• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.151-152
• /
• 2020

When concrete is exposed to fire, the thermal decomposition of hydrates of Portland cement paste results in critical damage to the concrete structure of a building. Recently, nanosilica arose as the effective nano-additive which can enhance the thermal resistance of the cementitious materials. However, the mechanism of the enhancement was not elucidated specifically. In this study, we investigated the properties of calcium silicate hydrates(C-S-H)of the nanosilica incorporated cement paste after heating to different heating temperatures (200℃, 500℃, and 800℃) by 29Si nuclear magnetic resonance. The results showed that the polymerization of C-S-H of nanosilica incorporated samples was larger than ordinary cement paste after heating to 200℃, and C-S-H formed during heating process to 500℃ due to the pozzolanic reaction during heating process.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.35-44
• /
• 2015

Two main parameters were examined such as CSA content and polymer-binder ratio to find effects on the strength, water absorption, chloride ion penetration depth, carbonation depth, length change and chemical resistance of polymer-modified mortar with CSA and EVA polymer powder (EVAPP). As results, compressive, flexural, tensile, adhesive strengths, and length change of the polymer-modified mortar with CSA and EVAPP increases with increasing CSA content and polymer-binder ratio, although the water absorption, chloride ion penetration depth, and carbonation depth decrease with increasing polymer-binder ratio and CSA content, and also the chemical resistance decreases. Such strength and durability development is attributed to the high tensile strength of EVA polymer and the improved bond between cement hydrates and aggregates because of the addition of EVAPP and CSA.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.2
• /
• pp.203-210
• /
• 2012

Recently, the interest and demand for large-scale buildings and skyscrapers have been on the rise, and the performance of concrete is an area of high priority. Securing 'mass concrete and high strength concrete' is very important as a key construction technology. For high strength concrete, the high heat of hydration takes place inside the concrete because of the vitality of hydration in cement due to the large amount of powder, and leads to problems such as an increase of thermal stress due to the temperature difference with the outside, which results in cracks and slump loss. For this reason, measures to solve these problems are needed. This study aims to reduce the hydration heat of high strength concrete to control the hydration heat of mass concrete and high strength concrete, by replacing the type of admixture, The purpose of this study is to control the hydration heat of high strength concrete and mass concrete. Our idea for this purpose is to apply not only the types and contents of admixture but also incorporation mixing water to ice-flake. As a result of the test, the use of blast furnace slag and fly ash as admixture, and the use of ice-flake as mixing water can improve the liquidity of concrete and reduce slump loss. Significantly dropping the maximum temperature will contribute greatly to reducing cracks due to hydration heat in mass concrete and high strength concrete, and improve quality.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.5
• /
• pp.149-155
• /
• 1997

고로슬래그 미분말을 사용한 콘크리트\ulcorner 수화속도가 느려 어린 재령시 동해의 영향을받기 쉽다. 본 연구에서는 고로슬래그 미분말을 사용한 콘크리트의 동결융해 저항성을 알아보기 위해 고로슬래그 미분말의 치환율과 물-결합재비를 변화시켜 제조한 콘크리트에 대해 동결융해시험을 실시하였다. 또한 동일한 치환율, 물-결합재비의 콘크리트에 AE제를 첨가시켜 동결융해 저항성의 개선효과를 알아보았다. 시험결과 고로슬래그 미분말의 치환율이 증가할수록 동결융해 저항성은 작게 나왔다. 또한 non-AE 콘크리트의 경우 물-결합재비가 51%, 45%일 때 내구성지수는 각각 2.4%, 40.0%이하로 매우 나쁘게 나타났으나, AE콘크리트의 경우 물 -결합재비가 45%와 51%인 콘크리트의 내구성지수는 각각 90.2% 80.9%이상으로 동결융해 저항성이 매우 우수하게 나타났다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.1
• /
• pp.57-67
• /
• 2007

The service life of concrete structure is to a great extent influenced by crack developed at early ages of concrete material. Especially, hydration heat is a main cause of thermal cracking at mass concrete structures. The thermal cracking of massive structure is analyzed of the thermal cracking index which was presented Concrete Standard Specifications. The thesis analyzed the thermal cracking index which considered various variable (cement type, height of casting, curing condition, concrete mixing temperature, the unit cement content) at internal restricted mass concrete. The analysis result is denoted increase and decrease rate of thermal cracking index whenever the variables change. The results is helped to understand thermal cracking every time structures is designed and constructed. And I think that it is useful economic and stable design of mass concrete structures.

• Tunnel and Underground Space
• /
• v.32 no.6
• /
• pp.491-501
• /
• 2022

Bentonite has been proposed as a buffer and backfill material for high-level radioactive waste repository. Under such repository environment conditions, bentonite is subjected to combined thermal, hydrological, mechanical, and chemical processes. This study evaluates the feasibility of applying X-ray CT technology on the characterization of bentonite under hydration conditions using a newly developed testing cell. The cylindrical cell is made of platic material, with a removable cap to place the sample, enabling to apply vertical pressure on the sample and to measure swelling pressure. The hydration test was carried out with a sample made of Gyeonju bentonite, with a dry density of 1.4 g/cm³, and a water content of 20%. The sample had a diameter of 27.5 mm and a height of 34 mm. During the test, water was injected at a constant pressure of 0.207 MPa, and lasted for 7 days. After one day of hydration, bentonite swelled and filled out the space inside the cell. Moreover, CT histograms showed how the hydration process induced an initial increase and later progressive decrease on the density of the sample. Detailed profiles of the mean CT value, CT standard deviation, and CT gradient provided more details on the hydration process of the sample and showed how the bottom and top regions exhibited a decrease on density while the middle region showed an increase, especially during the first two days of hydration. Later, the differences in CT values with respect to the initial state decreased, and were small at the end of testing. The formation and later reduction of cracks was also characterized through CT scanning.

• Polymer(Korea)
• /
• v.37 no.3
• /
• pp.362-372
• /
• 2013

During extruder processing to manufacture cellulose fiber and film using cellulose-NMMO pre-dope produced by a new method, it seems to occur the changes of molecular weight and ${\alpha}$-cellulose content of cellulose upon thermal and mechanical degradation. In an extruder making cellulose solutions from the pre-dope obtained by high-speed mixer, the changes of cellulose molecular weight and ${\alpha}$-cellulose content resulted with the variations of processing temperature, concentration of cellulose, and residence time. The molecular weight and ${\alpha}$-cellulose content of cellulose decreased with decreasing cellulose concentration and increasing processing temperature. At 15% concentration and short residence time region, the change of ${\alpha}$-cellulose content was so high due to high-shear with an increase in temperature. From these processing conditions, the variations of ${\alpha}$-cellulose content and molecular weight showed different behaviors, and these processing conditions for making cellulose solution were found to be important factors.

• Applied Biological Chemistry
• /
• v.51 no.2
• /
• pp.108-113
• /
• 2008

Azoxystrobin applied by aqueous WP suspension 50 mg/l was slightly absorbed into cucumber leaf in the absence of activator surfactant 24 h after spraying, but was increased to 25.7% by adding polyoxyethylene monohexadecyl ether (12 moles of ethylene oxide, CE-12) 500 mg/l. Only 4.1% of kresoxim-methyl WDG 100 mg/l in the absence of surfactant was absorbed into cucumber leaf 24 h after spraying, but was increased to 58.0% by adding polyoxyethylene monooctadecyl ether (14 moles of ethylene oxide, SE-14) 1,000 mg/l. The effect of CE-12 500 mg/l on foliar uptake of kresoxim-methyl at 50 mg/l was twice bigger than on azoxystrobin. Fungicidal activity of azoxystrobin WP against cucumber powdery mildew was marginally increased by adding surfactants to facilitate foliar uptake of azoxystrobin, so that the further increase of azoxystrobin uptake into cucumber plant by the addition of adjuvant was not a practical mean for enhancing the formulation efficacy in view of fungicidal activity. It was not possible for kresoxim-methyl to assess the adjuvant effect on the fungicidal activity in a greenhouse trial due to the vapor effect of active ingredient.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.112-112
• /
• 2016

인체접촉시 니켈도금의 알러지 반응을 억제하기 위한 대체 도금기술인 비 시안계 Cu-Sn 합금도금을 개발함에 있어서, 황산구리5수화물과 황산제일주석을 금속염으로 하여 황산 및 계면활성제, 유화제 등을 포함한 각종 유기첨가제를 포함하였고 특히 은백색조의 외관 색상과 안정적인 Cu-Sn 합금전착을 위해 2종의 착화제인 EDTP($C_{14}H_{32}N_2O_4$)와 TEA(Triethanolamine)를 첨가한 비 시안계 Cu-Sn 합금 도금액을 도출하였다. Cu-Sn 합금도금 피막 조성의 균일화를 도모하기 위해서는 합금 도금액중의 Cu와 Sn 금속이온 농도를 일정하게 유지하는 것이 필요하다. 그러나 합금 도금액중 2가 주석이온($Sn^{2+}$)은 수용액중에서 4가 주석이온($Sn^{4+}$)으로 산화됨으로써 도금액 색상이 백탁이 되고 Stannic Hydroxide($Sn(OH)_4$, $SnO_2{\cdot}2H_2O$)이 생성되어 대량의 침전물이 침강하는 문제점이 발생되는 등 시간 경과에 따른 도금액의 경시 변화가 발생되었다. 상기 침전물은 연속여과에 의해 제거 가능하나 합금 도금액중 $Sn^{2+}$ 농도가 지속적으로 감소하게 된다. 이는 합금 도금액중 금속이온 비율이 변동함으로써 합금도금 피막의 조성비를 일정하게 유지하는 것이 곤란해진다. 이에 $Sn^{4+}$ 침전물 생성을 방지하기 위한 산화방지제를 개발하고 또한 산화방지제의 첨가에 따른 도금 피막 외관에 미치는 영향을 평가하여 외관 개선을 위한 광택제를 개발하고자 한다. 본 연구의 결과를 토대로 니켈도금과 동등 이상의 기능 특성을 갖는 비시안계 Cu-Sn 합금도금액을 개발하여 실용화하는 것을 목적으로 하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.68.2-68.2
• /
• 2017

인체접촉시 니켈도금의 알러지 반응을 억제하기 위한 대체 도금기술인 비 시안계 Cu-Sn 합금도금을 개발함에 있어서, 황산구리5수화물과 황산제일주석을 금속염으로 하여 황산 및 계면활성제, 유화제 등을 포함한 각종 유기첨가제를 포함하였고 특히 은백색조의 외관 색상과 안정적인 Cu-Sn 합금전착을 위해 2종의 착화제인 EDTP (Ethylenediaminetetrapropanol, $C_{14}H_{32}N_2O_4$)와 TEA (Triethanolamine)를 첨가한 비 시안계 Cu-Sn 합금 도금액을 도출하였다. Cu-Sn 합금도금 피막 조성의 균일화를 도모하기 위해서는 합금 도금액중의 Cu와 Sn 금속이온 농도를 일정하게 유지하는 것이 필요하다. 그러나 합금 도금액 중 2가 주석이온($Sn^{2+}$)은 수용액 중에서 4가 주석이온($Sn^{4+}$)으로 산화됨으로써 도금액 색상이 백탁이 되고 Stannic Hydroxide($Sn(OH)_4$, $SnO_2{\cdot}2H_2O$)이 생성되어 대량의 침전물이 침강하는 문제점이 발생되는 등시간 경과에 따른 도금액의 경시 변화가 발생되었다. 상기 침전물은 연속여과에 의해 제거 가능하나 합금 도금액 중 $Sn^{2+}$ 농도가 지속적으로 감소하게 된다. 이는 합금 도금액 중 금속이온 비율이 변동함으로써 합금도금 피막의 조성비를 일정하게 유지하는 것이 곤란해진다. 이에 $Sn^{4+}$ 침전물 생성을 방지하기 위한 산화방지제를 개발하고 또한 산화방지제의 첨가에 따른 도금 피막 외관에 미치는 영향을 평가하여 외관 개선을 위한 광택제를 개발하고자 한다. 본 연구의 결과를 토대로 니켈도금과 동등 이상의 기능 특성을 갖는 비 시안계 Cu-Sn 합금도금액을 개발하여 실용화하는 것을 목적으로 하였다.