• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.192-192
• /
• 2013

하이브리드 표면처리는 다른 표면처리법을 동시 또는 연속적으로 행하여 단일표면처리에 비해 더욱 우수한 특성을 부여시키기 위한 표면처리법이다. 본 연구는 붕소와 질소 원소를 이용한 하이브리드 표면처리를 오스테나이트계 스테인리스강인 STS 316L 소재에 적용하여 변화된 특성을 평가하였다. 본 실험에 사용된 하이브리드 표면처리법으로는 붕소분말을 이용한 보로나이징처리와 활성스크린을 이용한 이온질화처리법을 적용하였다. 하이브리드 표면처리된 STS 316L시편은 FE-SEM을 이용하여 표면형상 및 단면조직을 관찰하였으며 GDS와 XRD를 이용하여 깊이에 따른 원소 및 상분석을 실시하였다. 또한 마이크로비커스 경도계와 마모시험기를 이용하여 경도와 마모특성을 측정하였고, 염수분무시험을 통하여 해수환경에서 부식거동을 평가하였다.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.6
• /
• pp.78-88
• /
• 2000

The effect of post-weld heat treatment(PWHT) of SCM440 steel was investigated with parameters such as micro-Vickers hardness, corrosion potential, polarization behaviors, galvanic current, Al anode generating current and Al anode weight loss, etc. Each hardness of three parts(HAZ, BM, WM) by PWHT is lower than each of as-welded parts. However, hardness of WM area was the highest among those three parts in case of both PWHT and as-welded. Corrosion potential of WM part was the highest among those three parts and WM area was also acted as cathode without regard to PWHT. The magnitude of corrosion potential difference among three parts by PWHT was larger than that of three parts of as-welded, and corrosion current by galvanic cell of these three parts by PWHT was also larger compared to as-welded. Therefore, it is suggested that corrosion resistance property of SCM440 steel is decreased by PWHT than as-welded. However, both Al anode generating current and anode weight loss were also increased by PWHT compared to as-welded when SCM400 steel is cathodically protected by Al anode.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.6
• /
• pp.763-769
• /
• 2010

In recent times, there has been considerable interest in HIPS (High Impact Polystyrene) materials for their use in construction of office equipments, home electronics, housing for electronics appliances, packing containers, etc. However, these materials suffer from problems caused by fatigue fracture. Further, their strength is substantially affected by environmental conditions. Therefore, in this study, the effect of temperature was analyzed by performing a tensile test and a fatigue test. It was observed that the yield strength, the ultimate strength, and the fatigue life decreased relatively with an increase in temperature. Further, an S-N curve can be predicted by using the results of the tensile test and a micro-Vickers hardness test.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.797-801
• /
• 2003

The mechanical properties such as shear strength and the hardness of milli-size products that manufactured for various process parameters by forward extrusion using square dies are investigated. Shear strength test is implemented for the observation of relation between vickers hardness and shear strength in the interface of head and shaft part of a stepped pin. When the extrusion ratios of pure aluminum and pure copper billets increase, the hardness on both the surface and the center line of a pin also increase, especially the hardness on the surface is shown to be a little higher than on the center. The existence of knock-out pad in extrusion die caused hardness increase in the interface of a extruded pin. As compared shear strength with hardness of a pin, the approximated linear relations are suggested in this study.

• Journal of Ocean Engineering and Technology
• /
• v.16 no.6
• /
• pp.60-64
• /
• 2002

This paper describes the machining characteristics of the MoSi$_2$--based composites through the process of electric discharge drilling with various tubular electrodes. In addition to hardness characteristics, microstructures of Nb/MoSi$_2$laminate composites were evaluated from the variation of fabricating conditions, such as preparation temperature, applied pressure, and pressure holding time. MoSi$_2$-based composites have been developed in new materials for jet engines of supersonic-speed airplanes and gas turbines for high-temperature generators. These high performance engines may require new hard materials with high strength and high temperature-resistance. Also, with the exception of grinding, traditional machining methods are not applicable to these new materials. Electric discharge machining (EDM) is a thermal process that utilizes a spark discharge to melt a conductive material. The tool electrode is almost -unloaded, because there is n direct contact between the tool electrode and the work piece. By combining a non-conducting ceramic with more conducting ceramic, it was possible to raise the electrical conductivity. From experimental results, it was found that the lamination from Nb sheet and MoSi$_2$ powder was an excellent strategy to improve hardness characteristics of monolithic MoSi$_2$. However, interfacial reaction products, like (Nb, Mo)SiO$_2$and Nb$_2$Si$_3$formed at the interface of Nb/MoSi$_2$, and increased with fabricating temperature. MoSi$_2$composites, with which a hole drilling was not possible through the conventional machining process, enhanced the capacity of ED-drilling by adding MbSi$_2$, relative to that of SiC or ZrO$_2$reinforcements.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.21-25
• /
• 2007

In this study, the properties of Sn-0.7wt%Cu-Xwt%Re(X=$0.01{\sim}1.0$) older were investigated by using DSC(differential scanning calorimetry), wetting balance, victors hardness and tensile testers. The melting temperature of solder was increased with increasing the contents of rare earth element, and the melting temperature range of Sn-0.7Cu-($0.01{\sim}1.0$)Re solder was $233.9{\sim}234.7^{\circ}C$. The wettability with Sn-0.7Cu-0.1Re solder was higher than that of Sn-0.7Cu-0.01Re and Sn-0.7Cu-1.0Re solders, and the wettability of Sn-0.7Cu-0.1Re solder was higher than that of Sn-0.7wt%Cu-0.01w%P solder. Also, the hardness and tensile strength of solder were increased with increasing the contents of rare earth element.

• Journal of Advanced Marine Engineering and Technology
• /
• v.38 no.9
• /
• pp.1087-1093
• /
• 2014

Stainless steels stabilized with Ti or Nb are largely used in offshore and shipbuilding industries due to its excellent corrosion resistance. In this study, carbide stabilizers, Ti and Nb, were added to stainless steel 304 specimens with different concentrations(Ti: 0.26%, 0.71%, Nb: 0.29%, 0.46%, 0.71%), and their mechanical and electrochemical characteristics were evaluated. Micro-Vickers hardness testing was employed to characterize the mechanical characteristics with alloying elements. Electrochemical evaluation techniques including Tafel analysis, cyclic polarization experiment, galvanostatic experiment were utilized to compare the corrosion characteristics of the specimens. The result of hardness tests revealed that Nb containing specimens showed increasing hardness with increasing alloying contents while adding Ti had little effect on increase in hardness. In the case of electrochemical measurements, the electrochemical characteristics of the specimens were enhanced with increasing Nb contents while they were deteriorated with increasing Ti contents. As a result, different stabilizers and their contents may produce significant differences in electrochemical characteristics, and there such effect must be taken account of in development of stainless steels for marine environment.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.22 no.1
• /
• pp.138-144
• /
• 2016

Titanium is resistant to general corrosion and in sea water because of the passivity layer film on the surface of material, but may be attacked by environments that cause breakdown of the protective oxide layer including hydrochloric, sulfuric and phosphoric acids. In this study, the Ti alloys were solution heat treatment 5hours at $1066^{\circ}C$ and $966^{\circ}C$, and followed by aging heat treated, 1, 4, 8 and 16 hours in $500^{\circ}C$, $600^{\circ}C$ and $650^{\circ}C$ respectively. The heat treated specimens were measured micro Vicker's hardness, and then accomplished electrochemical polarization test for comparing corrosion in 1N sulfuric acid solution. Additionally, micro structures were taken for corrosion tested specimens. The results showed that corrosion resistance was higher in solution heat treated alloy than base and age heat treated metal. Measured corrosion resistants were increased as increasing aging heat treatment time and temperature.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.34 no.3
• /
• pp.220-225
• /
• 2014

Generally, the nonlinearity of ultrasonic waves is measured using a nonlinear parameter ${\beta}$, which is defined as the ratio of the second harmonic's magnitude to the power of the fundamental frequency component after the ultrasonic wave propagates through a material. Nonlinear parameter ${\beta}$ is recognized as an effective parameter for evaluating material degradation. In this paper, we evaluated the nonlinear parameter of Al6061-T6 which had been subjected to an artificial aging heat treatment. The measurement was using the transmitted signal obtained from contact-type transducers. After the ultrasonic test, a micro Vickers hardness test was conducted. From the result of the ultrasonic nonlinear parameter, the microstructural changes resulting from the heat treatment were estimated and the hardness test proved that these estimates were reasonable. Experimental results showed a correlation between the ultrasonic nonlinear parameter and microstructural changes produced by precipitation behavior in the material. These results suggest that the evaluation of mechanical properties using ultrasonic nonlinear parameter ${\beta}$ can be used to monitor variations in the mechanical hardness of aluminum alloys in response to an artificial aging heat-treatment.

• Journal of the Korean Society for Railway
• /
• v.13 no.4
• /
• pp.447-454
• /
• 2010

The defects of rail head induced by fatigue and deterioration are mainly classified by two types ; one occurred on the surface of rail head the another occurred on the inner rail head. This study performed the surface irregularity measurement of rail head according to the passing tonnage in the urban railway. Also, we carried out microscopic structure test, chemical component test and micro-hardness test for the specimen which is the used rail on metro line by accumulated passing tonnage. As a result of this study, for new rail, it should be performed initial grinding in order to remove 0.3mm of de-carbonized layer. The preventive-cyclic grinding for preventing RCF defects is proposed two options : grinding by the whole line and grinding by specified sections.