• Elastomers and Composites
• /
• v.34 no.5
• /
• pp.414-422
• /
• 1999

SBR, polyurethane and epoxy latex were separately blended with ethylene-vinyl acetate(EVA) emulsion In $0{\sim}50%$. EVA emulsion was not reacted with latexes in liquid phase and mixtures had good stroage stability. The viscosity of cement mixtures was elevated to 20,000cps in $0.5{\sim}2.0$ hours by mixing. The mixtures mixed with pigment represented high viscosity and showed higher viscosity as time goes by. Mixtures had higher hardness with mixing SBR than mixing epoxy or urethane. The hardness was suddenly increased over cement content 30%. showed pencil hardness $H{\sim}2H$ in $50{\sim}60%$. The increase of hardness in high solids was depended upon not only the condensation of latexs but also the coagulation and adhesion of cement particle.

• Elastomers and Composites
• /
• v.33 no.3
• /
• pp.149-158
• /
• 1998

SBR latex, polyurethane latex and epoxy latex were separately mixed with polyvinyl acetate emulsion. The various physical properties were examined for the mixtures. Epoxy mixtures gave a transparent film. Both polyurethane and SBR mixtures showed opaque film with high viscosity. In SBR and polyurethane increase in hardness was dependent on the evaporation rate of water, but in epoxy it was dependent on the degrees of crosslink. Epoxy's showed excellent water-resistance. SBR showed a good flexural strength and impact strength. When vinyl acetate emulsion was mixed with less than 10% latex paper tube showed the ductile fracture, but over latex content 20%, it showed the brittle fracture.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.283-284
• /
• 2010

This study was evaluated the mechanical and physical performance of ultra rapid hardening roller compacted concrete. Mix proportion were compared with mix proportion without latex about mechanical and physical performance. The test results showed that mix proportion with latex presented excellent performance due to pore filling effect of latex for unification behavior.

• Resources Recycling
• /
• v.15 no.2 s.70
• /
• pp.10-17
• /
• 2006

The purpose of this study was to evaluate the effects of blast-furnace slag on strength development and durability of latex-modified concrete (LMC) and ordinary portland cement concrete as slag contents. Main experimental variables were performed latex contents (0%, 10%, 15%) and slag contents (0%, 30%). The compressive and flexural strengths, chloride-ion rapid permeability and chemical attacks resistance were measured to analyze the characteristic of the developed LMC and BS-LMC(latex-modified concrete added blast-furnace slag) on hardened concrete. The test results showed that compressive and flexural strength of BS-LMC increased as the slag contents increased from 0% to 30% at the long term of curing. It considers blast furnace slag used when latex content was up to 10%. The permeability resistance of BS-LMC(latex 10%, blast 30%) was extremely good at the curing time 90 days. Also. the effects of added blast furnace slag on OPC and LMC were increased on the permeability and chemical attacks resistance.

• Resources Recycling
• /
• v.17 no.5
• /
• pp.11-18
• /
• 2008

The purpose of this study was to evaluate the effects of blast-furnace slag on chemical attack and carbonation of latex-modified concrete (LMC) and ordinary portland cement concrete as slag contents. Main experimental variables were performed latex contents (0%, 15%) and slag contents (0%, 30%, 50%). The compressive strengths, chemical attacks resistance and carbonation depth were measured to analyze the characteristic of the developed LMC and BS-LMC(latex-modified concrete added blast-furnace slag) on hardened concrete. The test results showed that compressive strength of BS-LMC with blast-furnace slag content 30% was quite similar to it of OPC without slag content. The structural quality deterioration was concerned when blast slag content was up to 50%. However, carbonation restraint of BS-LMC with blast-furnace slag 30% was bigger then that of opc. Also, the effects of added latex on OPC and BS-LMC were increased on the carbonation restraint and chemical attacks resistance.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.6
• /
• pp.1743-1751
• /
• 2014

It is well known that latex modification can lead to enhancement compressive and flexural performance, tensile bond strength, chloride penetration resistance and freezing-thawing resistance for concrete. For these, many studies for LMC pavement have been widely conducted more than those for conventional pavement concrete. However, due to several problems such as noise and construction cost, new approaches for LMC have been executed to improve the performance of LMC. Recently, Remicon LMC was developed in order to solve the problems of LMC. In this study, the durability of Remcion LMC was compared with latex and mineral additive mixing ratio. From the results, when latex and mineral additive were mixed in Remicon LMC, compressive, flexural and bond strength were satisfied with Korea Highway Construction Guide Specification. And, it showed that the qualitative effect of latex and mineral additive mixing ratio on the durability of Remicon LMC was investigated experimentally. Also, the latex mixed in Remicon LMC must be at least 8%, in order to ensure the durability equivalent or higher than conventional LMC.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.1A
• /
• pp.205-211
• /
• 2006

The purpose of this study was to evaluate the effects of fly-ash on strength development and durability of latex-modified concrete (LMC) and ordinary portland cement concrete (OPC). Main experimental variables were latex contents (0%, 10%, 15%) and fly-ash content (0, 10%, 20%, 30%). Air content and slump tests were performed to check the basic properties of fresh concretes, and compressive strength, flexural strength, rapid chloride ion permeability and chemical resistance were measured to analyze the basic properties of hardened concretes. The test results showed that air contents of LMC with fly ash decreased as fly-ash contents increased from 0% to 30%. Compressive and flexural strength developments of LMC with fly ash were quite similar to those of LMC without fly ash. However, the long-term flexural strength development of LMC with fly ash after 90 days were bigger than that of LMC without fly ash. Chloride ion permeability and chemical resistance decreased rapidly as the content of fly ash increased. Thus, fly ash could be used at LMC in order to reduce water permeability.

• Korean Chemical Engineering Research
• /
• v.50 no.5
• /
• pp.789-794
• /
• 2012

For the purpose of development of the latex suitable for polymer cement mortar, experiments on the preparation of carboxylated styrene butadiene latex by the method of the two-step emulsion polymerization were performed. Methyl methacrylate, methacrylic acid and acrylic acid were selected as carboxylic co-monomer, styrene and butadiene as monomer, sodium dodecylbenzene sulfonate and sodium salt of lauryl sulfonate as anionic emulsifiers, and nonylphenoxy poly (ethyleneoxy) ethanol (n=10, 20, 40) as latex stabilizer. Potassium persulfate and sodium bisulfite were also used as redox initiator, and sodium monohydrogen phosphate and potassium carbonate as electrolytes. The effects of categories and concentration of carboxylic co-monomer, molecular weight control agent, crosslinking agent, and styrene/butadiene monomer ratio on the characteristics of latex were investigated. Polymerization recipes for preparation of polymer cement mortar could be proposed. The prepared latexes were tested for the physical properties such as compressive and flexural strength when latexes were mixed with cement mortar. The results showed that the latex could be adapted to polymer cement mortar. Also, it was recognized that the compressive and flexural strength were exhibited 25.4% and 45.3% respectively higher improvement than the quality standards at 28 days curing time.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.3
• /
• pp.73-81
• /
• 1999

This paper was intended to evaluate the effect of the blending condition of pigments on the packing structure of coating color and the interaction between pigments and latices on the optical and interior properties of coated paper. It has been studied many ways to modify the coating structure to induce the interaction among coating components as followings ; 1) to use dispersant for pigment, 2) to control the charge density and the type of surface charge of latex, 3) to support the water retention by adding water retention agent or flow modifier. This paper was performed through the introduction of interaction between pigments which were two kinds of clays and one precipitated calcium carbonate(PCC) and ionic latices of which anionic and amphoteric respectively under the certain blending condition of pigments where their blending ratio of clays to calcium carbonate was 70pph to 30pph. The reason is that packing volume of pigments was highest in that region and thixotropical behavior appears in measuring rheology of coating color. We measured the properties of coating color, interaction with pigments and latex, and properties of coated paper and its printability. As a results, we could find out that amphoteric latex had a great influence on the interaction with pigments, especially clays, no matter what grade and also affected the coating structure significantly in case that this blending condition was 70(clays) to 30(PCC). It produced a powerful effect on the forming of bulky and smooth coating structure and in turn improved the printability of coated paper.

• Membrane Journal
• /
• v.6 no.3
• /
• pp.166-172
• /
• 1996

For the preparation of polybutadiene latexes with suitable particle size, membrane e$$\mu$sification, which is capable of easy and uniform control of particle size, was used in this study. The parameters were the type and amount of surfactants, amount of additive and pressure. Particle size and distribution of prepared latexes were measured and compared with those of e$$\mu$sion prepared by homogenizer. To investigate the membrane e$$\mu$sification mechanism, theoretical drop size was calculated by Harkins-Brown equation. When the amount of surfactant with more than 0.2 wt%(based on DDI water) was added in the continuous phase, the stable e$$\mu$sion was prepared. Other parameters showed little relationship with particle size and distribution. In this membrane e$$\mu$sification, the essential factor for determining the particle size was the pore size of the membrane.