• Membrane Journal
• /
• v.21 no.1
• /
• pp.55-61
• /
• 2011

$BaCo_{0.7}Fe_{0.22}Nb_{0.08}O_{3-{\delta}}$ oxide was synthesized by solid state reaction method. Dense ceramic membrane was prepared using as-prepared powder by pressing and sintering at $1,200^{\circ}C$. XRD result of membrane showed single perovskite structure. Leakage and oxygen permeation test were conducted on the membrane sealed by glass ring as a sealing material. The oxygen permeation flux increased with increasing temperature and pressure difference and maximum oxygen permeation flux was $2.3mL/min{\cdot}cm^2$ at $950^{\circ}C$ with $Po_2$ = 0.63 atm of oxygen partial pressure. The oxygen permeation in the condition of air with $CO_2$ (300 ppm) as feed stream decreased as much as only maximum 2.9% in comparison with air feed stream. It indicated $BaCo_{0.7}Fe_{0.22}Nb_{0.08}O_{3-{\delta}}$ membrane is more stable than another membrane for carbon dioxide.

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.706-711
• /
• 2002

High-pure tantalum powder was fabricated through Na reduction process and has been produced by using $K_2$TaF$_{7}$, and KCI, KF for raw material and diluent, respectively. A raw material and diluent were charged at the hestalloy bomb by the weight rate of 1:2, 1:1, 1:0.5 and 1:0.25 each other, investigated properties of morphology, chemical composition and yield and particle size after reduced. Ta metal has been achieved by reduction of $K_2$$TaF_{7}$ 500g with 1% sodium in excess of stoichiometric amount in the charge at a reduction temperature of $850^{\circ}C$ for 3hours. According to amount of the diluent, a formation of the powder doesn't have an effect. The diluent prevented the temperature rising caused from the heat of reaction and it maintained the speed of reducing reaction. But in the mixture ratio of raw material and diluent in the 1 : 2 and 1 : 0.25, an oxide and partially not reacted K were detected. As the amount of diluent increased, the size of tantalum powder decreased. According as raw material and the mixture ratio of diluent change from 1:0.25 to 1:2, the size is decreased from 5$\mu\textrm{m}$ to 1$\mu\textrm{m}$, and a particle size distribution which is below 325 mesh in fined powder increases from 71% to 83%. In the case of average size of Tantalum powder which is the mixture ratio (1:0.5), we would get the Ta powder with grain size about 3$\mu\textrm{m}$, which come close to the average size (2~4$\mu\textrm{m}$) of tantalum powder which is used commonly in the present is Ta powder about 3$\mu\textrm{m}$.

• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.312-316
• /
• 2000

A study has been made to investigate the effects of hot isostatic pressing(HIP ping) on bond strength and elevated temperature characteristics of thermal barrier coating(TBC). The specimens were prepared by HIPping of TBC which is composed of the ceramic top coat(8wt%$Y_2$$O_3$-$ZrO_2$) and the metallic bond coat on the matrix of IN738LC superalloy. The results showed that the porosity and microcracks in the ceramic top coat of TBC were significantly decreased by HIP. As a result, the bond strength of the HIPped coating was increased above 48% compared to that of as-coated specimen and microstructure was homogenized. It was found that the thermal cycle resistance of HIPped coating was inferior to that of as-coated specimen. It was considered that this result was mainly caused by the reduction of internal defects in the top coat layer which could play a role in relaxing the thermal stress due to a large difference in thermal expansion between TBC and matrix.

• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.257-263
• /
• 2000

Thermoelectric properties of the 0.05wt% $SbI_3$-doped n-type $Bi_2(Te_{0.95}Se_{0.05})_3$ alloy, prepared by melting/grinding and hot pressing, were investigated with variation of the annealing time up to 36 hours. The electron concentration of the 0.05wt% SbI$_3$-doped n-type $Bi_2(Te_{0.95}Se_{0.05})_3$ alloy decreased with increasing the annealing time. The figure-of-merit of the 0.05wt% $SbI_3$-doped n-type $Bi_2(Te_{0.95}Se_{0.05})_3$ alloy was improved from $2.1{\times}10^{-3}/K$ to $2.35{\times}10^{-3}/K$ by annealing at $500^{\circ}C$ for 3 hours. When annealed longer than 12 hours, however, the figure-of-merit decreased substantially due to the increase of the electrical resistivity.

• Korean Chemical Engineering Research
• /
• v.48 no.2
• /
• pp.172-177
• /
• 2010

This study reports the high-temperature oxidation kinetics, ASR(area specific resistance), and interfacial microstructure of metallic interconnects coated with conductive oxides in oxidation atmosphere at $800^{\circ}C$, The conductive material LSC($La_{0.8}Sr_{0.2}CoO_3$, prepared by Solid State Reaction) was coated on the Crofer22APU. The contact behavior of coating layer/metal substrate was increased by sandblast. The electrical conductivity of the LSC coated Crpfer22APU was measured by a DC two probe four wire method for 4000hr, in air at $800^{\circ}C$. Microstructure and composition of the coated layer interface were investigated by SEM/EDS. These results show that a coated LSC layer prevents the formation and growth of oxide scale such as $Cr_2O_3$ and enhances the long-term stability and electrical performance of metallic interconnects for SOFCs.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.359-366
• /
• 2002

The purpose of this study is to investigate the properties of LSGM electrolyte and LSM cathode. The unit cell based on the optimum conditions and processing for high performance was fabricated and measured. The single phase of $LaGaO_3$ was obtained on sintering at $1500^{\circ}$ for 6h with composition of $(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}와 (La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ and $(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$. The grain size of the sintered body was about $10∼30{\mu}m$ and electrical conductivity was 0.13 S/cm measured at $800^{\circ}$. The single phase of $LaMnO_3$ structure in $(La1-xSrx)MnO_3$ system was obtained at x=0∼0.2 and the particle size of the synthesized powder was about 40 nm. The unit cell was prepared by firing at $1200^{\circ}$ for 1h with $(La_{0.9}Sr_{0.1})MnO_3$ cathode and 0.9NiO-0.1YSZ anode screen-printed on surfaces of $(La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ electrolyte. The grain size of the electrode was close to $1{\mu}m$ and the electrode had porous structure. The maximum power density of unit cell showed $0.3W/cm^2$ at $800^{\circ}$.

• Restorative Dentistry and Endodontics
• /
• v.32 no.3
• /
• pp.191-197
• /
• 2007

Mineral trioxide aggregate (MTA) would influence healing of periapical tissues by modulating the production of growth factors and cytokines from PDL fibroblasts, however, the studies are insufficient. Therefore, the purpose of this study was to monitor the expression of transforming growth factor-beta1 $(TGF-\beta1)$, fibroblast growth factor-2 (FGF-2), and interleukin-6 (IL-6) from PDL fibroblasts in the presence of MTA. The human PDL fibroblasts were seeded onto the set MTA or IRM at a level of $1\times10^5$ cells per unit well, and further incubated for 6, 12, 24, and 48 hours. The levels of $TGF-\beta1$, FGF-2 and IL-6 from the supernatant were measured by enzyme-linked immunosorbent assay (ELISA) The data were analyzed using one-way ANOVA. The level of $TGF-\beta1$ was down-reg ulated when the cells were grown in the presence of MTA except at 6 hours. The levels of FGF-2 release were significantly suppressed when PDL fibroblasts were grown in the presence of MTA or IRM at all time intervals (p < 0.05). The expressions of IL-6 from MTA treated co)Is were comparable to those of untreated control cells throughout the observation periods. We presume that this material inhibits the stimulatory function of growth factors on granulation tissue formation and in turn, it promotes the healing process modulated by other bone-remodeling cells.

• Journal of Korean Society of Environmental Engineers
• /
• v.22 no.6
• /
• pp.1073-1081
• /
• 2000

The photo-oxidation of an aqueous humic acid solution using $TiO_2$ sols. which is transparent in visible range, was studied. The $TiO_2$ sols were prepared by a process wherein hydrogen peroxide was added to a gel of $TiO(OH)_2$ originated from hydrolysis of $TiCl_4$, and the resulting titanium peroxo solution(TPS) was heated. The concentration of $TiO_2$ used for photo-oxidation was about 100ppm, determined by comparing the photoluminescence(PL) intensity measured as a function of $TiO_2$ concentration. $TiO_2$ sols aged at $100^{\circ}C$ for more than 12h were found to exhibit a maximum rate in photocatalytic decomposition of humic acid. and the efficiency was better than that of Degussa P25. In addition, the resulting aqueous humic acid after photocatalytic decomposition with sols had an excellent transmittance of visible light, while that treated with Degussa P25 was still turbid. caused by $TiO_2$ particles.

• Journal of Applied Biological Chemistry
• /
• v.55 no.2
• /
• pp.123-127
• /
• 2012

In order to develop eco-friendly biopesticide, an entomopathogenic bacterium Photorhabdus temperata M1021 has been lyophilized via freeze-drying along with protective agents such as skim milk, starch, sodium alginate, glucose and sodium glutamate to protect cells from lysis. Freeze-drying powder of P. temperata M1021 containing 7% skim milk (w/v) showed highest survival rate of 63% among all the protective agents used in trials. Furthermore, the freeze-dried microbial powder showed 75% of survival rate after stored at $4^{\circ}C$ for 4 weeks at air contact conditions. Injection toxicity of the freeze-dried sample was tested against larvae of Galleria mellonella. A dose of $2.0{\times}10^1$ cells of P. temperata M1021 killed 100% of the G. mellonella larvae within 4 days after injection. Moreover, $2.0{\times}10^0$ cells caused 50% mortality within the 4 days after injection. Freeze-dried P. temperata M1021 strains exhibited effective insecticidal activity and could be a better candidate for being used as a biopesticide.

• Journal of radiological science and technology
• /
• v.28 no.1
• /
• pp.1-7
• /
• 2005

High-quality single crystals of pure $Li_2B_4O_7$ as well as $Li_2B_4O_7$ doped with Cu, Mn and Mg impurities (1.0mol%, respectively) have been grown from the melt of $Li_2CO_3+2B_2O_3$ by Czochralski method in platinum crucibles. To study the thermoluminescent properties, $Li_2B_4O_7$ series single crystal TLDs were made by cutting in the size of $4{\times}5{\times}1\;mm^3$. The glow curves show two or three peaks which can be easily deconvoluted. It is observed that room temperature($20{\sim}30^{\circ}C$) fadings of the dosimetric peaks of $Li_2B_4O_7$ series single crystal TLDs were about 10 % for 30 days. The relative photon energy response for $Li_2B_4O_7$ series single crystal TLDs were about 85 % when the responses were normalized to that measured with $^{60}Co\;(1.25\;MeV)\;{\gamma}-rays$. The measured data are in a good agreement with theoretical ones. The $Li_2B_4O_7$ series single crystal TLDs fabricated in this work can be used for monitoring personal and environmental radioactivity.