• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.11
• /
• pp.5915-5922
• /
• 2013

In this study, with the aim of improving the performance of shale to allow for its use as coarse aggregate for concrete, we coated shale aggregates with water repellents and polymers and evaluated their physical properties such as density, water absorption rate, wear rate, and stability depending on the coating method. In addition, the effects of the performance improvement were evaluated by assessing the properties of fresh concrete produced by varying the shale substitution ratio, as well as the compressive strength, flexural strength, and freeze-thaw resistance according to curing ages. The test results revealed that the absolute dry densities of all coated aggregates satisfied the standard density for coarse aggregates for concrete(>$2.50g/cm^3$),and the absorption rate of the shale aggregate coated with water repellent decreased by about 50% compared with that of uncoated shale. The wear rate of the polymer-coated shale decreased by up to 13.0% compared with that of uncoated shale. All coated aggregates satisfied the stability standard for coarse aggregates for concrete(${\leq}12$). The water repellent-induced performance improvement decreased the shale aggregates' slump by about 20~30mm compared with that of the uncoated shale aggregates, and the air content of the repellent-coated shale aggregate increased by up to 0.9% compared with that of the uncoated shale aggregate. The compressive strength of the polymer-coated shale aggregates at a curing age of 28 days was RS(F) 95.7% and BS(F) 90.0%, and the flexural strength was RS(F) 98.0 % and BS(F) 92.0% of the corresponding values of concretes produced using plain aggregates. Furthermore, the concrete using polymer-coated shale aggregates showed a dynamic modulus of elasticity of RS(F) 91% and BS(F) 88% after 300 freeze-thaw cycles, thus demonstrating improved freeze-thaw durability.

• Transactions of the Korean hydrogen and new energy society
• /
• v.21 no.4
• /
• pp.313-320
• /
• 2010

Carbon cloth was impregnated into PTFE emulsion. PTFE is a fluoropolymer used as a coating material in various fields due to its hydrophobicity and excellent mechanical properties. In this study, PTFE emulsion was prepared different particle size of 5~500 nm and $3{\sim}5{\mu}m$. FE-SEM and FT-IR spectroscopy were used microscopic observation and investigation of chemical structure change after PTFE coating. Mass variations, gas permeability and water contact angles were analyzed to determine a GDL performance of PTFE coated carbon cloth. PTFE coated carbon cloth show different mass increase according as PTFE concentration and the number of coating times. Water contact angle of PTFE coated carbon cloth was not effected by size of PTFE particle and the number of coating time; meanwhile, gas permeability was rapidly changed at carbon cloth coated by emulsion with size of $3{\sim}5{\mu}m$ PTFE particle.

• Transactions of the Korean hydrogen and new energy society
• /
• v.20 no.5
• /
• pp.424-431
• /
• 2009

Treatment for water repellency on the carbon supports of GDL which composed a part of MEA has been suggested as a solution to prevent flooding. PTFE is a fluoropolymer that has hydrophobic property and a PTFE emulsion was selected as waterproof agent in this investigation. Carbon paper was coated by PTFE emulsion with different particle size of 5~500 nm and 3~$5\;{\mu}m$ as various concentration. PTFE coated carbon paper has difference in weight variation changed proportionally at PTFE concentration and coating times. Then gas permeability of the coated carbon paper with emulsion of 3~$5\;{\mu}m$ PTFE was changed vastly. Characteristics of carbon paper coated with different PTFE emulsion were analyzed by FE-SEM, FT-IR spcetroscopy and were evaluated by weight variations, gas permeability and water contact angle.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.1
• /
• pp.217-223
• /
• 2005

This study is on the evaluation of three kinds of surface protectors for protecting reinforced concrete against corrosion of reinforcing steel by chloride attack and carbonation. In this study, the test has been carried out on the performance of specimens applied with surface protectors for anti-corrosion and anti-carbonation. The result showed that specimens applied with the three kinds of surface protectors, were excellent in resistance to the corrosion of reinforcing steel and carbonation. Especially the specimen applied with finish coating in conjunction with hydrophobic primer showed great reduction in the corrosion of reinforcing steel and carbonation.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.63-64
• /
• 2023

In order to reduce the high absorption ratio of spent coffee grounds, this study examined the compressive strength and absorption ratio of mortar replacing coated spent coffee grounds according to the type of water repellent. In order to examine this, as the water repellent used, a silane-based water repellent (fluorine-based water repellent) and an acrylic-based water repellent, which are film-type water repellents, and a silane/siloxane-based water repellent, which are penetration-type water repellents, were used. The spent coffee grounds were coated with each of three water repellents, and mortar was prepared by mixing cement and fine aggregate. As a result of the experiment, the compressive strength and absorption ratio of the mortar replaced with coated spent coffee grounds coated with the film-type water repellent were superior to the penetration-type water repellent. Therefore, in order to reduce the high absorption ratio of spent coffee grounds, a suitable water repellent is a film-type water repellent. Among them, it is judged that the acrylic type has excellent water repellency and is suitable.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.12.2-12.2
• /
• 2009

전자 디스플레이 산업의 중요성과 미래사회에서 요구되는 정보기기로써 유연한 기판을 사용한 소자에 대한 수요가 급격히 증가하고 있으며, 이들 산업에 응용되기 위해서는 저비용, 고생산 공정이 요구되고 있다. 이를 위해 인쇄전자 기술에 대한 연구가 활발히 진행되고 있다. 특히, 금속배선은 모든 소자의 기본이면서 낮은 저항과 높은 신뢰성을 동시에 요구하고 있어 인쇄전자 기술이 해결해야 할 가장 어려운 난제 중의 하나이다. 따라서 본 연구에서는 낮은 저항과 높은 신뢰성을 만족시킬 수 있는 새로운 금속배선 공정으로서 폴리이미드 필름을 초발수 처리한 후 친수 패턴을 하여 전도성 잉크에 함침함으로서 친수 패턴을 따라 금속배선이 이루어 지도록 하는 방법을 제안하고자 한다. 폴리이미드 필름의 표면을 플라즈마 처리하여 표면에 나노돌기를 형성시키고 불소기를 함유한 코팅층을 형성시킴으로써 물에 대한 접촉각이 $150^{\circ}$이상이 되도록 초발수 처리할 수 있었다. 초발수 처리된 폴리이미드 기판에 쉐도우 마스크를 사용하여 UV조사함으로써 조사된 부분만 친수성을 가지는 패턴을 형성하였다. 이렇게 친수 패턴이 제작된 초발수 폴리이미드 유연기판을 실버잉크에 함침함으로써 선폭 $200{\mu}m$를 가지는 금속배선을 형성시켰다. 형성된 금속배선의 단면 형상을 측정하였으며, 열처리를 통하여 비저항이 $30{\mu}{\Omega}$-cm를 얻을 수 있었다. 통상 1회의 함침으로는 금속배선의 두께가 150nm정도로 금속배선으로 사용하기에는 얇아 배선의 두께를 증가시키기 위하여 수 회 함침을 시도하여 $2{\mu}m$의 두께로 증가시킬 수 있었다. 이때 선폭과 선간 간격은 크게 변하지 않고 두께만 증가시킬 수 있었다. 이는 금속배선을 형성한 후에도 폴리이미드 유연기판의 초발수성은 그대로 유지되어 여러번 함침할 때 잉크가 이미 형성된 배선에만 묻게 되어 두께는 증가하나 선폭과 선간 간격은 증가하지 않는 것으로 판단된다. 사용한 실버잉크는 실버의 함량은 10~20wt%인 수계 잉크였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.94-94
• /
• 2018

무인자동차 및 전기자동차 등 전장부품 및 메인보드에서의 오염 방지와 전자파에 의한 신호 간섭 현상에 따른 기기의 오작동을 방지하고자 MWCNT의 clustering 및 tangling현상을 활용하여 self cleaning 기능을 갖는 super hydrophobic 표면과 high aspect ratio에 의한 percolation 현상을 활용하여 전자파 차폐를 위한 낮은 표면저항을 만족하는 복합 재료로 구성된 코팅에 관하여 연구하였다. 이를 위해 isopropyl alcohol(IPA)을 용매로 산처리 한 MWCNT와 무기바인더, 불소계 실란을 첨가하여 초음파 분산을 함으로써 코팅액을 제조하였다. 이를 full cone nozzle type, 흡상식 스프레이 조건으로 알루미늄 시편위에 스프레이 코팅 후 열경화 하여 접촉각측정기로 측정 결과 $160^{\circ}$이상의 초발수 표면과 Low Resistivity Meter로 표면저항을 측정한 결과 $10^3{\Omega}/cm^2$ 이하의 낮은 코팅막을 구현하였으며 내구성 실험을 위한 항온항습 장비로 $80^{\circ}C$의 내열테스트 및 80%와 $80^{\circ}C$조건하에서의 내습테스트 결과 표면에 이상 없음을 확인하였고 열전도율 측정을 위해 밀도 측정 결과 $2.68g/cm^3$, 비열 측정 결과 $0.85J/g^{\circ}C$가 열확산율 측정결과 $88.64mm^2/s$가 측정 되었으며 밀도, 비열, 열확산율을 곱한 값인 $201.9W/m{\cdot}K$의 열전도를 갖는 코팅막을 구현하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.197-198
• /
• 2012

PTFE(polytetrafluoroethylene) 타겟을 RF 스퍼터링에 의하여 Si 기판과 슬라이드 글라스에 코팅하였다. PTFE의 기초 실험조건으로 타겟 건 파워, 공정시간, 압력 및 바이어스 파워를 변화시켰다. PTFE 필름의 특성은 조건별 두께를 비교하였고, 분광광도계에 의한 투과도를 측정하였다. PTFE의 발수 특성과 스퍼터링 공정 조건을 확인하고자 접촉각 측정을 실시하였다. 타겟 건의 파워 및 시간에 따라 증착속도의 차이가 있었으며, 광학적인 투과도에서도 변화가 있음을 알 수 있었다. 발수특성을 나타내는 PTFE의 스퍼터링에 의한 접촉각 측정을 통해 다양한 조건별 접촉각 특성을 확인하였다.

• Journal of the Korean Society of Visualization
• /
• v.21 no.3
• /
• pp.15-22
• /
• 2023

This research introduces an innovative approach for fabricating microstructure surfaces using spray-coating deposition. The resulting surface, referred to as Magnetically Responsive Microstructures (MRM), exhibits hierarchically structured micro-pillar arrays with remarkably high aspect ratios. The fabrication process involves precisely mixing PDMS and hexane with Carbonyl iron powders, followed by ultrasonication and spray-coating on the top of a PDMS substrate placed on the neodymium magnet. The MRM surface shows hydrophobic properties, characterized by a contact angle surpassing 150° and an aspect ratio exceeding 10. Through a comprehensive exploration of critical parameters, including spray amount, magnet-substrate distance, and solution ratio enhanced dynamic tunability and exceptional hydrophobic characteristics are attained. This novel approach holds significant potential for diverse applications in the realm of dynamically tunable microstructures and magnetically responsive surfaces.

• Journal of Adhesion and Interface
• /
• v.20 no.4
• /
• pp.146-154
• /
• 2019

In this study, alkoxysilane-functionalized amphiphilic polymer (AFAP), which have hydrophilic segment and hydrophobic segment functionalized by alkoxysilane group at the same backbone, was synthesized and used as a dispersant and control agent for reaction rate in the preparation of colloidally stable organic-inorganic (O-I) hybrid sols. After reaction with fluorosilane compounds, fluorinated O-I hybrid sols were prepared and coated onto glass substrate to form hydrophobic O-I hybrid coating films through low-temperature curing process. Surface hardness and hydrophobicity of cured coating films were varied with type of solvent and composition of AFAP and fluorinated alkoxysilane compounds. At appropriate solvent and composition of fluorinated alkoxysilane compounds, O-I hybrid coating film having high transparency and surface hardness could be prepared, which could be applicable to cover window of solar cell and displays.