• Journal of dental hygiene science
• /
• v.10 no.5
• /
• pp.373-378
• /
• 2010

To test the effects of representative fluoride vanishes-1.23% APF gel and 5% NaF Fluoride Varnish-on the surface structure of pit and fissure sealant, this study classified samples of pit and fissure sealant into five groups: Group I deposited in distilled water for ten minutes, Group II treated with APF gel for one minute, Group III treated with APF gel for four minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes. An abrasion test was carried out to measure changes in weight, along with observation of the surface structure by using an optical microscope, consequently drawing the following conclusions. 1. The results of the abrasion test using pit and fissure sealant, Concise, showed that Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05); the results of the abrasion test using Eco-S showed Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05). 2. The results of observation using an optical microscope showed that application of APF gel made the filler remarkable due to loss of substrate and that Group III treated with APF gel for four minutes had the toughest surface, followed by Group II treated with APF gel for one minute, Group I deposited in distilled water for ten minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes.

• Applied Chemistry for Engineering
• /
• v.32 no.6
• /
• pp.653-658
• /
• 2021

Polyvinylidene fluoride (PVDF) is a promising coating material because of its outstanding processability. The PVDF coating, however, has limitations in anti-corrosion application due to its weak hydrophobicity compared to that of other fluoropolymers. In this study, plasma fluorination was performed using carbon tetrafluoride (CF₄) gas to improve anti-corrosion properties of PVDF. The fluorine content and hydrophobicity of PVDF were investigated in different CF₄ flow rates, followed by the determination of anti-corrosion properties. The fluorine content on the surface of the PVDF film increased by up to 46.70%, but the surface free energy was independent of CF₄ flow rate. Meanwhile, the surface roughness of the PDVF film tended to increase by up to 150% and then decrease with increasing CF₄ flow rate. It is considered that the plasma fluorination affects the surface free energy due to the introduction of fluorine functional groups and surface etching. In addition, the degree of corrosion of the PVDF-coated Fe plate was significantly reduced from 49.2% to 19.0% compared to that of the uncoated Fe plate. In particular, the degree of corrosion of the fluorinated PVDF-coated Fe plate was 13.6%, which was 28.4% lower than that of the PVDF-coated Fe plate, showing improved anti-corrosion protection.

• Journal of the Korean Chemical Society
• /
• v.47 no.2
• /
• pp.147-154
• /
• 2003

In this study, the fluorinated carbon blacks(CB) were used to reduce the negative temperature coefficient (NTC) phenomenon of the CB-filled high density polyethylene(HDPE) compounds in the fluorination pressure of 0.1-0.4 MPa. The changes in surface properties of the CB were investigated by using FT-IR, XPS and contact angle measurements. From the FT-IR results, the fluorinated CB showed the C-F absorption peak at 1400-1000 cm$^{-1}$ and the peak intensity was increased with increasing the fluorination pressure. Also, the analysis of XPS spectra of the fluorinated CB indicated that fluorine content was increased with increasing the fluorination pressure. Meanwhile, the surface free energy of the fluorinated CB was decreased with increasing the fluorination pressure. Consequently, the increase of fluorine contents on CB made a disappearance of NTC behaviors of CB/HDPE compounds, which was probably due to the reduction of CB reaggregation after melting point of the HDPE, resulting from decreasing the surface free energy of CB particles.

• Journal of dental hygiene science
• /
• v.10 no.2
• /
• pp.95-100
• /
• 2010

The purposes of this study were to examine the effect of different fluoridated bleaching solution on the changes in physical and chemical characteristics of tooth. Forty-eight bovine incisors were divided into four groups to receive bleaching treatments, over a 14days period, as follows: no treatment; 10% carbamide peroxide (CP) bleaching; 10% CP containing 0.05% fluoride; and 10% CP containing 0.1% fluoride. All the specimens were highly polished and discolored with commercial COCK.Color and enamel changes were determined with colorimeter, microhardness tester, scanning electron microscope, atomic force microscopy. All the collected data were analyzed with one-way ANOVA. After the bleaching, bleached groups showed the color change(E*). Microhardness of 10% CP group decreased after tooth bleaching. But microhardness of containing fluoride bleached groups increased after tooth bleaching. Enamel surface of 10% CP bleached group showed any apparent morphology and roughness changes compared to the enamel which was stored in distilled water only. These results demonstrated that Fluoridated 10% Carbamide Peroxide have appreciable bleaching effect on bovine teeth and were not adversely affects enamel. Supporting influence of fluoride-containing bleaching solution on remineralization could be observed and further research must be carried out in various active environments to confirm these results clinically.

• Applied Chemistry for Engineering
• /
• v.26 no.1
• /
• pp.92-98
• /
• 2015

In this study, phenol-based activated carbons (ACs) were fluorinated at various fluorine partial pressures (0.01~0.03 MPa) and the $Cr^{6+}$ ion adsorption of fluorinated ACs was investigated. According to BET and XPS results, the specific surface area and total pore volume of fluorinated ACs increased by 24.7 and 55.8%, respectively, and fluorine functional groups were introduced to AC surface. The most optimized condition of $Cr^{6+}$ ion adsorption was confirmed at the fluorine partial pressure of 0.02 MPa. And also the removal efficiency of $Cr^{6+}$ ion was up to 98% at 300 mg/L of the initial concentration, and these results showed an approximately three-fold increase compared to that of using untreated ACs. Furthermore, the $Cr^{6+}$ ion adsorption of fluorinated ACs was completed in less than 30 min in contrast with untreated ACs, which was expected to be an increase of the affinity between $Cr^{6+}$ ions and ACs surfaces by fluorination.

• Applied Chemistry for Engineering
• /
• v.29 no.6
• /
• pp.677-681
• /
• 2018

In this study, the carbon block was prepared using the fluorinated coke and binder pitch by molding compression to increase its density. After fluorination, it is confirmed that the fluorine element on the coke surface was introduced up to 24.14 at% using XPS analysis. The wettability between the fluorinated coke and binder pitch was evaluated according to the reaction temperature. From the result of contact-angle tests, it can be found that the wettability was improved up to 64.7% as more fluorine atoms were introduced on the surface of cokes. Also, the density of the carbon block with the highest amount of fluorine increased with 6.8% compared to that of using the carbon block prepared by the untreated cokes.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.11a
• /
• pp.31-31
• /
• 2011

섬유제품은 대부분은 흡수성 또는 흡유성을 가지고 있어 물이나 기름이 등을 쉽게 흡수하는 성질이 있다. 이러한 성질 때문에 물이나 기름 등의 접촉에 의한 얼룩과 오염이 잘 되는 단점을 가지고 있다. 이러한 문제점을 해소하기 위하여 원단에 대한 발수, 발유, 방오가공 등이 연구되어 왔으며 섬유의 고유한 화학적, 기계적 물성을 유지하면서 표면과 이면이 다른 특성을 가지도록 유도하여 기능성을 부여하는 편면가공을 주목을 받게 되었다. 본 연구에서는 불소계로 발수처리 된 PET직물에 저온 Plasma와 Sputter을 이용하여 직물의 한쪽 면에는 친수성과 다른 면에는 발수성이 동시에 나타나는 편발수에 관한 실험을 했다. 불소계로 발수처리 된 시료와 저온 Plasma처리된 시료와 Sputter처리된 시료(처리면, 미처리면)를 접촉각 5회 측정하여 평균값을 나타냈다. 발수처리 된 시료의 평균 접촉각 값은 $149^{\circ}$이며, 저온 Plasma의 평균값은 $45^{\circ}$(처리면) $128^{\circ}$(미처리면), Sputter는 $74^{\circ}$(처리면) $144^{\circ}$(미처리면) 으로 가공처리 된 시료에는 양면의 접촉각이 확연한 차이가 나타난 걸로 미루어 보아 편면발수효과가 얻어졌다고 판단된다. SEM 측정을 통하여 관찰한 경우, 발수처리 된 시료에서는 불소계 발수제의 흔적이 보였다. 저온 Plasma, Sputter 처리된 시료에서는 처리시간이 높아짐에 따라서 시료표면에 코팅된 불소계 발수제 막들이 점점 파괴되는 것을 관찰할 수 있었다. 그리고 건식가공으로 인하여 처리된 표면에는 Etching작용이 일어나 표면적이 넓어져 친수화가 일어난 것으로 생각된다. 이처럼 저온 Plasma가공과 Sputter가공으로 편발수를 얻을 수 있다면 에너지 절약, 처리공정과 시간단축 등 여러 가지 장점이 기대된다.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.386-390
• /
• 2016

The surface of carbon nanotubes (CNTs) was modified by fluorination and applied to conductive materials to improve the energy efficiency of a capacitive desalination (CDI) electrode. CNTs were fluorinated at room temperature with a mixed gas of fluorine and nitrogen, and activated carbon based CDI electrodes were then prepared by adding 0-0.5 wt% of untreated CNTs or fluorinated CNTs with respect to the activated carbon. Fluorinated CNTs showed improved dispersibility in the electrode and also slurry as compared to untreated CNTs, which was confirmed by the zeta potential and scanning electron microscopy. Fluorinated CNTs added electrodes showed higher desalination efficiency but lower energy consumption than those of using untreated CNTs added electrodes. This was attributed to the decrease in the resistance of CDI electrodes due to the improved dispersibility of CNTs by fluorination.

• Korean Chemical Engineering Research
• /
• v.54 no.6
• /
• pp.830-837
• /
• 2016

In order to improve the compressive strength of graphite foams (GFms), mesophase pitch (MP) was stabilized in air atmosphere and then fluorinated at different conditions. The Fluorine/Carbon (F/C) in surface-chemical contents of fluorinated MP has range of 23.75%~61.48% according to the different fluorine partial pressure. The compressive strengths of GFms prepared from fluorinated MP were increased in proportion to the apparent densities. The compressive strength of the GFm produced from MP with 35.93% of F/C (%) showed maximum value in $2.93{\pm}0.06MPa$, which was increased up to 27.95% than that of the GFm prepared from un-fluorinated MP. This result was attributed that the interface bonding between of MPs due to fluorine functional groups with high surface energy helped to improve compressive strength of the GFm.

• The korean journal of orthodontics
• /
• v.2 no.1
• /
• pp.23-28
• /
• 1971

In this study, sections of twenty eight teeth were used to investigate the effect of topical application of $8\%$ stannous fluoride on the decalcification rate of enamel surfaces stripped in a manner suggested for orthodontic purpose. The enamel treated with a single application of a fluoride had a significantly lower tile rate of decalcification for the first 96 hours to lactate buffer solution. After double application of fluoride, decalcification rate decreased signicantly. This study suggested that the continuing protection of stripped surfaces should be sought by regularly scheduled treatment of the enamel with the topical application of fluoride and regular use of a fluoride containing dentifrice.