• 산업기술연구
• /
• 제25권A호
• /
• pp.49-56
• /
• 2005

Recently, very-early strength latex-modified concrete(below ; VES-LMC) has been developed for repairing and overlaying the old concrete bridge deck. VES-LMC provides the advantage of very-early-strength, as well as high flexural strength, bond strength, durability, resistance to corrosion, reduced water permeability and resistance to damage from freeze-thaw cycles. The compressive and flexural strength of VES-LMC are 21 MPa and 4.5 MPa at 3 hours after concrete placing, respectively. However, VES-LMC would have a relatively large shrinkage at early-age because of reduced water-cement ratio, big water self-dissipation, and rapid hydration reaction. Therefore, the purpose of this study was to evaluate the early-age and restrained shrinkage of VES-LMC, having an experimental variables such as latex contents and cement types. The latex contents included 0%, 5%, 10%, 15% and 20%, and the cement types included ordinary portland cement and very-early strength cement.

• 콘크리트학회논문집
• /
• 제14권3호
• /
• pp.402-408
• /
• 2002

본 연구에서는 SBR 라텍스 및 재유화형 EVA 분말수지를 혼입한 투수성 폴리머 시멘트 콘크리트를 제조하여 투수성 폴리머 시멘트 콘크리트의 공극률, 투수계수, 강도 및 동결융해 저항성에 미치는 폴리머-시멘트비의 영향을 구명하였다. 그 결과, 투수성 폴리머 시멘트 콘크리트의 공극률, 연속공극률 및 투수계수는 폴리머-시멘트비의 증가에 따라 감소하는 경향을 보였으며, 압축, 인장 및 휨강도는 폴리머-시멘트비의 증가에 따라 증가하였다. 또한 투수성 폴리머 시멘트 콘크리트의 동결융해 저항성 역시 폴리머의 혼입에 따라 증진되었다. 이와 같은 효과는 폴리머의 혼입에 의해 시멘트 수화물과 골재간의 접착성이 개선되기 때문이라 판단된다.

• 콘크리트학회논문집
• /
• 제14권3호
• /
• pp.315-320
• /
• 2002

본 연구에서는 고로슬래그 미분말을 이용한 SBR혼입 폴리머 시멘트 콘크리트의 강도 성상에 미치는 고로슬래그 치환율 및 폴리머 결합재비의 영향에 대하여 구명하였다. 그 결과, 고로슬래그 미분말을 이용한 SBR혼입 폴리머 시멘트 콘크리트의 압축, 인장 및 휨강도는 폴리머-결합재비 및 고로슬래그 치환율의 증가에 따라 증가하였으며, 고로슬래그 치환율 40%에서 가장 높은 강도를 나타내었다. 특히 고로슬래그 치환율 40%의 SBR혼입 폴리머 시멘트 콘크리트의 인장 및 휨강도는 폴리머 미혼입의 강도보다 약 2배 이상의 높은 강도를 보였다. 이와 같이 높은 강도의 발현은 SBR 폴리머의 높은 인장강도와 SBR라텍스의 혼입에 의한 시멘트 수화물과 골재간의 접착성이 개선되었기 때문이라 판단된다.

• KSBB Journal
• /
• 제8권4호
• /
• pp.320-327
• /
• 1993

스티렌/아크렬 라텍스 폴리머를 폴리에릴렌이민으 로 표면처 리하여 얻은 PEI-microspheres는 그 표면 화학적 특성이 효소의 고정화에 적합하여 배당체의 합성반응에 서 필요로 하는 alginate-enclosed micro­s spheres biocatalyst를 제조할 수 있었고 라텍스 폴리머 표변에 형성된 폴리에틸렌이민 피막은 효소 부근에 친수성 분위기를 유지하여 높은 효소활성을 나 타내었을 뿐만 아니라, 생성된 배당체가 효소에 접 근하여 가수분해되는 반응을 억제하여 배당체의 수 율과 농도를 크게 증가시 켰으므로 alginate-en closed microspheres에 의한 배당체의 합성반응이 연속생산공정으로 연구개발 될 수 있다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2009년도 추계 학술논문 발표대회
• /
• pp.179-182
• /
• 2009

Concrete containing styrene-butadiene latex is widely used, nowadays, as a protective system for bridge. Latex modification mortar have taken advantage of latex modification concrete advantage that is used in existing, Also, when repair, protection and sticking performance of concrete overlay waterproof agent were known as that are good. Replace and experimented from fine aggregate to recycled aggregate to secure economic performance than existing latex modification concrete. Recycled fine aggregate has low quality because it contains large amount of old mortar. So, its usage is limited to a lower value-add, such as the roadbed material etc. This study is purposed to improve the performance of mortar made of recycled fine aggregate. For this, recycled aggregate mortar was produced with latex, and fluidity, strength were examined. Test result indicate that mortar using recycled fine aggregate is higher compressive and flexural strength than mortar using river sand.

• 한국HCI학회논문지
• /
• 제10권2호
• /
• pp.57-64
• /
• 2015

본 논문은 문학비평에서 사용되는 파라텍스트라는 개념을 통해 모바일 혼합현실 기술의 가치와 의미, 속성을 새롭게 조명한다. 물리적 장소가 메인텍스트이자 고정된 체계인 '랑그(langue)'라면 일반 사용자들이 현장에 남기는 참여적 저작과 시공간적 흔적과 발화는 '빠롤(parole)'에 해당하며, 이들이 혼합된 모바일 혼합현실 스토리텔링을 파라텍스트로 보았다. 이에 대한 구현 가능한 방법과 미적 변용의 실험 및 응용들을 제시함으로써 모바일 혼합현실 공간의 파라텍스트 개념을 구체화했다.

• 대한건축학회논문집:구조계
• /
• 제35권5호
• /
• pp.153-160
• /
• 2019

The purpose of this study was to investigate the mechanical and durability characteristics of latex-modified concrete using ultra rapid hardening cement : four types of mechanical tests including compressive strength, modulus of elasticity, flexural strength and bond strength were performed; and seven types of durability tests including resistance of concrete to chloride ion penetration, freeze-thaw resistance, scaling resistance, coefficient of thermal expansion, cracking tendency, abrasion resistance and drying shrinkage were performed. Required material performance of each test was determined in accordance with the Korea specification for repair of concrete and pavement repairing materials. The test results satisfied the required material performances, and presented a good mechanical and durability characteristics. In particularly, the materials showed early development of compressive strength, flexural strength and bond strength at 3 and 4 hours after curing. SEM photos were also taken to investigate the micro structures of the materials after chloride ion penetration test.

• 콘크리트학회논문집
• /
• 제15권2호
• /
• pp.273-279
• /
• 2003

본 연구에서는 MMA/BA 합성 라텍스를 이용하여 폴리머 시멘트 모르타르의 성질에 영향을 미치는 모노머비의 효과를 검토하고, 시멘트 혼화용 폴리머로서의 개발적용을 위해 필요한 기초적 실험 데이터를 얻기 위한 것이다. 실험결과, MMA/BA모노 머비에 따른 폴리머 시멘트 모르타르의 세공경 분포는 MMA/BA의 비가 60 : 40, 70 : 30에서 미세공극량이 크게 증가했으며, 전세공용적은 감소하였다. 또한 모노머비에 관계없이 폴리머 시멘트 비가 증가할수록 그 효과는 더욱 커지는 것으로 나타났다. 일반적으로 MMA/BA 혼입 폴리머 시멘트 모르타르의 압축강도는 MMA 결합재량 70% 및 폴리머-시멘트비 15%에서 가장 우수하게 나타났으며, 흡수율과 염화물 이온 침투저항성은 MMA 결합재량보다는 폴리머-시멘트비에 의해 크게 지배되는 것으로 나타났다. 모노머비를 변화한 MMA/BA 합성 라텍스 혼입 폴리머 시멘트 모르타르의 성질에 영향을 미치는 중요한 인자는 MMA 결합재량의 변화에 의한 세공경분포의 변화와 폴리머-시멘트비로 나타났다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제22권2호
• /
• pp.68-75
• /
• 2018

본 연구에서는 기존의 균열보수 주입공법의 문제점을 해결하기 위하여 일반포트와는 다르게 중앙부에 높은 압력을 견딜 수 있도록 저장관의 재질은 고탄성 라텍스를 사용하였으며, 균열부위에 보수용액을 주입시 콘크리트 균열 내부에 존재하고 있는 공기가 배출될 수 있도록 TPS 공법을 개발 하였다. 또한 보수용액의 역류를 차단하는 밸브를 주입구에 설치한 새로운 주입식 포트를 개발하고 이에 대한 물리적 특성을 분석하였다. 분석 결과, 기존 주사기 공법에 비해 보수용액 주입속도가 향상되고, 시험조건에서 균열부위가 완전히 충전되는 것을 알 수 있었다. 보수 후의 품질은 압축강도 및 인장강도의 경우 주사기 공법 적용시에는 보수 후 약 20% 정도 저하하는 것으로 나타났고, TPS 공법 은 보수 후 강도가 오히려 약 2~7% 증가하는 경향으로 나타났다. 본 연구 결과를 통하여 탄성저장관을 사용한 주입식 포트 공법은 기존의 주사기 공법과 비교하여 주입성능 및 보수 후 품질이 증가하는 것을 알 수 있었고, 이를 활용하여 실구조물 적용 및 상용화를 위한 기반 자료로서 활용하고자 한다.

• 한국산학기술학회논문지
• /
• 제11권11호
• /
• pp.4635-4642
• /
• 2010

라텍스로 개질된 콘크리트는 높은 휨강도 뿐만아니라 부착강도 및 투수저항성이 좋은 재료특성을 제공한다. 이러한 이점을 활용한 초속경 라텍스개질 콘크리트(VES-LMC)에 관련된 연구결과는 재료에 관한 것이 대부분으로, VES-LMC로 덧씌우기 보강된 RC 보의 부착 경계면 거동특성에 대한 체계적인 연구는 미진하다. 따라서 본 논문에서는 VES-LMC로 보강된 철근콘크리트 보의 비선형 휨 거동에 대한 특성을 알아보고자 ABAQUS를 매개변수 연구를 수행한 결과 다음과 같은 결과를 얻을 수 있었다. 비선형 휨 해석을 위하여 본 논문에 적용된 모델의 적합성 여부를 확인한 결과 실험값과 비교적 유사한 경향을 보이는 것을 확인 할 수 있었다. 두께가 증가함에 따라 최대 저항강도가 증가하는 경향을 보여주었으며, 또한 강성 이 증가하여 내하력이 증진되는 결과를 확인할 수 있었다. 부착강도를 변수로 해석한 결과, 전단강도가 증가함에 따라 휨 저항능력이 향상되는 결과를 확인 하였으며, 두 이질재료의 부착능력이 구조물의 내하력에 지배적인 인자로 작용하는 것을 알 수 있었다.