• Journal of the Korean Ceramic Society
• /
• v.41 no.7
• /
• pp.560-566
• /
• 2004

To fabricate the continuously porous alumina bodies by multi-extrusion process, carbon powder and ethylene vinyl acetate were used as a pore forming agent and a binder, respectively. As the change of extrusion pass number, reduction ratio as well as the volume fraction of core and tube, the porous alumina bodies having various kind of pore size and porosity could be obtained. The porous bodies showed continuous pore shape, high specific surface as well as high bending strength, which were compared with those of commercial alumina bodies. In-vitro study was carried out using MG-63 osteoblast cells to investigate of their biocompatibility. As a result, the cells grew well on top and bottom as well as inside surface of pore. From the result of in-vivo study of 3-dimensional porous alumina bodies using rats, it was confirmed that any inflammatory response was not found in the subcutaneous tissue around porous body. Also the porous bodies removed from the rats were fully covered with well-developed fibrous tissues and showed the formation of new capillary blood vessels.

• Journal of the Korean Ceramic Society
• /
• v.41 no.7
• /
• pp.541-547
• /
• 2004

Addition of large particles restrains densification by small particles in mixed particle systems. In the present study, large SiC whiskers or particles were introduced into small particles for restraining densification and the mixtures were sintered using yttrium aluminum garnet (Y$_3$A1$\sub$5/O$\sub$12/, YAG) as a sintering additive. By controlling the content of large SiC whiskers or particles and the applied pressure during sintering, porous SiC ceramics, with a porosity ranging from 0.3% to 39%, were fabricated. Porosity increased with increasing the content of restraining materials. SiC whiskers were more effective than large SiC partcles for restraining densification. Permeability of the porous SiC ceramics increased with increasing the porosity. Flexural strength decreased with increasing porosity. A noticeable increase in strain to failure was observed in the porous ceramics with a porosity ranging from 18% to 39%.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.57.1-57.1
• /
• 2012

금속을 용해 응고시킬 때 생성되는 소위, 주조 결함이나 소결금속 내의 기공은 재료의 성능이나 강도를 현저하게 낮추는 결함으로서 예전부터 기피되어 왔다. 또한, 재료공정에 있어서도 여하의 기공이나 기포가 없는 치밀한 고강도 및 고기능성 재료를 개발하는 것에 최대한의 주의와 관심을 기울여 왔다. 반면에 자연계의 천연물이나 인공물을 둘러보면 그 대부분이 다공질임을 쉽게 눈치챌 수 있다. 예를 들어 목재, 지엽 등의 생물을 시작해서 콘크리트 등의 인공물, 우리 체내의 뼈도 전형적인 다공질구조로 구성되어 있다. 이러한 구조로부터 재료의 재질제어 이외에 구조제어라는 새로운 어프로치를 고려할 수 있고, 최근 들어, 금속재료에 있어서도 이러한 다공질 구조에 관한 연구가 활성화되어 충격흡수재, 생체재료, 베어링재료 등의 다양한 응용이 전개되고 있다. 원주상의 방향성 기공을 갖는 로터스 금속의 제조 원리는 용융금속의 높은 가스용해도와 고체금속의 낮은 가스고용도의 차이를 이용하여 응고할 때 고용되지 않는 가스원자가 기포를 형성시키는 것이다. 수소용해도는 모든 금속에 있어서 온도상승에 따라 증가하지만 융점에 있어서 용해도의 불연속적 증가를 나타내며 응고할 때 고액계면에서 다량의 가스를 방출하고 기공 생성을 야기한다. 특히, 고 액상에 있어서 수소용해도 차가 큰 마그네슘, 니켈, 철, 동 등은 기포를 생성하기 쉽다. 또한 기공의 배열구조를 제어하기 위해 일방향응고법를 이용하여 기공에 방향성을 부여한다. 외관상 기공구조가 연근뿌리를 닮은 것으로 부터 로터스 금속이라는 명칭이 널리 알려져 있다. 이와 같은 제조방법에 의해 로터스 금속은 기공 방향, 기공크기, 기공률을 자유롭게 제어할 수 있고 우수한 기계적 성질이 기존의 발포금속, 소결금속과 전혀 다른 특성을 가지고 있다. 이러한 기공구조는 용해온도, 응고속도, 분위기 가스압, 불활성가스와의 혼합체적비 등의 제어를 통해서 조절할 수 있다. 이와 같이 제조한 방향성 다공질금속은 BT (인플란트, 생체적합성, 저탄성, 경량), ST (초음속기엔진부품, 경량), IT (고성능수냉모듈), ET(고온촉매, 필터)의 분야로의 응용을 기대한다.

• The Journal of the Petrological Society of Korea
• /
• v.26 no.2
• /
• pp.143-152
• /
• 2017

As weathering processes, micro-cavities are formed on the surface of rocks, and in particular, the porous structure is increased in feldspar. Adsorption and antibacterial tests were carried out to clarify the environmental function of porous feldspar porphyry. Almost all the heavy metals were adsorbed in the feldspar filter and the adsorption rate could be controlled by changing the filter length. The shake flask method of fabric coated with 5% and 7% feldspar powder showed very high antibacterial activity of 98% and 99.9%, respectively. The cation exchange capacity at a particle size of $10{\mu}m$ was 114.63 meq/100g probably due to the porous structure. The potential value of porous feldspar porphyry as a resource is sufficient based on the results of the experiment.

• Journal of the Korean Vacuum Society
• /
• v.6 no.3
• /
• pp.242-248
• /
• 1997

Porous silicons were prepared by dry etching as well as by chemical etching. The latter is a conventional method used by many researchers. Meanwhile, the former is a new method we developed. Also the porous silicon structure was made by E-beam lithography technique. However, due to the limit of this technique, minimum size we could produce was about 0.3 $\mu\textrm{m}$ in diameter on silicon wafer. In a new method, the porous silicon microstructure was fabricated by using Reactive Ion Etching method after covering with diamond powder on 4 inch wafer by using spin coater. In this method, diamond powder acted as a mask. The morphology of samples prepared under many different conditions were analysed be SEM and AFM. And we measured PL spectra for the samples. Based on these results, we observed the structure of a few hundreds $\AA$ in size from porous silicon which was made by dry etching with diamond powder. Also the PL peak for these samples lied around 590 nm compared to 760 nm for chemically etched porous silicon.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.1
• /
• pp.124-130
• /
• 1998

The Raman scattering was studied from the porous silicons which were made by changing anodization current. As the current density was increased, it was observed that Raman was gradually far from the value of 520.5 $\textrm{cm}^{-1}$ and the full width half maximum increased. The decrease of radius of cylindrical porous crystal was calculated and the increase of its length was investigated through AFM.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.11a
• /
• pp.446-461
• /
• 2005

본 연구에서는 반응소결 탄화규소 다공질 지지체 개발을 위하여 SiC/C로 이루어진 성형체를 사용한 Si melt infiltration 공정 및 SiC/C/Si으로 이루어진 성형체를 사용하는 Si embedding 공정 개발이 이루어졌다. 개발된 반응소결 탄화규소 다공질 지지체의 기공률은 38% 이상이었으며 평균기공은 130 ${\mu}m$ 크기이었다. Si melt infiltration 방법으로 제조된 반응소결 탄화규소 다공질 지지체의 파괴강도는 상용 반응소결 탄화규소 지지체의 파괴강도보다 최대 200% 이상 높게 나타났다. 본 연구에서는 용융 Si의 침윤공정을 이용하여 반응소결 탄화규소 여과층을 갖는 반응소결 탄화규소 필터 및 그 제조공정이 개발되었다. 개발된 반응소결 탄화규소 필터의 필터 특성은 상용 탄화규소 필터의 필터 특성과 대체적으로 대등한 것으로 조사되었다.

• Journal of Energy Engineering
• /
• v.10 no.3
• /
• pp.266-271
• /
• 2001

Buoyancy-driven natural convection is analysed by employing a linear stability theory in hori-zontal porous media with net through flow. Darcy's law is used to model the flow characteristics in porous media. Bated on the results of linear stability analysis, a heat transfer correlation was obtained by employing weakly nonlinear analysis. As the net through flow increases, the system becomes more stable and the effect of the Darcy-Rayleigh number on the Nusselt number decreases.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1760-1762
• /
• 2000

본 논문은 기존의 $Si_{3}N_4$, SiN 물질 대신 Pt를 사용해 HF 용액속에서 다공질 실리콘과 전극을 동시에 형성하는 기술을 개발하였다. Pt를 실리콘 웨이퍼 위에 직접 증착한 후 습식 에칭과 Lift-off 공정을 사용하여 Pt를 패터닝하였다. 습식 에칭은 에칭용액의 온도를 일정하게 유지하는 것이 중요하며, 증착한 Pt 박막이 BOE 에칭에 견디고, Lift-off 공정이 가능하기 위해서는 기판온도를 l100$^{\circ}C$ 이하로 해야한다. Pt를 사용하면 기존의 mask에서 발생하는 가장자리 부분에서의 전류 집중이 방지되기 때문에 다공질 실리콘이 일정한 깊이로 형성되고, Al대신 오믹 전극으로 사용할 수 있다. 현재 Pt를 mask와 전극으로 이용한 P-I-N UV detector, 광 바이오센서, 습도센서 제작등에 응용 연구가 진행되고 있다.

• Solar Energy
• /
• v.15 no.1
• /
• pp.39-51
• /
• 1995

A numerical scheme based on a coordinate transform into stream function-velocity potential is proposed to solve heat and momentum transfer in porous media with phase change. A significant simplification of both computational domain and governing equations can be achieved by the transform. The dispersion term in the flow through porous media, which is important at the phase change interface, can be successfully incorporated into the numerical scheme without introducing any further computational complications.