The purpose of this research was to evaluate on the properties of fresh and hardened high-performance concrete(HPC) incorporating high-reactivity metakaolin(HRM). Setting time, heat of hydration, compressive strength, resistance to chloride-ion penetration, and repeated freezing and thawing test were carried out in order to investigate the properties of fresh and hardened state concrete. The properties of the HRM concrete were also compared with those of the portland cement concrete and silica fume(SF) concrete. The laboratory test results indicate that HRM material can be used as a supplementary cementitious material to produce high-performance concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.639-642
• /
• 2005

Main components of metakaolin(MK) were $SiO_2\;and\;Al_2O_3$. and specific surface was 2.2 times larger than that of ordinary portland cement(OPC). MK indicated the fine particle and fiber texture. Flow value of mortar with MK was decreased linearly each $13\%$ as the replacement ratio of MK was increased each $5\%$. Compressive strength of mortar with MK was increased more than that of mortar with OPC by 3days. Compressive strength of mortar with $10\%$ MK was about 83MPa at 28 days. When MK was replaced with $10\%$ of cement volume, flexural strength and modulus of elasticity of mortar was indicated the maximum value at 28 days.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.23-26
• /
• 2003

Metakaolin is a cementitious material for producing high-strength concrete. This material is now used as substitute for silica-fume. In this paper, we studied the properties of fresh concrete such as slump-flow, air content, and the feature of strength of hardened concrete according to the substitute ratio of metakaolin, silica-fume. In the fresh concrete test, the time depend loss of slump-flow & air content is good to 10-15% substitute ratio of metakaolin. And, in the strength test, 10-15% substitute ratio of metakaolin is good for producing high-strength concrete also. But, allowing for economical efficiency, we concluded that 10% is a adequate substitute ratio for producing high performance concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.47-52
• /
• 2003

This study was performed to investigate the flow behavior of fresh concrete. strength properties, and durability properties on the chloride penetration resistance of hardened concrete containing Meta-Kaolin(MK) in the range from common strength to high strength to facilitate the use. The results are compared with properties of concrete containing Si1ca Fume(SF). As a result. superplasticizer required in MK concrete was decreased by 8-28% compared to SF concrete with the same slump, but MK concrete became more sticky than SF concrete. It was also found that considering the strength, the optimal cement replacement ratio of MK was 15%, and MK had concrete durable and dense by decreasing the average pore diameter of concrete.

• 한국농공학회논문집
• /
• 제50권5호
• /
• pp.51-60
• /
• 2008

This study is to relate the bond characteristics of CFRP rebar in high strength concrete incorporated with silica fume(SF) and metakaolin(MK). An direct bond test were performed to evaluate the effect of SF and MK on bond properties of high-strength concrete and CFRP rebar. The high strength concrete mix included four SF and MK mixes with 0%, 5%, 10% and 15%. Results of bond performance experiment in relation to pullout vs slip behavior of FRP rebar and high strength showed better performance of SF than MK. Also, the results showed the improved bond strength as replacement ratio of SF and MK increased. The relative bond strength in which $1.3{\sim}3.2$ of estimated values were obtained.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.433-436
• /
• 2005

The Fly-ash makes an Alumino-silicate gel when it mixes an alkali or a silicate solution. This Alumino-silicate gel is produced to the activation of an alkali silicate. And this act to the binder and makes a combine of particles. This study involved mechanical strengths of an Alumino-silicate Gel based the Fly-ash with an alkali solution. NaOH, KOH were utilized to an alkali solution. The alkali solution concentration was varied from 6 to 12M and the some added also the Meta-kaolin, Waterglass so that it made high the mechanical performance. Based on the experimental result, the compressive strengths increased as the quantity of the Meta-kaolin increased. And a mechanical strengths appeared according to the concentration of an alkali solution so that it was different. XRD, FT-IR have been used to characterize mechanical performance.

• 한국농공학회논문집
• /
• 제54권5호
• /
• pp.9-16
• /
• 2012

In this study, the effect of metakaoline and silica fume on the bond performances of structural polyvinyl alcohol (PVA) fiber in cement mortar, including bond strength, interface toughness, and microstructure analysis are presented. Metakaoline and silica fume contents ranging from 0 % to 15 % are used in the mix proportions. Pullout tests are conducted to measure the bond performance of PVA fiber from cement mortar. Test results showed the incorporation of metakaoline and silica fume can effectively enhance the PVA fiber-cement mortar interfacial properties. Bond strength and interface toughness increased with metakaoline and silica fume content up to 10 % in cement mortar and decreased when the metakaoline and silica fume content reached 15 %. The microstructural observation confirms the findings on the interface bond mechanism drawn from the fiber pullout test results.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.211-212
• /
• 2021

This study was conducted to derive quantitative air void volume calculation techniques in various complexes with porosity. Calculation of voids in a complex is an essential factor in improving mechanical properties, and quantitative measurement techniques are needed because the environment is not constant to apply the currently used ASTM criteria. Using the analysis technique obtained through 2D image analysis, it is believed that meaningful results can be derived through Micro CT analysis results and cross-check later.

• 콘크리트학회논문집
• /
• 제17권1호
• /
• pp.129-137
• /
• 2005

최근 양질의 하천골재가 고갈상태에 직면함에 따라 쇄석 골재의 사용이 보편화되고 있지만 쇄석 골재 사용으로 야기될 수 있는 알칼리-실리카 반응에 대한 문제를 검토하지 않은 채 콘크리트 재료로 사용하고 있는 실정이다. 알칼리-실리카 반응은 콘크리트에 유해한 팽창을 일으키는 작용으로서, 반응결과 알칼리-실리카 겔이 형성되고 이러한 겔이 수분을 계속 흡수함으로써 체적 팽창을 일으켜 콘크리트에 균열이 발생된다. 골재의 알칼리-실리카 반응성을 판정하는 방법은 암석학적 판정법, 화학법 및 모르타르 바 법이 일반적으로 사용되지만, 이 중에서 모르타르 바 법이 비교적 신뢰성이 높다. 본 연구에서는 모르타르바 시험방법 중 ASIM C 227과 ASIM C 1260을 선택하여 암석 유형별로 수집한 12종의 골재들을 대상으로 쇄석 골재의 반응성을 비교, 분석하였다. 또한 본 연구에서는 반응성 골재의 입자크기 및 입도가 모르타르 바의 알칼리-실리카 반응 팽창에 미치는 영향에 관하여 검토하였다 혼화재의 용도는 상당히 많지만 본 연구에서는 쇄석 골재 사용으로 문제되고 있는 알칼리-실리카 반응에 있어서 플라이애쉬, 고로슬래그미분말, 실리카퓸 및 메타카올린을 혼화재료로 사용할 경우 알칼리-실리카 반응에 미치는 영향을 알아보고자 시멘트에 대한 혼화재의 치환율을 달리하여 ASTM C 1260 시험법으로 알칼리-실리카 반응에 대한 팽창 저감효과를 평가하여 보았다. 본 연구에서는 혼화재의 치환율을 0, 5, 10, 15, 25 및 $35\%$로 하였으며, 모르타르 유동성 시험을 병행하여 어느 정도의 유동성을 갖는 혼화재는 45, $55\%$까지 치환율을 증가하여 길이변화 시험을 수행하였다. 시멘트 중량에 대한 혼화재 치환율이 플라이애쉬는 $25\%$, 실리카퓸은 $10\%$, 메타카올린은 $25\%$, 고로슬래그미분말은 $35\%$일 경우 알칼리-실리카 반응에 의한 팽창을 가장 효과적으로 방지할 수 있는 것으로 판단된다.

• 콘크리트학회논문집
• /
• 제21권2호
• /
• pp.179-186
• /
• 2009

고강도콘크리트의 취약점으로 지적되고 있는 화재시의 폭렬현상에 대한 대책을 마련하기 위해 각 계의 노력이 활발한 현 상황에서 각종 폭렬 저감성 재료 및 새로운 개념의 소재에 대한 적정 혼입비율을 구명해야 하는 긴요한 상황이다. 본 연구에서는 메타카올린, 페타이어칩, 폴리프로필렌섬유 및 강섬유의 4가지 기능성 소재를 대상으로, 기본적인 품질 요건은 물론, 내화성능에 최적의 효과를 나타낼 수 있는 배합비를 실험적, 통계적으로 도출하고자 하였다. 여기서, 실험은 4인자 3수준의 직교배열표를 이용하여 최소실험법으로 계획하고, 통계적 분석은 반응표면분석 기법을 이용하였다. 그 결과, 80 MPa급 고강도콘크리트의 내화성능 보강인자로 선정된 기능성 소재간에는 복합 사용시 상호 보완적인 기여를 하는 것으로 확인되었다. 한편, 반응표면분석을 통해 도출한 내화성능 보강인자의 최적조건은 메타카올린을 실리카퓸 대신 80% 수준으로 용적치환하고, 폐타이어칩은 잔골재 대신 3% 수준으로 용적치환하는 경우와 폴리프로필렌 섬유를 전체용적에 대하여 0.2% 수준으로 첨가하는 한편, 강섬유를 혼입하지 않는 것이 고강도콘크리트의 기초 특성과 내화특성을 고루 만족할 수 있는 것으로 분석되었다.