Preparation of Aluminum Hydroxide by Recycling of Aluminum Dross

알루미늄드로스로부터 수산화알루미늄 제조

Aluminum dross should be recycled in consideration of characteristics of the dross and its reutilization after processing. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing aluminum hydroxide. Sample dross was classified according to its size. The dross smaller than $850\mu$m was leached with sodium hydroxide solution to extract the remaining aluminum from the dross into the solution, and then aluminum hydroxide precipitate was recovered (rom the leach liquor. Purity of the obtained aluminum hydroxide was above 98% and size of the sample was in range of $\3~39mu$m. Recovery of aluminum hydroxide precipitate was highest on condition that A/C ratio of the solution was 0.5 and pulp density was 14~16% at the leaching step. From the result, it was suggested that this process could be applicable to recycling of aluminum dross.

알루미늄드로스는 드로스의 특성과 처리 후 용도를 고려하여 재활용하여야 한다. 본 연구에서는 국내 재생 알루미늄업체에서 발생된 알루미늄드로스를 수산화알루미늄의 원료로 재활용하고자 하였다. 드로스 시료를 크기에 따라 선별하고, $850mu$m 보다 작은 크기의 드로스를 수산화나트륨 용액으로 침출하여 드로스 중의 잔류 알루미늄을 용액 중으로 분리 추출하고, 침출용액에서 석출반응에 의하여 수산화알루미늄 침전물을 회수하였다. 시험 제조한 수산화알루미늄의 순도는 98% 이상이었고, 입경은 $3~39\mu$m 범위였다. 또한, 침출시 드로스의 장입량, NaOH 농도 및 광액농도가 수산화알루미늄의 회수율에 미치는 영향을 조사한 결과 폐드로스를 A/C비 0.5, 광액농도 14~16%로 침출하는 것이 석출시 회수율이 가장 높았다. 본 연구결과를 알루미늄드로스 재활용의 한 가지 방법으로 제안하고자 한다.