• Composites Research
• /
• v.17 no.6
• /
• pp.14-21
• /
• 2004

Failure process, mode and strength of unidirectional composite single lap bonded joints were investigated experimentally with respect to bonding methods, those are, co-curing with and without adhesive and secondary bonding. The co-cured joint specimens without adhesive had the largest failure strength. Progressive failures along the adhesive layer occurred in the secondary bonded specimens. In the co-cured specimens with adhesive film which had better material strength and adhesion performance, delamination failure occurred and the joint strengths were less than those of secondary bonded specimens. Delamination failure did not occur in the secondary bonded specimens because of earlier crack growth and progressive failure in the adhesive layer. Therefore, failure strength of composite bonded Joints were not always proportionate to material strength and adhesion performance of the adhesive due to the weakness of delamination in composite materials. The effects of surface roughness, bondline thickness and fillets were also studied on secondary bonded specimens.

• Composites Research
• /
• v.20 no.6
• /
• pp.8-14
• /
• 2007

Debonding failure characteristics of the composite skin-stiffener specimens were experimentally investigated. The influences of bonding methods, types of stiffener shape and various secondary bonding parameters were evaluated. Present test results combined with the previous test results[1] showed that the failure displacement of the skin-stiffener specimens well evaluates the skin-stiffener debonding failure strength of the composite stiffened panels. The specimens with an open type stiffener had lower bending stiffness and larger failure displacement than those with a closed type stiffener. Secondary bonding and co-curing with adhesive had better failure strength than co-curing without adhesive film. Secondary bonded specimens failed by adhesive failure and co-cured specimens failed by delamination failure. As the bondline thickness was thinner, the skin-stiffener specimens had higher failure strength. The fillets had no influence on failure strength of the specimens. The influence of the surface roughness was shown according to types of stiffener shape.

• Journal of Korea Ship Safrty Technology Authority
• /
• s.37
• /
• pp.2-11
• /
• 2014

본 연구에서는 최근, 전기자동차 및 소형 레저용 선박을 중심으로 연구가 진행 중인, 대용량 이차전지의 용량 증대를 위하여 필요한 내부 전극 접합 기술에 관하여 연구하였다. 종래의 초음파 용접으로 적층할 수 있는 적층량의 한계를 극복하기 위한 방안으로 전극 소재에 직접 가열을 통한 용접 방법이 아닌 용가제 금속을 적용하여 전극을 접합시켜, 통전성과 인장강도를 증대시킴과 동시에 열적요인으로 인한 전극표면에 화학적 활성물질의 변성을 최소화할 수 있는 저온 접합 방법에 대하여 연구하였다. 부연하여 용접을 위하여 무리하게 출력을 상승시킬 경우 용접열의 영향으로 전극의 변형 및 활성물질의 변성을 야기함과 동시에 최종 페키징 이후 출력저하, 발열 등, 배터리의 안정성을 저하시키는 요인으로 작용한다. 따라서 본 연구에서는 고주파 유도가열을 통한 유도 가열 방식의 접합 방법과 용융 도금을 통한 용가제 금속의 전처리를 통한 종래와는 차별화된 전극접합 방법을 소개한다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.3
• /
• pp.315-321
• /
• 2010

Co-cured single lap joints under cyclic tensile loads fail initially at the tip of the interface corner between the two adherents. The failure mechanism is complex because it is related to corrosion fatigue. Corrosion behavior at the interface affects the failure of the joints because corrosion deteriorates fatigue resistance. In this study, we clarified the cause of interfacial corrosion in co-cured single lap joints under cyclic tensile loads. The failure mechanism was also analyzed by observing the failed surfaces of specimens and the stress distribution along the interface. The surface roughness at the interface and the stacking sequence of the composite adherent were examined to investigate their effects on failure of the joint.

• Journal of the Korean Ceramic Society
• /
• v.37 no.10
• /
• pp.994-1000
• /
• 2000

Mn-Ni-Co계 스피넬을 모재로 선택하여 상업용 페라이트 등 다양한 종류의 Fe-스피넬과 동시 소결 가능성을 검토할 목적으로 각 소재의 소결 거동, 서미스터와의 계면 반응이나, 2차상의 형성 등에 대해 알아보았다. 대부분의 페라이트 조성이 Mn 스피넬과 새로운 2차상을 형성하지는 않는 것을 알 수 있었다. 상업용 페라이트의 경우 115$0^{\circ}C$ 소결 온도에서 접합이 가능한 조성은 다량의 액상이 존재하며 접합계면의 폭이 상대적으로 넓으므로 서미스터 특성에도 좋지 않은 영향을 줄 수 있을 것으로 생각된다. 반면에 MFN1과 MFN2 조성은 접합계면에서 새로운 2차상이 형성되지 않고 원소의 상호확산도 작아 NTC 서미스터의 동시소결용 보호재로서의 가능성이 높은 것으로 확인되었다.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.20 no.4
• /
• pp.833-839
• /
• 2016

In this paper, we propose a selective feature extraction algorithm between Markov transition probability and co-occurrence probability for an effective image splicing detection. The Features used in our method are composed of the difference values between DCT coefficients in the adjacent blocks and the value of Kullback-Leibler divergence(KLD) is calculated to evaluate the differences between the distribution of original image features and spliced image features. KLD value is an efficient measure for selecting Markov feature or Co-occurrence feature because KLD shows non-similarity of the two distributions. After training the extracted feature vectors using the SVM classifier, we determine whether the presence of the image splicing forgery. To verify our algorithm we used grid search and 6-folds cross-validation. Based on the experimental results it shows that the proposed method has good detection performance with a limited number of features compared to conventional methods.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.27-29
• /
• 2003

최근 레이저와 아크를 동시에 사용하여 용접 속도와 품질을 향상시킬 수 있는 하이브리드 용접 기술이 개발되어 활발히 연구가 진행되고 있다. 레이저와 아크를 동시에 사용하게 되면 각각의 열원이 서로 영향을 주어 새로운 용접 열원으로서 동작하게 되는데 특히 레이저에 의해서 발생하는 모재의 금속 증기는 아크 플라즈마의 안정화를 가져오는 것으로 알려져 있다. 또한 금속 증기 속의 이온과 전자가 아크 플라즈마의 음극점을 형성하는데 도움을 줌으로써 플라즈마의 국부적인 온도 상승을 가져오게 된다. 본 연구에서는 effective electrical potential 개념을 도입하여 이러한 현상을 해석하였고 용접 조건에 따른 플라즈마의 거동 변화를 시뮬레이션 하였다.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.10
• /
• pp.96-100
• /
• 1990

The cordierite ($2MgO,2Al_{2}O_{3},5SiO_{2}$) is of great interest for packaging substrates of multilayer IC. The Cu layer was fabricated on the cordierite substrate by the screen printing method and the adhesion properties of the interfaces at the different cosintering conditions were studied. When cosinted in the $Ar+H_{2}O$atmosphere good adhesion was obtained and the heating was found out to be an important factor for the adhesion.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.42-42
• /
• 2009

마찰교반접합 (Friction Stir Welding)은 1991년 영국 TWI에서 개발된 접합 법으로서 회전하는 툴이 재료내부에 삽입되면 툴과 재료사이에서 발생하는 마찰열에 의하여 온도가 상승하게 되어 재료는 연화되고, 이러한 재료 내부에서 회전하는 툴이 이동하게 되면 재료 내부는 기계적 교반에 의해 소성변형이 일어남과 동시에 접합이 이루어진다. 마찰교반접합은 동적 재결정에 의한 접합부의 미세한 결정립 형성으로 인하여 기계적 특성이 향상되며 보호 가스가 필요 없어 친환경적임과 동시에 용융 용접 법에 비해 접합 시 에너지 소모가 적으며 또한 접합 후 접합부에서의 변형이 상대적으로 적다는 장점이 있다. 이러한 장점을 가진 마찰교반접합은 알루미늄 합금, 마그네슘 합금 그리고 동 합금과 같은 저 융점 비철재료에 많은 연구와 적용 사례들이 있어왔다. 하지만 최근에는 일반 탄소강, 연강, 오스테나이트계 스테인리스강, 니켈 합금, 티타늄 합금과 같은 고융점 재료에도 연구 및 적용이 진행되고 있는 추세이다. 페라이트계 스테인리스강은 가격이 비싼 Ni을 함유하지 않아 오스테나이트계 스테인리스강에 비하여 강재의 가격은 낮으면서도 고온특성 및 내식성이 우수하여 건축용, 자동차 배기계용으로 널리 사용되고 있다. 하지만 이런 장점을 가진 페라이트계 스테인리스강을 기존의 용융 용접 법으로 접합 시 용접부 및 열영향부에서의 결정립의 조대화로 인한 인성 및 연성이 저하되며, 특히 예민화된 열영향부 입계 내에 Cr 탄화물이 석출되어 입계주변에 Cr 결핍 층을 형성되어 입계부식이 발생되는 문제점이 발생된다. 본 연구에서는 마찰교반접합을 이용하여 두께 3mm의 409 스테인리스강에 대해 맞대기 접합을 실시하였다. 접합 변수를 툴의 재료 (WC-12wt%Co, $Si_3N_4$)로 하여 접합을 실시하였고 접합 후 외관상태 점검, 광학 현미경과 주사 전자 현미경을 통하여 미세조직을 관찰하였으며 황산-황산동 부식 시험을 실시하여 접합부의 부식 특성을 평가하였다.

• Composites Research
• /
• v.18 no.1
• /
• pp.1-9
• /
• 2005

A methodology is presented for the failure prediction of composite single-lap bonded joints considering both of composite adherend failure and bondline failure. An elastic-perfectly plastic model of adhesive and a delamination failure criterion are used in the methodology. The failure predictions have been performed using finite element method and the proposed methodology. The failure prediction results such as failure mode and strength have very good agreements with the test results of joint specimens with various bonding methods and parameters. The influence of variations in the effective strength (that is, adhesion performance) and plastic behavior of adhesive on the failure characteristics of composite bonded Joints are investigated numerically. The numerical results show that optimal joint strength is archived when adhesive and delamination failure occur in the same time.