /
• pp.58-64
• /
• 2016

Paper industry discharges many by-products and quantity of PSA (Paper sludge ash) has been increased. In this study, hydration water was added to PSA for use as cement admixture. PSA with added water was mixed with anhydrite and this mixture was used as cement substitute. Physical properties of PSA cement were changed by contents of PSA, but PSA cement containing PSA less than 10% had similar properties to those of OPC. Compressive strength of PSA cement mortar had a certain relationship with $Ca(OH)_2$ content. Compressive strength at 3 days increased, as $Ca(OH)_2$ content increased. However, the strength at 28 days increased, as $Ca(OH)_2$ content decreased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.4
• /
• pp.152-158
• /
• 2007

This is a fundamental research to utilize alkali activated cement(AAC) in concrete. The compressive strength of AAC concrete were measured for the various mixing ratios of activator/fly ash, and the mixing ratios of water glass, NaOH, and water among the activators. The mixing ratio of fine and coarse aggregates was maintained constantly. The relationships between the compressive strength and mixing ratios were analyzed to find the optimal mixing ratio of AAC concrete. As the results, the optimal mixing ratio of activator/fly ash in AAC concrete was 0.7, and that of water glass, NaOH, water among the activator was 4.0:1.0:2.5 for the maximum compressive strength.

• Journal of the Korean GEO-environmental Society
• /
• v.11 no.4
• /
• pp.25-31
• /
• 2010

The amount of dredging clay will be greatly increased by the eco-rive project and port development in Korea. Geotechnical engineers have thrown their efforts into the new ways for effective re-uses of the dredging clay such as the material for reclamation, and so on. However, very high initial water content and low strength causes unexpected difficulties in the aspect of trafficablility or time for consolidation. Therefore, the injection of cement stabilizer is used as one of ways to improve reclaimed ground. However, it also makes an argument by heavy metal from cement stabilizer. In this paper constant rate of strain consolidation test and normal consolidation test were performed to investigate behavior characteristics of the consolidation about soil-cement include lean mixed cement to reduce the environmental loads by the cement. The experimental results of consolidation characteristics about soil-cement include lean mixed cement influenced by mixing ratio. Especially it was observed that mixing ratio of 4%~6% leads not only the reduction of consolidation settlement, but time for consolidation.

• Resources Recycling
• /
• v.15 no.3 s.71
• /
• pp.74-80
• /
• 2006

In this article, we would like to investigate a durability characterization of cement mortar with inert filler, which is ground calcium carbonate(GCC). The kinds of techniques to evaluate cement mortar are chloride ion ingress, carbonation and sulfate attack. For the experimental result of the resistance of chloride ion ingress, carbonation and sulfate attack, as the addition of GCC makes decreasing the permeability by micro-filler effect, the specimens of $5{\sim}15%$ ratio of replacement are superior to the GCC0 mortar specimen with respect to durability of cement matrix in this scope.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.2
• /
• pp.943-948
• /
• 2013

In this study, the characteristics of polymer-modified mortar which include UM resin, eco-friendly resin, was studied for improving the durability of concrete. UM and cement mortar were mixed with a certain percentage. Eco-friendly UM resin polymer-modified mortar was evaluated by compressive strength, splitting tensile strength, flexural strength, water absorption and chemical resistance experiments. The characteristics of eco-friendly UM resin polymer-modified mortar were evaluated by experiments. Performance of compressive strength and splitting tensile strength were decreasing. On the other hand, performance of flexural strength, water absorption and chemical resistance were increasing. Eco-friendly UM resin polymer-modified mortar reinforced concrete durability performance is excellent.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.4C
• /
• pp.213-220
• /
• 2008

A study on cemented sand reinforced with short fibers was carried out to improve its unconfined compressive strength and brittle behavior. Nak-dong River sand was mixed with Portland cement and polyvinyl alcohol (PVA) fibers. A PVA fiber widely used for concrete reinforcement is randomly distributed into cemented sand. Nak-dong River sand, cement and fibers with optimum water content were compacted in 5 layers and then cured for 7 days. The effect of fiber reinforcement rather than cementation was emphasized by using a small amount of cement. Weakly cemented sand with a cement/sand ratio less than 8% was fiber-reinforced with different fiber ratios and tested for unconfined compression tests. The effect of fiber ratio and cement ratio on unconfined compressive strength was investigated. Fiber-reinforced cemented sand with 2% cement ratio showed up to six times strength to non-reinforced cemented sand. Because of ductile behavior of fiber-reinforced specimens, an axial strain at peak stress of specimens with 2% cement ratio increases up to 7% as a fiber ratio increases. The effect of 1% fiber addition into 2% cemented sand on friction angle and cohesion was analyzed separately. When the fiber reinforcement is related to friction angle increase, the 8% of applied stress transferred to 1% fibers within specimens.

• Resources Recycling
• /
• v.15 no.2 s.70
• /
• pp.24-31
• /
• 2006

The duality of recycled fine aggregate (RS) which was produced at the waste concrete crushing was investigated. The compressive strength, flexural strength and absorption of mortar utilized with RS were examined. It was evaluated on the application of RS as precast concrete aggregate. The density and absorption of RS were $2.31g/cm^3$ and 8.07% respectively, the quality of RS was satisfied with the criterion of KS F 2573 type 2. The maximum 28days compressive strength of mortar mixed with blended cement MRS1, MRS2 and MRS3 were developed with 15.8, 27.4 and 48.7MPa respectively, in condition to curing temperature $40^{\circ}C$ and water-cement ratio 37.5%. When blended cement MRS1 and MRS2 were used, the maximum flexural strength of mortar was developed at curing temperature $40^{\circ}C$ and water-cement ratio 35.0%. When blended cement MRS3 was used, the maximum flexural strength of mortar was developed at curing temperature $40^{\circ}C$ and water-cement ratio 37.5%. The absorption of mortar mixed with blended cement MRS1, MRS2 and MRS3 were indicated the range of $8.3{\sim}7.3%,\;6.5{\sim}8.5%$ and $3.5{\sim}6%$ respectively. Therefore, when the ratio of blended cement and RS is appropriately centre]led, it would be expected that MRS1, MRS2 and MRS3 will be able to apply the variable low strength, medium strength and high strength precaste concrete.

• Journal of the Korean Geotechnical Society
• /
• v.18 no.4
• /
• pp.75-83
• /
• 2002

This paper is to investigate the mechanical characteristics of light-weighted soils (LWS) consisting of expanded polystyrene(EPS), dredged clays and cement by using both uniaxial and triaxial compression tests. The mechanical characteristics of the compressive strength of LWS are analysed with varying initial water contents of dredged clays, EPS ratio, cement ratio, and curing stress. In the triaxial compression state, it is found that the compressive strength of LWS containing EPS is independent on the effective confined stress. As the EPS ratio decreases($A_E$<2%) and cement ratio increases($A_c$>2%), the behavior characteristics of triaxial compressive strength-strain relationship is similar to that of cemented soil which decreases rapidly in compressive strength after ultimate compressive strength. For the applications of LWS to ground improvements which require the compressive strength of up to 200kPa, the optimized EPS ratio and initial water content of dredged clay are estimated to be 3~4% and 165~175%, respectively. Also, the ultimate compressive strength under both triaxial test and uniaxial compression states are almost constant for a cement ratio of up to 2% and then critical cement ratio of this LWS shall be 2%.

• Journal of the Korean Geotechnical Society
• /
• v.18 no.1
• /
• pp.113-125
• /
• 2002

Ground improvement technique of cement stabilization via Deep Soil Mixing with dry cement is gaining popularity, particularly in Japan and other parts of Southeast Asia and in Scandinavia. Cement can be mixed with deep soft clay deposits, typical of marine environments, to improve the bearing capacity and/or reduce the compressibility of the material so that an otherwise poor site can be developed. However, the strength/deformation behaviour and resulting soil structure of the clay-cement mixture is presently not well understood with respect to both dry and wet mix methods. An extensive laboratory test was carried out to determine the mechanical characteristics of kaolin-cement, with some brief examination of the effects of curing environment. Laboratory tests include triaxial tests, unconfined compression tests, isotropic consolidation testis and oedometer tests. Cement contents up to 10 percent were considered and water curing was employed. Samples were cured for 7 to 112 days while submerged in distilled water. Conventional laboratory tests were also performed. In this paper, the laboratory testing program is described and various sample preparation techniques are discussed. Preliminary triaxial compression test results and trends at varying moisture contents, cement contents, confining pressures and curing times will be presented.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.475-482
• /
• 2020

In this study, three levels of solid capsules were prepared according to the composition ratio of core materials for the crystal growth type self-healing solid capsule, and a cement mortar was prepared with the crystal growth type self-healing solid capsule. The prepared solid capsule was mixed with 3% of the cement mass to evaluate the healing properties according to the crack induction age of the cement mortar. As a result of test, the crack healing properties according to the crack induction age of cement mortar mixed of solid capsules, it was confirmed that the self-healing performance of the cement mortar with the solid capsules was increased self-healing performance of 7 days than 28 days. This is because the unhydrated binder remains.