• Journal of Advanced Marine Engineering and Technology
• /
• v.41 no.3
• /
• pp.230-237
• /
• 2017

In this study, electrochemical methods were used to determine the optimum protection potential of S355ML steel for the cathodic protection of offshore wind-turbine-tower substructures. The results of potentiodynamic polarization experiments indicated that the anodic polarization curve did not represent a passivation behavior, while under the cathodic polarization concentration, polarization was observed due to the reduction of dissolved oxygen, followed by activation polarization by hydrogen evolution as the potential shifted towards the active direction. The concentration polarization region was found to be located between approximately -0.72 V and -1.0 V, and this potential range is considered to be the potential range for cathodic protection using the impressed current cathodic protection method. The results of the potentiostatic experiments at various potentials revealed that varying current density tended to become stable with time. Surface characterization after the potentiostatic experiment for 1200 s, by using a scanning electron microscope and a 3D analysis microscope confirmed that corrosion damage occurred as a result of anodic dissolution under an anodic polarization potential range of 0 to -0.50 V, which corresponds to anodic polarization. Under potentials corresponding to cathodic polarization, however, a relatively intact surface was observed with the formation of calcareous deposits. As a result, the potential range between -0.8 V and -1.0 V, which corresponds to the concentration polarization region, was determined to be the optimum potential region for impressed current cathodic protection of S355ML steel.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.18 no.6
• /
• pp.569-576
• /
• 2012

In general, aluminum alloys forms the passive film($Al_2O_3$, $Al_2O_3{\cdot}3H_2O$) in neutral solution. However, the passive film created on the surface will be destroyed by chloride ions contained in sea water so the corrosion will occur. In this study, in order to solve the problem of corrosion under a seawater environment, potentiostatic protection techniques were applied to Al-4.5%Mg-0.6%Mn aluminum alloy in seawater. At polarization experiments, active state were observed at anodic polarization and concentration polarization by reduction of dissolves oxygen and activation polarization were found at anodic polarization. As a results of potentiostatic experiment, calcareous deposit were created much more as applying time increase from the turning point of the concentration polarization and activation polarization and crevice corrosion was partially observed between calcareous deposit and surface of base metal. Overall potentiostatic anodic polarization experiment was difficult to apply potentiostatic corrosion protection technology by occurrence of active state, whereas potentiostatic cathodic polarization experiment examined optimum corrosion protection condition of -1.1 V~-0.75 V within the range of concentration polarization considered various applying time.

• Journal of the Korean Chemical Society
• /
• v.46 no.1
• /
• pp.19-25
• /
• 2002

We measured the variations of potentials and current densities for several polymers. The results were carefully examined to identify various factors such as temperature and pH to influence the potential and rate. The Tafel slope for anodic dissolution was determined by the polarization effect under these conditions. The optimum conditions were established for each case. The second anodic current density peak and maximum current density were designated as the relative polarization sensitivity $(I_r/I_f)$. The mass-transfer coefficient value $({\alpha})$ was determined by the Tafel slope for anodic dissolution on the basis of the polarization effect under optimum conditions.

• 한국가스학회:학술대회논문집
• /
• 2000.09a
• /
• pp.117-117
• /
• 2000

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.112-112
• /
• 2018

알루미늄 합금은 내구성과 내식성이 우수한 경량 재료이다. 그 중 Al-Mg계 5083 Al 합금은 가공성 및 용접성이 우수하여 선체 재료로 널리 이용되고 있다. 이는 선체 중량의 경량화로 인해, 연료비 절감과 빠른 선속 등 다양한 이점을 지니기 때문이다. 그러나 선박의 고속화에 따라 선체에 가해지는 유체충격이 증가하고, 압력 저하에 기인하여 캐비테이션-침식 손상이 증가할 뿐만 아니라, 염소이온이 존재하는 해수환경에서는 침식과 부식의 시너지효과로 인하여 재료의 손상이 더욱 가속화된다. 이에 대한 다양한 방지책들이 제안되고 있으나, 강한 충격압을 동반한 캐비테이션 침식-부식 복합 손상 환경에서는 다소 한계가 있다. 따라서 본 연구에서는 알루미늄 5083에 대하여 캐비테이션 환경 하에서 일정 전위를 인가하며 침식-부식 손상이 최소화 되는 전위 구간을 규명하고자 하였다. 먼저, 분극 실험을 선행하여 재료의 전기화학적 거동을 파악 한 후 적용 전위구간을 선정하여, 해당 전위를 인가한 상태에서 캐비테이션 실험을 실시하였다. 전기화학적 분극실험과 캐비테이션-전기화학 복합 실험은 $25^{\circ}C$의 해수 하에서 실시하였으며, 시험편의 노출면적은 $3.24cm^2$으로 하였다. 분극 실험은 개로전위로부터 +3 V까지 2 mV/s의 분극속도로 전위를 인가하였고, 기준전극으로 Ag/AgCl, 대극으로 백금전극을 사용하였다. 캐비테이션-전기화학 복합 실험은 정전위를 인가한 상태에서 대향형 진동법으로 진동수 20 kHz, 진폭 $30{\mu}m$ 진동을 20분간 가하였으며, 혼팁과 시험편 사이의 거리는 1 mm로 일정하게 유지하였다. 실험 후 표면 손상의 정량적 분석을 위해 인가된 전위별 전류밀도를 비교하고, 무게감소량을 측정하였으며, 손상경향 파악을 위하여 3D광학현미경과 주사전자현미경(SEM)을 통해 표면을 분석하였다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.4
• /
• pp.66-74
• /
• 2013

In this study, corrosion potential ($E_{corr}$), corrosion rate, and polarization resistance were measured aimed at inorganic inhibitors (passive film type) and organic inhibitors (absorption type). The experiment was conducted using potentiostat for the variable molar ratio and chloride ion concentration of the components of inhibitors in an aqueous solution of saturated calcium hydroxide targeting corrosion. As a result, it was possible to ensure an anticorrosive performance of at least a 1.2 molar ratio of inorganic inhibitors. Also, the organic inhibitors ensured the prevention of the anticorrosive performance of at least about a 0.3 molar ratio. It also showed the tendency that between polarization resistance and corrosion rate, Ecorr and corrosion rate is inversely proportional to the linear. Conversely, the tendency between polarization resistance and Ecorr is proportional to the linear. Also, a distinct difference in organic and inorganic inhibitors' relationship to Ecorr, corrosion rate, and polarization resistance was not shown.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.19 no.1
• /
• pp.79-84
• /
• 1983

The test specimen, designated the double cantilever beam, was employed for a fracture mechanics study of stress corrosion cracking (SCC) of type 5083 Al-alloy in seawater. Stress intensities for this DCB specimen were calculated by using compliance, strain energy release rate and relation between stress intensity and strain energy release rate. Analytical expression for compliance as a function of crack length was obtained by applying beam theory. It was investigated that the polarization potentials affected the growth rate and surface of stress corrosion cracking. The results are as follows, The critical stress intensity was 134.81-148.38kg/mm super(3/2) and K sub(Ii) under polarization potentials was 75.92-145.78kg/mm super(3/2). The minimum stress corrosion crack growth rate was occurred at-987mV SCE. Insoluble compound on $\beta$ phase was looked into through SCC. The greater anodic potential is, the larger insoluble compound on $\beta$ phase becomes.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.143-143
• /
• 2016

알루미늄 합금은 내구성과 내식성이 우수할 뿐만 아니라 다양한 표면개질을 통해 그 표면 특성을 더욱 향상시킬 수 있다. 특히 Al-Mg계 5083-H321 Al 합금의 경우 가공성 및 용접성이 우수하여 선체 재료로 널리 이용되는데, 이는 선체중량의 경량화가 가능하여 연료비 절감과 빠른 선속 등 다양한 이점을 지니기 때문이다. 그러나 선속의 고속화에 따라 선체에 가해지는 유체충격이 증가하고 정압 저하에 기인하여 캐비테이션-침식 손상이 증가할 뿐만 아니라 해수환경 특성 상염소이온의 존재로 부식이 가속화되는 등 침식 및 부식의 시너지효과로 손상은 크게 증가한다. 이에 대한 방지대책으로 다양한 표면개질 기법이 제안되고 있으나 강한 충격압이 동반된 캐비테이션 침식-부식 복합 손상 환경에서는 표면처리만으로는 불가능할 수 있다. 따라서 본 연구에서는 양극산화된 5083-H321을 대상으로 캐비테이션 환경 하에서 일정 전위를 인가하여 침식-부식 손상이 최소화되는 최적전위를 규명하고자 한다. 이를 위해 먼저 분극 실험을 통해 재료의 전기화학적 거동을 바탕으로 임의의 전위를 선정하고 해당 전위를 인가한 상태에서 캐비테이션 실험을 실시하였다. 이때 분극실험과 캐비테이션-전기화학 복합실험 모두 $25^{\circ}C$의 해수에서 실시하였으며, 전기화학적 분극실험은 유효면적이 $3.24cm^2$인 시편에 2 mV/s의 분극속도로 0 ~ -3 V 까지 인가하였고, Ag/AgCl 기준전극과 백금대극을 사용하였다. 캐비테이션-전기화학 복합 실험은 정전위를 인가한 상태에서 $30{\mu}m$의 진폭으로 20분간 실시하였으며, 혼팁과 시험편 사이의 거리는 1 mm로 일정하게 유지하였다. 실험 후 표면 손상의 정량적 분석을 위해 인가된 전위별 전류밀도를 비교하고, 무게감소량을 측정하였으며, 손상특성 분석을 위해 3D현미경과 주사전자현미경(SEM)을 통해 표면을 분석하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.96-96
• /
• 2018

금속재료 중 알루미늄(Al)은 일반적으로 많이 사용되는 철강재에 비해 그 비중이 약 $1/3(2.7g/cm^3)$인 경량이고 열전도율이 약 3배($196kcal/^{\circ}C$, $20^{\circ}C$)로 높은 특성 등을 갖고 있다. 또한 대량생산에 의한 경제성을 가지기 때문에 건축 구조재, 전기 및 가전 등 다양한 산업 분야에서 널리 사용되고 있다. 특히, 위와 같은 특성으로 인해 열교환기의 종류에서 응축기(Condenser) 및 증발기(Evaporator)는 알루미늄(Al)을 널리 사용하고 있다. 하지만 단일 응축기 부품에도 이종 알루미늄 소재가 사용됨에 따라 갈바닉 부식이 발생할 수 있다는 단점이 있다. 따라서 본 연구에서는 현재 상용되고 있는 열교환기 중 응축기에서의 이종 알루미늄 재료로 인해 나타나는 갈바닉 부식 특성을 관찰-분석-연구 하였다. 본 연구에 사용된 알루미늄 재료는 현재 응축기 재료 중에서 각각 Tube와 Fin으로 널리 상용되고 있는 Al 1100과 Al 3003을 사용하였다. 표면 모폴로지는 SEM을 통해 관찰하였고 EDS를 통해 조성원소를 분석하였다. 또한 내식성 평가를 위해 5% NaCl 환경에서의 SST(Salt spray test, 염수분무시험) 시험과 3% NaCl 용액 내 자연침지 시험 및 탈기된 3% NaCl 용액 내 전기화학적 동전위 양극 분극 시험을 진행하였으며 더불어 갈바닉 부식 시험에 따른 혼합 전위 측정 및 외관 관찰을 하였다. 각 재료는 실험에 대해 동일한 표면적을 노출시켜 시험하였다. 5% NaCl 환경에서의 염수분무 시험 결과 Fin(Al 3003)의 경우에는 Tube(Al 1100) 보다 빠른 부식거동을 보이며 국부적인 공식부식(Pitting corrosion)이 촉진되었다. Tube(Al 1100)의 경우에는 치밀한 Al2O3 형성과 부식에 따른 Al(OH)3를 생성함에 따라 Fin(Al 3003)에 비해 느린 부식거동을 보였다. 3% NaCl 용액 내 자연 침지 및 전위 측정 결과 초기 전위는 Fin(Al 3003, 약 -0.85V/SCE)이 Tube(Al 1100, 약 -1.05V/SCE)에 비해 더 높은 값을 가지며 약 72시간 이후 Tube(Al 1100) 시편이 더 안정적인 전위 값을 나타냈다. 이는 안정적인 Al(OH)3 피막 형성에 기인한 것으로 사료된다. 탈기된 3% NaCl 용액 내 전기화학적 동전위 양극 분극 시험 결과 Fin(Al 3003) 시편에서 더 귀한 부식 전위 값을 나타냈지만 부식 전류는 더 낮은 값을 나타냈다. 상기 시험 결과를 바탕으로 Fin-Tube 간 장기간 접촉 시에는 갈바닉 부식이 발생할 수 있을 것으로 사료된다. 갈바닉 부식 시험 결과 초기 혼합 전위는 약 -1.05 V/SCE를 나타냈으며 약 288시간 경과 후 약 -0.85 V/SCE 값을 나타냈다. 이는 자연 전위 측정 및 동전위 양극 분극 시험에서의 부식 전위 값에서 알 수 있듯이 더 비한 전위인 Tube(Al 1100) 시편이 Fin(Al 3003) 시편에 대해 희생양극적(Sacrificial anode)인 역할을 한 것을 확인할 수 있었다. 또한 갈바닉 부식 전위 측정 간 외관 관찰에서도 Tube(Al 1100) 시편은 빠르게 흑변 하는 것을 확인할 수 있었으며 Fin(Al 3003) 시편은 침지 300시간 이후에도 초기와 유사한 표면 상태 및 광택을 유지하였다. 이상의 SST 시험, 자연 침지 시험, 전기화학적 양극 분극 시험 및 갈바닉 부식 시험 결과를 바탕으로 단일 부품 내 이종 알루미늄 소재 간 접촉 및 그에 따른 갈바닉 부식 발생을 확인할 수 있었다. 따라서 동종 성분이라고 할지라도 단일 부품 제작 시에는 그 사용 환경에 따라 이종 금속 재료의 사용에 대한 재고가 필요할 것으로 사료된다.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.20 no.6
• /
• pp.81-87
• /
• 1983

The body surface ECG(electrocardiogram) is produced by the electric fields caused by the propagation of action potentials within the myocardial cells. The repolarization phase of the action potential is very sensitive to factors of clinical importance. Therefore, in this paper of the inverse electrocardiography, we studied a method of estimating the uniform action potentials during repolarization phase from the body surface ECG using digital signal identification techniques. The estimated action potential of a normal was similar to that of clinical data in the repolarization phase.