• Resources Recycling
• /
• v.21 no.5
• /
• pp.58-64
• /
• 2012

Ti button type ingots were prepared by recycling of Ti turning scraps using vacuum arc melting process for production of consumable arc electrode. The behavior of impurities such as Fe, W, O, and N in the Ti button ingots was investigated and the properties of the Ti button ingots were also evaluated. In the case of oxygen gaseous impurity, the oxygen layers on the surface of the Ti turning scraps were easily removed by the first vacuum arc melting. On the other hand, the solute oxygen in the Ti turning scraps was not removed by the next melting. In the case of Fe, major impurity in the Ti turning scraps, the removal degree in the final Ti button ingot refined by vacuum arc melting for 20 minutes was approximately 43 %, which is due to the vapor pressure difference between Ti and Fe. As a result, the Ti button ingots with ASTM grade 3 could be obtained by multiple vacuum arc melting from the Ti turning scraps. Therefore, it was confirmed that the preparation of consumable electrode for vacuum arc remelting could be possible by recycling of Ti turning scraps.

• Resources Recycling
• /
• v.18 no.5
• /
• pp.44-51
• /
• 2009

Fundamental study has been made on the recovery of copper from the electronic scrap by hydrometallurgical process. Nitric acid was used as a leaching agent to dissolve the metals such as Cu, Sn, Pb, Fe etc. from the crushed electronic scraps. TBP was employed to extract nitric acid from the strong nitric acid leaching solutions and to reclaim nitric acid. From the experimental results, Cu was effectively leached by 3.0-4.0 M nitric acid. And 95% of nitric acid in the leaching solution was extracted by 60% TBP, and 98% of nitric acid was stripped from the loaded organic phase by distilled water and it was possible to reuse as a leaching agent.

• The Journal of the Korea Contents Association
• /
• v.11 no.10
• /
• pp.242-256
• /
• 2011

The activity to share personal daily life through social media is becoming more common. In this case, photographs as well as text are used a lot; it has been as easy as winking to clip others' photographs just as it's very easy to take and post pictures. If the picture is the photographic work protected by the copyright law, however, the clipping should be paid close attention. If you use others' photographic works without authorization, you infringe their copyright; if you post them on your social media such as blog, you infringe the right of reproduction, interactive transmission and exhibition. Even though the clipping is permitted, if you'd like to use the photographic works for a profit-making purpose, you should get additional authorization. Others' photographic works are occasionally altered and used for the purpose of avoiding the argument in relation to the infringement of copyright; this act means that it's the infringement of the right of reproduction, the right to preserve the integrity and the right of the production of derivative works for degrees of alteration. We can download others' photographic works with a few mouse clicks thanks to the technology of capturing the screen; we have to recognize that all the acts technically possible are not always legal.

• Resources Recycling
• /
• v.15 no.6 s.74
• /
• pp.41-47
• /
• 2006

A study for recovering of copper and lead from electronic scraps has been carried out using a combination of bioleaching and solvent extraction. It was found that the citric acid generated by Aspergillus niger could be an imporant leaching agent acting in the solubilization of copper, iron, lead and tin from the electronic scrap. Copper could be selectively extracted by 10% LIX84 from the leaching solution and it recoved 99.9% of metallic copper by electrowinning process. Tin and iron were extracted from the remaining solution by 10% Alamine336 and stripped by NaCl solution. Finally, tin could be recovered as a metallic precipitates from the mixed solution of tin and iron by cementation with iron powder.

• Resources Recycling
• /
• v.23 no.3
• /
• pp.61-70
• /
• 2014

Tin has been widely used to solder, tin plated steel, bronze alloy, sputtering target for transparent electrode and chemical additives. It has been widely reported to the recycling technologies for tin scraps because of the scarcity and economic efficiency of the reserve. This study was analyzed by using open/registered patents KR, US, CN, JP and EP related to recycling technologies for processing scrap, sludges, waste fluid for plating process and spent alloy containing tin in between 1970 and 2013. Patents were collected using key-words searching and filtered by filtering criteria. The trends of the patents were analyzed by year, country, appliant and technology.

• Resources Recycling
• /
• v.3 no.1
• /
• pp.9-16
• /
• 1994

Fine cobalt metal powders was produced from domestic Stellite scrap by decomposing it with molten sodium hydroxide. Complete decomposition of the scrap could be obtained with the weigth ratio of sodium hydroxide to Stellite being about 2 at the temperature ranges of $750~800^{\circ}C$ for an hour. The cobalt-bearing compound was identified as $Co_2O_3{\dot}H_2O$ by X-ray analysis and D.T.-T.G.a.. The compound was then digested in HCI to form cobalt chloride, and after iron removal by adjusting the pH of the solution, cobaltous or cobaltic hydroxide was precipitated at the pH of about 13 or 4, respectively. The precipitates were reduced by hydrogen in the temperatures of $400~500^{\circ}C$ to fine cobalt powders of high purity with the size of 1.0 to $1.5\mu\textrm{m}$. The recovery of cobalt from Stellite scrap was about 75~86% by weight.

• Resources Recycling
• /
• v.21 no.2
• /
• pp.59-65
• /
• 2012

The refining effect of tantalum by electron beam melting(EBM) process for recycling tantalum scraps was investigated in the study. The purity of the tantalum metals refined by EBM was evaluated using glow discharge mass spectrometry (GDMS). From the result of GDMS, most impurities in the tantalum metals were removed by EBM down to a few mass ppm levels. The purity of the refined tantalum scraps was improved up to 5N (99.9991%) from 4 N (99.996%) of the initial tantalum scraps. The amount of metallic impurities in the tantalum was decreased from 30 ppm to 8 ppm. In addition, the gaseous impurities in the tantalum were decreased from 470 ppm to 50 ppm. Therefore a possibility of refining method for recycling tantalum scraps by EBM process was confirmed in this study.

• Resources Recycling
• /
• v.29 no.1
• /
• pp.70-80
• /
• 2020

This study investigates the effect of flux type and mixing ratio on efficiency in aluminum can scrap recycling using induction furnace. The removal of surface coating layer of aluminum can scrap was possible through heat treatment at about 500 ℃ for about 30 min. The temperature for the melting process was set to be slightly above the melting temperature of the aluminium can scrap. The molten metal treatment was performed with different types of flux and mixing ratio. As a result, The optimum efficiency of Al recovery ratio was revealed when the process was performed with at least 3 wt.% of the flux (Salt and MgCl₂ mixture of ratio 70:30) at 750 ℃. The mechanical property of the recovered Al alloy showed that the tensile strength is about 249 MPa and elongation is about 14 %. This result was found to be similar to the mechanical property of the virgin Al 5083 alloy.

• Resources Recycling
• /
• v.30 no.2
• /
• pp.46-52
• /
• 2021

Off-grade Ti generated from smelting and mechanical processing has a high oxygen content. In this work, off-grade Ti was deoxidized using Mg and a chloride mixture as the reductant and flux, respectively. The experiments were conducted in the α-Ti temperature range (1,023~1,123 K) and the effects of the reaction time, reaction temperature, quantitiy of Mg and chloride ratio on deoxidation were investigated. Notably, when YCl3 is used as the flux to react with MgO, it is possible to reduce the activity of MgO. Therefore Ti can be deoxidized using Mg. In this study, the O content was decreased from 0.5 wt% to 0.1004 wt% at 1073 K, for 6 hours, with Mg=3.6 g and $X_{YCl_3}=0.22$.

• Clean Technology
• /
• v.15 no.3
• /
• pp.180-185
• /
• 2009

The ethylene-propylene rubber (EPDM) scrap generated from automobile weatherstrip manufacturing process was used to make a thermoplastic elastomer through blending with polypropylene. The surface activated EPDM powder was obtained by the high temperature and shear pulverizer. The addition of surfactant resulted in more surface activated EPDM powder and the optimum loading amounts of surfactant was 1.5 phr. Maleic anhydride was grafted onto polypropylene by reactive blending to give functionalized polypropylene. The wetting property between EPDM scrap and polypropylene was improved by the addition of poly (ethylene-co-acrylic acid) as a compatibilizing agent. Poly(ethylene-co-acrylic acid) decreased the surface tension of polypropylene and thus would contribute to the wettability with EPDM powder.