• Resources Recycling
• /
• v.12 no.3
• /
• pp.46-53
• /
• 2003

Recycling of aluminum dross is an important issue in the secondary aluminum industries. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing alumina refractories. Sample dross was classified according to its size. The dross smaller than 1 mm was leached with sodium hydroxide solution to extract the remained aluminum from the dross into the solution. and then aluminum hydroxide precipitate was recovered from the leach liquor. The waste residue in the leaching was washed, dried and roasted. Most remained metallic components in the residue was changed into oxide through the processes. The roasted dross was made into alumina castable refractories by mixing with aggregates and a binder. Bending strength of the tested castable specimen was over $25\;kg/\textrm{m}^2$ and compressive strength over $80\;kg/\textrm{cm}^2$, which satisfied the Korean Standard value respectively. From the results, it was suggested that this process could be applicable to recycling of aluminum dross.

• Resources Recycling
• /
• v.5 no.1
• /
• pp.14-20
• /
• 1996

For recycl~ng alumhx~rn dross, the cbaraclcrislics of dross and ils reutll~zalin~af~te r plocsssing should he considered. Nurn~llumd ross was classified according to iB sire in this shldy. Tbe dross larger Illan 3001~1w as directly re-meltcd to recover aluminum, and the s~nallerd ~ossw as leachcd and riln~tedl o scparalc 111s eri~lerls alt and to oxidize the rnelals contained in the dross. As a rcwlt, amount of the dross uscd lo be dircarded ahcr processing could hc reduced Also, lhc chem~cal culnposit~ons of a domzstic alumlnum dross and the changes in con~posilii~ndsu ring processings were investigated. and Cound that most mctaU'ic aluminum in the dross was changed inlu alu~n~numox ide lhruugli the roasting. Tile processed dross would he ulillzed for malerials such as alumina, alumma cemenl or tilcs.

• Resources Recycling
• /
• v.10 no.5
• /
• pp.8-15
• /
• 2001

Aluminum dross should be recycled in consideration of characteristics of the dross and its reutilization after processing. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing aluminum hydroxide. Sample dross was classified according to its size. The dross smaller than $850\mu$m was leached with sodium hydroxide solution to extract the remaining aluminum from the dross into the solution, and then aluminum hydroxide precipitate was recovered (rom the leach liquor. Purity of the obtained aluminum hydroxide was above 98% and size of the sample was in range of $\3~39mu$m. Recovery of aluminum hydroxide precipitate was highest on condition that A/C ratio of the solution was 0.5 and pulp density was 14~16% at the leaching step. From the result, it was suggested that this process could be applicable to recycling of aluminum dross.

• Resources Recycling
• /
• v.26 no.5
• /
• pp.77-84
• /
• 2017

White and black dross are resulted from the recycling of aluminum. There are no established processes to recover valuable materials from black dross. Hydrometallurgical processes seem to be suitable for the treatment of aluminum dross. The salts in the black dross are recovered by dissolving with water. The residues are treated by either alkaline or acid leaching. Although the leaching rate of alumina by NaOH is lower than that by acid, its intermediates are more suitable to the production of alumina-based materials. The future direction for the treatment and recovery of valuable materials from aluminum dross is discussed.

• Resources Recycling
• /
• v.27 no.5
• /
• pp.61-68
• /
• 2018

The aluminum dross is oxide generated on the surface of the molten metal during the aluminum melting process and it is divided into white dross and black dross according to presence of the Salt flux. White dross has high metal content and is recycled via the melting process. Black dross is largely berried, because the it has a low metal content and difficulty in separating the components. Black dross contains a salt components such as NaCl and KCl, and inorganic materials such as $Al_2O_3$ and MgO, and it is necessary to study the technology to recover and recycle such valuable resources. In this study, a process for recycling aluminum black dross was proposed. The inorganic and soluble substances present in the black dross were separated through crushing-dissolution-solid/liquid separation-decompression evaporating. By controlling the ratio of water and black dross, the recovery condition of the separated product was optimized and we confirmed the highest Salt flux recovery efficiency 91 wt.% at black dross:water ratio 1:9. Finally, Through the synthesis of zeolite using recovered ceramic material, the materialization possibility of black dross was confirmed.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.216-216
• /
• 2015

용융아연 도금 공정에서 강판이 도금욕에 침적되는 동안 강판으로부터 용출되는 Fe는 도금욕 내 Al, Zn와 반응하여 다양한 형태의 드로스를 형성시키는 원인이 된다. 이들 드로스는 강판 표면에 다양한 형태의 결함을 야기하므로, 실제 도금 공정에서 도금욕 내 발생하는 드로스의 생성거동에 관한 이해는 필수적이다. 따라서 본 연구에서는 도금욕 내 $Fe_xAl_yZn_z$계 드로스 생성에 미치는 도금욕 내 Al 및 Fe 함량의 영향에 대해 고찰하였으며, in-situ sampling 기법 및 finger rotating method를 이용하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.10
• /
• pp.5919-5924
• /
• 2014

Accumulated dross adhered to the cutting support degrades the cutting accuracy and aggravates the working environment by reducing the efficiency of the dust collector. Furthermore, the cutting machine and product can be damaged by the scattering of molten metal. In this study, an attempt was made to increase the productivity of steel cutting process and improve the working environment by dross control. The dross adhesion characteristics were invested by a cutting experiment and the design concept for a dross removal machine was devised. Finally, a cutting support cleaning system and its operating algorithm were developed. The applicability of the developed system was examined and verified by a long-term field test after installation of the plasma arc cutting system of a shipyard.

• Resources Recycling
• /
• v.26 no.6
• /
• pp.58-64
• /
• 2017

Leaching of black dross with HCl solution was conducted to find a suitable process to recover valauble materials. In this work, the leaching behavior of the components was compared between black dross and the residues after water treatment. All the components except $TiO_2$ in the black dross were dissolved by HCl solution in the experimental ranges. Treatment of the black dross with water to recover the salts has negative effect on the leaching of $Al_2O_3$, MgO and $SiO_2$. The reactions occuring during the leaching were discussed. At an optimum leaching condition of 3 M HCl and $90^{\circ}C$, the leaching percentage of $Al_2O_3$, MgO and $SiO_2$ was 85, 100 and 40%, respectively.

• Resources Recycling
• /
• v.10 no.4
• /
• pp.42-47
• /
• 2001

Recycling of aluminum dross is a significant issue in domestic aluminum industry. In this study, formed ceramic materials were prepared using aluminum dross mixed with feldspar powders to investigate its application as industrial materials and utilization of aluminum dross. In the prepared sample, feldspar was melted at the sintered temperature, and its phase was trans-formed into amorphous, and spinel ($MgA1_2$$O_4$) phase in the dross was remained clearly. Density of the test specimen Increased from 0.91 to 0.65 gr/㎤ and water absorbance decreased from 2.5 to 1.7f% with increasing of sintered time at the sintered temperature $1220^{\circ}C$ with composition of feldspar 55 wt%, dross 40wt% and bentonite 5 wt%. At the same experimental conditions, bending strength of the test specimen was 10.8 MPa, and heat conductivity was 0.34 W/m.K with sintered time 30 minutes.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2001.05a
• /
• pp.409-411
• /
• 2001

(주)서울암면은 현무암, 안산암, 백운석등의 천연원료를 사용하는 기존 공정 대신에 제철소에서 발생하는 고로슬래그를 주원료로 이용하는 공정으로 암면을 제조하고 있다. 본 연구에서는 재활용율이 낮은 산업부산물인 전기로 슬래그, 폐주물사, 알루미늄 드로스 둥을 암면원료로 대체사용하는 기술을 개발하고자 하였다. 시험생산은 전기로슬래그와 석탄을 분체로 혼합한 브리켓트를 만들어, 기존원료의 많은 부분을 대체하여 큐폴라로에 장입하여 생산하였으며 폐주물사, 알루미늄 드로스 등의 첨가율도 조절하였다. 생산된 암면 제품은 한국공업규격인 KS F4701 암면 단열재 시험법에 규정된 규격을 만족하였다.