• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.6
• /
• pp.1-10
• /
• 2014

In this study, thirteen reinforced concrete beams, ground granulated blast furnace slag, replacing recycled coarse aggregate with PVA fiber (BSPG series) and recycled coarse aggregate with hybrid fiber ($BSPGR_1$, $BSPGR_2$ series), and standard specimen (BSS) were constructed and tested under monotonic loading. Experimental programs were carried out to improve and evaluate the Structural performance of such test specimens, such as the load-displacement, the failure mode, and the maximum load carrying capacity. All the specimens were modeled in 1/2 scale-down size. Test results showed that test specimens ($BSPGR_1$, $BSPGR_2$ series) was increased the compressive strength by 13%, the maximum load carrying capacity by 4~21% and the ductility capacity by 4~28% in comparison with the standard specimen (BSS). And the specimens ($BSPGR_1$, $BSPGR_2$ series) showed enough ductile behavior and stable flexural failure.

• The Journal of the Korea Contents Association
• /
• v.13 no.9
• /
• pp.392-399
• /
• 2013

The purpose of this study is to identify the manufacturing possibility of non-cement mortar using blast furnace slag and alkali accelerator. In this experimental study, the blast furnace slag which is the by-product of the steel industry substitute for cement, and the potassium hydroxide(KOH), calcium hydroxide ($Ca(OH)_2$) and sodium hydroxide(NaOH) as stimulus were added to each specimen. And the analysis on reaction property of non-cement mortar was conducted by measurement such as flexural and compressive strength, XRD, EDS and SEM. From the test results, it can be founded that $SiO_2$ and CaO included in the blast furnace slag are released and make the calcium silicate hydrate like the hydration reaction of the cement. Also, the continued study is need to reduce emission of $CO_2$ because of major content in filed of the building construction.

• Honam Mathematical Journal
• /
• v.2 no.1
• /
• pp.1-8
• /
• 1980

논문(論文)[3] (본(本) 논문(論文) 제1부(第1部))에서 미분가능다양체(微分可能多樣體) M 위의 (n-1)차(次) 미분형식(微分型式) ${\beta}^{(n-1)}$이 Compact인 Carrier를 가지면 ${\int}d{\beta}^{(n-1)}=0$이며, (p-1)차(次) 미분형식(微分型式) ${\beta}^{(p-1)}$과 p차(次) 미분가능쇄(微分可能쇄鎖) $C^{(p)}=\Sigma\limits_ik_iS_i{^{(p)}}$에 대(對)하여 ${\int\limits_{c^{(p)}}}d{\beta}^{(p-1)}={\int\limits_{{\partial}{c}^{(p)}}}{\beta}^{(p-1)}$이 성립(成立) (Stokes 정리(定理)의 일반화(一般化))⋯등(等) M위의 적분(積分)에 관한 여러 가지 성질(性質)들을 구명(究明)하였다. 이 성질(性質)들을 토태(土台)로 하여 본(本) 논문(論文)에서는; 제2절(第2節)에서 미분가능다양체(微分可能多樣體) M위의 Lie 도함수(導函數)의 정의(定義)와 Lie적분(微分)에 관(關)한 여러가지 성질(性質)들을 고찰(考察)하고, 제3절(第3節)에서 div X와 Laplace 작용소(作用素) ${\Delta}f$의 정의(定義) 및 실(實) n차원(次元) 가부호미분가능(可符號微分可能) 다양체(多樣體) M 위에서의 divX와 ${\Delta}f$의 적분(積分)에 관(關)한 성질(性質), 즉(卽) $V=\sqrt{{\mid}g{\mid}}dx^1{\Lambda}{\cdots}{\Lambda}dx^n{\in}A^n(M)$에 대(對)하여 $$\int_MdivXV\limits=\int_M{\Delta}fv=0$$인 관계(關係)가 성립(成立)함을 구명(究明)한다. (정리(定理) 3.3)

• Cement Symposium
• /
• no.24
• /
• pp.96-101
• /
• 1996

• Proceedings of the Korean Magnestics Society Conference
• /
• 1992.10a
• /
• pp.52-53
• /
• 1992

• Ceramist
• /
• v.12 no.2
• /
• pp.13-19
• /
• 2009

• Proceedings of the Petrological Society of Korea Conference
• /
• 2004.05a
• /
• pp.53-58
• /
• 2004

• Applied Chemistry for Engineering
• /
• v.28 no.3
• /
• pp.360-368
• /
• 2017

In order to investigate the durability of high performance polymer concrete composites, polymer concrete specimens were prepared using the ortho-type unsaturated polyester resin (UPR) and iso-type UPR as a polymer binder and the calcium carbonate and silica fine powder as a filler. The durability of polymer concrete specimens was measured by hot water resistance, chemical resistance, pore analysis and SEM observation. The compressive strength of the specimen using the iso-type UPR was higher than that of using the ortho-type UPR, and the compressive strength of the specimen using the silica fine powder was higher than that of using the calcium carbonate filler. From hot water resistance results, it was found that the specimen using the iso-type UPR was superior to that of using the ortho-type UPR and the specimen using the calcium carbonate filler was superior to that of using the silica fine powder. The compressive strength reduction rate was measured after the chemical resistance test and the sodium hydroxide solution showed the highest reduction rate, followed by sulfuric acid, hydrochloric acid and calcium chloride solutions. When using the alkaline solution of sodium hydroxide, the weight reduction rate of the specimen using calcium carbonate was lower than that of using silica fine powder, while for the acidic solutions of sulfuric acid and hydrochloric acid, the weight reduction rate of the specimen using the silica fine powder was lower than that of using calcium carbonate.

• Communications of the Korean Mathematical Society
• /
• v.19 no.3
• /
• pp.389-425
• /
• 2004

심프렉틱 다양체는 미분다양체와 케러다양체 사이에 있는 다양체로서 심프렉틱 구조를 갖는 다양체이다. 케러다양체의 성질들을 얼마나 확장할수 있는지, 미분다양체와 다른 성질은 무엇이 있는지 연구함은 흥미있는 일이다. 심프렉틱 구조로부터 준복소구조가 정의되어 2차원 부분다양체를 나타내는 슈도-호로모르픽 사상이 정의되고, 이들은 모듀라이 공간이 된다. 또한 심프렉틱 구조는 메트릭과 에너지를 정의하여 노비코프환을 정의한다. 여기서 모듀라이 공간의 위상구조가 그로모브-위튼 불변량을 정의한다. 이 불변량은 심프렉틱 다양체 연구에 핵심적인 역할을 한다. 이 논문은 그로모브-위튼 불변량의 여러 가지 성질과 그 응용에 대한 여러 학자들의 결과를 소개하는 해설 논문이다.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.05a
• /
• pp.143-148
• /
• 2004

고로슬래그 미분말과 플라이 애쉬와 같은 재료들이 콘크리트의 내구성과 장기강도 증진을 목적으로 혼합재로서 사용되고 있다. 본 연구에서는 고로슬래그 사용 몰탈의 내구성 증진 특성을 활용하기 위하여 고로슬래그 미분말에 알칼리 자극제를 첨가한 알칼리 활성화 슬래그계 무기결합재 사용 몰탈의 내구성과 물리적 특성을 평가하였다. 실험결과, 몰탈의 초기 압축강도 발현에 알칼리 자극제가 큰 영향을 미치는 것을 확인하였다. 또한 알칼리 자극제가 첨가된 몰탈의 화학적 저항성을 평가하기 위하여 공시체를 재령 28 일 후, 5% 황산($H_2SO_4$) 용액에 침지하여 압축강도 및 질량 변화를 관찰하였다. 그 결과, 보통포틀랜드 시멘트로 제조한 몰탈의 경우, 황산용액 침지 후 압축강도가 54% 감소하였다. 반면 고로슬래그 미분말을 첨가한 몰탈의 경우, 약 10% 강도가 감소하였다. 질량변화의 경우, 보통포틀랜드 시멘트로 제조한 공시체는 17%, 고로슬래그 미분말을 첨가한 몰탈은 3%의 질량변화를 보였다. 이 결과로서 고로슬래그 미분말을 첨가한 몰탈의 경우, 화학적 저항성과 물리적 특성이 우수한 것을 확인하였다.