이 연구는 CBN을 건전한 브레이징을 하기 위해서, CBN과 금속필러메탈 접합계면에서의 금속성분과 산화물, 탄화물의 거동을 분석하는데 있다. 진공 인덕션 브레이징으로 온도는 $950{\sim}1100^{\circ}C$에서 브레이징 유지시간은 $5{\sim}30$분로 실시하였다. 금속필러로는 Ni-7Cr-3Fe-3B-4Si(wt.%)와 Ag-25Cu-5Ti(wt.%)을 사용하여 브레이징된 CBN은 $950{\sim}1000$도, 유지시간 10분 사이에서 각각 건전한 계면과 표면을 얻을 수 있었으며, 계면에서 Ti-rich상과 화합물이 확인되었다. 이상의 결과로 부터 화합물의 생성과 건전한 접합공정은 브레이징 온도와 시간이 좌우하며, N과 B, Ti의 함유량이 CBN의 브레이징 접합 특성의 중요변수로 생각되어진다. CBN과 Ni계/Ag계 브레이징 필러의 계면에서의 미세조직 및 화학반응의 메커니즘은 SEM, EPMA, XRD를 이용하여 분석하였다.
Purpose: In this study, brazing characteristics of $ZrO_2$ and Ti-6Al-4V brazed joints with increasing temperature were investigated. Materials and methods: The sample size of the $ZrO_2$ was $3mm{\times}3mm{\times}3mm$ (thickness), and Ti-6Al-4V was $10mm(diameter){\times}5mm(thickness)$. The filler metal consisted of Ag-Cu-Sn-Ti was prepared in powder form. The brazing sample was heated in a vacuum furnace under $5{\times}10^{-6}$ torr atmosphere, while the brazing temperature was changed from 700 to $800^{\circ}C$ for 30 min. Results: The experimental results shows that brazed joint of $ZrO_2$ and Ti-6Al-4V occurred at $700-800^{\circ}C$. Brazed joint consisted of Ag-rich matrix and Cu-rich phase. A Cu-Ti intermetallic compounds and a Ti-Sn-Cu-Ag alloy were produced along the Ti-6Al-4V bonded interface. Thickness of the reacted layer along the Ti-6Al-4V bonded interface was increased with brazing temperature. Defect ratios of $ZrO_2$ and Ti-6Al-4V bonded interfaces decreased with brazing temperature. Conclusion: Thickness and defect ratio of brazed joints were decreased with increasing temperature. Zirconia was not wetting with filler metal, because the reaction between $ZrO_2$ and Ti did not occur enough.
브래이징은 모재보다 용점이 낮은 재료를 접합매체(납재)로 하여, 450.deg. C 이상의 온도에서 모재를 녹이지 않고 납재만 용융시켜, 모재의 틈새에 용융된 납재를 침투(모세관 유입) 시킴 으로써 접합하는 방법이다. 브레이징은 (1) 한 번에 여러 곳을 접합할 수 있어 대량생산이 용이 하고, (2) 이종금속의 접합이 용이하며, (3) 복잡한 면의 접합이 가능하고, (4) 박판 및 세선의 접합이 용이하며, (5) 기밀, 수밀에 강하고 접합 강도가 우수하다는 장점으로 인해 적용범위가 점차 확대되고 있다. 국내에서도 현재 수많은 업체에서 브레이징을 제품생산에 적용하고 있으나 브레이징 기술은 그리 높지 않은 상태이다. 그러나 최근 브레이징 분야에 대한 기술개발 욕구가 증대되고 있는 상황이어서, 브레이징에 대한 기술과 정보의 보급 필요성이 대두되고 있다. 이에 필자는 일본의 브레이징 자료를 중심으로 브레이징에 관한 기초 지식을 기술하고 덧붙여 연구 동향을 소개하고자 한다.
이 연구는 cBN과 활성 Ag계 금속필러메탈을 이용하여 접합계면에서의 금속성분과 화합물, 탄화물의 거동을 분석하는데 있다. 진공 브레이징은 $900{\sim}1000^{\circ}C$에서 $25^{\circ}C$ 간격으로, 유지 시간은 각각 5, 10, 15, 20분으로 실시하였다. Ag-Cu-Ti을 사용하여 브레이징된 cBN은 $950{\sim}1000$도, 유지시간 10분 사이에서 각각 건전한 계면과 표면을 얻을 수 있었으며, 계면에서 Ti-rich상과 화합물이 확인되었다. 이상의 결과로 부터 화합물의 생성과 건전한 접합공정은 브레이징 온도와 시간이 좌우하며, N과 B, Ti의 함유량이 cBN의 브레이징 접합 특성의 중요변수로 생각되어진다. cBN과 Ag계 브레이징 필러의 계면에서의 미세조직 및 화학반응의 메커니즘은 DTA, SEM, EPMA, XRD를 이용하여 분석하였다.
The microstructure change of brazed $Si_3N_4$/Stainless steel 316 joint with Cu buffer layer were examined to clarify the effects of brazing process conditions such as brazing time and temperature on the mechanical properties and reliability of brazed joints. For the brazed joint above 900${\circ}C$, the Cu buffer layer was completely dissolved into brazing alloy and the thickness of reaction product formed at $Si_3N_4$/brazing alloy joint interface was abruptly increased, which could increase the amounts of residual stress developed in the joint. The fracture strength of brazed $Si_3N_4$/Stainless steel 316 joint with Cu buffer layer at 950${\circ}C$ was much reduced comparing to those of joints brazed at the lower temperature. But, it was found that the effects of brazing time was not critical on the mechanical properties as well as the reliability of $Si_3N_4$/Stainless steel 316 joint with Cu buffer layer brazed at the temperature below 900${\circ}C$.
One of the most important considerations to braze Cu-Al dissimilar materials is control of brittle metallic compound which makes it difficult to obtain a sound brazed joint. Nowdays, several attempts were made to control the metallic compound. But effective method for controlling metallic compound was not established. In this point of view, commercially pure aluminum and copper were used as base metal and Al-Si-X and Zn-Al-X alloy systems were developed as filler metal. Brazing was carried out to find optimum conditions for Cu-Al dissimilar joint. The results obtained in this study were summarized as follows: 1) The joint brazed by Al-Si-X filler metal showed good brazeability and mechanical properties. The tensile strength of the joint brazed over solidus temperature was more than 90% of Al base metal. Especially, the joint brazed at liquidus temperature was fractured in the Al base metal. 2) Fluorides fluxes(a mixture of potassium fluoro-aluminates) were used to improve surface cleanliness of base metal and wettability of Al-Si-X filler metal. It was melted at the temperature about 1$0^{\circ}C$ lower than that of the filler metal, and made appropriate brazing environment. Therefore, it could be a proper selection as flux.
Proceedings of the Korean Society of Propulsion Engineers Conference
/
2000.04a
/
pp.36-36
/
2000
액체로켓엔진에 사용되는 2000psi이상의 고압 연소실(Combustion Chamber)의 냉각은 내피(Inner Shell)에 기계 가공된 냉각통로(Cooling Channel)로 냉각제를 흘려보내는 재생냉각방식이 널리 사용되며 기계 가공된 냉각 통로는 외피(Outer Shell)에 의해서 지지 밀봉된다. 일반적으로 내피 재료는 순수한 구리보다 강도가 우수하고 열전도도는 유사한 구리합금을 사용하고, 외피는 강도가 우수한 스테인레스 강을 사용하여 브레이징 접합된 구조를 형성한다. 브레이징 공정은 조립품을 약 $450^{\cire}C$ 이상의 액상선을 갖는 삽입금속(Filler Metal)을 사용하여 적당한 온도($450^{\cire}C$ ~ 모재의 고상선)에서 가열하여 접합시키는 방법으로, 용융 금속의 젖음 현상(Wetting Phenomena), 접합 틈새(Joint Clearance)로의 용융 삽입금속의 유입(Capillary Phenomena)과 접합 계면의 반응을 통해서 접합이 이루어진다. 이는 일반적인 접합 공정과 비교하여 모재의 변형이 적고, 이종 금속 간의 접합이 용이하며, 복잡한 부품을 정밀하게 접합할 수 있는 장점이 있으나, 접합될 제품의 표면 상태 및 분위기(Atmosphere), 접합될 부품간의 조립 틈새, 가열 싸이클(Heating Cycle) 등에 대한 공정 확립 및 관리가 매우 중요하다. 재생냉각 구조를 갖는 연소실은 우선 접합면의 형상이 매우 복잡하여 균일한 접합 틈새를 유지하면서 접합시키기가 매우 어려우며, 고온, 고압의 환경에서 작동하므로 일부 접합면이 접합되지 않을 경우 내피의 변형 및 파괴가 발생하고, 브레이징 시 용융된 삽입금속이 냉각통로 내로 유입될 경우 연소 시 이부근에서 재료의 용융이 발생될 수 있다. 따라서, 이러한 현상을 방지하기 위해서는 진공 분위기 하에서 적절한 접합 틈새를 유지할 수 있는 공정 및 장비의 개발이 필요하다.
The microstructure and bond strength were investigated on the SiC/SiC and SiC/mild steel joints brazed by Ag-5at%Ti alloy. Ag-5at%Ti-2at%Fe and -5at%Fe brazing alloys were also used to see the effects of Fe addition on the bond strength of SiC/SiC brazed joints. Brazing temperature and brazing gap were selected and examined as brazing variables. The microstructure of SiC/SiC brazed joints was affected by Fe addition to the Ag-5at%Ti alloy, but the bond strength was not. Increasing brazing temperature also changed the microstructure of $Ti_5Si_3$ reaction layer and brazing alloy matrix of the SiC/SiC and SiC/mild steel joints, but not the bond strength. Brazing gap had a great effects on the bond strength. Decreasing brazing gap from 0.2 mm to 0.1 mm in SiC/SiC brazing increased the bond strength from 187 MPa to 263 MPa and, in SiC/mild steel brazing, from 189 MPa to 212 MPa. It was concluded that the most important parameter on the bond strength in SiC/SiC and SiC/mild steel brazing was the relative ratio between brazing gap and specimen size.
An advantage offered by brazing over fusion welding is that strong joints may be produced at relatively low heat input. To minimize the thermal effects and maintain the desired dimension of assemblies. the CO$_{2}$ laser beam can be applied to the brazed joint of pin and plate as a micro heat source. This paper presents a analysis model of the laser brazing process considering the laser beam mode and heat flow in brazed parts by using the finite element method. The simulation results were compared with the experimental results obtained from the infrared temperature sensing system. Based on these results, the proper process parameters were investigated to get a good joining quality. The influence of the beam mode change was examined with respect to the temperature distribution and joint quality.
소형 PEMFC(Proton Exchange Membrane Fuel Cell)는 전기를 만들기 위해서 고순도의 수소를 필요로 한다. 각각의 마이크로 성형된 금속박판(스테인레스 스틸, 알루미늄)을 진공 브레이징법으로 접합하여 수소공급용 소형 개질기를 제작하였다. 마이크로 채널의 내부는 졸-겔법(스테인레스 스틸)과 양극산화법(알루미늄)으로 촉매를 지지하기 위한 다공성 $Al_2O_3$ 층을 형성시켰다. 스테인레스 스틸 박판은 에칭과 브레이징에 유리하였으나, 표면산화층 코팅을 균일하게 하여 안정적인 촉매반응을 유도하기 위한 균일한 표면 산화층 형성이 힘들었다. 반면 알루미늄 박판은 표면 산화층 형성이 상대적으로 용이했으며, 촉매를 상하지 않는 낮은 온도에서의 적층이 가능했다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.