• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1061-1065
• /
• 1999

The effect of particle size of coating powder and coating temperature on the thickness of coating layer formed on metal surface was studied by using XRD, SEM and EDXS. Coating powder was separated according to particle size by 3 steps and coating temperatures were varied from $950^{\circ}C$ to $980^{\circ}C$. Calorizing carried out at air and Ar conditions for 5 hrs, respectively. XRD result show that $Al_2O_3$ and AlN were formed during calorizing at air condition. The thickness and Al content of coating layer increased as the particle size of coating powder decreased and coating temperature increased.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.568-568
• /
• 2012

뛰어난 물리적, 전기적 특성을 가진 단일벽 탄소나노튜브는 여러 분야에서 응용 가능성이 매우 높은 물질이다. 그러나 단일벽 탄소나노튜브의 전기적 특성은 나노튜브의 직경과 카이랄리티(chirality)에 매우 강하게 의존되기 때문에 균일한 직경과 카이랄리티를 갖는 단일벽 탄소나노 튜브만의 사용은 나노튜브 기반의 전자소자 응용에서 매우 중요하다. 균일한 직경과 카이랄리티의 단일벽 탄소나노튜브를 얻는 방법은 나노튜브 합성을 통한 직접적인 방법과 후처리 기술을 통해 가능하며, 최근에는 금속 나노입자를 촉매로서 화학기상증착(Chemical vapor deposition, CVD)을 이용하여 좁은 직경 분포를 갖는 단일벽 탄소나노튜브의 합성이 보고되었다. 화학기상 증착은 용이하게 단일벽 탄소나노튜브를 합성하며, 성장된 나노튜브의 직경은 촉매금속 나노입자의 크기에 의해 결정된다. 본 연구는 크기가 제어된 산화철 나노입자를 촉매금속으로 사용하여 열화학기상증착법을 이용해 직경분포가 매우 좁고 균일한 단일벽 탄소나노튜브를 합성하였다. 합성된 단일벽 탄소나노튜브 직경과 카이랄리티는 라만 분광법(Raman spectroscopy)과 투과 전자현미경(Transmission electron microscope)을 이용하여 분석하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.191-191
• /
• 2013

금속 산화물 촉매 입자는 특정한 파장에 의해서 활성화되면서 전자-정공 쌍을 생성한다. 광촉매원리를 이용하면 전자 정공 제공을 통해 기존의 물질 주위에 활성 라디칼을 생성하고 물질의 특성을 변화시킬 수 있다. 이런 독특한 특성을 이용한 금속산화물의 다양한 연구가 물리, 화학, 재료, 생명 분야에서 이루어지고 있다. 본 연구에서는 광촉매 입자와 대기압 플라즈마와의 특성을 활용하여 발생되는 물리적 특성과 재료적인 특성을 이용한 응용 연구에 대한 내용을 다루고 있다. 특히 광촉매로 가장 많이 사용되는 $TiO_2$가 $200^{\circ}C$ 이하 저온 플라즈마 방전가스에 의해 상변화되는 현상을 다루고 이에 대한 구체적인 재료 분석을 실시 하였다. 즉, 저온의 알곤과 알곤/산소 대기압 플라즈마에 의해 처리된 $TiO_2$의 결정성 변화에 대해서 조사하였고 이를 이용하여 유사 작용제의 분해에 대한 연구를 하였다. 신경작용제(VX: nerve agent)의 유사작용제인 말라치온(Malathion)뿐만 아니라 셀룰로우즈(cellulose) 계의 복잡한 구조의 화학유기물 등을 대기압 플라즈마를 이용해 분해시킬 수 있음을 알 수 있었다. 본 연구에서는 대기압 플라즈마와 금속산화물의 결정성 변화에 대한 분석을 통해 기능성화된 촉매입자를 이용한 효과적인 화학물질의 분해를 소개하고, 대기압 플라즈마의 나노 소재기술로의 높은 응용가능성도 함께 살펴보았다.

• Composites Research
• /
• v.13 no.1
• /
• pp.50-60
• /
• 2000

This paper presents an analytical method considering tensile strength enhancement in hybrid $Al_2O_3$ fiber/particle/aluminum composites(MMCs). The tensile strength and elastic modulus of the hybrid MMCs are even 20% higher than those of the fiber reinforced MMCs with same volume fraction of reinforcements. This phenomenon is explained by the cluster model which is newly proposed in this research, and the strengthening mechanisms by a cluster is analyzed using simple modified rule of mixtures. From the analysis, it is observed that cluster structure in hybrid MMCs increase the fiber efficiency factor for the tensile strength and the orientation factor for the elastic modulus. The present theory is then compared with experimental results which was performed using squeeze infiltrated hybrid MMCs made of hybrid $Al_2O_3$ short fiber/particle preform and AC8A alloy as base metal, and the agreement is found to be satisfactory.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.301-301
• /
• 2011

최근 고밀도 메모리 반도체의 재료와 빠른 응답을 요구하는 나노입자를 이용한 비휘발성 메모리 소자의 제작에 대한 연구가 활발히 진행되고 있다. 그에 따른 기존의 플래쉬 메모리가 가지는 문제점을 개선하기 위해서 균일하고 규칙적으로 분포하는 새로운 나노소재의 개발과 비휘발성, 고속 동작, 고집적도, 저전력 소자의 공정기술이 요구되고 있다. 또한 부유게이트에 축적되는 저장되는 전하량을 증가시키기 위한 새로운 소자구조 개발이 필요하다. 한편, 실리 사이드 계열의 나노입자는 금속 나노입자와 달리 현 실리콘 기반의 반도체 공정에서 장점을 가지고 있다. 따라서 본 연구에서는 화합물 중에서 비휘발성 메모리 장치의 전기적 특성을 향상 시킬 수 있는 실리사이드 계열의 바나듐 실리사이드(V3Si) 박막을 열처리 과정을 통하여 수 nm 크기의 나노입자로 제작하였다. 소자의 제작은 p-Si기판에 실리콘산화막 터널층(5 nm 두께)을 건식 산화법으로 성장 후, 바나듐 실리사이드 금속박막을 RF 마그네트론 스퍼터 시스템을 이용하여 4~6 nm 두께로 터널 베리어 위에 증착하고, 그 위에 초고진공 마그네트론 스퍼터링을 이용하여 SiO2 컨트롤 산화막층 (20 nm)을 형성시켰다. 여기서 V3Si 나노입자 형성을 위해 급속 열처리법으로 질소 분위기에서 800$^{\circ}C$로 5초 동안 열처리하여 하였으며, 마지막으로 열 기화 시스템을 통하여 알루미늄 전극(직경 200 ${\mu}m$, 두께 200 nm)을 증착하여 소자를 제작하였다. 제작된 구조는 금속 산화막 반도체구조를 가지는 나노 부유게이트 커패시터이며, 제작된 시편은 투사전자현미경을 이용하여 나노입자의 크기와 균일성을 확인했다. 소자의 전기적인 측정을 E4980A capacitor parameter analyzer와 Agilent 81104A pulse pattern generator system을 이용한 전기용량-전압 측정을 통해 전하저장 효과 및 메모리 동작 특성들을 분석하고, 열처리 조건에 따라 형성되는 V3Si 의 조성을 엑스선 광전자 분광법을 이용하여 확인하였다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.822-828
• /
• 2001

Bayer process is based on the extraction of aluminium trihydroxide from bauxite. The process is operated with the several criteria such as primary crystal size, particle size distribution and yield etc.. In this study basing on the previous results, an investigation on the effect of chemical grade and smelting grade aluminium trihydroxide precipitation condition were undertaken. As a result, particle size was 42∼44${\mu}$m form chemical grade product and 74∼77${\mu}$m for smelting grade product. The yield and solubility by acid of chemical grade product was higher than smelting grade product. The attrition index of smelting grade product was lower than that of other commercial product because primary crystal size of the smelting grade product was small.

• Applied Chemistry for Engineering
• /
• v.31 no.6
• /
• pp.591-595
• /
• 2020

Intensive pulsed light (IPL) technique enables energy to be transferred to a target substance in a short time per millisecond at room temperature under an ambient atmosphere. Due to the growing interest in flashlights with excellent functionality among various technologies, light-sintering research on metal particles using IPL has been carried out representatively. Recently, examples of the application of IPL to various material synthesis have been reported. In the present article, various strategies using IPL including the manufacture of flexible electrodes and the synthesis of metal-organic frameworks were discussed. In particular, the process of improving oxidation resistance and electrical conductivity of electrodes, and also the metal-organic framework synthesis from metal surface were explained in detail. We envision that the review article can be of great help to researchers who investigate electrode manufacturing and material synthesis using IPL.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.447-447
• /
• 2013

최근 전자산업의 발전으로 차세대 디스플레이 소자로 산화물반도체가 주목받고 있다. 산화물 반도체는 저온공정, 높은 이동도 및 투과율을 가지기 때문에 이러한 공정이나 물성 측면에 있어 기존의 a-Si, LTPS 등을 대채할 만한 소자로서 연구가 활발이 이루어지고 있다. 특히 고해상도 및 고속구동이 진행됨에 따라 높은 이동도의 필요성이 대두되고 있다. 본 연구에서는 IGZO 산화물 반도체 박막트랜지스터의 이동도 개선을 위해 나노입자를 사용하였다. 게이트전극으로 사용된 Heaviliy doped P-type Si 기판위에 200 nm의 SiO2 절연층을 성장시킨 후, 채널로 작동하기 위한 IGZO 박막을 증착하기 전에 10~20 nm 크기의 니켈, 금 나노입자를 부착시켰다. 열처리 온도는 $350^{\circ}C$, 90분동안 진행하였고, 100 nm의 알루미늄 전극을 증착시켜 TFT 소자를 제작하였다. TFT 소자가 동작할 시, IGZO 박막 내부의 전자들은 게이트 전압으로 인해 하부로 이동하여 채널을 형성, 동시에 드레인 전압으로 인한 캐리어들의 움직임으로 인해 소자가 동작하게 된다. 본 연구에서는 채널이 형성되는 계면 부근에 전도성이 높은 금속 나노입자를 부착시켜 다수 캐리어인 전자가 채널을 통과할 때 전류흐름에 금속 나노입자들이 기여하여 전기적 특성의 변화에 어떠한 영향을 주는지 연구하였다. 반응시간을 조절하여 기판에 붙는 나노입자의 밀도 변화에 따른 특성과 다양한 크기(5, 10, 20 nm)를 갖는 금, 니켈 나노입자를 포함한 IGZO TFTs 소자를 제작하여 전달특성, 출력특성의 변화를 비교하였고, 실질적인 채널길이의 감소효율과 캐리어 이동도의 변화를 비교분석 하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.133-133
• /
• 2011

최근 나노입자를 이용한 비휘발성 메모리 소자의 제작에 대한 연구가 진행되고 있다. 특히, 실리사이드 계열의 나노입자를 적용한 소자는 일함수가 크지만 실리콘 내의확산 문제를 가지고 있는 금속 나노입자와 달리 현 실리콘 기반의 반도체 공정 적용이 용이한 잇 점을 가지고 있다. 따라서 본 연구에서는 실리사이드 계열의 화합물 중에서 4.63 eV인 Vanadium Silicide ($V_3$Si) 박막을 열처리 과정을 통하여 수 nm 크기의 나노입자로 제작하였다. 소자의 제작은 p-Si기판에 5 nm 두께의 $SiO_2$ 터널층을 dry oxidation 방법으로 성장시킨 후 $V_3$Si 금속박막을 RF magnetron sputtering system을 이용하여 3~5 nm 두께로 tunnel barrier위에 증착시켰다. Rapid thermal annealing법으로 질소 분위기에서 $1000^{\circ}C$의 온도로 30초 동안 열처리하여 $V_3$Si 나노 입자를 형성 하였으며. 20 nm 두께의 $SiO_2$ 컨트롤 산화막층을 ultra-high vacuum magnetron sputtering을 이용하여 증착하였다. 마지막으로 thermal evaporation system을 통하여 Al 전극을 직경 200, 두께 200nm로 증착하였다. 제작된 구조는 metal-oxide-semiconductor구조를 가지는 나노 부유 게이트 커패시터 이며, 제작된 시편은 transmission electron microscopy을 이용하여 $V_3$Si 나노입자의 크기와 균일성을 확인했다. 소자의 전기적인 측정은 E4980A capacitor parameter analyzer와 Agilent 81104A apulse pattern generator system을 이용한 전기용량-전압 측정을 통해 전하저장 효과를 분석하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.367.1-367.1
• /
• 2016

투명 전극은 유기 발광소자, 태양전지, 센서와 같은 다양한 분야에 응용되고 있으며, indium-tin-oxide(ITO)는 현재 다양한 소자의 투명 전극으로 가장 많이 사용하고 있다. 그러나 높은 가격과 유연성이 좋지 않은 ITO 소재를 대체하는 기술로 현재 금속 나노와이어를 사용하려는 시도가 진행되고 있다. 금속 나노 와이어 투명전극은 높은 전도성, 높은 광학적 투과율, 간단한 공정, 우수한 유연성 및 열 안정성의 장점을 가지고 있어 플렉서블 소자에 응용 가능성을 보여주고 있다. 본 연구에서는 금속 나노와이어 투명전극 기판 제작 방법과 이를 이용한 유기 쌍안정 메모리 소자의 전기적 특성을 관찰하였다. 세척한 PET 기판 위에 금속 나노와이어를 스핀코팅 방법으로 분산하고, 그 위에 금속 나노와이어의 표면 거칠기와 전도성을 증진하기 위해 PEDOT:PSS 층을 스핀코팅하여 플렉서블 투명전극을 제작하였다. 플렉서블 금속 나노와이어 투명전극 기판을 하부 전극으로 사용하고, 그 위에 금 나노입자가 포함된 유기물 층을 다시 한번 스핀코팅 방식으로 적층하였다. 마지막으로 알루미늄 상부 전극을 열 증착하여 비휘발성 메모리 소자를 제작하였다. 이렇게 제작된 소자의 전류-전압 측정 결과는 높은 전도도와 낮은 전도도의 차이를 갖는 전기적 특성을 확인할 수 있다.