• Restorative Dentistry and Endodontics
• /
• v.14 no.2
• /
• pp.38-48
• /
• 1989

The purpose of this study was to investigate the proper consistency of root canal sealer needed in obtaining an efficient canal obturation in injection-thermoplasticized low-temperature ($70^{\circ}C$) gutta-percha method. The sealer was made by incorporating zinc oxide powder into $0.5m{\ell}$ of eugenol and then the $0.5m{\ell}$ of mixture slurry was placed between two flat glass plates. The consistency was determined by measuring the degree of spread of the slurry at loading the 120gm of weight from the top plate. The sealer was prepared according to P/L ratio corresponding to the acquired consistency of 65.45mm, 46.80mm, 28.95mm and 22.60mm. The distal roots were obtained by cutting off from 125 extracted human lower molars and the root canals were prepared by using step-back method. The prepared canals were coated with the sealers on their walls and obturated by using the injection-thermoplasticized low-temperature ($70^{\circ}C$) gutta-percha method. All specimens were immersed in 2% methylene blue dye solution for 48 hours at $37^{\circ}C$. Calipers was used to measured the dye penetration into the root canals from apical constrictions. The results were as follows : The canals obturated without sealer showed significantly more leakage than the canals obturated with sealer. Within the consistency from 65.45mm to 22.60mm, the sealer of 65.45mm appeared significantly better than that of 28.95mm and 22.60mm in the canals obturated by injection-thermoplasticized gutta-percha method, and better than that of 46.80mm without statistical significance.

• Restorative Dentistry and Endodontics
• /
• v.31 no.5
• /
• pp.337-343
• /
• 2006

The purpose of this study was to estimate the relation between techniques used for microleakage from dye penetration and for marginal adaptation from SEM evaluation of the restoration. Using high speed #330 bur class V cavities ($4{\times}3{\times}1.5 mm$ around CEJ) were prepared on the buccal surface of 20 extracted human molars. Six dimples as reference points for SEM and dye penetration evaluation were made with 1/2 round bur. Cavity was bulk filled with microhybrid composite resin (Esthet X) and all-in-one adhesive (Xeno III). Teeth were stored in saline solution for one day, after then, they were finished and polished using Sof-Lex system. Fifty percent silver nitrate dye solution was used for the evaluation of microleakage and resin replica was used for marginal adaptation. All of these were done after 1000 times thermocycling between 5 and $55^{\circ}C$. Vertical sections were made through three dimples of restoration to obtain samples for the evaluation of dye penetration and inner marginal adaptation. Outer adaptational estimation was done with an intact restoration before sectioning. Dye penetration was determined in three degrees and percentage of outer and inner leaky margin was estimated from SEM image The data were analysed statistically: Spearman's rho test were used to check relationships between two methods. The result were as follows : 1. There were significant relationships between degree of dye penetration and inner and outer marginal adaptations each (p < 0.01). 2. However, there was no significant relationship between the results or inner and outer marginal adaptation. Within the results of this study, relationship between the percentage of marginal adaptation and microleakage shows significant relationship. However, inner and outer marginal adaptation did not show any significant relationship mutually.

• Korean Journal of Food Science and Technology
• /
• v.31 no.3
• /
• pp.720-726
• /
• 1999

High voltage pulsed electric fields (PEF) technology is a non-thermal technique which is applicable to extract useful components froms biological materials. This research suggested the possibility for extracting carotenoid pigments from Phaffia rhodozyma by PEF treatments. The yeast cell suspensions were treated with high voltage pulses in a recycled PEF treatment chamber which consists a pair of thin plates of stainless steel adhering to a small chamber with approximately $1{\sim}4\;mm$ gap. A 2.5 log reduction in survivability and more than 98% of electropermeabilization of the yeast cells could be achieved by PEF treatment for $300\;{\mu}s$ with an electric field of 30 kV/cm and pulse duration of $1\;{\mu}s$. When the yeast cell suspended in 0.01% NaCl solution were treated with PEF under various conditions, carotenoid pigments were not extracted. However, the PEF treatment of the yeast cell suspensions in 0.01% $CaCl_2$ solution, have positive effects on the extraction of carotenoid pigments ($27.3\;{\mu}g/g$ of dried yeast).

• Journal of Korean Society of Forest Science
• /
• v.81 no.4
• /
• pp.357-362
• /
• 1992

To understand water flow path in the cells of Robinia pseudoacacia and Pyrus ussuriensis and obtain color wood from them, this experiment was performed by penetrating 0.5% acidic fuchsin and 0.5% fast green solution into the living wood of them. A comparison was made of the wood structure and water flow path from Robinia pseudoacacia containing the ring-porous wood with tyloses, and Pyrus ussuriensis including solitary diffuse-porous wood with distinct fiber pits. The dye penetrated into vessel elements in the early wood of two growth rings from bark in Robinia pseudoacacia, but permeated all xylem in fonts ussuriensis. In Robinia pseudoacacia, the vessels of heart wood and intermediate wood were not stained because of tyloses.

• The Journal of the Korean dental association
• /
• v.12 no.8
• /
• pp.613-617
• /
• 1974

The authors have studied the marginal leakage of various dental cements; Fynal cement (Caulk), Zinc cement (S.S. White) Carbo cement (Shofu, Poly-carboxylate cement), EBA cement (Opotow alumina cement), Propac (G-C's zinc oxide euginol cement), and Super cement (Shofu oxyphosphate zinc cement), by means of penetration of 2% methylene blue solution between orden crown restorations and human teeth in 150 cases. The result revealed as follow 1. None of the cements tested were free from dye penetration. 2. There was a wide difference in dye penetration among the trade brands of dental cement when immersed in dye solution before setting of cements. 3. EBA cement and Carbo cement showed comparatively low grade of dye penetration at the restorative margins.

• Restorative Dentistry and Endodontics
• /
• v.4 no.1
• /
• pp.29-34
• /
• 1978

The purpose of this study was to measure penetration of dye stuff(5% Methylene blue, Hematoxylin, Crystal violet and Safranin-O) on silicate cement, Adaptic, Hi-pol and unfilled resin. Each filling material was mixed on the mixing pad and the mixed material was inserted with condensation force of 500gr, 1000gr and 2000gr and without condensation force into preformed glass tube (10mm in diameter and 10mm in height). The specimen was stored in the air for 24 hours, then specimen was immersed in various dye solution (5% methylene blue, hematoxin, crystal violet and safranin-O) for different period of time (l hour and 24 hours). These dye-treated specimen was cut horizontally at the middle portion and the dye penetration in cut surface was measured. Following results were obtained. 1. Pentration of various dye was excessive in silicate cement with and without Condensation force. 2. There has been no evidence of dye penetration in unfilled resin. 3. Dye penetration occurced with in 1 hour period and the extending time didn't affect the dye penetration.

• Restorative Dentistry and Endodontics
• /
• v.30 no.2
• /
• pp.112-120
• /
• 2005

This study was done to evaluate whether there were any differences in microleakage of class V composite restorations according to restoration site and cavity size. Total sixty-four restorations were made in molar teeth using Esthet-X. Small ($2\;{\times}\;2\;{\times}\;1.5\;mm$) and large ($4{\times}2{\times}1.5\;mm$) restorations were made at the buccal/lingual surface and the proximal surface each. After 1,000 times of thermocycling ($5^{\circ}\;-\;55^{\circ}C$), resin replica was made and the percentage of marginal gap to the whole periphery of the restoration was estimated from SEM evaluation. Thermocycled tooth was dye penetrated with $50\%$ silver nitrate solution. After imbedding in an auto-curing resin, it was serially ground with a thickness of 0.25 mm. Volumetric microleakage was estimated after reconstructing three dimensionally. Two-way ANOVA and independent T-test for dye volume, Mann-Whitney U test for the percentage of marginal gap, Spearman's rho test for the relationship between two techniques were used, The results were as follows : 1. The site and size of the restoration affected on the microleakage of restoration. Namely, much more leakage was seen in the proximal and the large restorations rather than the buccal/lingual and the small restorations. 2. Close relationship was found between two techniques (Correlation coefficient = 0.614/ P = 0.000). Within the limits of this study, it was noted that proximal and the large restorations leaked more than buccal/lingual and the small restorations. Therefore, it should be strictly recommended large exposure of margins should be avoided by reducing unnecessary tooth reduction.

• Restorative Dentistry and Endodontics
• /
• v.36 no.5
• /
• pp.385-396
• /
• 2011

Objectives: This study evaluated the effects of adhesion variables such as the priming concepts of canal wall and the curing modes of adhesives on the sealing ability of a resin-based root canal filling system. Materials and Methods: Apical microleakage of the Resilon-RealSeal systems filled with 3 different combinations of adhesion variables was compared with the conventional gutta-percha filling using a dye penetration method. Experimental groups were SEDC, Resilon (Resilon Research LLC) filling with self-etch RealSeal (SybronEndo) primer and dual-cure RealSeal sealer; NELC, Resilon filling with no etching, Scotchbond Multi-Purpose (3M ESPE) primer application and light-curing adhesive; and TELC, Resilon filling with Scotchbond Multi-Purpose primer and adhesive used under total etch / wet bonding and lightcure protocols. GPCS, gutta-percha filling with conventional AH26 plus sealer, was the control group. Results: The median longitudinal dye penetration length of TELC was significantly shorter than those of GPCS and SEDC (Kruskal-Wallis test, p < 0.05). In the cross-sectional microleakage scores, TELC showed significant differences from other groups at 2 to 5 mm from the apical foramen (Kruskal-Wallis test, p < 0.05). Conclusions: When a resin-based root canal filling material was used, compared to the self-etching primer and the dual-cure sealer, the total etch/wet-bonding with primer and light-curing of adhesive showed improved apical sealing and was highly recommended.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.2
• /
• pp.255-261
• /
• 2002

The purpose of this study was to compare the microleakage pattern of flowable composite resin to sealant, composite resin used in preventive resin restoration and glass ionomer cement used as liner. 120 extracted sound human molars were divided into 6 groups : group 1 and 2:sealant ; group 3 and 4:preventive resin restoration ; group 5 and 6:sandwich technique restoration. For the experimental groups(group 2, 4 and 6), flowable composite resin(Tetric flow) was used. For the control group, Concise was used as sealant material(group 1), Z-100 with Concise were used as preventive resin restoration(group 3), and Vitrebond was used as cavity liner(group 5). All the restorations were thermocycled and the degree of dye penetration was evaluated with stereomicroscope. The microleakage of each group was measured and statistically analyzed. The results of the present study were as follows : 1. In group 1 and 2, there was no statistically significant difference in microleakage between Concise and Tetric flow(p>0.05). 2. In groups of preventive resin restorations, there was no statistically significant difference in microleakage between Z-100 with Concise and Tetric flow(p>0.05). 3. The microleakage of Vitrebond and Tetric flow used as liner showed no statistically significant difference(p>0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.4
• /
• pp.604-610
• /
• 2005

This study was to evaluate the effects of several light curing units on the microleakage of composite resin restorations in primary teeth. The types of curing units were traditional low intensity halogen light(Optilux 360), plasma arc light(Filpo) low heat plasma arc light(Aurys) and high intensity LED(Freelight 2). After preparing cavities on sound primary teeth, cavities were filled with composite resin(Z100) using the same resin bond agent(Scotchbond Multi-Purpose) and were cured with each curing light system. After storing each specimen in sterile water for 24 hours, thermal circulation was done 1,000 times followed by pigmentation using 2% methylene blue solution. Each specimen was sliced and the degree of pigmentation was graded. When microleakage is graded, the average of Aurys was 0.95 which was the lowest and Freelight 2(1.05), Filpo(1.25), Optilux 360(1.30) followed. But values were not shown statistically significant difference (P>0.05). The results suggest that the newly developed curing units which has advantage in children by decreasing discomfort and procedure time can increase the microleakage of the composite resin.