• The Journal of Information Technology
• /
• v.5 no.2
• /
• pp.11-16
• /
• 2002

In this study, acrylic water-soluble coatings were prepared by the white pigment($TiO_2$) and acrylic resin. The basic properties of acrylic water-soluble coatings were measured, and the maintenance of perfume was investigated by FT-IR spectrophotometer and sensory test.

• The Journal of Information Technology
• /
• v.7 no.1
• /
• pp.105-110
• /
• 2004

In this study, acrylic water-soluble coatings were prepared by the white pigment($TiO_2$) and acrylic resin. The basic properties of acrylic water-soluble coatings were measured, and the maintenance of perfume was investigated by FT-IR spectrophotometer and sensory test.

• Polymer Science and Technology
• /
• v.6 no.3
• /
• pp.226-241
• /
• 1995

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2009.11a
• /
• pp.125-126
• /
• 2009

본 연구는 수용성 폴리우레탄 코팅 제품의 문제점인 코팅층간의 끈적임 문제, 내구성 문제 등을 개선하기 위해 졸-겔법을 이용하여 구형의 실리카 나노무기입자를 제조하고, 또한 주형을 이용한 다른 모양의 나노구조체를 합성하여 수성폴리우레탄 수지에 일정 비율 혼합하여 필름을 제조하여 수성 폴리우레탄 필름 대비 물성 향상에 관한 연구이다.

• Fire Science and Engineering
• /
• v.23 no.5
• /
• pp.78-83
• /
• 2009

17 kinds of fire resistant paint which are currently used were painted on the MDF, to find flame resistance performance and smoking characteristics according to principal ingredient and characteristics of fire resistant paint. 45 degree combustion test and smoke density test were conducted to investigate the flame resistance performance and smoking characteristics. According to the 45 degree combustion test, acrylic resin type fire resistant paint showed the most excellent fire resistance performance. And the water soluble fire resistant paint showed better fire resistance performance compare to the solvent soluble paints. Also gloss paint showed better fire resistance performance than the flat paint. Based on the smoke density test, the smoke generation of fire resistant treated specimen of acrylic resin type was least. And the water soluble fire resistant paint generate little smoke than solvent soluble fire resistant paint.

• Journal of Life Science
• /
• v.16 no.5
• /
• pp.759-766
• /
• 2006

Acute promyelocytic leukemia (APL) is a myeloid leukemia caused by over-expression of fusion protein, PML/RAR$({\alpha})$, which was the result of chromosomal translocation and induces the blockage of differentiation of affected promyelocytes. Pharmacological dose of retinoic acid induces the activation of and subsequent degradation of PML/RAR$({\alpha})$ fusion protein, and then APL cells undergo through the normal differentiation pathway. Arsenic trioxide has proved effective in causing remission of acute promyelocytic leukemia by inducing apoptosis of this tumor cells, whereas the heterogeneity of cellular susceptibility to this cytotoxic agent limited its usage on more types of tumors in clinic. This work showed that arsenic trioxide could induce apoptosis of a panel of acute promyelocytic leukemic cell lines, all-trans-retinoic acid (ATRA) sensitive NB4 cells and ATRA resistant UF-1 cell. They were investigated with regard to the correlation between the inherent or intrinsic cellular level of GSH and the apoptotic susceptibility of the cells to arsenic trioxide. We manifested, in two cell types, the inherently existed difference in intracellular GSH level reactive to the arsenic trioxide, and a positive correlation between the GSH level and their apoptotic sensitivity to arsenic trioxide. And it showed that arsenic trioxide could differentiate promyelocytic cancer cells to the cells possessed of dendritic cell surface markers. Unravelling the cause of the different susceptibility between leukemic cells and proving that promyelocyte could be differentiated to dendritic cells by arsenic trioxide will help not only to understand the mechanism underlying the complete remission of acute promyelocytic leukemia induced by arsenic trioxide, but also to expand its clinical usage.

• Proceedings of the KAIS Fall Conference
• /
• 2009.12a
• /
• pp.84-87
• /
• 2009

본 연구는 건축용 바닥재로 널리 이용되는 PVC 상재의 표면을 열에 의한 손상으로부터 보호하기 위하여 기존에 사용하는 광경화형 우레탄-아크릴 수지에 내열성(anti-cigar burning)을 향상시킨 광경화형 수성도료 개발에 관한 것이다. PVC 바닥상재용으로 사용되는 내열기능성이 없는 우레탄-아크릴 수지에 인계화합물을 주원료로 합성한 내열재, 구아니딘을 주원료로 합성한 내열재, 일시적 방염제로 사용되는 제 2인산암모늄을 수지의 양 대비 함량(wt%)을 10, 20, 30%로 변화하여 첨가한 후 배합하여 수지의 내열성을 향상시킨 코팅액을 제조하였다. 제조한 코팅액은 코팅층의 두께조절이 가능한 Bar-coating을 사용하여 PVC 바닥상재에 코팅한 후, 내열성, 부착력, 내화학성, 코팅두께 등의 코팅층 표면물성을 평가하였다. 연구결과, 수지에 인계화합물을 주원료로 합성한 내열재 30%를 혼합하여 제조한 코팅액을 Bar-coater No.12로 코팅한 코팅표면이 열에 의한 손상이 가장 적고, 부착력 100%, 내화학성 양호로 가장 좋은 물성을 보였다. 전반적으로 내열재 함량이 높고 코팅 두께가 두꺼울수록 내열성이 우수한 것으로 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.4
• /
• pp.344-350
• /
• 2011

In this study, LVLs of radiata pine were fabricated with non-preservative treated veneers, CuAz treated veneers, and ACQ treated veneers, using aqueous vinyl urethane adhesive and phenol modified resorcinol resin adhesive. Then density gradient, bonding strength, bending properties and decay resistance of LVLs were evaluated. As results, the cone-shaped and higher density gradient pattern was found in layer close to glueline. After cyclic water boiled test, the LVL bonded with aqueous vinyl urethane resin adhesive was delaminated in all layers or partly delaminated including check, chasm in glueline layer. In the case of LVL bonded with phenol modified resorcinol resin adhesive, despite slight cupping due to great glueline stress and vertical check between glueline layers, it was observed that the bonding strength to delamination was higher, owing to most absence of delamination through overall glueline. On the other hand, in the decay test, mass loss by brown rot fungi was greater than white rot fungi in LVL bonded with aqueous vinyl urethane resin adhesive. However, in LVL bonded with phenol modified resorcinol resin adhesive, the mass loss by brown rot fungi was slight and non-preservative treated LVL was low. The mass loss of preservative-treated LVL was 0 (zero), showing the high decay resistance effect.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.1 s.129
• /
• pp.87-96
• /
• 2005

This study was carried out to evaluate the shear bond strength and adhesive bond durability of structural glued laminated timber (glulam) manufactured with mixed species lumber of Korean red pine, Korean pine and Japanese larch, using resorcinol adhesive and water-based polymeric-isocyanate adhesive (WPI). Each board used as a glulam lamina was graded by visual inspection. The visual lumber grade of the all species was very low due to the large size and number of knots and the steep slope of grain. In view of the results, appropriate pruning, sawing and drying processes might be needed to produce high grade lamina lumber with small knot size and drying defect free. Shear bond strength of every tested glulam specimen ranged between 7.9 and $9.9N/mm^2$, and much higher than the Korean Standard (KS) for glulam shear bond strength, $7.1N/mm^2$. There was not much shear bond strength difference between wood/resorcinol and wood/WPI. The resorcinol adhesive bond durability exceeded KS requirements. However, delamination on the end-grain surfaces of WPI glulam submerged in both room temperature and boiling water severely occurred, and its durability did not meet KS requirements. Further investigations may be required, and special care should be taken, to ensure long service life of WPI glulam used for exterior application. Results of this study are expected to be useful for improvement of mechanical properties and structural performance of mixed species glulam.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.2
• /
• pp.608-613
• /
• 2010

This study is on development of UV-cured water soluble coating composition which have more improved anti-cigar burning to prevent a surface of PVC tile from damage of heat. To make an anti-cigar burning coating solution, thermostable agent that synthesize main materials phosphorus compound, guanidine and ammonium phosphate dibasic used temporary flame retardants, changing their contents from 10 to 30wt% against quantities of resin and compounded. After coating PVC tiles using bar-coating method that can adjust a thickness, we estimated surface properties of coated layer such as anti-cigar burning, adhesive power, chemical resistance, thickness of coating, and so on. Results showed that a coating composition added 30 wt% of phosphorus compound and coated with No.12 bar-coater had the best optimized surface property in anti-cigar burning effect, adhesive power and chemical resistance. Also, we could find anti-cigar burning effect was improved as thermostable agents content and coating thickness increased.