• 한국농공학회논문집
• /
• 제54권6호
• /
• pp.159-167
• /
• 2012

In the present study, an investigation has been made on the application of cement-bentonite soil mixtures as the countermeasure against leachate produced by buried animal carcasses. For this purpose, the strength characteristics of the cement-bentonite soil mixtures mixed with geotextile and metakaolin. After the mixtures with different contents of the cement (0 %, 10 %), bentonite (0 %, 5 %, 10 %, 15 %, 20 %), and weathered soil (100 %, 95 %, 90 %, 85 %, 80 %) were prepared, metakaolin and geotextile were added with different contents (metakaolin : 0 %, 5 %, 10 %, 15 %, 20 % of the cement weight; geotextile : 0 %, 0.5 %, 1 %, 1.5 %, 2 %). Experimental results suggested that the early strength of the mixture increases due to the pore filling, the hydration acceleration, and the pozzolan reaction when metakaolin of 5~10 % of the cement weight was added. In addition, the compressive strength increase when 0.5~1 % geotextile contents were added, and the above these contents, the rate of strength increase was gradually decreased because of the fibrous tangles.

• 한국디지털건축인테리어학회논문집
• /
• 제12권4호
• /
• pp.87-95
• /
• 2012

Autoclaved lightweight concrete (ALC), also known as autoclaved aerated concrete (AAC), is a lightweight, precast building material that simultaneously provides structure, insulation. ALC is a unique building material. Because of its cellular nature, it is lightweight, self-insulating, as well as sound and fireproof. ALC products include blocks, wall panels, floor and roof panels, and lintels. Recently, the use of ALC has became increasingly popular. However, ALC have high water absorption, low compressive strength and popout the origin of the low surface strength in its properties. Thus, this study is to improve the fundamental strength by controls of increasing of admixtures and chemical reactants. Admixtures make use of meta kaolin and silica fume, chemical reactants make use of sodium silicate and sodium hydroxide. From the test result, the ALC using admixtures and chemical reactants have a good fundamental properties compared with plain ALC. These good fundamental properties is caused by the admixtures and chemical reactants of ALC by the reason of the micro filling effect and chemical binding of C-S-H gel, tobermolite and quartz.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.425-428
• /
• 2005

In this study, the experiment was carried out to investigate and analyze the strength properties and flowability of concrete using meta kaolin. The main experimental variables were water/binder ratio 40.0$\%$, water content 170kg/$m^{3}$ and mineral admixtures such as slag powder, silica fume and meta kaolin. According to the test results, the principle conclusions are summarized as follows. 1) The flowing property of concrete that uses meta kaolin appears to be the same to that of the silica fume concrete, but the slump flow that evaluates the compaction ability of concrete shows the most favorable performance. 2) The air content of the concrete that uses meta kaolin can be effectively controlled for the target performance in compliance with the use of AE agent. 3) When it comes to the strength of concrete that uses meta kaolin, the most favorable development of strength occurs when the replacement rate is 10$\%$, in case of the silica fume, and the slag power. In addition, as the replacement rate increases, so becomes the development of concrete strength favorable.

• 한국건설순환자원학회논문집
• /
• 제3권4호
• /
• pp.374-381
• /
• 2015

화재에 대한 건축물의 내화성능 확보를 위해서는 온도가 상승하더라도 허용범위 이내로 제어하고 탈락이나 손상 등이 발생하지 않아야 한다. 이에 대한 대책으로 부재 외면에 내화모르타르로 마감을 하는 것이 가장 효율적인 방법이다. 내화 마감모르타르는 고온에서 강도변화가 작고 열적으로 안정하며 열전도율이 낮은 경량재료라면 효과적으로 성능발현이 가능할 것이다. 본 연구는 내화 마감모르타르 개발을 위한 연구로 비교적 내화성능이 우수한 플라이애시 및 메타카올린 기반의 알칼리 활성화 결합재와 펄라이트 및 유리 발포 경량골재의 고온 특성에 대해 검토하였다. 실험결과 열전도율이 낮고 고온에서 비교적 안정적인 특성을 발현하여 내화 마감모르타르로 적용이 가능할 것으로 판단된다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.261-264
• /
• 2004

In this study, the experiment was carried out to investigate and analyze the strenth properties and flowability of ultra-high strength concrete accroding to types of mineral admixtures and cements. The main experimental variables were water/binder ratio $25.0\%$, water content $160kg/m^3$ and mineral admixtures such as fly ash, silica fume and meta kaolin. According to the test results, the principle conclusions are summarized as follows 1) In case of using admixtures, superplasticizer amount need more than plain concrete. 2) According to kinds of admixtures and cements, the viscosity of concrete show much difference. 3) The autogeneous shrinkage of ultra-high strength concrete is profitable that use admixture, and heat of hydration is desirable that apply considering countermeasure enough in the advance. 4) Meta kaolin is excellent in side but has viscosity enlargement efficiency a little. But, problem estimates that is not to make design strength to and $70N/mm^2$ if use mixing condition with water-binder ratio properly.

• 한국건설순환자원학회논문집
• /
• 제10권3호
• /
• pp.252-260
• /
• 2022

국내에서 카올린 순도가 낮은 저품질의 고령토는 고순도의 고령토보다 월등히 많은 매장량과 우수한 경제성에도 불구하고 제품으로 활용되지 못하고 대부분 사장되고 있다. 본 연구의 목적은 국산 저품질 고령토를 석회석 소성점토 시멘트(LC³)의 원료로 활용할 수 있는 가능성과 최적의 소성온도를 도출하는 것으로, 고령토의 소성온도(600 ℃, 700 ℃, 800 ℃, 900 ℃)에 따른 LC³ 페이스트의 수화물 생성과 기계적 특성을 평가하기 위해 등온 열량 측정, X-선 회절 분석, 열 중량 분석 및 압축강도 시험을 실시하였다. 결과적으로 국산 저품질 고령토 점토는 클링커의 50 %를 대체하였음에도 불구하고 수화 3일차부터 메타카올린의 포졸란 반응에 의해 카르보알루미네이트 수화물과 C(A)SH를 생성하여 OPC와 거의 동등하거나 그 이상의 강도를 나타냈으며, 소성온도에 따라 강도발현에 큰 차이가 발생하는 것으로 나타났다.

• 한국해양공학회지
• /
• 제26권3호
• /
• pp.26-32
• /
• 2012

Recently, concrete using multicomponent blended cement has been required to increase the freeze-thaw and sulfate resistances of concrete structures exposed to a marine environment. Thus, the purpose of this study was to propose the use of concrete containing multicomponent blended cement as one of the alternatives for concrete structures exposed to a marine environment. For this purpose, batches of concrete containing ordinary portland cement (OPC), binary blended cement (OPC-G, G: ground granulated blast slag), ternary blended cement (OPC-GF, F: fly ash), and quaternary blended cement (OPC-GFM, M: mata-kaolin) were made using a water-binder ratio of 50%. Then, the durability levels, including thesulfate and freeze-thaw resistances, were estimated for concrete samples containing OPC, OPC-G, OPC-GF, and OPC-GFM. It was observed from the tests that the durability levels of the concrete samples containing OPC-G and OPC-GF were found to be much better than that of the concrete containing OPC. The optimum mixing proportions were a40% replacement ratio of ground granulated blast slag for the binary blended cement and a30% replacement ratio of ground granulated blast slag and 10% fly ash for the ternary blended cement.

• 한국구조물진단유지관리공학회 논문집
• /
• 제17권3호
• /
• pp.89-96
• /
• 2013

1990년대 후반부터 사용된 폴리머 콘크리트로 제작된 맨홀은 이 맨홀이 가지고 있는 다양한 장점 때문에 현재까지 널리 이용되고 있다. 그러나, 고유가 시대로 접어들면서 석유화학 재료의 가격인상과 더불어 폴리머 콘크리트의 제조원가가 상승되고 이에 따른 폴리머 콘크리트의 약점이 대두되고 있다. 따라서, 고가의 폴리머 콘크리트로 제작된 맨홀의 뛰어난 휨강도를 대체할 수 있는 경제적인 시멘트 콘크리트 맨홀의 개발이 요구되어 왔다. 본 연구에서는 비정질 칼슘알루미네이트 (Armorphous calcium aluminate, ACA)계의 속경형 시멘트기술을 기반으로 플라이 애쉬와 고로슬래그, 실리카 퓸, 메타카올린 등의 산업부산물을 이용하여 시멘트의 사용량을 최소화시킴으로써 $CO_2$를 저감시킬 수 있는 친환경적인 맨홀용 고인성 콘크리트를 개발하고자 하였다. 연구결과, 경제적이고 친환경적이면서도 요구성능을 만족시키는 시멘트 콘크리트 맨홀을 개발하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.409-412
• /
• 2008

콘크리트는 골재, 시멘트와 물이 주 구성성분이나 성능 및 내구성 향상으로 고품질화, 현장작업의 능률향상, 운반, 경제성 등의 목적을 위하여 다양한 형태의 혼화재료가 사용되고 있다. 특히, 혼화재가 시멘트 대체재로 사용되면서 콘크리트의 고강도화, 내구성 증진, 수화열 감소 등의 효과를 얻고 있다. 그러나, 이러한 혼화재를 사용함에 있어 성능평가 및 기준이 아직 국내에서는 정립되지 않고 있어 현장의 품질관리를 위해 현재 많이 사용되고 있는 플라이애쉬, 실리카 흄, 고로슬래그 미분말, 최근 환경 친화성이 우수한 혼화재료인 메타카올린 등을 적용한 2성분계 콘크리트의 물-결합재비 및 혼입율에 따른 역학적 특성에 대한 검토가 필요한 실정이다. 따라서, 본 연구에서는 현재 많이 사용하고 있는 혼화재중 고로슬래그의 중성화 특성을 확인하고자 고로슬래그 미분말을 사용한 60MPa${\sim}$80MPa의 고강도 콘크리트를 제작하여 물결합재비 26%, 30%, 34%의 변수와 고로슬래그 미분말 치환율을 30%, 45%, 60%로 달리하여 강도 및 중성화 시험을 실시 하였으며 X선 회절분석(XRD, X-Ray Diffraction)을 이용하여 화학 조성물 성분변화를 분석하였다.

• 한국건축시공학회지
• /
• 제10권1호
• /
• pp.147-153
• /
• 2010

폐콘크리트를 굵은 골재의 대체 재료로 재활용하게 되면, 건설폐기물의 증가위기와 천연골재의 고갈문제를 해결해 줄 수 있다. 그러나 순환골재는 콘크리트용 골재의 품질보다 저하되는 경향이 있기 때문에, 이를 개선하여 콘크리트 재료로 활용해야 한다. 순환골재 콘크리트의 내구성에 관한 논문은 부족한 실정이므로, 본 연구에서는 염화물 확산계수에 의해 포졸란재를 혼입한 순환골재 콘크리트의 염화물 확산성에 대한 기초적인 자료를 제시하는데 그 목적이 있다. 주요 결과로는 다음과 같다. 1) 재령에 따라 포졸란재를 혼입한 순환골재 콘크리트의 압축강도가 증가하였으며, 염화물 확산성은 감소하였다. 2) 모든 재령에서, 순환굵은골재의 치환율이 30%인 경우 고로슬래그 및 메타카올린을 혼입한 순환골재 콘크리트의 염화물 확산계수는 플레인 콘크리트와 유사하거나 더 낮은 결과를 나타내었다.